KR970065742A - 재질의 분산이 적고 용접성이 우수한 고강도고인성 후강재의 제조방법 - Google Patents
재질의 분산이 적고 용접성이 우수한 고강도고인성 후강재의 제조방법 Download PDFInfo
- Publication number
- KR970065742A KR970065742A KR1019970009014A KR19970009014A KR970065742A KR 970065742 A KR970065742 A KR 970065742A KR 1019970009014 A KR1019970009014 A KR 1019970009014A KR 19970009014 A KR19970009014 A KR 19970009014A KR 970065742 A KR970065742 A KR 970065742A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- steel
- high strength
- high toughness
- excellent weldability
- Prior art date
Abstract
본 발명은 강재간에 재질의 분산이 적고 용접성이 우수한 고강도고인성 후강재의 제조방법에 관한 것으로서, C:0.001∼0.25wt%, Mn:1.0∼3.0wt%,Ti:0.005∼0.20wt%, Nb:0.005∼0.20wt%, B:0.0003∼0.0050wt% 및 Al:0.01∼0.100wt%을 함유하며, 잔부는 실질적으로 Fe 및 불가피적 불순물의 조성으로 이루어지고 또 변태개시온도(Bs)가 670℃이하인 강소재를, Ac3점∼1,350℃의 온도로 가열한 후 열간압연을 실시하고, 계속해서 10℃/s이하의 냉각 속도로 냉각하는 것을 특징으로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 미세한 그래뉼러베이나이틱페라이트조직을 나타낸 현미경조직 사진, 제2도는 후강판에 있어서의 냉각속도와 강도와의 관계를 나타낸 도면이다.
Claims (13)
- C:0.001∼0.25wt%, Mn:1.0∼3.0wt%, Ti:0.005∼0.20wt%, Nb:0.005∼0.20wt%, B:0.0003∼0.0050wt% 및 Al:0.01∼0.100wt%을 함유하며, 잔부는 실질적으로 Fe및 불가피적 불순물의 조성으로 이루어지고 또 변태개시온도(Bs)가 670℃이하인 강소재를, Ac3점∼1,350℃의 온도로 가열한 후 열간압연을 실시하고, 계속해서 10℃/s이하의 냉각 속도로 냉각하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항에 있어서, 상기 조성이 하기 (1)식을 만족하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.130Mn+2500Nb≥296 (1)
- 제1항에 있어서, 최종 마무리온도를 800℃이상으로 열간압연을 실시하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 재1항내지 제3항중 어느 한 항에 있어서, 상기 강재가 또한 V:0.04∼0.15wt%, N:0.0035∼0.01000wt%를 함유하는 조성으로 이루어진 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 내지 제3항중 어느 한 항에 있어서, 상기 강재가 또한 V:0.005∼0.04wt%를 함유하는 조성으로 이루어진것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 또는 제3항에 있어서, 상기 강재가 또한 Si:0.60wt%이하, Cr:0.2wt%이하, Ni:0.05∼2.0wt%, Mo:0.5wt%이하, W:0.5wt%이하 및 Cu:0.05∼0.7wt%중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어지며, 또한 하기 (2)식을 만족하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.130Mn-13Ni+2500Nb+55Cu≥296 (2)
- 제1항 내지 제3항중 어느 한 항에 있어서, 상기 강재가 또한, REM:0.02wt%이하 및 Ca:0.006wt%이하중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어진 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 또는 제3항에 있어서, 상기 강제가 V:0.04∼0.15wt%, N:0.0035∼0.01000wt%를 함유하며, 또한 Si:0.60wt%이하, Cr:0.2wt%이하, Ni:0.05∼2.0wt%, Mo:0.5wt%이하, W:0.5wt%이하 및 Cu:0.05∼0.7wt%중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어지며, 하기(2)식을 만족하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법. 130Mn-13Ni+2500Nb+55Cu≥296
- 제1항 내지 제3항중 어느 한 항에 있어서, 상기 강제가 V:0.005∼0.04wt%를 함유하며, 또한 Si:0.60wt%이하, Cr:0.2wt%이하, Ni:0.05∼2.0wt%, Mo:0.5wt%이하, W:0.5wt%이하 및 Cu:0.05∼0.7wt%중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어진 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 내지 제3항중 어느 한 항에 있어서, 상기 강재가 V:0.04∼0.15wt%, N:0.0035∼0.01000wt%를 함유하며,또한 REM:0.02wt%이하 및 Ca:0.006wt%이하중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어진 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 강재가 V:0.005∼0.04wt%를 함유하며 또한 REM:0.02wt%이하 및 Ca:0.006wt%이하중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어진 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.
- 제1항 또는 제3항에 있어서, 상기 강재가 V:0.04∼0.15wt%, N : 0.0035∼0.01000wt%를 함유하며,또한 Si : 0.60wt%이하, Cr : 0.2wt%이하, Ni : 0.05∼2.0wt%, Mo : 0.5wt%이하, W : 0.5wt%이하 및 Cu : 0.05∼0.7wt%중에서 선택된 1종류 또는 2종류 이상을 함유하며, 또한 REM:0.02wt%이하 및 Ca:0.006wt%이하중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어지며, 하기 (2)식을 만족하는 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.130Mn-13Ni+2500Nb+55Cu≥296 (2)
- 제1항 또는 제3항에 있어서, V:0.005∼0.04wt%를 함유하며, 또한 Si:0.60wt%이하, Cr:0.2wt%이하, Ni:0.05∼2.0wt%, Mo:0.5wt%이하, W:0.5wt%이하 및 Cu:0.05∼0.7wt%중에서 선택된 1종류 또는 2종류 이상을 함유하며, 또한 REM:0.02wt%이하 및 Ca:0.006wt%이하중에서 선택된 1종류 또는 2종류 이상을 함유하는 조성으로 이루어진 것을 특징으로 하는 재질의 분산이 적고 용접성이 우수한 고강도 고인성 후강재의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.