LU87916A1 - Procede pour le revetement au trempe d'une bande d'acier en continu - Google Patents
Procede pour le revetement au trempe d'une bande d'acier en continu Download PDFInfo
- Publication number
- LU87916A1 LU87916A1 LU87916A LU87916A LU87916A1 LU 87916 A1 LU87916 A1 LU 87916A1 LU 87916 A LU87916 A LU 87916A LU 87916 A LU87916 A LU 87916A LU 87916 A1 LU87916 A1 LU 87916A1
- Authority
- LU
- Luxembourg
- Prior art keywords
- coating
- weight
- strontium
- vanadium
- amount
- Prior art date
Links
- 238000000576 coating method Methods 0.000 title claims description 106
- 239000011248 coating agent Substances 0.000 title claims description 87
- 229910000831 Steel Inorganic materials 0.000 title claims description 36
- 239000010959 steel Substances 0.000 title claims description 36
- 238000000034 method Methods 0.000 title claims description 22
- 230000008569 process Effects 0.000 title description 10
- 229910052712 strontium Inorganic materials 0.000 claims description 42
- 229910045601 alloy Inorganic materials 0.000 claims description 40
- 239000000956 alloy Substances 0.000 claims description 40
- CIOAGBVUUVVLOB-UHFFFAOYSA-N strontium atom Chemical compound [Sr] CIOAGBVUUVVLOB-UHFFFAOYSA-N 0.000 claims description 32
- 230000017260 vegetative to reproductive phase transition of meristem Effects 0.000 claims description 27
- 229910052720 vanadium Inorganic materials 0.000 claims description 24
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims description 24
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 claims description 18
- 229910052804 chromium Inorganic materials 0.000 claims description 18
- 239000011651 chromium Substances 0.000 claims description 18
- 229910000611 Zinc aluminium Inorganic materials 0.000 claims description 14
- HXFVOUUOTHJFPX-UHFFFAOYSA-N alumane;zinc Chemical compound [AlH3].[Zn] HXFVOUUOTHJFPX-UHFFFAOYSA-N 0.000 claims description 14
- 229910052710 silicon Inorganic materials 0.000 claims description 14
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims description 13
- 239000010703 silicon Substances 0.000 claims description 13
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 12
- 229910052782 aluminium Inorganic materials 0.000 claims description 12
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims description 7
- 238000003618 dip coating Methods 0.000 claims description 7
- 239000011701 zinc Substances 0.000 claims description 7
- 229910052725 zinc Inorganic materials 0.000 claims description 7
- 238000012360 testing method Methods 0.000 description 28
- 239000000047 product Substances 0.000 description 24
- 230000007797 corrosion Effects 0.000 description 11
- 238000005260 corrosion Methods 0.000 description 11
- 238000007792 addition Methods 0.000 description 8
- 238000010438 heat treatment Methods 0.000 description 7
- 238000012986 modification Methods 0.000 description 7
- 230000004048 modification Effects 0.000 description 7
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 6
- 239000000203 mixture Substances 0.000 description 6
- 238000005452 bending Methods 0.000 description 5
- 238000005336 cracking Methods 0.000 description 5
- 230000006872 improvement Effects 0.000 description 5
- 239000007921 spray Substances 0.000 description 5
- 150000003839 salts Chemical class 0.000 description 4
- 230000000007 visual effect Effects 0.000 description 4
- 238000006243 chemical reaction Methods 0.000 description 3
- 238000001816 cooling Methods 0.000 description 3
- 230000007423 decrease Effects 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 238000011156 evaluation Methods 0.000 description 3
- 230000002349 favourable effect Effects 0.000 description 3
- 229910000765 intermetallic Inorganic materials 0.000 description 3
- 229910052742 iron Inorganic materials 0.000 description 3
- 239000002245 particle Substances 0.000 description 3
- 239000000523 sample Substances 0.000 description 3
- 238000000540 analysis of variance Methods 0.000 description 2
- 230000008901 benefit Effects 0.000 description 2
- 239000008199 coating composition Substances 0.000 description 2
- 238000010276 construction Methods 0.000 description 2
- 230000007547 defect Effects 0.000 description 2
- 239000006185 dispersion Substances 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 230000001747 exhibiting effect Effects 0.000 description 2
- 238000009434 installation Methods 0.000 description 2
- 239000006101 laboratory sample Substances 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- 238000004611 spectroscopical analysis Methods 0.000 description 2
- 239000000758 substrate Substances 0.000 description 2
- 230000002123 temporal effect Effects 0.000 description 2
- 238000011282 treatment Methods 0.000 description 2
- 229910018125 Al-Si Inorganic materials 0.000 description 1
- 229910021364 Al-Si alloy Inorganic materials 0.000 description 1
- 241001163841 Albugo ipomoeae-panduratae Species 0.000 description 1
- 229910018520 Al—Si Inorganic materials 0.000 description 1
- 101100428768 Arabidopsis thaliana VSR1 gene Proteins 0.000 description 1
- 101100428770 Arabidopsis thaliana VSR2 gene Proteins 0.000 description 1
- 229910001297 Zn alloy Inorganic materials 0.000 description 1
- 238000005275 alloying Methods 0.000 description 1
- 238000013459 approach Methods 0.000 description 1
- 238000004364 calculation method Methods 0.000 description 1
- 238000004210 cathodic protection Methods 0.000 description 1
- 230000000052 comparative effect Effects 0.000 description 1
- 230000008021 deposition Effects 0.000 description 1
- 238000006073 displacement reaction Methods 0.000 description 1
- 230000005496 eutectics Effects 0.000 description 1
- 238000007654 immersion Methods 0.000 description 1
- 238000009776 industrial production Methods 0.000 description 1
- JEIPFZHSYJVQDO-UHFFFAOYSA-N iron(III) oxide Inorganic materials O=[Fe]O[Fe]=O JEIPFZHSYJVQDO-UHFFFAOYSA-N 0.000 description 1
- 238000009533 lab test Methods 0.000 description 1
- 238000012423 maintenance Methods 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 238000001000 micrograph Methods 0.000 description 1
- 230000000877 morphologic effect Effects 0.000 description 1
- 231100000989 no adverse effect Toxicity 0.000 description 1
- 230000008520 organization Effects 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 238000011160 research Methods 0.000 description 1
- 238000005204 segregation Methods 0.000 description 1
- 230000035945 sensitivity Effects 0.000 description 1
- 239000011856 silicon-based particle Substances 0.000 description 1
- 238000007711 solidification Methods 0.000 description 1
- 230000008023 solidification Effects 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/12—Aluminium or alloys based thereon
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S428/00—Stock material or miscellaneous articles
- Y10S428/922—Static electricity metal bleed-off metallic stock
- Y10S428/9335—Product by special process
- Y10S428/939—Molten or fused coating
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
- Y10T428/1275—Next to Group VIII or IB metal-base component
- Y10T428/12757—Fe
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12785—Group IIB metal-base component
- Y10T428/12792—Zn-base component
- Y10T428/12799—Next to Fe-base component [e.g., galvanized]
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Coating With Molten Metal (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
- Secondary Cells (AREA)
- Battery Electrode And Active Subsutance (AREA)
- Paints Or Removers (AREA)
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| BE9000420A BE1004077A3 (fr) | 1990-04-13 | 1990-04-13 | Procede pour le revetement au trempe d'une bande d'acier en continu. |
| BE9100298A BE1004839A7 (fr) | 1991-04-02 | 1991-04-02 | Produit en acier pourvu d'un revetement a base de zinc-aluminium presentant un fleurage ameliore. |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| LU87916A1 true LU87916A1 (fr) | 1992-03-03 |
Family
ID=25662523
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| LU87916A LU87916A1 (fr) | 1990-04-13 | 1991-04-10 | Procede pour le revetement au trempe d'une bande d'acier en continu |
Country Status (17)
| Country | Link |
|---|---|
| US (2) | US5217759A (cs) |
| JP (1) | JP3163303B2 (cs) |
| KR (1) | KR100206444B1 (cs) |
| AT (1) | AT399725B (cs) |
| AU (1) | AU640770B2 (cs) |
| CA (1) | CA2040376C (cs) |
| CZ (1) | CZ281134B6 (cs) |
| DE (1) | DE4111410C2 (cs) |
| ES (1) | ES2038885B1 (cs) |
| FI (1) | FI96124C (cs) |
| FR (1) | FR2660937B1 (cs) |
| GB (1) | GB2243843B (cs) |
| IT (1) | IT1247038B (cs) |
| LU (1) | LU87916A1 (cs) |
| NL (1) | NL194086C (cs) |
| RU (1) | RU2009044C1 (cs) |
| SE (2) | SE510563C2 (cs) |
Families Citing this family (22)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP2777571B2 (ja) * | 1991-11-29 | 1998-07-16 | 大同鋼板株式会社 | アルミニウム−亜鉛−シリコン合金めっき被覆物及びその製造方法 |
| WO1996003748A1 (en) * | 1994-07-27 | 1996-02-08 | Minnesota Mining And Manufacturing Company | Tape cartridge base plate comprising a novel aluminum alloy |
| GB2320033B (en) | 1996-12-05 | 2001-06-06 | Fmc Corp | Improvements in strength and wear resistance of mechanical components |
| JP3983932B2 (ja) * | 1999-05-19 | 2007-09-26 | 日新製鋼株式会社 | 表面外観の良好な高耐食性Ｍｇ含有溶融Ｚｎ−Ａｌ系合金めっき鋼板 |
| JP4409007B2 (ja) * | 1999-10-12 | 2010-02-03 | 日新製鋼株式会社 | 表面性状に優れる高耐食性溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板の製造方法 |
| JP3580258B2 (ja) * | 2001-02-14 | 2004-10-20 | 住友金属工業株式会社 | 意匠性に優れた溶融Ａｌ−Ｚｎ系合金めっき鋼板とその製造方法 |
| JP3566261B2 (ja) * | 2001-03-19 | 2004-09-15 | Ｊｆｅスチール株式会社 | 加工性及び耐食性に優れた塗装溶融Ａｌ−Ｚｎ合金めっき鋼板およびその製造方法 |
| JP3566262B2 (ja) * | 2001-03-19 | 2004-09-15 | Ｊｆｅスチール株式会社 | 加工性に優れた溶融Ａｌ−Ｚｎ合金めっき鋼板及びその製造方法 |
| JP3563063B2 (ja) * | 2001-03-19 | 2004-09-08 | Ｊｆｅスチール株式会社 | 加工性及び耐食性に優れた潤滑被覆溶融Ａｌ−Ｚｎ合金めっき鋼板およびその製造方法 |
| JP3599716B2 (ja) * | 2002-03-19 | 2004-12-08 | Ｊｆｅスチール株式会社 | 表面外観および曲げ加工性に優れた溶融Ａｌ−Ｚｎ系合金めっき鋼板およびその製造方法 |
| JP2004107730A (ja) * | 2002-09-19 | 2004-04-08 | Jfe Steel Kk | 曲げ加工性と耐剥離性に優れた溶融Ａｌ−Ｚｎ系めっき鋼板 |
| JP4050978B2 (ja) * | 2002-11-27 | 2008-02-20 | 新日本製鐵株式会社 | 鮮映性の優れた高耐食性塗装鋼板 |
| AU2003901424A0 (en) * | 2003-03-20 | 2003-04-10 | Bhp Steel Limited | A method of controlling surface defects in metal-coated strip |
| AU2004221793C1 (en) * | 2003-03-20 | 2023-09-28 | Bluescope Steel Limited | A method of controlling surface defects in metal-coated strip |
| AU2005336202B2 (en) * | 2005-09-01 | 2010-12-23 | Nippon Steel Corporation | Hot dip Zn-Al based alloy plated steel product excellent in bending workability and method for production thereof |
| NZ575788A (en) * | 2006-08-30 | 2012-03-30 | Bluescope Steel Ltd | Steel strip coated with aluminium, zinc, silicon alloy |
| KR20090038756A (ko) * | 2007-10-16 | 2009-04-21 | 유니온스틸 주식회사 | 용융 알루미늄계 도금강판 및 그 제조방법 |
| WO2009055843A1 (en) * | 2007-10-29 | 2009-05-07 | Bluescope Steel Limited | Metal-coated steel strip |
| NZ586488A (en) | 2008-03-13 | 2013-04-26 | Bluescope Steel Ltd | ALUMINIUM, ZINC, SILICON, MAGNESIUM ALLOY METAL COATED STEEL STRIP WITH VARIATION IN COATING THICKNESS CONTROLLED TO REDUCE Mg2Si IN THE SURFACE |
| JP5851845B2 (ja) | 2009-03-13 | 2016-02-03 | ブルースコープ・スティール・リミテッドＢｌｕｅｓｃｏｐｅ Ｓｔｅｅｌ Ｌｉｍｉｔｅｄ | Ａｌ／Ｚｎベースの被膜を有する腐食保護 |
| CN102712988B (zh) * | 2010-01-06 | 2014-12-31 | 蓝野钢铁有限公司 | 金属镀覆钢带 |
| JP2013194295A (ja) * | 2012-03-21 | 2013-09-30 | Nippon Steel & Sumikin Coated Sheet Corp | めっき金属板、遮熱塗装金属板及び遮熱塗装金属板の製造方法 |
Family Cites Families (24)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3136632A (en) * | 1958-05-26 | 1964-06-09 | Kaiser Aluminium Chem Corp | Aluminum base alloy |
| US3782909A (en) * | 1972-02-11 | 1974-01-01 | Bethlehem Steel Corp | Corrosion resistant aluminum-zinc coating and method of making |
| DE2308281A1 (de) * | 1973-02-20 | 1974-08-22 | Metallgesellschaft Ag | Ueberzuege aus aluminium oder aluminiumlegierungen auf metallischen substraten |
| DD110057A1 (cs) * | 1974-03-06 | 1974-12-05 | ||
| US3952120A (en) * | 1974-05-31 | 1976-04-20 | Bethlehem Steel Corporation | Aluminum-zinc coated low-alloy ferrous product and method |
| US4287008A (en) * | 1979-11-08 | 1981-09-01 | Bethlehem Steel Corporation | Method of improving the ductility of the coating of an aluminum-zinc alloy coated ferrous product |
| EP0037143B1 (fr) * | 1980-03-25 | 1985-03-20 | CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif | Procédé de revêtement à chaud |
| AU543013B2 (en) * | 1980-08-19 | 1985-03-28 | Lysaght, J. (Australia) Ltd. | Hot-dip coating of ferrous strands |
| US4418984A (en) * | 1980-11-03 | 1983-12-06 | Hughes Aircraft Company | Multiply coated metallic clad fiber optical waveguide |
| JPS57110601A (en) * | 1980-12-29 | 1982-07-09 | Mitsui Mining & Smelting Co Ltd | Zinc alloy powder for mechanical plating |
| US4361448A (en) * | 1981-05-27 | 1982-11-30 | Ra-Shipping Ltd. Oy | Method for producing dual-phase and zinc-aluminum coated steels from plain low carbon steels |
| US4389463A (en) * | 1981-07-23 | 1983-06-21 | United Technologies Corporation | Zinc-aluminum hot dip coated ferrous article |
| US4456663A (en) * | 1981-12-02 | 1984-06-26 | United States Steel Corporation | Hot-dip aluminum-zinc coating method and product |
| GB8318156D0 (en) * | 1983-07-05 | 1983-08-03 | Ae Plc | Aluminium based bearing alloys |
| JPS60125360A (ja) * | 1983-12-12 | 1985-07-04 | Nippon Soda Co Ltd | 溶融亜鉛合金メッキ鋼材およびその製造方法ならびにフラックス組成物 |
| EP0148740A1 (fr) * | 1983-12-22 | 1985-07-17 | CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif | Procédé de revêtement à chaud et bain de composition améliorée pour sa mise en oeuvre |
| JPS60230952A (ja) * | 1984-04-27 | 1985-11-16 | Daido Metal Kogyo Kk | アルミニウム系摺動合金 |
| GB8420699D0 (en) * | 1984-08-15 | 1984-09-19 | Singer A R E | Flow coating of metals |
| US4595600A (en) * | 1984-11-13 | 1986-06-17 | Fl Industries, Inc. | Metal cladding of wire by atomization spraying |
| GB2182348B (en) * | 1985-09-13 | 1989-08-23 | Nippon Dia Clevite Co | Aluminium alloy and its use in a two-layer bearing material |
| US4789522A (en) * | 1986-06-27 | 1988-12-06 | Queen's University At Kingston | Castable zinc-aluminum alloys |
| IT1195979B (it) * | 1986-07-14 | 1988-11-03 | Centro Speriment Metallurg | Lega a base di zinco-alluminio per rivestimenti di manufatti d'acciaio |
| US4722871A (en) * | 1986-08-14 | 1988-02-02 | Cosmos Engineering, Inc. | Zinc-aluminum alloy coatings for steel |
| JP2534280B2 (ja) * | 1987-02-05 | 1996-09-11 | 日本パーカライジング株式会社 | 亜鉛系複合めっき金属材料およびめっき方法 |
-
1991
- 1991-04-09 DE DE4111410A patent/DE4111410C2/de not_active Expired - Fee Related
- 1991-04-09 SE SE9101053A patent/SE510563C2/sv not_active IP Right Cessation
- 1991-04-09 SE SE9101053D patent/SE9101053L/xx not_active Application Discontinuation
- 1991-04-10 AT AT0075191A patent/AT399725B/de not_active IP Right Cessation
- 1991-04-10 CZ CS911006A patent/CZ281134B6/cs unknown
- 1991-04-10 LU LU87916A patent/LU87916A1/fr unknown
- 1991-04-10 IT ITTO910255A patent/IT1247038B/it active IP Right Grant
- 1991-04-11 FR FR9104669A patent/FR2660937B1/fr not_active Expired - Fee Related
- 1991-04-11 JP JP17160191A patent/JP3163303B2/ja not_active Expired - Fee Related
- 1991-04-12 US US07/684,285 patent/US5217759A/en not_active Expired - Fee Related
- 1991-04-12 KR KR1019910005999A patent/KR100206444B1/ko not_active Expired - Fee Related
- 1991-04-12 FI FI911773A patent/FI96124C/fi active
- 1991-04-12 CA CA002040376A patent/CA2040376C/en not_active Expired - Fee Related
- 1991-04-12 GB GB9107831A patent/GB2243843B/en not_active Expired - Fee Related
- 1991-04-12 NL NL9100638A patent/NL194086C/nl not_active IP Right Cessation
- 1991-04-12 ES ES9100937A patent/ES2038885B1/es not_active Expired - Fee Related
- 1991-04-12 AU AU75024/91A patent/AU640770B2/en not_active Ceased
- 1991-04-12 RU SU914895154A patent/RU2009044C1/ru active
-
1992
- 1992-11-30 US US07/983,212 patent/US5279903A/en not_active Expired - Fee Related
Also Published As
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| LU87916A1 (fr) | Procede pour le revetement au trempe d'une bande d'acier en continu | |
| EP1170118B1 (fr) | Tôles en alliage d'aluminium plaquées pour éléments de structure d'aéronefs | |
| Afseth et al. | Effect of thermo-mechanical processing on filiform corrosion of aluminium alloy AA3005 | |
| FR2853666A1 (fr) | ALLIAGE Al-Zn A HAUTE RESISTANCE,PROCEDE DE PRODUCTION DE PRODUITS EN UN TEL ALLIAGE, ET PRODUITS OBTENUS SELON CE PROCEDE | |
| FR2855834A1 (fr) | Produit ouvre en alliage a grande tolerance aux dommages, en particulier pour des applications dans le domaine aerospatial | |
| FR2841263A1 (fr) | PROCEDE DE PRODUCTION D'UN PRODUIT EN ALLAIGE Al-Mg-Si EQUILIBRE A HAUTE RESISTANCE, ET PRODUIT SOUDABLE ET MATERIAU DE REVETEMENT POUR AVION, OBTENUS PAR UN TEL PROCEDE | |
| EP1544315B1 (fr) | Produit corroyé sous forme de tôle laminée et élément de structure pour aéronef en alliage Al-Zn-Cu-Mg | |
| EP1114877A1 (fr) | Element de structure d'avion en alliage Al-Cu-Mg | |
| EP2235224A1 (fr) | Produit lamine en alliage aluminium-lithium pour applications aeronautiques | |
| EP0521138B1 (fr) | Alliages d'aluminium, les substrats revetus de ces alliages et leurs applications | |
| CA1139645A (fr) | Procede de traitement thermique des alliages aluminium - cuivre - magnesium - silicium | |
| FR2620734A1 (fr) | Alliage metallique refractaire multiphase, oxycarbure ou oxycarbonitrure, a variation progressive de durete a partir de la surface | |
| FR2472618A1 (fr) | Barre coulee en alliage d'aluminium pour produits travailles presentant des proprietes mecaniques et une " travaillabilite " ameliorees, et procede de fabrication | |
| FR2501237A1 (fr) | Alliage a base de cobalt | |
| EP0939141B1 (fr) | Tôle dotée d'un revêtement d'aluminium résistant à la fissuration | |
| Alavandi et al. | Investigation of the influence of Ni and Cu additions on the wear behavior of spray formed Al-15Si alloy at elevated temperature | |
| Sugimaru et al. | Zinc alloy coated steel wire with high corrosion resistance | |
| Relue et al. | Corrosion performance of different aluminum alloy deposits fabricated by lateral friction surfacing | |
| FR2473417A1 (fr) | Procede de fabrication d'un article metallique resistant a l'usure et article ainsi fabrique | |
| FR2593831A1 (fr) | Procede de revetement protecteur d'un produit en fer ou en acier et produit revetu | |
| FR3087206A1 (fr) | Tôle en alliage 2XXX à haute performance pour fuselage d’avion | |
| BE1004077A3 (fr) | Procede pour le revetement au trempe d'une bande d'acier en continu. | |
| BE1004839A7 (fr) | Produit en acier pourvu d'un revetement a base de zinc-aluminium presentant un fleurage ameliore. | |
| KR850001322B1 (ko) | 내식성이 우수한 알루미늄-아연 합금 피복 철금속제품의 제조방법 | |
| JPH0548296B2 (cs) |