JPS59169821A - パリソン - Google Patents

パリソン

Info

Publication number
JPS59169821A
JPS59169821A JP58042413A JP4241383A JPS59169821A JP S59169821 A JPS59169821 A JP S59169821A JP 58042413 A JP58042413 A JP 58042413A JP 4241383 A JP4241383 A JP 4241383A JP S59169821 A JPS59169821 A JP S59169821A
Authority
JP
Japan
Prior art keywords
neck
piece
part piece
biaxially stretched
parison
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP58042413A
Other languages
English (en)
Other versions
JPH0224202B2 (ja
Inventor
Tatsuo Kato
達夫 加藤
Noboru Kato
登 加藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Petrochemical Industries Ltd
Original Assignee
Mitsui Petrochemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Petrochemical Industries Ltd filed Critical Mitsui Petrochemical Industries Ltd
Priority to JP58042413A priority Critical patent/JPS59169821A/ja
Publication of JPS59169821A publication Critical patent/JPS59169821A/ja
Publication of JPH0224202B2 publication Critical patent/JPH0224202B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明はポリエチレンテレフタレート樹脂製二軸延伸中
空体成形用のパリソンの製造方法に関する。更に詳しく
は、それぞれ別個に成形された未延伸の首部片と非品性
の有底胴部片とを溶融接着してなるパリソンの製造方法
に関する。
ホ゛リエチレンテレフタレー）樹脂（以下ｐＥＴと呼ぶ
ことがある）の二軸延伸中空体は機械的強度、剛性、耐
熱性、耐薬品性、耐油性、透明性、耐ガス透過性に優れ
るので、醤油、液体洗剤、化粧品等の容器として近年広
く使われるようになった。ＰＥＴの二軸延伸中空体は通
常射出成形あるいは押出成形により予め非品性のパリソ
ン（二軸延伸中空成形前の前駆成形体、プリフォーム）
を成形し、次いで該パリソンを中空成形用金型内で縦方
向及び横方向に延伸することにより得られるが、中空体
の首部は二軸延伸成形時にパリソンを金型を取り付ける
際に把持する為、全く二軸延伸されない。この為、二軸
延伸された胴部と異なり、首部は非晶状態のまま中空体
となるので、二軸延伸することによって充分に発揮され
る前記性能が首部では発揮されないという欠点を有して
いる。
前記欠点を解消する方法として、例えばパリソンあるい
は二軸延伸中空成形時に首部のみを徐冷して結晶化させ
ることにより性能を改善する方法（特開昭５４−６６９
６９号公報）が提案されているが該方法では首部と胴部
とが繋がっている為、首部の結晶化度を上げようとする
と胴の一部も結晶化が進み、パリソンで実施すると首部
に近いところの二軸延伸がされ難く、また成形体で実施
すると首部だけでなく肩部または胴部の一部迄も結晶化
して白化したりする虞れがあった。又、予め二軸延伸成
形された首部と胴部とを一体に溶着固定したパリソン（
特開昭５４−９０３６５号公報）を用いる方法が提案さ
れているが、二軸延伸された首部では螺子が加工出来な
いので、繰返し容器を密閉することが困難であり、また
二軸延伸成形された首部と胴部とをインサート成形で溶
着しようとしても、首部が殆ど溶融されないので充分な
溶着が出来ず、二軸延伸成形時あるいは使用時に溶着部
から首部と胴部とが離れたりする虞れがあった。
また完全に溶着させる為、首部をも加熱溶融させると熱
により収縮して製品としての価値をなくす虞れがあった
。
一方、前述の如く、二軸延伸中空成形は、必ず予め成形
されたパリソンを用い、しかもそのパリソンは殆どが射
出成形によって成形されるので、成形上パリソンの胴部
と首部の径がほぼ同一である必要があった。しかもパリ
ソンの厚みは４ｍｍが限界でそれ以上厚くなると結晶化
が起こり、二軸延伸中空成形が出来なくなるので、中空
体の強度からも自ずと延伸倍率には限界があった。その
為、大型容器では必然的に首部も大きくなり、取扱いが
不便であり、また大きなキャップを必要とすることから
、コストアップの要因ともなっている。
以上の点に鑑み、種々検討した結果、未延伸の首部片と
有底胴部片とをそれぞれ別個に成形し、次いで該首部片
と非品性の有底胴部片とを溶融接着してパリソンと成し
、該パリソンを用いて二軸延伸中空成形を行うことによ
り、上記欠点を改善することが可能であることを知った
。すなわち、この方法で首部片として予め結晶化したも
のを用いれば、胴部を白化させることなく、首部の強度
を改善できるし、該首部片として所望の口径のものを用
いれば、所望の大きさの首部を有する大型容器を製造す
ることが可能である。
本発明は、それぞれ別個に成形された未延伸の首部片と
非品性の有底胴部片の被着部を溶融して接着することを
特徴とするポリエチレンテレフタレート樹脂二軸延伸中
空体成形用のパリソンの製造方法を提供するものである
。
本発明に用いるポリエチレンテレフタレート樹脂とは、
通常ジカルボン酸成分の８０モ）Ｌ７％以上、好ましく
は９０モル％以上がテレフタル酸であり、グリコール成
分の８０モ／Ｉ／％以上、好ましくは９０モル％以上が
エチレングリコールである結晶性の熱可塑性ポリエステ
／Ｌ／ｗ脂である。尚、残余の他のジカルボン酸として
は、具体的には例えばイソフタル酸、ジフェニルエーテ
／Ｌ’−４１４’−ジカルボン酸、ナフタリン−１，４
または２．６−ジカルボン酸等の芳香族ジカルボン酸、
シュウ酸、コ／％り酸、アジピン酸、セバシン酸、ウン
デカジカルボン酸等の脂肪族ジカルボン酸、ヘキサヒド
ロテレフタル酸等の脂環族ジカルボン酸等が挙げられ、
他のグリコール成分としては、プロピレングリコール、
１．４−７’タンジオ−μ、ネオペンチルグリコール等
の脂肪族グリコール、シクロヘキサンジメタノ＋＋　）
し等のｔｉｌｌグリコール、ビスフェノール等の芳香族
ジヒドロキシ化合物等が挙げられる。テレフタル酸及び
エチレングリコールが上記範囲であれば、共重合体でも
ＰＥＴと他のポリエステルとの混合物であってもよい。
本発明におけるパリソンは第１図に示す如く未延伸の首
部片１及び胴部片２はそれぞれ別個に成形されるが、首
部片の胴部側３は、胴部片と溶融接着する為に、同一径
である必要がある。未延伸の首部片は通常射出成形によ
り成形される。
胴部片２は必ずしも射出成形で成形する必要はなく、押
出成形により成形されたパイプの一端を有底化したもの
でもよい。胴部片２は、前記首部片１と溶融接着後二軸
延伸中空成形を行う為、必ず非品性であらねばならない
。非品性の胴部片２は例えばＰＥＴを溶融賦形し、急冷
することにより得られる。
成形された未延伸の首部片１を非晶性の有底胴部片２七
溶融接着する前に未延伸の首部片１を加熱処理して結晶
化させておくと、首部の強度が改善され、しかも胴部は
従来の透明で優れた機械的強度を備えたＰＥＴの二軸延
伸中空成形体が得られるので好ましい。
また第２図に示す如く、非品性の有底胴部片の径に比べ
て小さな口径を有する首部片４を用いると、口径の小さ
な首部を有する大型容器が得られるので、キャップのコ
ストダウン、或いは大容量で任意の口径の容器が得られ
るので、その用途は多岐に亙る。その際、前述の如く、
首部片を結晶化させておくと口部の強度が向上するので
好ましい。
また、首部片と非品性の有底胴部片に添加する顔料ある
いは染料を異なった色にすれば、口部と本体とが異なっ
た中空体が得られ、デザイン上二種の色づけが出来る利
点がある。
未延伸の首部片と非品性の有底胴部片との溶融接着は、
通常ポリオレフィン樹脂等に使用されているバラを溶接
等により容易に行い得る。その際、首部片及び有底胴部
片のいずれの被着部分も溶融させねばならない。いずれ
か一方だけ溶融させて接着させても、充分な接着力は得
られない。
前記方法により得られた結晶化した首部あるいは小口径
の首部と非品性の有底胴部とからなるパリソンは、公知
の方法、例えば首部を把持した後パリソンの有底胴部を
９０〜１１０°Ｃに加熱した後、二軸延伸中空金型内で
縦方向に２〜２．５倍、横方向に６〜５倍延伸すること
により中空成形体となすことが出来る。
本発明の方法により得られたパリソンを用いることによ
り前述の如く、例えば結晶化した首部を有するパリソン
からは、口部強度に優れた二軸延伸中空成形体が、小口
径の首部を有するパリソンからは、口径が小さくしかも
大容量の二軸延伸中空成形体が得られ、また首部と胴部
で異なった色にもできるので、それぞれ高温充填の食品
容器（ジュース、ソース等）、大型貯蔵容器（生ビール
樽、酒樽等）に好適である。
次に実施例を挙げて本発明を更に具体的に説明する０ 実施例１ １　Ｖ　＝　０−８のＰＥＴを用い首部片を射出成形し
、これを１３０°Ｃのオーブン中で約２時間熱処理し、
結晶化させた。一方、有底胴部片は金型温度２０°Ｃの
射出成形により急冷し、非晶性有底胴部片を得た。次に
両者を２８０’Ｃにて１０〜２０秒の加熱によりバット
溶接を行った。この様にして得られたプレフォームを１
１０°Ｃに再加熱し、縦２．５倍、横４．３倍の二軸延
伸ボ）／しを得た。このボトルについてその強度を調べ
た結果は以下の通りである。
【図面の簡単な説明】
第１図は本発明に係わるパリソンの断面図、及び第２図
は本発明に係わる小口径首部片を有するパリソンの断面
図である。 １・・・首部片　　　　　２・・・有底胴部片４・・・
小口径首部片 出願人　　三井石油化学工業株式会社 代理人　　山　　口　　　　　和

Claims (2)

    【特許請求の範囲】
  1. （１）それぞれ別個に成形された未延伸の首部片と非品
    性の有底胴部片の被着部を溶融して接着することを特徴
    とするポリエチレンテレフタレート樹脂二軸延伸中空体
    成形用のパリソンの製造方法。
  2. （２）前記首部片が結晶性の首部片である特許請求の範
    囲（１）項記載の方法。 （２）前記首部片が有底胴部片の胴径に比べて小さい口
    径である特許請求の範囲（１）または（２）項記載の方
    法。
JP58042413A 1983-03-16 1983-03-16 パリソン Granted JPS59169821A (ja)