KR900702092A - 고속 용융방사방법 및 장치 - Google Patents

고속 용융방사방법 및 장치

Info

Publication number
KR900702092A
KR900702092A KR1019900700023A KR900700023A KR900702092A KR 900702092 A KR900702092 A KR 900702092A KR 1019900700023 A KR1019900700023 A KR 1019900700023A KR 900700023 A KR900700023 A KR 900700023A KR 900702092 A KR900702092 A KR 900702092A
Authority
KR
South Korea
Prior art keywords
strand
cooling
heating
polymer
spinneret
Prior art date
Application number
KR1019900700023A
Other languages
English (en)
Other versions
KR970007428B1 (ko
Inventor
쿠쿨로 죤
주니어 폴 에이. 터커
첸 가오-유안
린 천-이예
덴턴 제프리
런드버그 페르디난드
Original Assignee
프랭클린 디. 하아트
노스 캐롤라이나 스테이트 유니버시티 C/O 알라이드-시그날 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=22705540&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR900702092(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 프랭클린 디. 하아트, 노스 캐롤라이나 스테이트 유니버시티 C/O 알라이드-시그날 인코포레이티드 filed Critical 프랭클린 디. 하아트
Publication of KR900702092A publication Critical patent/KR900702092A/ko
Application granted granted Critical
Publication of KR970007428B1 publication Critical patent/KR970007428B1/ko

Abstract

내용 없음

Description

고속 용융방사방법 및 장치
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도 : 본 발명의 방사시스템의 개요도. 제3도 : 4000m/min에서 온-라인 지역 가열(OLZH)의 공기 온도에 대한 복굴절율및 결정도 변화를 나타낸 그래프. 제5도 : 본 발명에 따른 온-라인 지역가열적용(with OLZH) 및 비적용(w/o OLZH)고속용융방사에 의하여 생산된 두가지 PET 섬유의 WAXS 수평분포도.

Claims (10)

  1. 방적돌기로 부터 용융 중합체를 압출하여 연속 스트랜드를 형성하고; 방적 돌기로부터 용융 중합체 스트랜드를 제1냉각지역에 도입, 통과시켜, 스트랜드의 유리전이온도 이상에서 미리정해진 최적 결정화 온도 범위로 스트랜드를 냉각시키고; 제1냉각 지역을 통과한 스트랜드를 가열지역에 도입. 통과시켜, 상기 최적 결정화 온도 범위내의 온도에서 잠시 동안 스트랜드가 유지되도록 그 스트랜드를 가열시키고; 가열지역을 통과한 스트랜드를 제2냉각지역에 도입하여 스트랜드를 냉각 및 고화시키며; 고화된 스트랜드를 3000m/min 이상의 고속으로 감아회수(테이프-업)하는 것을 특징으로 하는, 개선된 물성을 갖는 직물섬유 제조를 위한 고속 용융방사방법.
  2. 제1항에 있어서, 상기 가열단계가 스트랜드를 등온 조건하에 유지시키는 것임을 특징으로 하는 방법.
  3. 제1항에 있어서, 중합체가 폴리에틸렌 테페르탈레이트임을 특징으로 하는 방법.
  4. 제3항에 있어서, 가열단계가 80-160℃의 온으로 적용됨을 특징으로 하는 방법.
  5. 제3항에 있어서, 가열단계가 160℃의 등온으로 유지되는 것임을 특징으로 하는 방법.
  6. 제1항에 있어서, 가열단계에서 스트랜드가 0.005초 이하의 시간동안 가열되는 것임을 특징으로 하는 방법.
  7. 방적 돌기로 부터 용융 폴리에틸렌 테레프탈레이트 중합체를 압출하여 연속 스트랜드를 형성하고; 방적 돌기로 부터의 용융 폴리에틸렌 테레프탈레이트 스트랜드를 제1냉각지역에 도입, 통과시켜, 80-160℃온도범위에서 미리정해진 최적 결정화 온도 범위로 용융 스트랜드를 공기 냉각 시키고; 제1냉각지역을 통과한 스트랜드를 가열지역에 도입. 통과시켜, 80-160℃의 상기 최적 결정화 온도 범위내의 온도에서 0.005초 이하 기간동안 스트랜드가 유지되도록 그 스트랜드를 공기 가열시키고; 가열지역을 통과한 스트랜드를 제2냉각지역에 도입하여, 냉각공기로 냉각 및 고화시키며; 고화된 스트랜드를 3000m/min 이상의 고속으로 감아회수(테이프-업)함것을 특징으로 하는, 향상된 물성을 갖는 직물 섬유 제조를 위한 고속 용융 방사방법.
  8. 제7항에 있어서, 가열단계에서 스트랜드가 140℃의 온도로 유지됨을 특징으로 하는 방법.
  9. 다음 수단들을 포함하여 구성됨을 특징으로 하는, 향상된 물성의 직물 섬유제조를 위한 고속 용융방사 시스템.
    (a) 방적돌기로 부터 용융 중합체를 압출하여 연속적인 스트랜드를 형성하는 수단; (b) 방적돌기로 부터의 용융 중합체 스트랜드를 수용하도록 위치되며, 스트랜드 유리전이온도 이상에서 미리정해진 최적 결정화 온도 범위로 그 스트랜드를 냉각시켜 주는 제1냉각 수단; (c) 상기 제1냉각수단으로 부터의 중합체 스트랜드를 수용하도록 위치되며, 상기 최적 결정화온도 범위내의 온도에서 잠시동안 스트랜드가 유지되도록 그 스트랜드를 가열 하여 주는 가열수단; (d) 상기 가열수단으로 부터의 중합체 스트랜드를 수용하도록 위치되며, 그 스트랜드를 냉각 및 고화시켜 주는 제2냉각 수단; 및 (e) 고화된 스트랜드를 3000m/min 이상의 고속으로 회수하는 테이크-업 수단.
  10. 다음 수단들을 포함하여 구성됨을 특징으로 하는, 향상된 물성을 갖는 폴리에틸렌 테페프탈레이트 직물 제조를 위한 고속 용융방사 시스템.
    (a) 방적돌기로 부터 용융 폴리에틸렌 테레프탈레이트 중합체를 압출하여 연속 스트랜드를 형성하는 수단; (b) 방적돌기로 부터 용융 폴리에틸렌 테레프탈레이트 스트랜드를 수용하도록 위치되며, 80-160℃ 온도범위에서 미리 정해진 최적 결정화 온도로 그 스트랜드를 냉각시켜 주는 제1냉각 수단; (c)상기 제1냉각수단으로 부터의 중합체 스트랜드를 수용하도록 위치되며, 80-160℃ 범위의 상기 최적 결정화온도 범위내에서 스트랜드가 유지되도록 그 스트랜드를 공기가열시켜 주는 가열수단;(d)상기 가열수단으로 부터의 중합체 스트랜드를 수용하도록 위치되며, 그 스트랜드를 공기 냉각 및 고화시켜 주는 제2냉각 수단; 및 (e) 고화된 스트랜드를 3000m/min 이상의 고속에서 고속 테이크-업 수단.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019900700023A 1988-05-09 1989-05-04 고속 용융방사방법 및 장치 KR970007428B1 (ko)