MX360240B - Lámina de acero para miembro estampado en caliente y método para producirla. - Google Patents

Lámina de acero para miembro estampado en caliente y método para producirla.

Info

Publication number
MX360240B
MX360240B MX2013010601A MX2013010601A MX360240B MX 360240 B MX360240 B MX 360240B MX 2013010601 A MX2013010601 A MX 2013010601A MX 2013010601 A MX2013010601 A MX 2013010601A MX 360240 B MX360240 B MX 360240B
Authority
MX
Mexico
Prior art keywords
steel plate
steel
hot
produce
seconds
Prior art date
Application number
MX2013010601A
Other languages
English (en)
Other versions
MX2013010601A (es
Inventor
Maki Jun
Tanahashi Hiroyuki
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2013010601A publication Critical patent/MX2013010601A/es
Publication of MX360240B publication Critical patent/MX360240B/es

Abstract

Se proporciona una placa de acero para proporcionar miembros por estampado en caliente, los miembros tienen propiedades de fatiga excelentes iguales a las de las placas de acero de alta resistencia ordinarias que tienen la misma resistencia que la placa de acero. También se proporciona un proceso para producir la placa de acero. La placa de acero para miembros estampados en caliente, contiene, en términos de % en masa, 0.15-0.35% de C, 0.01-1.0% de Si, 0.3-2.3 de Mn, y 0.01-0.5% de Al, con el resto comprendiendo Fe e impurezas inevitables, en donde las impurezas comprenden hasta 0.03% de P, hasta 0.02% de S, y hasta 0.1% de N como componentes químicos. La placa de acero se caracteriza porque la dureza de Vicker de la placa de acero medida en sitios ubicados a una distancia de 20 µm desde una superficie de la placa de acero hacia la dirección de espesor de la placa tiene una desviación estándar de 20 o menos. Esta placa de acero se produce a través de una etapa de recocido por recristalización que comprende: una primera fase en la cual una placa de acero laminada en frío obtenida por laminación en caliente y después de laminar en frío un acero que contiene los componentes químicos se calienta de la temperatura ambiente a 600-700°C en una proporción de calentamiento promedio de 8-25°C/segundos; y una segunda fase en la cual la placa de acero se calienta con éxito a 720-820°C en una proporción de calentamiento promedio de 1-7°C/segundos.
MX2013010601A 2011-03-18 2012-03-16 Lámina de acero para miembro estampado en caliente y método para producirla. MX360240B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011060893 2011-03-18
PCT/JP2012/056917 WO2012128225A1 (ja) 2011-03-18 2012-03-16 ホットスタンプ部材用鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2013010601A MX2013010601A (es) 2013-10-01
MX360240B true MX360240B (es) 2018-10-26

Family

ID=46879372

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2013010601A MX360240B (es) 2011-03-18 2012-03-16 Lámina de acero para miembro estampado en caliente y método para producirla.

Country Status (11)

Country Link
US (1) US20140004378A1 (es)
EP (1) EP2687620A4 (es)
JP (1) JP5605503B2 (es)
KR (1) KR20130126714A (es)
CN (1) CN103443317A (es)
BR (1) BR112013023792A2 (es)
CA (1) CA2829327C (es)
MX (1) MX360240B (es)
RU (1) RU2560890C2 (es)
WO (1) WO2012128225A1 (es)
ZA (1) ZA201307377B (es)

Families Citing this family (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL2703511T3 (pl) * 2011-04-27 2018-10-31 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka na elementy wytłaczane na gorąco i sposób jej wytwarzania
CN103103453B (zh) * 2013-02-18 2015-02-04 无锡市派克重型铸锻有限公司 一种核电管道件材料锻件及制造工艺
CN103173691B (zh) * 2013-02-18 2014-12-10 无锡市派克重型铸锻有限公司 一种升船机安全机构锁定块及其制造工艺
CA2904122C (en) * 2013-03-14 2018-07-10 Nippon Steel & Sumitomo Metal Corporation High strength steel sheet excellent in delayed fracture resistance and low temperature toughness, and high strength member manufactured using the same
KR101568549B1 (ko) * 2013-12-25 2015-11-11 주식회사 포스코 우수한 굽힘성 및 초고강도를 갖는 열간 프레스 성형품용 강판, 이를 이용한 열간 프레스 성형품 및 이들의 제조방법
JP6269079B2 (ja) * 2014-01-14 2018-01-31 新日鐵住金株式会社 ホットスタンプ用鋼板およびその製造方法
BR112016018119B8 (pt) * 2014-02-05 2020-12-15 Arcelormittal S A chapa de aço, método para produzir uma chapa de aço e uso de uma chapa de aço
EP3128017A4 (en) 2014-03-31 2017-10-04 Nippon Steel & Sumitomo Metal Corporation Hot-stamped steel material
US10308996B2 (en) 2015-07-30 2019-06-04 Hyundai Motor Company Hot stamping steel and producing method thereof
JP6508176B2 (ja) * 2016-03-29 2019-05-08 Ｊｆｅスチール株式会社 ホットプレス部材およびその製造方法
RU2654093C2 (ru) * 2016-05-23 2018-05-16 Открытое акционерное общество "Магнитогорский металлургический комбинат" Высокопрочная высокотвердая сталь и способ производства листов из нее
BR112019016673A2 (pt) * 2017-02-20 2020-04-14 Nippon Steel Corporation chapa de aço
BR112019016858A2 (pt) * 2017-02-20 2020-04-07 Nippon Steel Corporation corpo estampado a quente
CA3053661A1 (en) * 2017-02-20 2018-08-23 Nippon Steel Corporation Hot stamped body
US11591675B2 (en) 2017-02-20 2023-02-28 Nippon Steel Corporation Steel sheet and method for producing same
US20200001342A1 (en) * 2017-02-20 2020-01-02 Nippon Steel Corporation Hot stamped body
CN107881415B (zh) * 2017-11-15 2019-09-27 东北大学 一种耐高温磨损钢板及其制造方法
CN113891952A (zh) * 2019-05-28 2022-01-04 塔塔钢铁艾默伊登有限责任公司 用于生产热冲压零件的钢带材、片材或坯料，零件以及将坯料热冲压成零件的方法
US12311427B2 (en) * 2020-02-26 2025-05-27 Nippon Steel Corporation Method of manufacturing overlapped hot stamp molded body, and overlapped hot stamp molded body
CN115667571B (zh) * 2020-08-20 2024-12-03 日本制铁株式会社 热压部件
CN112226690B (zh) * 2020-09-30 2022-02-15 鞍钢股份有限公司 1800MPa级热冲压车轮轮辋用酸洗钢板及其制造方法
CN112251669B (zh) * 2020-09-30 2022-02-18 鞍钢股份有限公司 2000MPa级热冲压车轮轮辐用热轧钢板及其制造方法
CN112226691B (zh) * 2020-09-30 2022-02-15 鞍钢股份有限公司 1800MPa级热冲压车轮轮辐用热轧钢板及其制造方法
CN112267065B (zh) * 2020-09-30 2022-02-15 鞍钢股份有限公司 2000MPa级热冲压车轮轮辋用酸洗钢板及其制造方法
CN112267066B (zh) * 2020-09-30 2022-02-15 鞍钢股份有限公司 1800MPa级热冲压车轮轮辋用热轧钢板及其制造方法
CN112267067B (zh) * 2020-09-30 2022-02-18 鞍钢股份有限公司 2000MPa级热冲压车轮轮辋用热轧钢板及其制造方法
EP4273281A4 (en) * 2021-02-10 2024-06-05 Nippon Steel Corporation HOT STAMPED MOLDED BODY
CN115141985B (zh) * 2021-03-31 2023-05-09 宝山钢铁股份有限公司 一种高淬透性中碳高钛含硼钢及其板坯连铸生产方法
WO2022239866A1 (ja) * 2021-05-13 2022-11-17 日本製鉄株式会社 ホットスタンプ用鋼板及びホットスタンプ成形品
WO2023079344A1 (en) * 2021-11-05 2023-05-11 Arcelormittal Method for producing a steel sheet having excellent processability before hot forming, steel sheet, process to manufacture a hot stamped part and hot stamped part
KR20240027174A (ko) * 2022-08-22 2024-03-04 주식회사 포스코 표면품질이 우수한 열간 성형용 냉연강판, 열간 성형 부재 및 그들의 제조방법
KR102883695B1 (ko) * 2022-12-20 2025-11-10 주식회사 포스코 냉연강판 및 그 제조방법
CN120945284B (zh) * 2025-09-16 2026-04-28 暨南大学 一种选区激光熔化成形超高强韧低合金钢及其制备方法与应用

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU1032039A1 (ru) * 1982-02-04 1983-07-30 Физико-технический институт АН БССР Штампова сталь
JP2859270B2 (ja) 1987-06-11 1999-02-17 旭光学工業株式会社 カメラの視線方向検出装置
JPH07967B2 (ja) 1987-08-04 1995-01-11 ワイケイケイ株式会社 自動ドアの制御方法
CA2336373C (en) * 1999-02-22 2007-02-27 Nippon Steel Corporation High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof
WO2002055751A1 (en) * 2000-12-29 2002-07-18 Nippon Steel Corporation High-strength molten-zinc-plated steel plate excellent in deposit adhesion and suitability for press forming and process for producing the same
JP3582512B2 (ja) * 2001-11-07 2004-10-27 住友金属工業株式会社 熱間プレス用鋼板およびその製造方法
KR100646619B1 (ko) * 2001-10-23 2006-11-23 수미도모 메탈 인더스트리즈, 리미티드 열간 프레스 방법, 이를 위한 도금 강철재 및 이의 제조방법
JP3582511B2 (ja) * 2001-10-23 2004-10-27 住友金属工業株式会社 熱間プレス成形用表面処理鋼とその製造方法
US8021497B2 (en) * 2003-07-29 2011-09-20 Voestalpine Stahl Gmbh Method for producing a hardened steel part
US7906220B2 (en) * 2003-09-29 2011-03-15 Nisshin Steel Co., Ltd. Steel/aluminum welded structure
JP2005200670A (ja) 2004-01-13 2005-07-28 Nippon Steel Corp 高強度部品の製造方法
JP4673558B2 (ja) 2004-01-26 2011-04-20 新日本製鐵株式会社 生産性に優れた熱間プレス成形方法及び自動車用部材
JP4449795B2 (ja) * 2005-03-22 2010-04-14 住友金属工業株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
JP4464864B2 (ja) * 2005-04-27 2010-05-19 株式会社神戸製鋼所 耐結晶粒粗大化特性と冷間加工性に優れた軟化焼鈍の省略可能な肌焼用鋼
JP4728710B2 (ja) * 2005-07-01 2011-07-20 新日本製鐵株式会社 加工性に優れる熱延鋼板およびその製造方法
US20080286603A1 (en) * 2005-12-01 2008-11-20 Posco Steel Sheet for Hot Press Forming Having Excellent Heat Treatment and Impact Property, Hot Press Parts Made of It and the Method for Manufacturing Thereof
JP4733522B2 (ja) 2006-01-06 2011-07-27 新日本製鐵株式会社 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法
JP4833698B2 (ja) 2006-03-16 2011-12-07 新日本製鐵株式会社 ダイクエンチ用高強度鋼板
JP4725415B2 (ja) * 2006-05-23 2011-07-13 住友金属工業株式会社 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5499560B2 (ja) * 2009-08-12 2014-05-21 Ｊｆｅスチール株式会社 成形性と耐ねじり疲労特性に優れた自動車足回り部材用高張力鋼材及びその製造方法
JP5644094B2 (ja) * 2009-11-30 2014-12-24 新日鐵住金株式会社 延性及び曲げ性の良好な引張最大応力９００ＭＰａ以上を有する高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法

Also Published As

Publication number Publication date
EP2687620A4 (en) 2014-10-15
WO2012128225A1 (ja) 2012-09-27
EP2687620A1 (en) 2014-01-22
KR20130126714A (ko) 2013-11-20
CA2829327A1 (en) 2012-09-27
BR112013023792A2 (pt) 2016-12-06
RU2560890C2 (ru) 2015-08-20
JPWO2012128225A1 (ja) 2014-07-24
US20140004378A1 (en) 2014-01-02
CN103443317A (zh) 2013-12-11
MX2013010601A (es) 2013-10-01
CA2829327C (en) 2017-02-14
ZA201307377B (en) 2014-06-25
JP5605503B2 (ja) 2014-10-15
RU2013146540A (ru) 2015-04-27

Similar Documents

Publication Publication Date Title
BR112018010370A2 (pt) método para produzir uma chapa de aço elétrica não orientada
MX368319B (es) Método de fabricación y método para miembro conformado por prensado en caliente.
MX2017000188A (es) Metodo para producir una hoja de acero revestida o no revestida de resistencia ultra alta y hoja obtenida por dicho metodo.
MX359051B (es) Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente.
BR112015017719A2 (pt) método para produzir folha de aço elétrico de grão orientado
MX363038B (es) Metodo para producir hoja de acero laminada en frio.
BR112013023792A2 (pt) chapa de aço para elemento gravado a quente e método de produção da mesma
IN2015DN00613A (es)
MX2015011022A (es) Metodo para la produccion de lamina de acero electrico de grano orientado.
MX2018006621A (es) Metodo para producir lamina de acero electrico de grano orientado.
MX2018007645A (es) Metodo para producir una hoja de acero de alta fuerza que tiene ductilidad y formabilidad mejoradas y hoja de acero obtenida.
MX378125B (es) Método de fabricación de hoja de acero galvanizado para estampación en caliente, hoja de acero galvanizado y recocido por inmersión en caliente para estampación en caliente y método de fabricación de las mismas, y componente estampado en caliente.
MX378759B (es) Lámina de acero eléctrico de grano no orientado y método para la producción de la misma, y núcleo de motor y método para la producción del mismo.
MX2017000177A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia, ductilidad y capacidad de formacion mejoradas.
BR112014015514B8 (pt) processo de fabricação de uma tira de liga magnética leve, tira de liga magnética leve e processo para fabricar um componente magnético
MX2016013771A (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
MX347081B (es) Método para fabricar una lámina de acero eléctrico de grano orientado..
GB2437955A (en) Method for producing hot-formed steel product
BR112018009722A2 (pt) método para produção de uma chapa de aço elétrica não orientada
BR112017004145A2 (pt) chapa de aço laminada a frio, método de fabricação de chapa de aço laminada a frio, membro de automóvel e instalação para fabricação de chapa de aço laminada a frio
MX350226B (es) Hoja de acero laminado en frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion.
MX389187B (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
MX2017010031A (es) Hoja de acero laminada en caliente, miembro de acero, y metodo para fabricar hoja de acero laminada en caliente.
MX380199B (es) Método para producir una hoja de acero de alta resistencia que tiene capacidad de formación mejorada y hoja obtenida por dicho método.
WO2016014424A3 (en) System and method for producing a hardened and tempered structural member

Legal Events

Date Code Title Description
FG Grant or registration