MX2020006698A - Material de acero chapado con aleacion de zinc que tiene excelente resistencia a la corrosion despues de ser procesado y metodo para manufacturarlo. - Google Patents
Material de acero chapado con aleacion de zinc que tiene excelente resistencia a la corrosion despues de ser procesado y metodo para manufacturarlo.Info
- Publication number
- MX2020006698A MX2020006698A MX2020006698A MX2020006698A MX2020006698A MX 2020006698 A MX2020006698 A MX 2020006698A MX 2020006698 A MX2020006698 A MX 2020006698A MX 2020006698 A MX2020006698 A MX 2020006698A MX 2020006698 A MX2020006698 A MX 2020006698A
- Authority
- MX
- Mexico
- Prior art keywords
- plated steel
- steel material
- processed
- corrosion resistance
- zinc alloy
- Prior art date
Abstract
La presente invención se relaciona a un material de acero chapado que se puede utilizar para un automóvil, un electrodoméstico, un material de construcción, y los similares y, más particularmente, a un material de acero chapado con aleación de zinc que tiene excelente resistencia a la corrosión después de ser procesado y un método para manufacturarlo.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020170180328A KR102031465B1 (ko) | 2017-12-26 | 2017-12-26 | 가공 후 내식성 우수한 아연합금도금강재 및 그 제조방법 |
PCT/KR2018/015826 WO2019132336A1 (ko) | 2017-12-26 | 2018-12-13 | 가공 후 내식성 우수한 아연합금도금강재 및 그 제조방법 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2020006698A true MX2020006698A (es) | 2020-08-20 |
Family
ID=67063942
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2020006698A MX2020006698A (es) | 2017-12-26 | 2018-12-13 | Material de acero chapado con aleacion de zinc que tiene excelente resistencia a la corrosion despues de ser procesado y metodo para manufacturarlo. |
Country Status (7)
Country | Link |
---|---|
US (1) | US11566314B2 (es) |
EP (1) | EP3733918B1 (es) |
JP (2) | JP7244722B2 (es) |
KR (1) | KR102031465B1 (es) |
CN (1) | CN111527232A (es) |
MX (1) | MX2020006698A (es) |
WO (1) | WO2019132336A1 (es) |
Families Citing this family (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102590172B1 (ko) * | 2020-04-21 | 2023-10-19 | 닛폰세이테츠 가부시키가이샤 | 용융 도금 강판, 및 그 제조 방법 |
JP2023530374A (ja) * | 2020-06-19 | 2023-07-14 | ポスコ カンパニー リミテッド | 耐食性、加工性及び表面品質に優れためっき鋼板、並びにその製造方法 |
KR102395455B1 (ko) * | 2020-08-27 | 2022-05-09 | 현대제철 주식회사 | 용융아연도금 강판의 제조 방법 |
KR102381828B1 (ko) * | 2020-12-18 | 2022-04-01 | 주식회사 포스코 | 내식성 및 표면 품질이 우수한 도금 강판 및 이의 제조방법 |
KR102453008B1 (ko) * | 2020-12-21 | 2022-10-12 | 주식회사 포스코 | 내식성, 가공성 및 표면 품질이 우수한 도금 강판 및 이의 제조방법 |
KR102453010B1 (ko) * | 2020-12-21 | 2022-10-12 | 주식회사 포스코 | 내식성 및 내열성이 우수한 도금 강판 및 이의 제조방법 |
KR102499192B1 (ko) * | 2021-09-27 | 2023-02-16 | 순천대학교 산학협력단 | Zn-Al-Mg-Si계 합금도금강판의 제조방법 및 Zn-Al-Mg-Si계 합금도금강판 |
CN114645231A (zh) * | 2022-02-11 | 2022-06-21 | 河钢股份有限公司承德分公司 | 一种热基板双面锌层镀锌板的制备方法 |
Family Cites Families (29)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2783453B2 (ja) * | 1990-10-09 | 1998-08-06 | 新日本製鐵株式会社 | 溶融Zn−Mg−Alめっき鋼板及びその製造方法 |
JPH06306461A (ja) | 1993-04-28 | 1994-11-01 | Nippon Steel Corp | 外観性に優れた合金化溶融亜鉛めっき鋼板の製造法 |
JP2000265255A (ja) * | 1999-03-16 | 2000-09-26 | Nisshin Steel Co Ltd | 耐熱性を改善した溶融Zn−Al系合金めっき鋼板およびその製造法 |
JP2001295015A (ja) * | 2000-02-09 | 2001-10-26 | Nisshin Steel Co Ltd | 高Al含有溶融Zn−Al−Mg系めっき鋼板 |
JP3684135B2 (ja) * | 2000-04-11 | 2005-08-17 | 新日本製鐵株式会社 | 耐食性の優れたSi含有高強度溶融亜鉛めっき鋼板とその製造方法 |
JP2001355055A (ja) | 2000-04-11 | 2001-12-25 | Nippon Steel Corp | 未塗装加工部ならびに塗装端面部の耐食性に優れた溶融Zn−Al−Mg−Siめっき鋼材 |
JP2002113502A (ja) * | 2000-10-05 | 2002-04-16 | Nkk Corp | 鋼帯の製造方法及びその装置 |
JP4683764B2 (ja) | 2001-05-14 | 2011-05-18 | 日新製鋼株式会社 | 耐食性に優れた溶融Zn−Al−Mg系合金めっき鋼材 |
US6677058B1 (en) * | 2002-07-31 | 2004-01-13 | Nisshin Steel Co., Ltd. | Hot-dip Zn plated steel sheet excellent in luster-retaining property and method of producing the same |
AU2003275688B2 (en) | 2002-10-28 | 2006-12-14 | Nippon Steel Corporation | High corrosion-resistant hot dip coated steel product excellent in surface smoothness and formability, and method for producing hot dip coated steel product |
UA84778C2 (ru) * | 2004-06-29 | 2008-11-25 | Корус Сталь Б. В. | Стальная полоса с покрытием из цинкового сплава, нанесенное методом горячего оцинкования, и способ ее производства |
JP4546884B2 (ja) | 2004-07-07 | 2010-09-22 | 新日本製鐵株式会社 | 加工部耐食性に優れる表面処理めっき鋼板 |
JP4757581B2 (ja) * | 2005-09-20 | 2011-08-24 | 新日本製鐵株式会社 | 溶接性に優れる高耐食性溶融めっき鋼板とその製造方法 |
BRPI0621421B8 (pt) | 2006-01-30 | 2019-05-21 | Nippon Steel & Sumitomo Metal Corp | chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada e recozida e métodos de produção das mesmas |
JP5588112B2 (ja) * | 2008-03-27 | 2014-09-10 | 株式会社神戸製鋼所 | 耐食性に優れたクロメートフリー被覆溶融亜鉛めっき鋼板 |
KR101143180B1 (ko) * | 2009-05-19 | 2012-05-08 | 주식회사 포스코 | 용융 아연합금 도금욕, 용융 아연합금 도금강재 및 그 제조방법 |
JP5499664B2 (ja) | 2009-11-30 | 2014-05-21 | 新日鐵住金株式会社 | 疲労耐久性に優れた引張最大強度900MPa以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法 |
JP5556186B2 (ja) * | 2010-01-15 | 2014-07-23 | 新日鐵住金株式会社 | 高耐食性溶融亜鉛めっき鋼板 |
MX354008B (es) * | 2010-06-09 | 2018-02-08 | Sanoh Kogyo Kk | Tubo de metal para tuberia de vehiculo y metodo de tratamiento de superficie para tubo. |
CA2826225C (en) * | 2011-02-28 | 2020-07-21 | Nisshin Steel Co., Ltd. | Zn-al-mg based alloy hot-dip plated steel sheet, and method for producing the same |
US9481148B2 (en) | 2011-06-30 | 2016-11-01 | Nippon Steel and Sumitomo Metal Corporation | High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof |
JP5748829B2 (ja) | 2013-12-03 | 2015-07-15 | 日新製鋼株式会社 | 溶融Zn合金めっき鋼板およびその製造方法 |
KR20150070841A (ko) | 2013-12-17 | 2015-06-25 | 동부제철 주식회사 | 고내식 도금강판 및 그 제조방법 |
RU2695690C1 (ru) | 2013-12-19 | 2019-07-25 | Ниссин Стил Ко., Лтд. | СТАЛЬНОЙ ЛИСТ С ПОКРЫТИЕМ ИЗ СИСТЕМЫ НА ОСНОВЕ Zn-Al-Mg, ПОЛУЧЕННЫМ ПОГРУЖЕНИЕМ В РАСПЛАВ, ИМЕЮЩИЙ ПРЕВОСХОДНУЮ СПОСОБНОСТЬ К ОБРАБАТЫВАЕМОСТИ, И СПОСОБ ЕГО ИЗГОТОВЛЕНИЯ |
KR101714935B1 (ko) * | 2014-12-24 | 2017-03-10 | 주식회사 포스코 | 용접성 및 가공부 내식성이 우수한 아연합금도금강재 및 그 제조방법 |
CN105483547A (zh) | 2015-12-03 | 2016-04-13 | 武汉钢铁(集团)公司 | 家电用深冲耐指纹电镀锌板及其制备方法 |
KR101726090B1 (ko) | 2015-12-22 | 2017-04-12 | 주식회사 포스코 | 표면품질 및 도금밀착성이 우수한 고강도 용융아연도금강판 및 그 제조방법 |
KR102075182B1 (ko) | 2015-12-24 | 2020-02-10 | 주식회사 포스코 | 도금성이 우수한 고강도 용융 아연계 도금 강재 및 그 제조방법 |
JP6087461B1 (ja) * | 2016-04-26 | 2017-03-01 | 日本ペイント・インダストリアルコ−ティングス株式会社 | 表面処理鋼材 |
-
2017
- 2017-12-26 KR KR1020170180328A patent/KR102031465B1/ko active IP Right Grant
-
2018
- 2018-12-13 MX MX2020006698A patent/MX2020006698A/es unknown
- 2018-12-13 JP JP2020534879A patent/JP7244722B2/ja active Active
- 2018-12-13 WO PCT/KR2018/015826 patent/WO2019132336A1/ko unknown
- 2018-12-13 CN CN201880084547.0A patent/CN111527232A/zh active Pending
- 2018-12-13 EP EP18893849.2A patent/EP3733918B1/en active Active
- 2018-12-13 US US16/771,097 patent/US11566314B2/en active Active
-
2022
- 2022-11-18 JP JP2022184876A patent/JP2023025076A/ja active Pending
Also Published As
Publication number | Publication date |
---|---|
US20210002751A1 (en) | 2021-01-07 |
JP2021508771A (ja) | 2021-03-11 |
EP3733918A4 (en) | 2021-03-10 |
KR20190078434A (ko) | 2019-07-04 |
JP7244722B2 (ja) | 2023-03-23 |
CN111527232A (zh) | 2020-08-11 |
EP3733918B1 (en) | 2022-08-31 |
EP3733918A1 (en) | 2020-11-04 |
KR102031465B1 (ko) | 2019-10-11 |
JP2023025076A (ja) | 2023-02-21 |
US11566314B2 (en) | 2023-01-31 |
WO2019132336A1 (ko) | 2019-07-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2020006644A (es) | Material de acero chapado con aleacion de zinc que tiene excelente calidad de superficie y resistencia a la corrosion, y metodo para manufacturarlo. | |
MX2020006698A (es) | Material de acero chapado con aleacion de zinc que tiene excelente resistencia a la corrosion despues de ser procesado y metodo para manufacturarlo. | |
EP3561116A4 (en) | ALUMINIZED PLATED STEEL MATERIAL HAVING EXCELLENT CORROSION RESISTANCE, ALUMINUM ALLOY PLATED STEEL MATERIAL USING THE SAME, AND METHOD FOR MANUFACTURING THE ALUMINIZED PLATED STEEL MATERIAL, AND ALLOY PLATED STEEL MATERIAL ALUMINUM | |
EP3642377C0 (en) | IRON-BASED ALLOY SUITABLE FOR PROVIDING A HARD AND CORROSION-RESISTANT COATING ON A SUBSTRATE, ARTICLES HAVING A HARD AND CORROSION-RESISTANT COATING AND METHOD FOR PRODUCING SAME | |
SI3102711T1 (sl) | Utrdljiva nikelj-krom-železo-titan-aluminijeva zlitina z dobro obrabno obstojnostjo, obstojnostjo proti lezenju, korozijsko obstojnostjo in obdelovalnostjo | |
SI3102710T1 (sl) | Utrjena nikelj-krom-kobalt-titan-aluminijeva zlitina z dobro obrabno obstojnostjo, obstojnostjo proti lezenju, korozijsko obstojnostjo in obdelovalnostjo | |
EP3733920A4 (en) | STEEL PLATED WITH A ZINC ALLOY WITH EXCELLENT CORROSION RESISTANCE AND SURFACE SMOOTH AND METHOD FOR ITS MANUFACTURING | |
EP3719157A4 (en) | HIGH STRENGTH GALVANIZED STEEL SHEET AND METHOD FOR MANUFACTURING IT | |
EP3561141A4 (en) | FIRE ALUMINUM STEEL MATERIAL WITH EXCELLENT CORROSION RESISTANCE AND WORKABILITY AND MANUFACTURING METHOD THEREFOR | |
EP3239346A4 (en) | Zn alloy plated steel sheet having excellent phosphatability and spot weldability and method for manufacturing same | |
EP3730636A4 (en) | HIGH STRENGTH STEEL SHEET OF EXCELLENT WORKABILITY, AND PROCESS FOR MANUFACTURING THE SAME | |
MX2017012919A (es) | Metodo para el fosfatado libre de niquel en superficies de metal. | |
EP3730672A4 (en) | COMPOSITION OF SURFACE TREATMENT SOLUTION FOR ZINC ALLOY PLATED STEEL SHEET BY HOT DIP IMMERSION PROVIDING EXCELLENT RESISTANCE TO CORROSION AND DARKENING, ZINC ALLOY PLATED STEEL SHEET BY HOT DIP IMMERSION SURFACE TREATED USER, AND ITS MANUFACTURING PROCESS | |
EP3530768A4 (en) | PLATED STEEL SHEET, METHOD FOR PRODUCING A HOT-GALVANIZED STEEL SHEET AND METHOD FOR PRODUCING ALLOY HOT-GALNATED STEEL SHEET | |
EP3561155A4 (en) | LUBRICATED COATED STEEL WITH EXCELLENT WELDABILITY AND CORROSION RESISTANCE | |
EP3369838A4 (en) | Zinc alloy plated steel sheet having excellent bending workability and manufacturing method therefor | |
SI3102712T1 (sl) | Utrjena nikelj-krom-titan-aluminijeva zlitina z dobro obrabno obstojnostjo, časovno trajno mirujočo trdnostjo, korozijsko obstojnostjo in obdelovalnostjo | |
EP3561147A4 (en) | STEEL PLATED WITH ZINC ALLOY WITH EXCELLENT WELDABILITY AND CORROSION RESISTANCE | |
EP2957658A4 (en) | METALLIC ELEMENT HAVING EXCELLENT CORROSION RESISTANCE, MANUFACTURING METHOD THEREOF, REPAIR MATERIAL, AND METAL ELEMENT REPAIR METHOD | |
EP3124582A4 (en) | Aqueous lubricating coating agent having excellent corrosion resistance and workability, and metal material | |
MX2019007489A (es) | Material de acero chapado de aleacion que tiene excelente resistencia a la corrosion y alta calidad de superficie y metodo de fabricacion del mismo. | |
EP3399060A4 (en) | MAGNESIUM ALLOY WITH EXCELLENT MECHANICAL PROPERTIES AND CORROSION RESISTANCE AND METHOD FOR THE PRODUCTION THEREOF | |
WO2017026683A8 (ko) | 표면외관이 우수한 전기아연도금강판용 아연 플래쉬 도금 용액, 이를 이용한 전기아연도금강판의 제조방법 및 전기아연도금강판 | |
HUE060741T2 (hu) | Al-Mg-Mn ötvözetbõl készült, fokozott korrózióellenállással rendelkezõ lemeztermék elõállításának módszere | |
MX2022008507A (es) | Buje resistente a la corrosion que incluye malla metalica. |