JPS6038129A - 厚手のプラスチツクスシ−トの接続方法 - Google Patents

厚手のプラスチツクスシ−トの接続方法

Info

Publication number
JPS6038129A
JPS6038129A JP58146696A JP14669683A JPS6038129A JP S6038129 A JPS6038129 A JP S6038129A JP 58146696 A JP58146696 A JP 58146696A JP 14669683 A JP14669683 A JP 14669683A JP S6038129 A JPS6038129 A JP S6038129A
Authority
JP
Japan
Prior art keywords
seal tape
heat
heat seal
thick plastic
sheets
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP58146696A
Other languages
English (en)
Other versions
JPH0224652B2 (ja
Inventor
Yoshio Hayamizu
速水　義雄
Kazuo Ogawa
小川　和雄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ube Corp
Original Assignee
Ube Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ube Industries Ltd filed Critical Ube Industries Ltd
Priority to JP58146696A priority Critical patent/JPS6038129A/ja
Publication of JPS6038129A publication Critical patent/JPS6038129A/ja
Publication of JPH0224652B2 publication Critical patent/JPH0224652B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 この発明は、特定のホントメルトタイプの接着剤層と源
橋ポリオレフィン層とからなるヒートシールテープを使
用して、加熱接着により厚手のプラスチックスシートを
接続する方法に係る。
最近、広い幅を有する厚手のプラスチックスシートを、
潅厩用の河川、小さい池などに全面的に敷いて、水が地
中にしみこんでしまうことを防止しようとする試みが行
われつつある。
−ＪＩ＆に、約１龍以上の厚手のプラスチックスシート
は、大きな幅のシートを成形機から直接成形して得るこ
とが困難であり、成形機から直接成形される厚手のシー
トの幅が最大クラスで約２００印程度であったので、広
い幅を有する厚手のプラスチックスシートを製造するた
めには、複数のシートを互いに貼り合わせて接続するこ
とによって行われていたのである。
しかし、厚手のプラスチックスシートを貼り合わせて接
続する方法としては、例えば、厚手のシートを熱融着す
る方法が通常行われるのであるが、その熱融着が、厚い
シートの熱伝導の悪いために極めて困難であって、実際
には、特別の装置を備えた工場でしか行われておらず、
（その工場生産の広い幅のシートにも幅に制限がありせ
いぜい約１０ｍ程度であり）、河川、池などの潅既の施
工現場におい°Ｃ長大な厚手のシートの接続を簡易的に
行うことができなかったのである。
従って、広い幅を存する厚手のプラスチックスシートに
よる湿温用の防水施工という上述の試みは実施されるこ
とが少なかったのである。
この発明者らは、施工現場においても容易に厚手のプラ
スチックスシートを接続する方法について、鋭意研究し
た結果、特定のボットメルトタイプの接着剤層と架橋ポ
リオレフィン層とからなるヒートシールテープを使用し
て、約５０〜１１０℃の低温度でヒートシールテープを
１７手のプラスチックスシートの端縁部に仮接着して、
次いで高温にヒートシールテープを加熱して加熱接着す
ることにより厚手のプラスチックスシートを接続する方
法を見いだし、この発明を完成した。
すなわち、この発明は、約５０−１１０”Ｃの範囲内の
融点を有する接着剤成分を少なくとも１０重量％含有し
ていて、約５０〜１１０℃の低温度で仮接着の可能なホ
ントメルトタイプの接着剤層と架橋ポリオレフィン層と
からなるヒートシールテープを、２枚の厚手のプラスチ
ックスシートの接続すべき端縁部同士の上に沿って重ね
合わせながら、ヒートシールテープの接着剤層および／
または前記端縁部の表面を予備加熱して、約５０〜ｌｌ
Ｏ℃の低温度でヒートシールテープを仮接着して、 次いで、その仮接着されているヒートシールテープの外
側面から充分に加熱し押圧力を加え、厚手のプラスチッ
クスシートの端縁部とヒートシールテープとを加熱接着
することを特徴とする厚手のプラスチックスシートの接
続方法に関する。
この発明の方法は、加熱によってシートの接続を行いな
がら、厚手のプラスチックスシートの端縁部以外に大き
な熱履歴を与えず、その端縁部においても極めて表面的
で短時間の加熱であるので厚手のプラスチックスシート
が接続作業中に大き（波打ってしまったり、融解して破
れてしまうことがない。
また、この発明の方法で得られる接続された厚手のプラ
スチックスシートの接続部は、上述のように大きい熱履
歴を受けないようにヒートシールテープの仮接着が行わ
れた後にホットメルトタイプの接着剤層の加熱接着が行
われるので、その加熱接着面に気泡を生じたり、水道と
か皺ができたりすることがなく、防水性の優れた強固な
接合によって接続が行われているのである。
さらに、この発明の方法は、厚手のプラスチックスシー
トとヒートシールテープとを適宜配置すること、部分的
な加熱作業とが主体であるので、必要な資材があれば、
施工現場でも、工場でも簡単に実施することができるの
である。
以下、この発明について、図面も参考にして、さらに詳
しく説明する。
第１図は、厚手のプラスチックスシートの端縁部の上に
、ヒートシールテープを仮接着している状況を例示する
斜視図である。
第２図は、厚手のプラスチックスシートの端縁部の上に
、仮接着されたヒートシールテープを、さらに加熱して
その厚手のシートに加熱接着している状況を例示する斜
視図である。
第３図は、この発明の方法によって接続された厚手のプ
ラスチックスシートを例示する平面図および側面図であ
る。
この発明の方法において第３図に示すように使用される
ヒートシールテープは、約５０〜１１０℃の範囲内、特
に約６０〜１００℃の範囲内の融点を有する接着剤成分
、例えば、粘着付与剤（タッキファイヤ−）、重合体成
分、その他の充填剤などを少なくとも１０重量％、特に
２０〜１００重量％含有していて、約５０〜１１０℃の
低温度で仮接着の可能なホントメルトタイプの接着剤Ｉ
Ｈ３と、架橋ポリオレフィンＮ４とからなるヒートシー
ルテープ２である。
前記のホントメルトタイプの接着剤層３は、主として、
オレフィン系（共）重合体と粘着付与剤とを含存する加
熱溶融性の接着剤（ホントメルトタイプの接着剤）で形
成されていることが好ましく、前記の約５０〜１１０℃
の範囲内の温度での仮接着における厚手のプラスチック
スシートの表面に対する粘着力または接着力（１８０度
剥離、引張り速度１０ｎ／分、２０℃）が約０．０１〜
１゜０ｋｇ／ｃｇ＋、特に約０．０５〜０．８ｋｇ／ａ
ｍ程度であって、さらに、約１２０〜２５０℃の高温に
充分に加熱して行う加熱接着における厚手のプラスチッ
クスシートの表面に対する接着力が約２．０〜３０ｋｇ
／ａｍ、特に約４．０〜２５ｋｇ／ｃｍ程度である接着
剤で形成されていることが好ましい。
そのような接着剤に使用されるオレフィン系（共）重合
体としては、例えば、ポリエチレン、ポリプロピレン、
ポリ塩化ビニル、エチレン・酢酸ビニル共重合体、エチ
レン・プロピレンＪ’＝　ｍ　合体、またエチレン・エ
チルアクリレート共重合体、エチレン・メチルアクリレ
ート共重合体、エチレン・エチルメタアクリレート共重
合体などのエチレン・　（メタ）アクリレート共重合体
、あるいはエチレン・アクリル酸共重合体、エチレン・
メタクリル酸共重合体などのエチレン・　（メタ）アク
リル酸共重合体など、並びに、それらの重合体の変性物
（例えば、マレイン化ポリエチレン、マレイン化ポリプ
ロピレンなど）を挙げることができ、それらは単独また
は二種類以上の混合物として用いてもよい。
また、前記の接着剤に使用される粘着付与剤としては、
公知のホントメルトタイプの接着剤において一般に使用
される粘着付与剤から任意に選択することができ、その
粘着付与剤の例としては、ロジンまたはロジン誘導体、
ピネン系樹脂、クマロン樹脂、クマロン・インデン樹脂
、その他の脂肪族または脂環族炭化水素樹脂、芳香族炭
化水素樹脂などを挙げることができ、それらの中でも融
点が約１１０℃以下、とくに約６０〜１００℃であるも
のが最適である。
この発明において、ヒートシールテープに設けられてい
る接着剤層は、前述の成分の他に、例えば、タルク、炭
カル、シリカ、アルミナ、マイカ、カーボンブラックな
どの無機充填剤、または、酸化防止剤、着色剤、軟化剤
などの添加剤が配合されていてもよい。
この発明の方法においては、前記の接着剤として、例え
ば、ポリオレフィンまたは変性ポリオレフィン（特にエ
チレン系重合体）約５０〜９５重量％、特に６０〜９０
重景％と重量点が約１１０℃以下、特に約６０〜１００
℃である粘着付与剤約５〜５０重量％、特に１０〜４０
重量％とを主成分として含有しているボッ１−メルトタ
イプの接着剤が、約５０〜１１０℃の範囲内の温度で厚
手のプラスチックスシー１〜（特にポリオレフィンシー
ト）の表面に対して仮接着し、さらに約１２０〜２５０
℃の高温に加熱して加Ｑ接着することができ、その接着
後の接着力が充分に高いので、特に、適当である。
なお、この発明において、ピー１シールテープの接着剤
層は、電子線、Ｘ線、α線、β線、γ線などの高エネル
ギー線の照射によるが、または、過酸化物などの架橋剤
の化学反応によって、重合体成分について適度の架橋が
なされていることが、厚手のプラスチックスシートに対
する接着力の向上のためにとくに適当であり、その架橋
の程度が、後述のゲル分率で示して、約５〜５０％、特
にｌＯ〜４０％程度であることが最適である。
前記のゲル分率とは、測定すべき試料を、キシレン中に
入れて、約１０時間、約１３０℃の温度で還流しながら
溶解させ、そのキシレンに溶解し　゛なかった試料の重
量（Ａｇ）を、使用した全試料の重量（Ｂｇ）で割って
得られた値を１００倍した値である。
ゲル分率＝　（Ａ／Ｂ）Ｘ１００　（％）この発明の方
法において使用されるヒートシールテープの架橋ポリオ
レフィン層４は、例えば、ポリエチレン、ポリプロピレ
ン、エチレン・プロピレン共重合体、エチレン・酢酸ビ
ニル共重合体などのオレフィン系重合体を主成分とし、
および、他の重合体、可塑剤、酸化防止剤、ｆｆ燃燃剤
剤充填剤（炭カル、シリカ、アルミナ、マイカ、カーボ
ンブランクなど）、着色剤などが配合されているポリオ
レフィン樹脂組成物から、押し出し成形などによって、
ポリオレフィンフィルムまた。はシート（厚さ約１００
〜３０００μ、特に１５０〜２５００μ）を形成し、そ
のポリオレフィンフィルムまたはシートを電子線、Ｘ線
、α線、γ線などで架橋して得られた架橋ポリオレフィ
ンフィルムまたはシートで形成されていればよく、その
架橋ポリオレフィンフィルムまたはシートの架橋の程度
が、ゲル分率で示して、約２０〜９０％、特に３０〜８
０％程度であることが好ましい。
前記のヒートシールテープは、例えば、前述のポリオレ
フィン樹脂組成物から押出し成形でポリオレフィンフィ
ルムまたはシートを形成し、そのフィルムまたはシート
の上に接着剤を押出すラミネート法で被覆して、接着剤
層を形成し、次いで、そのｆｆｆｌｉｆ体（シート）を
接着剤層側から電子線などで架橋して、部分的に架橋さ
れた接着剤層と、架橋ポリオレフィン層とからなるテー
プとして製造することができ、そのほか、別々に架橋ポ
リオレフィンフィルムまたはシートと、接着剤シートと
を製造しておき、両者を貼り合わせることによって積層
体（シート）を形成し、さらに接着剤層側から電子線照
射などで架橋することによっても製造することができる
。
この発明では、ヒートシールテープにおける接着剤層と
架橋ポリオレフィン層とは、特にそれらの厚さが限定さ
れるものではないが、例えば、接着剤層の厚さが、約０
．１〜３．０　ｍ讃、特に０．１〜２゜５鰭程度であり
、架橋ポリオレフィン層の厚さが、約０．１　＝　４．
０顛、特に０．１〜３．０１ｌＩＩ程度であって、また
、接着剤層と架橋ポリオレフィン層との厚さの比が、約
１：１０〜３：１程度であり、さらに、ヒートシールテ
ープ全体の厚さが、約０．５〜５關、特に１〜４＋ａｍ
程度であることが、その取扱に便利な柔軟性を有するた
め、あるいは接続後に充分な機械的強度を有するために
好ましい。また、ヒートシールテープの幅（そのテープ
の長手方向に直角の方向の長さ）は、約５〜５Ｑｃｍ、
特に１０〜５０ｃｍ程度であることが好ましい。
なお、この発明においては、前記のヒートシールテープ
は、架橋ポリオレフィン層の外側に、さらに耐熱性およ
び／または耐炎性の補強材層（例えば、ガラスクロス層
、アルミ箔層、アスベスト層など）が設けられていても
よい。
この発明の方法においては、まず、第１図に示すように
、２枚の厚手のプラスチックスシート１゜１°が、その
接続すべき端縁部同士を一部重ね合わされて配置されて
いて、前述の接着剤層３と架橋ポリオレフィン層４とを
有するヒートシールテープ２を、その２枚のｊｖ−手の
シー１−１’、１”の接続すべき端縁部同士の上に沿っ
て、重ね合わせながら、そのヒートシールテープ２の接
着剤層３および／または厚手のシート１，１゛の接続す
べき端縁部の表面を、例えば、ガスバーナー５の火炎な
どで予備加熱して、約５０〜１１０℃、特に６０〜１０
０℃の低温度でそのヒートシールテープ２を仮接着（お
よび／または粘着）するのである。
この発明の方法では、前述のそのヒートシールテープ２
を厚手のシート１．ｌ’　の接ｂｅずべき端縁部同士の
上に沿って、重ね合わ一部る作業において、ヒートシー
ルテープ２の供給を、そのテープの緊張状態で行うこと
が好ましい。
また、前述のように、２枚の厚手のプラスチ・ノクスシ
ート１，１”の接続ずべき端縁部同士を一部重ね合わせ
て配置する場合に、その重ね合わせられた端縁部同士の
間に両面テープなどを介在させて、両シートを仮に固定
すると、両シートの重ね合わせた部分がずれることがな
く、上述のヒートシールテープを仮接着する作業が容易
になるので好ましい。
また、この発明の方法では、上述のヒートシールテープ
を仮接着する作業において、仮接着されつつあるヒート
シールテープ２の上面に、例えば、押さえ付はロール６
　（例えば、金属ロール、ゴムロール、スポンジロール
、段差ロールなど、またはそれらの組合せロール）によ
る押圧力を加えるＶとが、ヒートシールテープ２を厚手
のポリオレフィンシートの接続すべき端縁部に対して（
特に重ね合わせに伴う段差部に対して）全面的に均一に
仮接着することができるので望ましい。
この発明においては、比較的低温度で、特定のヒートシ
ールテープを、厚手のプラスチックスシートの接続すべ
き端縁部同士の上に一旦仮接着することが、特に重要で
ある。すなわち、この発明では、この前段階の作業を行
うことによって、後続の本接着の作業が、ヒートシール
テープに皺、ずれの生ずることもなく、またヒーＩ・シ
ールテープと厚手のシートとの間に気泡、ばがれを生ず
ることもなく、効果的に行われるし、しかも、厚手のシ
ートに過剰の熱＠歴を与えることがないので、厚手のシ
ート自体が熱的に変形（カール）したり、皺になったり
、融解して破れたりすることがなく、厚手のシートの耐
久性を１１１な・うこともほとんどないのである。
この発明の方法においては、＋’＋ｉＪ述のヒートシー
ルテープの仮接着に続いて、第２１２１に示゛」゛よう
に、その仮接着されているヒートシールテープ２を、そ
の外側面から、例えば、ガスバーナー５′の火炎などで
、約１２０〜２５０°Ｃの高温度に加熱し、前述と同様
の押さえ付はロール６′　（特に、弾性ロール、スポン
ジロールなど）で押圧力を加え、厚手のプラスチックス
シート１．１°の端縁部と、ヒートシールテープ２とを
約１２０〜２５０℃、特に１３０〜２００℃の高温度で
加熱接着（融着）するのである。
この発明では、前述の高温度での加熱接着において、ガ
スバーナー５′の火炎が、前記仮接着されているヒート
シールテープ２の両端より外側にまで到達しないように
、適当な防炎壁、防炎用衝立などを設置したり、または
、防炎シートまたは板などをヒー　トシールテーブ２の
重ね合わされている両側の厚手のシートの表面に配置し
ておくことが適当である。
この発明では、前述の予備加熱および１ｌＩＩ温度の加
熱は、前記のガスバーナーの火炎で行うばかりではなく
、他の公知の加熱手段、例えば、電気ヒーター、赤外線
ヒーター、他の熱線ヒーター、加熱ロール、電気ゴテ、
加熱媒体の吹きつげなどで行うこともでき、また、押さ
えイ」けロールについても他の押さえ付は手段を用いて
もよい。
さらにこの発明の方法では、例えば、ヒートシールテー
プの仮接着作業を完結したのちに、それに続く高温度で
の加熱接着作業を行うことも、あるいは、両者の作業を
ほとんど同時にわずかな時間差で近接して連続的に行う
こともできる。
この発明の方法は、極めて単純な操作によって、厚手の
プラスチックスシー１−を接続できるので、湿温用の河
川、溜池などの施工現場で幅２ｍ以下の厚手のプラスチ
ックスシートの多数枚を次々と接続して長大な広幅のシ
ートを形成し同時に施設することができる。
この発明の方法で接続される厚手のプラスチックスシー
トは、潅ｔＫ用の河川、溜池などに施設して充分な耐久
性、耐候性、さらに機械的強度、防水性を示しうるもの
であれば、どのような種類のプラスチックスシー（・で
あってもよく、例えば、ポリエチレン、ポリプロピレン
、ポリ塩化ビニル、エチレン・酢酸ビニル共重合体、エ
チレン・プロピレン共重合体などのオレフィン系重合体
を主成分とする樹脂組成物から成形された厚さ約０．５
〜５鰭、特に１〜４鮪程度であり、幅約５０〜２０θ印
であるポリオレフィンシート（特にポリエチレン／ン、
エチレン・酢酸ビニル共重合体などのエチレン系重合体
のシート）が適当である。
この発明の方法で接続されたプラスチックス（ポリオレ
フィン）シートは、第３図に示すように、厚手のプラス
チックスシート１，１″の端縁部が互いに重ね合わされ
ている部分が、ヒートシールテープ２で接着剤層３を介
して強力に接合されているので、この接続部分が、充分
な強度、防水性を有しており、湿温用の河川、溜池に現
場で施設して防水用として使用することができる。
【図面の簡単な説明】
第１図は、厚手のプラスチ・ノクスシートの端縁部の上
に、ヒートシールテープを仮接着している状況を例示す
る斜視図である。 第２図は、厚手のプラスチ・ノクスシートの端縁部の上
に、仮接着されたヒートシールテープを、さらに加熱し
てその厚手のシートに加熱接着している状況を例示する
斜視図である。 第３図は、この発明の方法によって接続された厚手のプ
ラスチックスシートを例示する平面図および側面図であ
る。 １．１’　？厚手のプラスチックスシート、２；ヒート
シールテープ、３；接着剤層、４；架橋ポリオレフィン
層、５．５”　；ガスバーナー、６゜６°　；押さえ付
はロール。 特許出願人　宇部興産株式会社

Claims (1)

  1. 【特許請求の範囲】 約５０〜１１０℃の範囲内の融点を有する接着剤成分を
    少なくとも１０重量％含有していて、約５０〜１１０℃
    の低温度で仮接着の可能なホントメルトタイプの接着剤
    層と架橋ポリオレフィン層とからなるヒートシールテー
    プを、２枚の厚手のプラスチックスシートの接続すべき
    端縁部同士の上に沿って重ね合わせながら、ヒートシー
    ルテープの接着剤層および／または前記端縁部の表面を
    予備加熱して、約５０〜１１０℃の低温度でヒートシー
    ルテープを仮接着して、　− 次イで、その仮接着されているヒートシールテープの外
    側面から充分に加熱し押圧力を加え、厚手のプラスチッ
    クスシートの＆Ｉｉｌ　ｋ１部とヒートシールテープと
    を加熱接着することを特徴とする厚手のプラスチックス
    シートの接続方法。
JP58146696A 1983-08-12 1983-08-12 厚手のプラスチツクスシ−トの接続方法 Granted JPS6038129A (ja)