JPS63139786A - 通電感熱転写記録リボン用ポリエステルフイルム - Google Patents
通電感熱転写記録リボン用ポリエステルフイルムInfo
- Publication number
- JPS63139786A JPS63139786A JP61287242A JP28724286A JPS63139786A JP S63139786 A JPS63139786 A JP S63139786A JP 61287242 A JP61287242 A JP 61287242A JP 28724286 A JP28724286 A JP 28724286A JP S63139786 A JPS63139786 A JP S63139786A
- Authority
- JP
- Japan
- Prior art keywords
- film
- parts
- polyester
- weight
- polyester film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
ルフイルムに関する。さらに詳しくは、本発明は、伺電
圧で通電することによりリボン自体で内部発生した熱で
感熱転写層を転写して記録するためのポリエステルフィ
ルムに関する。
圧で通電することによりリボン自体で内部発生した熱で
感熱転写層を転写して記録するためのポリエステルフィ
ルムに関する。
〔従来技術と発明が解決しようとする問題点〕近年情報
が著しく豊富となりその情報の迅速な伝達、記録等の必
要性が高まυ、情報処理システム、情報伝達システム及
び情報記録システム等の情報管理システムに関し、洩々
の開発がなされているが、これらの要真青に答えるべく
プリンター分野において、これオでの加熱ヘッドを用い
る通常の感熱転写プリンターに対し通電感熱型のプリン
ターが登場し普及しつつある。
が著しく豊富となりその情報の迅速な伝達、記録等の必
要性が高まυ、情報処理システム、情報伝達システム及
び情報記録システム等の情報管理システムに関し、洩々
の開発がなされているが、これらの要真青に答えるべく
プリンター分野において、これオでの加熱ヘッドを用い
る通常の感熱転写プリンターに対し通電感熱型のプリン
ターが登場し普及しつつある。
該通電感熱型のプリンターは、別名クワイエツト・ライ
ターとも呼ばれ、プリント時の音が静かでかつ、配優速
度を上げることができ、また鮮明な記録画傳を与えるこ
とから、近年極めて注目されている方式である。
ターとも呼ばれ、プリント時の音が静かでかつ、配優速
度を上げることができ、また鮮明な記録画傳を与えるこ
とから、近年極めて注目されている方式である。
通1感熱記録の原理は、図7に示したような通電感熱シ
ートにプリントヘッドから電流を流し抵抗−(カーボン
ブラック含有樹脂)を発熱させて、インキ#(顔料/ワ
ックス等から構成される。)を転写紙に転写させるもの
である。
ートにプリントヘッドから電流を流し抵抗−(カーボン
ブラック含有樹脂)を発熱させて、インキ#(顔料/ワ
ックス等から構成される。)を転写紙に転写させるもの
である。
同図中で導電l@は蒸着At%離型屑はポリケトンから
構成される。この通電感熱シートとしては図/に示した
方式の他にも図コで示した方式等も提案されている。い
ずれにせよ、°これらのit感熱シートを構成する層の
うち最も重要な層は、抵抗層である。現在この抵抗層は
カーボンブラックを含有せしめたポリカーボネートフィ
ルムが用いられている(@公昭57−/り3号公報参照
)。しかるに、該フィルムは、フィルム強關が弱く、溶
液製膜の為コストも高い。
構成される。この通電感熱シートとしては図/に示した
方式の他にも図コで示した方式等も提案されている。い
ずれにせよ、°これらのit感熱シートを構成する層の
うち最も重要な層は、抵抗層である。現在この抵抗層は
カーボンブラックを含有せしめたポリカーボネートフィ
ルムが用いられている(@公昭57−/り3号公報参照
)。しかるに、該フィルムは、フィルム強關が弱く、溶
液製膜の為コストも高い。
そこで、耐熱性、強度に優れかつ、溶融製膜可能なフィ
ルムが求められてきた。
ルムが求められてきた。
本発明者ら社、上記問題点を解決すべく使意検肘の結果
、導電性分散粒子としてカーボンブラックを特定量含有
させたポリエステルフィルムのうち、特定の物性を満足
するフィルムのみが、通電感熱転写記録リボン用フィル
ムとして好適であることを見い出し、本発明を構成する
に至った。
、導電性分散粒子としてカーボンブラックを特定量含有
させたポリエステルフィルムのうち、特定の物性を満足
するフィルムのみが、通電感熱転写記録リボン用フィル
ムとして好適であることを見い出し、本発明を構成する
に至った。
すなわち本発明の要旨は、導電性分散粒子としてカーボ
ンブラックをポリエステル100重量部に対し15重量
部以上60重を部以下含有し、その体積固有抵抗値が1
00〜106Ω・傭の範囲にあり、かつ300℃におけ
るメルトインデックス値が0.st/10m以上である
ことを特徴とする通電感熱転写記録リボン用ポリエステ
ルフィルムに存する。
ンブラックをポリエステル100重量部に対し15重量
部以上60重を部以下含有し、その体積固有抵抗値が1
00〜106Ω・傭の範囲にあり、かつ300℃におけ
るメルトインデックス値が0.st/10m以上である
ことを特徴とする通電感熱転写記録リボン用ポリエステ
ルフィルムに存する。
本発明でいうポリエステルとは、主としてポリエチレン
テレフタレート、ポリエチレン−2,6−ナフタレート
又はポリブチレンテレフタレートであるがこれらの共重
合体又は他のポリエステルとのブレンドが特に好ましい
。共重合成分としては、エチレングリコール、グロピレ
ングリコール、ブタンジオール、キシリレングリコール
、ビスフェノールA、ジエチレンクリコール、ポリエチ
レングリコール、ポリテトラメチレングリコール、ポリ
プロピレングリコール、 /、4’−シクロヘキサンジ
メタツール等のジオール成分、アジピン酸、セパシン酸
、フタル酸、イソフタル酸、p−オキシエトキシ安息香
酸、グリコール酸、テレフタル酸、2,6−ナフタリン
ジカルボン酸等の酸成分が挙げられる。
テレフタレート、ポリエチレン−2,6−ナフタレート
又はポリブチレンテレフタレートであるがこれらの共重
合体又は他のポリエステルとのブレンドが特に好ましい
。共重合成分としては、エチレングリコール、グロピレ
ングリコール、ブタンジオール、キシリレングリコール
、ビスフェノールA、ジエチレンクリコール、ポリエチ
レングリコール、ポリテトラメチレングリコール、ポリ
プロピレングリコール、 /、4’−シクロヘキサンジ
メタツール等のジオール成分、アジピン酸、セパシン酸
、フタル酸、イソフタル酸、p−オキシエトキシ安息香
酸、グリコール酸、テレフタル酸、2,6−ナフタリン
ジカルボン酸等の酸成分が挙げられる。
共重合成分は、全ジオール成分又は全酸成分中/!モル
チ以下であることが好ましい。/!モル俤を超えるとフ
ィルムの耐熱性、強度の低下をきたしてしまう。一方、
ポリプロピレンテレフタレート、ポリベンチレンビスベ
ンゾエート、3−3−ビス−(p−オキシフェニル)ペ
ンタンとテレフタル酸とのポリエステル、J−2−ビス
(3−メチルオキシフェニル)プロパンとテレフタル酸
とのポリエステル、−一2−ビス(p−オキシフェニル
)ペンタンとインフタル酸又はテレフタル酸とのポリエ
ステル、エチレンテレフタレートとエチレンイノフタレ
ートの共重合ポリエステ化、あるいは、セパケート、ア
ジペートなどの入った共重合ポリエステル等を/jy#
ilt%以下ブレンドしてもよい。又、必要に応じて他
ポリマー例えば、ポリカーボネート、ポリアミド、ポリ
オレフィン等をブレンドすることもさしつかえない。
チ以下であることが好ましい。/!モル俤を超えるとフ
ィルムの耐熱性、強度の低下をきたしてしまう。一方、
ポリプロピレンテレフタレート、ポリベンチレンビスベ
ンゾエート、3−3−ビス−(p−オキシフェニル)ペ
ンタンとテレフタル酸とのポリエステル、J−2−ビス
(3−メチルオキシフェニル)プロパンとテレフタル酸
とのポリエステル、−一2−ビス(p−オキシフェニル
)ペンタンとインフタル酸又はテレフタル酸とのポリエ
ステル、エチレンテレフタレートとエチレンイノフタレ
ートの共重合ポリエステ化、あるいは、セパケート、ア
ジペートなどの入った共重合ポリエステル等を/jy#
ilt%以下ブレンドしてもよい。又、必要に応じて他
ポリマー例えば、ポリカーボネート、ポリアミド、ポリ
オレフィン等をブレンドすることもさしつかえない。
本発明のフィルムは、その体積固有抵抗が/θO〜10
−〇・傭の範囲になければならない。
−〇・傭の範囲になければならない。
/θOΩ・mよシ低いと、導電性が良くなシすぎて抵抗
層の発熱量が小さくなり、インク転写に不適である。一
方10”Ω・傭を紹えると、導電性が小さすぎて放電破
壊する友め不適である。
層の発熱量が小さくなり、インク転写に不適である。一
方10”Ω・傭を紹えると、導電性が小さすぎて放電破
壊する友め不適である。
好ましくは、体積固有抵抗は、100〜104Ω・傭、
更に好プしくは100〜103Ω・傭の範囲にある。
更に好プしくは100〜103Ω・傭の範囲にある。
本発明に用いられる導電性分散粒子は、カーボンブラッ
クである。カーボンブラックの粒径は/θミクロン以丁
が好ましく、その含有量は、ポリエステル100重量部
に対し15重量部以上60重帝都以下でなければならな
い。/j重p部よシ少ないと3jf電性を満足しないし
60重量刑を超えると、押出製膜が不可能となる。好ま
しくは、/!重置部以上≠O重量部以下1%に好ましく
は、7jti!jt部以上30重を部以下である。カー
ボンブラックは、低#度で2#電性が々・い方が延伸性
が良好な為好ましい。それ故、カーボンブラックはその
ジブチルフタレート(DBP)吸油量が/ j Otd
/ / 00?以上のものを用いることが好ましく、更
に好ましくは200 yni/ /θθ2以上、数本好
ましくはJ 00 tytt / / 009以上であ
る。
クである。カーボンブラックの粒径は/θミクロン以丁
が好ましく、その含有量は、ポリエステル100重量部
に対し15重量部以上60重帝都以下でなければならな
い。/j重p部よシ少ないと3jf電性を満足しないし
60重量刑を超えると、押出製膜が不可能となる。好ま
しくは、/!重置部以上≠O重量部以下1%に好ましく
は、7jti!jt部以上30重を部以下である。カー
ボンブラックは、低#度で2#電性が々・い方が延伸性
が良好な為好ましい。それ故、カーボンブラックはその
ジブチルフタレート(DBP)吸油量が/ j Otd
/ / 00?以上のものを用いることが好ましく、更
に好ましくは200 yni/ /θθ2以上、数本好
ましくはJ 00 tytt / / 009以上であ
る。
本発明のフィルムは、300℃におけるメルトインデッ
クス値がOljり/10m1n以上であることが必須で
ある。これ以下のフィルムでは、通常の押出機で押し出
せないか、押し出すのだ極めて困難となる。このような
流動性を得る為には、ポリエステル中に、高級脂肪酸又
はその誘導体を、ポリエステル100重量部に対し0.
0/%J部以上、好ましくはo、or重量m以上、更に
好ましくは0.7重量部以上15重量部以下含有せしめ
ることが好ましい。0.0 /重量部よシ少ないと、流
動性改良の効果がなく、又15重量部を超えると、フィ
ルムの粘度が下がシすぎて好ましくない。
クス値がOljり/10m1n以上であることが必須で
ある。これ以下のフィルムでは、通常の押出機で押し出
せないか、押し出すのだ極めて困難となる。このような
流動性を得る為には、ポリエステル中に、高級脂肪酸又
はその誘導体を、ポリエステル100重量部に対し0.
0/%J部以上、好ましくはo、or重量m以上、更に
好ましくは0.7重量部以上15重量部以下含有せしめ
ることが好ましい。0.0 /重量部よシ少ないと、流
動性改良の効果がなく、又15重量部を超えると、フィ
ルムの粘度が下がシすぎて好ましくない。
又、本発明における高級脂肪族カルボン酸又はその誘導
体としては炭tA数//以上の高級脂肪族カルボン酸又
はその誘導体が好ましく、更に好ましぐは、高級脂肪族
モノカルボン酸又はその誘導体である。具体例としては
、カプリン酸、ラウリル酸、ステアリン酸、ノナデカン
酸。
体としては炭tA数//以上の高級脂肪族カルボン酸又
はその誘導体が好ましく、更に好ましぐは、高級脂肪族
モノカルボン酸又はその誘導体である。具体例としては
、カプリン酸、ラウリル酸、ステアリン酸、ノナデカン
酸。
アラキン酸、ベヘン酸、メリシン酸、カルナクバ酸、リ
グノセリン酸、セロチン酸、モンタンア 酸、ヘントリlコン酸、ペトロセリン酸、オレイン酸、
エリカ酸、リノール酸およびこれらの酸混合物並びに炭
素数7/以上の合成モノカルボン酸托が挙げられる。高
級脂肪族カルボン酸の誘導体としては、上記カルボン酸
の金属塩、エステル、アミド等が挙げられる。又、金桝
種としてはアルカリ金「及びアルカリ土類金属、例えば
、リチウム、ナトリウム、カリウム、バリウム、マグネ
シウム、カルシウム、ストロンチウム等が挙げられる。
グノセリン酸、セロチン酸、モンタンア 酸、ヘントリlコン酸、ペトロセリン酸、オレイン酸、
エリカ酸、リノール酸およびこれらの酸混合物並びに炭
素数7/以上の合成モノカルボン酸托が挙げられる。高
級脂肪族カルボン酸の誘導体としては、上記カルボン酸
の金属塩、エステル、アミド等が挙げられる。又、金桝
種としてはアルカリ金「及びアルカリ土類金属、例えば
、リチウム、ナトリウム、カリウム、バリウム、マグネ
シウム、カルシウム、ストロンチウム等が挙げられる。
本発明のポリエステルフィルムとしてl/i、未延伸で
熱固定したフィルムも使用不可能ではないが、強度、耐
熱性、表面性、厚A精塵の点で劣るため、−軸もしくは
二軸方向に少くとも/、を倍以上10倍以下の面積倍率
で延伸したのち、150℃以上の温度で/秒…1〜/θ
分間熱固定したものを用いるのが好捷しい。面積倍率が
/、2倍より低い場合には、強度、表面性、厚み精度の
改良が顕著でなく好ましくない。一方面積倍率が70倍
を超えると導電性の低下が著しく不適である。一方、本
発明のポリエステルの固有粘度はθ、If/dt以上好
ましくは0.弘2/#以上、更KtFFましくは0.s
t/dt以上である。固有粘度がθ、Jt/dlよシ低
いと、フィルムが極めてもろい上延伸が極めて困難であ
る。
熱固定したフィルムも使用不可能ではないが、強度、耐
熱性、表面性、厚A精塵の点で劣るため、−軸もしくは
二軸方向に少くとも/、を倍以上10倍以下の面積倍率
で延伸したのち、150℃以上の温度で/秒…1〜/θ
分間熱固定したものを用いるのが好捷しい。面積倍率が
/、2倍より低い場合には、強度、表面性、厚み精度の
改良が顕著でなく好ましくない。一方面積倍率が70倍
を超えると導電性の低下が著しく不適である。一方、本
発明のポリエステルの固有粘度はθ、If/dt以上好
ましくは0.弘2/#以上、更KtFFましくは0.s
t/dt以上である。固有粘度がθ、Jt/dlよシ低
いと、フィルムが極めてもろい上延伸が極めて困難であ
る。
この為、カーボンブラック等を含有せしめたポリエステ
ルチップを固相重合によシ固有粘度を上げるのも好まし
い方法である。
ルチップを固相重合によシ固有粘度を上げるのも好まし
い方法である。
又、本発明のポリエステルは、押出法にょシフイルム化
するが、その際スクリューとしては二軸の押出機を用い
るのが好ましい。かくして得られたフィルムの厚さは、
靭に限定されるものではないが2ミクロン〜!Oミクロ
ンであるのが好ましい。
するが、その際スクリューとしては二軸の押出機を用い
るのが好ましい。かくして得られたフィルムの厚さは、
靭に限定されるものではないが2ミクロン〜!Oミクロ
ンであるのが好ましい。
かくして、従来の溶液流延法によるカーボンブラック含
有ポリカーボネートフィルムに比べ、機械的性質、コス
ト等に優れた通!感熱転写すボン用フィルムが提供され
る。
有ポリカーボネートフィルムに比べ、機械的性質、コス
ト等に優れた通!感熱転写すボン用フィルムが提供され
る。
以下本発明を実施例によシ、具体的に説明するが、本発
明は、その要旨を超えない限り、これらの実施例に限定
されるものではない。なお本発明におけるフィルム及び
通電感熱転写リボンとしての特性評価については、下記
に示した方法による。
明は、その要旨を超えない限り、これらの実施例に限定
されるものではない。なお本発明におけるフィルム及び
通電感熱転写リボンとしての特性評価については、下記
に示した方法による。
ω 体積固有抵抗値(Ω・cm)
JISa−23irに従って測定し次。
(2) メルトインデックス値
宝工業昨メルトインデクサ−L20JによりJXB−に
−7210に準拠して荷重2010fKて測定した。
−7210に準拠して荷重2010fKて測定した。
(3)DBP吸油量
:J工8 Kご一コ/の吸油量測定A法によりアブツー
ブトメーターによシジプチル7タレー)(DBP)をカ
ーボンブラックに吸油させて測定した。
ブトメーターによシジプチル7タレー)(DBP)をカ
ーボンブラックに吸油させて測定した。
(4)固有粘度
試料200119をフェノール/テトラクロロエタン=
s o / joの混合溶媒−〇 N11に加え約/
10℃で7時間加熱溶解後、30℃で測定した。カーボ
ンブラックを含有する場合は上記溶解液を3万回転・時
間超遠心をかけてカーボンブラックを除いた後ポリマ一
部分のみで粘度を測定した。
s o / joの混合溶媒−〇 N11に加え約/
10℃で7時間加熱溶解後、30℃で測定した。カーボ
ンブラックを含有する場合は上記溶解液を3万回転・時
間超遠心をかけてカーボンブラックを除いた後ポリマ一
部分のみで粘度を測定した。
(5)機械的強度
東洋ボールドウィン製テンシロンUTM−1型を用いて
、20℃湿度t5%において、長さj OaI、巾ご、
、2jMの試料フィルムを50m/I!Iの速度で引張
り、破断した時の張力をFB (#/mil )その時
の伸びを”B(%) とした。
、20℃湿度t5%において、長さj OaI、巾ご、
、2jMの試料フィルムを50m/I!Iの速度で引張
り、破断した時の張力をFB (#/mil )その時
の伸びを”B(%) とした。
(6)通電感熱転写リボンの特性評価
イ鼻られた76μのフィルム上にアルミニウムを蒸着さ
せ、更にポリケトンの離形廣、顔料を含むカーボンブラ
ックインクをコーティングしてリボンを作成する。該リ
ボンをクワイエツトライターを用いたタイプライタ−(
よりM t7s−0)を用いて、印字して、その画・質
よシリボンとしての良否を判定した。
せ、更にポリケトンの離形廣、顔料を含むカーボンブラ
ックインクをコーティングしてリボンを作成する。該リ
ボンをクワイエツトライターを用いたタイプライタ−(
よりM t7s−0)を用いて、印字して、その画・質
よシリボンとしての良否を判定した。
(実施例7〜3)
吸油fj d 0wt1/ / 00 tの三菱化成社
製導電性カーボンブラックを、ステアリン酸マグネシウ
ムを7.0*tC’16含有せしめたポリエチレンテレ
フタレート(〔η)=O,gg) の粉体100重量
部に対しコji!rt部の印1合で混合しiro℃弘時
間窒素下で乾燥したのち、二軸の押出機を用いて押出し
ペレット化した。該ペレットを200℃真空下で同相重
合し、〔η〕=0.50のペレットを得た。該ペレット
を再度/rO′C≠時間窒素下で乾燥したのち、λ軸の
押出機にて300℃にて押出し、キャスティングドラム
上に冷却固化させ未延伸フィルムを得た。この際、静電
密着法にて密着固化させた。該未延伸フィルムを、表/
に示す延伸倍率で25℃にて縦方向、りO℃にて横方向
に延伸したのち、200℃にて熱固定して/≦μのフィ
ルムを得た。これらのフィルムの評価結果を表/に示す
。
製導電性カーボンブラックを、ステアリン酸マグネシウ
ムを7.0*tC’16含有せしめたポリエチレンテレ
フタレート(〔η)=O,gg) の粉体100重量
部に対しコji!rt部の印1合で混合しiro℃弘時
間窒素下で乾燥したのち、二軸の押出機を用いて押出し
ペレット化した。該ペレットを200℃真空下で同相重
合し、〔η〕=0.50のペレットを得た。該ペレット
を再度/rO′C≠時間窒素下で乾燥したのち、λ軸の
押出機にて300℃にて押出し、キャスティングドラム
上に冷却固化させ未延伸フィルムを得た。この際、静電
密着法にて密着固化させた。該未延伸フィルムを、表/
に示す延伸倍率で25℃にて縦方向、りO℃にて横方向
に延伸したのち、200℃にて熱固定して/≦μのフィ
ルムを得た。これらのフィルムの評価結果を表/に示す
。
(実施例4=)
実施例/において、ポリエチレンテレフタレート単独を
用いる代りにグリコール成分としそ分子−Jit、r、
oootvポリエチL/7グリコール0,2 dモルチ
を含有した共重合ポリエチレンテレフタレートを用い、
実施例/のカーボンブラック量をポリエステル100重
量部に対して30重量部に変更した以外は実施例/と同
様にして製膜し、76μのフィルムを得た。
用いる代りにグリコール成分としそ分子−Jit、r、
oootvポリエチL/7グリコール0,2 dモルチ
を含有した共重合ポリエチレンテレフタレートを用い、
実施例/のカーボンブラック量をポリエステル100重
量部に対して30重量部に変更した以外は実施例/と同
様にして製膜し、76μのフィルムを得た。
(比較例/)
実施例/において、カーボンブラック含有量をポリエス
テル100重量部に対して/Q重敷部とする以外は実施
例/とI8′1様にして/にμのフィルムを得た。
テル100重量部に対して/Q重敷部とする以外は実施
例/とI8′1様にして/にμのフィルムを得た。
(比較例2)
実施例/においてカーボンブラック含有量をポリエステ
ル100眞量部に対して35重量部とする以外は、実施
例/と園様にしてフィルム化しようとしたが、ペレット
に押出す際押出機のトルクが高くなりすぎて押出不可能
であった。
ル100眞量部に対して35重量部とする以外は、実施
例/と園様にしてフィルム化しようとしたが、ペレット
に押出す際押出機のトルクが高くなりすぎて押出不可能
であった。
(実力白側j)
実施例弘において、吸油11 J 40tnl/ /
0θ?のカーボンブラックに対して吸油431200
m//1ootのカーボンブラックを用い、その使用量
をポリエステル10θ重散部に対してsO重置部にする
以外lは実施例参と同様にしてfA膜し76μのフィル
ムを得た。しかしながら縦横の延伸倍量が2倍″x2倍
では11j〔伸出来なかった。
0θ?のカーボンブラックに対して吸油431200
m//1ootのカーボンブラックを用い、その使用量
をポリエステル10θ重散部に対してsO重置部にする
以外lは実施例参と同様にしてfA膜し76μのフィル
ムを得た。しかしながら縦横の延伸倍量が2倍″x2倍
では11j〔伸出来なかった。
(比較例3)
市販のカーボンブラック含有ボリカーボネートフイAム
(マクロホールKLj−100ワ;)くイニル社IL’
! )を用い評価した。
(マクロホールKLj−100ワ;)くイニル社IL’
! )を用い評価した。
表/よシ明らかなごとく本発明のポリエステルフィルム
は、機神的性質にすぐれかつ、印字性能にも優れた、低
コストの通電Wlc熱転写リボンの堤供を可能とする。
は、機神的性質にすぐれかつ、印字性能にも優れた、低
コストの通電Wlc熱転写リボンの堤供を可能とする。
図/及びlil、2は、通!感熱シートの層構成を示す
断面図である。 出 願 人 ダイアホイル株式会社 代 理 人 弁理士 長谷用 −ほか7名 図 1 図 2
断面図である。 出 願 人 ダイアホイル株式会社 代 理 人 弁理士 長谷用 −ほか7名 図 1 図 2
Claims (4)
- (1)導電性分散粒子としてカーボンブラックをポリエ
ステル100重量部に対して15重量部以上60重量部
以下含有し、その体積固有抵抗値が10^0〜10^6
Ω・cmの範囲にあり、かつ300℃におけるメルトイ
ンデックス値が0、5g/10mm以上であることを特
徴とする通電感熱転写記録リボン用ポリエステルフィル
ム。 - (2)ジブチルフタレート(DBP)吸油量が150m
l/100g以上のカーボンブラックを用いることを特
徴とする特許請求の範囲第1項記載の通電感熱転写記録
リボン用ポリエステルフィルム。 - (3)導電性分散粒子を含有するポリエステルフィルム
が一軸もしくは二軸方向に少くとも 1、8倍以上10倍以下の面積倍率で延伸され、かつ1
50℃以上の温度で熱固定されていることを特徴とする
特許請求の範囲第1項又は第2項記載の通電感熱転写記
録リボン用ポリエステルフィルム。 - (4)ポリエステル100重量部に対し、高級脂肪族カ
ルボン酸及び/又はその誘導体が0.01重量部以上1
5重量部以下含有されていることを特徴とする特許請求
の範囲第1項ないし第3項のいずれかに記載の通電感熱
転写記録リボン用ポリエステルフィルム。