JP5588112B2 - 耐食性に優れたクロメートフリー被覆溶融亜鉛めっき鋼板 - Google Patents
耐食性に優れたクロメートフリー被覆溶融亜鉛めっき鋼板 Download PDFInfo
- Publication number
- JP5588112B2 JP5588112B2 JP2009041261A JP2009041261A JP5588112B2 JP 5588112 B2 JP5588112 B2 JP 5588112B2 JP 2009041261 A JP2009041261 A JP 2009041261A JP 2009041261 A JP2009041261 A JP 2009041261A JP 5588112 B2 JP5588112 B2 JP 5588112B2
- Authority
- JP
- Japan
- Prior art keywords
- dip galvanized
- hot
- chromate
- galvanized layer
- steel sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
まず、本発明を特徴付ける溶融亜鉛めっき層について説明する。
測定装置:SPECTRUM ANALYTIK GmbH社製の「GDA750(装置名)」
測定条件:電力50W、2.5ヘクトパスカルのアルゴンガス中、グロー放電源(無水GDS)−Spectruma Analytik−Grimm型を使用、測定パルスは50%
クロメートフリー皮膜は、クロムさえ含んでいなければ特に制限はなく、有機系もしくは無機系、或いは有機無機複合系の防錆皮膜を使用できる。
本発明に用いられる鋼板は、溶融亜鉛めっき鋼板に用いられるものであれば特に限定されず、例えば、Alキルド鋼板やIF鋼などが挙げられる。
実験機を用いてAlキルド鋼(冷延鋼板、板厚は0.8mm)を下記の条件で溶融亜鉛めっきし、次いでクロメートフリー皮膜を被覆してクロメートフリー被覆溶融亜鉛めっき鋼板を得た。Alキルド鋼は、C:0.05%、Si:0.02%、Mn:0.19%、Al:0.047%、P:0.015%、S:0.012%を含有し、残部が鉄および不可避不純物からなる鋼板である。
整して行った。溶融亜鉛めっき浴の組成は、下記表1または表2に示す量のAlを含有し、残部はZnおよび不可避不純物である。
◎(合格) :白錆の発生無し。
○(合格) :白錆の発生面積率が0%を超え、10%以下。
△(不合格):白錆の発生面積率が10%を超え、30%以下。
×(不合格):白錆の発生面積率が30%を超えた。
上記実験例1において、溶融亜鉛めっき浴として、下記表3または表4に示す量のAlを含有し、残部がZnおよび不可避不純物であるめっき浴を用いる点と、赤外線ヒーターを用いて上記表1または表2に示す保持温度で10秒間等温保持する代わりに、赤外線ヒーターを用いて下記表3または表4に示す保持温度で15秒間等温保持する点以外は、上記実験例1と同じ条件で表面を平坦化させた溶融亜鉛めっき鋼板を得た。なお、本実験例では、実験機を用い、溶融亜鉛めっき浴から出た鋼板を炉内で保持しているため、440℃以下400℃超の温度域を通過する時間は、上記保持温度で保持した時間(15秒間)とほぼ等しくなっている。
Claims (3)
- 溶融亜鉛めっき層およびクロメートフリー皮膜を有するクロメートフリー被覆溶融亜鉛めっき鋼板であって、
前記溶融亜鉛めっき層は、Alを0.16〜0.22%(質量%の意味。以下、成分について同じ。)含有し、残部がZnおよび不可避不純物からなる溶融亜鉛めっき浴を用いて形成されたものであり、
前記溶融亜鉛めっき層について、高周波グロー放電発光分光分析による深さ方向のAl濃度プロファイルを測定したとき、前記溶融亜鉛めっき層の最表面から深さ20nmまででの領域にAl量の最大ピークを有しており、
前記溶融亜鉛めっき層の最表面から深さ20nmの位置におけるAlおよびOは、
Al:2.5%以上4.5%以下、および
O:2.0%以上10%以下
を満足することを特徴とする耐食性に優れたクロメートフリー被覆溶融亜鉛めっき鋼板。 - 前記溶融亜鉛めっき層の最表面におけるAlおよびOは、Al:1.0%以上、およびO:10.0%以上を満足するものである請求項1に記載のクロメートフリー被覆溶融亜鉛めっき鋼板。
- 請求項1または2に記載のクロメートフリー被覆溶融亜鉛めっき鋼板の製造方法であって、
前記溶融亜鉛めっき浴を用いると共に、
めっき後の冷却工程において、440℃以下400℃超の温度域を、O2ガス含有雰囲気下で、少なくとも10秒間かけて冷却することを特徴とするクロメートフリー被覆溶融亜鉛めっき鋼板の製造方法。