KR850004125A - 장갑판(Armour plate) 및 그 제조방법 - Google Patents
장갑판(Armour plate) 및 그 제조방법 Download PDFInfo
- Publication number
- KR850004125A KR850004125A KR1019840006842A KR840006842A KR850004125A KR 850004125 A KR850004125 A KR 850004125A KR 1019840006842 A KR1019840006842 A KR 1019840006842A KR 840006842 A KR840006842 A KR 840006842A KR 850004125 A KR850004125 A KR 850004125A
- Authority
- KR
- South Korea
- Prior art keywords
- armor plate
- substrate
- plate according
- cladding
- temperature
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (12)
- 충격(bombardment)에 대향한 측면에서 경도가 있는 상부층을, 또 그 대향측면에는 경도가 낮은 기재를 구성시켜 결합시킨 다음 열 처리 시킨 두층의 클래드강(clad steel)으로된 장갑판에 있어서, (가) 상기 상부층(top layer)에는 C 0.30―0.80wt%, Si 0.10―0.80wt%, Mn 0.40―1.20st%, P 0.015wt%까지, S 0.015wt%까지, Cr 0.20―2.80wt%, Mo 0.05―1.00wt%, Al 0.01―0.05wt%, Ni 0.40wt%까지 제거할 수 없는 불순물을 함유한 Fe 잔류 wt%를 조성하고, (나) 상기 기재(base materials)에는 C 0.17―040wt%, Si 0.10―0.80wt%, Mn 0.40―2.00wt%, P 0.025wt%까지, S 0.025wt%까지, Cr 0.10―1.50wt% Mo 0.05―1.50wt%, Al 0.01―0.05wt%, 제거할 수 없는 불순물을 함유한 Fe 잔류 wt%로 조성하여 상기 상부층의 탄소함량이 상기 기재의 함량 보다 현저하게 높도록 조성시킴을 특징으로 한 장갑판.
- 제1항에 있어서, 상기 기재에는 C 0.17―0.25wt%, Si 0.40―0.80wt%, Mn 0.70―1.20wt%, P 0.025wt%까지, S 0.25wt%까지, Cr 0.50―1.00wt%, Mo 0.20―0.60wt%, Al 0.01―0.05wt%, 제거할 수 없는 불순물을 함유한 Fe 잔류 wt%를 조성시킴을 특징으로 한 장갑판.
- 제1항에 있어서, 상기 기재에는 C 0.17―0.25wt%, Si 0.40―0.80wt%, Mn 0.70―1.20st%, P 0.025wt%까지, S 0.025wt%까지, Cr 0.50―1.00wt%, Mo 0.20―0.60wt%, Al 0.01―0.05wt%, 제거할 수 없는 불순물을 함유한 Fe 잔류 wt%를 조성시킴을 특징으로 한 장갑판.
- 제1항 내지 제3항중 어느 한 항에 있어서, 상기 기재 및 또는 상부층은 추가로 B―.008wt%까지, Ti 0.03―0.20wt%를 조성시킴을 특징으로 한 장갑판.
- 제1항 내지 제4항중 어느한 항에 있어서, 상기 기재는 추가로 Zr 0.01―0.12wt%를 조성시킴을 특징으로 한 장갑판.
- 제1항에 있어서, 상기 기재의 경도는 적어도 380HB이고, 상기 상부층과 상기 기재의 경도 차이는 적어도 130HB이나 300HB이하이며 바람직하게는 150―250HB임을 특징으로 한 장갑판.
- 제1항 내지 제6항 중 어느 한항에 의한 장갑판을 제조하는 방법에 있어서, 상부층(Top layer)과 기재(base materials)로된 두층의 클래드강(clad steel)을 단부 두께에 압연한 클래딩처리(cladding)를, 바람직하게는 폭발성 클래딩 처리후 단부 두께에 가열 압연처리를 하여 제조한 다음, 그 클레드강을 온도 880―980℃에서 가열시켜 이 온도에서 유지하고 상부층 일체와 기재의 대부분(〉75%)을 마텐사이트(martensite)로 전환되도록 냉각하여 열처리 시킴을 특징으로 한 장갑판의 제조방법.
- 제7항에 있어서, 클래딩 처리전 상부층, 기재의 두께비는 30:70―70:30의 범위에서 선택함을 특징으로 한 장갑판의 제조방법.
- 제7항 또는 제8항에 있어서, 압연―결합 클래딩 전 또는 폭발성 추가 열압연전 그 클래드강을 상부층이 내측에 기재가 외측에 있는 2중 상자(double box)로 되게 하고, 그 다음 밀봉된 2중 상자형의 클래딩강을 열처리 시킴을 특징으로 한 장갑판의 제조방법.
- 제1항 내지 제6항중 어느 하나의 항에 의한 장갑판을 제조하기 위한 제7항 내지 제9항중 어느 한 항에 있어서, 그 냉각 처리 조작을 오일(oil)중에서 고속으로 실시함을 특징으로 하는 장갑판의 제조방법.
- 제1항 내지 제6항중 어느 한항에 의한 장갑판을 제조하는 제9항에 있어서, 그 냉각처리를 물에 의해 고속으로 실시함을 특징으로 한 장갑판의 제조방법.
- 제10항 또는 제11항에 있어서, 템퍼링 후 처리에는 온도170―230℃에서 템퍼링 온도로 가열시켜 이 온도에서 유지시킨 다음 스틸에어(still air) 또는 유동공기중에서 실온으로 냉각시켜 구성함을 특징으로 한 장갑판의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.