JPH0224202B2 - - Google Patents
Info
- Publication number
- JPH0224202B2 JPH0224202B2 JP4241383A JP4241383A JPH0224202B2 JP H0224202 B2 JPH0224202 B2 JP H0224202B2 JP 4241383 A JP4241383 A JP 4241383A JP 4241383 A JP4241383 A JP 4241383A JP H0224202 B2 JPH0224202 B2 JP H0224202B2
- Authority
- JP
- Japan
- Prior art keywords
- neck
- piece
- parison
- biaxially stretched
- amorphous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
本発明はポリエチレンテレフタレート樹脂製二
軸延伸中空体成形用のパリソンに関する。さらに
詳しくは、それぞれ別個に成形された未延伸の首
部片と非晶性の有底胴部片とを溶融接着してなる
パリソンに関する。 ポリエチレンテレフタレート樹脂(以下PET
と呼ぶことがある)の二軸延伸中空体は機械的強
度、剛性、耐熱性、耐薬品性、耐油性、透明性、
耐ガス透過性に優れるので、醤油、液体洗剤、化
品等の容器として近年広く使われるようになつ
た。PETの二軸延伸中空体は通常射出成形ある
いは押出成形により予め非晶性のパリソン(二軸
延伸中空成形前の前駆成形体、プリフオーム)を
成形し、次いで該パリソンを中空成形用金型内で
縦方向及び横方向に延伸することにより得られる
が、中空体の首部は二軸延伸成形時にパリソンを
金型に取り付ける際に把持する為、全く二軸延伸
されない。この為、二軸延伸された胴部と異な
り、首部は非晶状態のまま中空体となるので、二
軸延伸することによつて充分に発揮される前記性
能が首部では発揮されないという欠点を有してい
る。 前記欠点を解消する方法として、例えばパリソ
ンあるいは二軸延伸中空成形時に首部のみを徐冷
して結晶化させることにより性能を改善する方法
(特開昭54―66969号公報)が提案されているが、
該方法では首部と胴部とが繋がつている為、首部
の結晶化度を上げようとすると胴部の一部も結晶
化が進み、パリソンで実施すると首部に近いとこ
ろの二軸延伸がされ難く、また成形体で実施する
と首部だけでなく肩部または胴部の一部迄も結晶
化して白化したりする虞れがあつた。又、予め二
軸延伸成形された首部と胴部とを一体に溶着固定
したパリソン(特開昭54―90365号公報)を用い
る方法が提案されているが、二軸延伸された首部
では螺子が加工出来ないので、繰返し容器を密閉
することが困難であり、また二軸延伸成形された
首部と胴部とをインサート成形で溶着しようとし
ても、首部が殆ど溶融されないので充分な溶着が
出来ず、二軸延伸成形時あるいは使用時に溶着部
から首部と胴部とが離れたりする虞れがあつた。
また完全に溶着させる為、首部をも加熱溶融させ
ると熱により収縮して製品としての価値をなくす
虞れがあつた。 一方、前述の如く、二軸延伸中空成形は、必ず
予め成形されたパリソンを用い、しかもそのパリ
ソンは殆どが射出成形によつて成形されるので、
成形上パリソンの胴部と首部の径がほぼ同一であ
る必要があつた。しかもパリソンの厚みは4mmが
限界でそれ以上厚くなると結晶化が起こり、二軸
延伸中空成形が出来なくなるので、中空体の強度
からも自ずと延伸倍率には限界があつた。その
為、大型容器では必然的に首部も大きくなり、取
扱いが不便であり、また大きなキヤツプを必要と
することから、コストアツプの要因ともなつてい
る。 以上の点に鑑み、種々検討した結果、予熱処理
された未延伸の首部片と、非晶性であつてかつ未
延伸の有底胴部片とをそれぞれ別個に成形し、次
い該首部片と非晶性の有底胴部片とを溶融接着し
て形成されたPET製のパリソンを用いて二軸延
伸中空成形を行うことにより、上記欠点を改善す
ることが可能であることを知つた。すなわち、本
発明によれば、胴部を白化させることなく、かつ
首部の強度が改善され、、しかも所望の大きさの
首部を有する大型容器が提供される。 本発明は、予熱処理された未延伸のPET製首
部片と、非晶性であつてかつ未延伸のPET製有
底胴部片の被着部とが溶融接着されていることを
特徴とするポリエチレンテレフタレート樹脂二軸
延伸中空成形体用パリソンが提供するものであ
る。 本発明に用いるポリエチレンテレフタレート樹
脂とは、通常ジカルボン酸成分の80モル%以上、
好ましくは90モル%以上がテレフタル酸であり、
グリコール成分の80ル%以上、好ましくは90モル
%以上がエチレングリコールである結晶性の熱可
塑性ポリエステル樹脂である。尚、残余の他のジ
カルボン酸としては、具体的には例えばイソフタ
ル酸、ジフエニルエーテル―4,4′―ジカルボン
酸、ナフタリン―1,4または2,6―ジカルボ
ン酸等の芳香族ジカルボン酸、シユウ酸、コハク
酸、アジビン酸、セバン酸、ウンデカジカルボン
酸等の脂肪族ジカルボン酸、ヘキサヒドロテレフ
タル酸等の脂環族ジカルボン酸等が挙げられ、他
のグリコール成分としては、プロピレングリコー
ル、1,4―ブタンジオール、ネオペンチルグリ
コール等の脂肪族グリコール、シクロヘキサンジ
メタノール等の脂環族グリコール、ビスフエノー
ル等の芳香族ジヒドロキシ化合物等が挙げられ
る。テレフタル酸及びエチレングリコールが上記
範囲であれば、共重合体でもPETと他のポリエ
ステルとの混合物であつてもよい。 本発明におけるパリソンは第1図に示す如く未
延伸の首部片1及び胴部片2はそれぞれ別個に成
形されるが、首部片の胴部側3は、胴部片と溶融
接着する為に、同一径である必要がある。未延伸
の首部片は通常射出成形により成形される。 胴部片2は必ずしも射出成形で成形する必要は
なく、押出成形により成形されたパイプの一端を
有底化したものでもよい。胴部片2は、前記首部
片1と溶融接着後二軸延伸中空成形を行う為、必
ず非晶性であらねばならない。非晶性の胴部片2
は例えばPETを溶融賦形し、急冷することによ
り得られる。 成形された未延伸の首部片1を非晶性の有底胴
部片2と溶融接着する前に未延伸の首部片1を加
熱処理して結晶化させておくと、首部の強度が改
善され、しかも胴部は従来の透明で優れた機械的
強度を備えたPETの二軸延伸中空成形体が得ら
れる。 また第2図に示す如く、非晶性の有底胴部片の
径に比べて小さな口径を有する首部片4を用いる
と、口径の小さな首部を有する大型容器が得られ
るので、キヤツプのコストダウン、或いは大容量
で任意の口径の容器が得られるので、その用途は
多岐に亙る。その際、前述の如く、首部片を結晶
化させておくと口部の強度が向上するので好まし
い。 また、首部片と非晶性の有底胴部片に添加する
顔料あるいは染料を異なつた色にすれば、口部と
本体とが異なつた中空体が得られ、デザイン上二
種の色づけが出来る利点がある。 未延伸の首部片と非晶性の有底胴部片との溶融
接着は、通常ポリオレフイン樹脂等に使用されて
いるバツト熔接等により容易に行い得る。その
際、首部片及び有底胴部片のいずれの被着部分も
溶融させねばならない。いずれか一方だけ溶融さ
せて接着させても、充分な接着力は得られない。 前記方法により得られた結晶化した首部あるい
は小口径の首部と非晶性の有底胴部とからなるパ
リソンは、公知の方法、例えば首部を把持した後
パリソンの有底胴部を90〜110℃に加熱した後、
二軸延伸中空金型内で縦方向に2〜2.5倍、横方
向に3〜5倍延伸することにより中空成形体とす
ることが出来る。 本発明の方法により得られたパリソンを用いる
ことにより前述の如く、例えば結晶化した首部を
有するパリソンからは、口部強度に優れた二軸延
伸中空成形体が、小口径の首部を有するパリソン
からは、口径が小さくしかも大容量の二軸延伸中
空成形体かが得られ、また首部と胴部で異なつた
色にもできるので、それぞれ高温充填の食品容器
(ジユース、ソース等)、大型貯蔵容器(生ビール
樽、酒樽等)に好適である。 次に実施例を挙げて本発明を更に具体的に説明
する。 実施例 1 IV=0.8のPETを用い首部片を射出成形して成
形し、これを130℃のオーブン中で約2時間熱処
理し、結晶化させた。一方、有底胴部片は金型温
度20℃の射出成形により急冷し、非晶性有底胴部
片を得た。次に両者を280℃にて10〜20秒の加熱
によりバツト熔接を行つた。この様にして得られ
たプリフオームを110℃に再加熱し、縦2.5倍、横
4.3倍の二軸延伸ボトルを得た。このボトルにつ
いてその強度を調べた結果は以下の通りである。 【表】
軸延伸中空体成形用のパリソンに関する。さらに
詳しくは、それぞれ別個に成形された未延伸の首
部片と非晶性の有底胴部片とを溶融接着してなる
パリソンに関する。 ポリエチレンテレフタレート樹脂(以下PET
と呼ぶことがある)の二軸延伸中空体は機械的強
度、剛性、耐熱性、耐薬品性、耐油性、透明性、
耐ガス透過性に優れるので、醤油、液体洗剤、化
品等の容器として近年広く使われるようになつ
た。PETの二軸延伸中空体は通常射出成形ある
いは押出成形により予め非晶性のパリソン(二軸
延伸中空成形前の前駆成形体、プリフオーム)を
成形し、次いで該パリソンを中空成形用金型内で
縦方向及び横方向に延伸することにより得られる
が、中空体の首部は二軸延伸成形時にパリソンを
金型に取り付ける際に把持する為、全く二軸延伸
されない。この為、二軸延伸された胴部と異な
り、首部は非晶状態のまま中空体となるので、二
軸延伸することによつて充分に発揮される前記性
能が首部では発揮されないという欠点を有してい
る。 前記欠点を解消する方法として、例えばパリソ
ンあるいは二軸延伸中空成形時に首部のみを徐冷
して結晶化させることにより性能を改善する方法
(特開昭54―66969号公報)が提案されているが、
該方法では首部と胴部とが繋がつている為、首部
の結晶化度を上げようとすると胴部の一部も結晶
化が進み、パリソンで実施すると首部に近いとこ
ろの二軸延伸がされ難く、また成形体で実施する
と首部だけでなく肩部または胴部の一部迄も結晶
化して白化したりする虞れがあつた。又、予め二
軸延伸成形された首部と胴部とを一体に溶着固定
したパリソン(特開昭54―90365号公報)を用い
る方法が提案されているが、二軸延伸された首部
では螺子が加工出来ないので、繰返し容器を密閉
することが困難であり、また二軸延伸成形された
首部と胴部とをインサート成形で溶着しようとし
ても、首部が殆ど溶融されないので充分な溶着が
出来ず、二軸延伸成形時あるいは使用時に溶着部
から首部と胴部とが離れたりする虞れがあつた。
また完全に溶着させる為、首部をも加熱溶融させ
ると熱により収縮して製品としての価値をなくす
虞れがあつた。 一方、前述の如く、二軸延伸中空成形は、必ず
予め成形されたパリソンを用い、しかもそのパリ
ソンは殆どが射出成形によつて成形されるので、
成形上パリソンの胴部と首部の径がほぼ同一であ
る必要があつた。しかもパリソンの厚みは4mmが
限界でそれ以上厚くなると結晶化が起こり、二軸
延伸中空成形が出来なくなるので、中空体の強度
からも自ずと延伸倍率には限界があつた。その
為、大型容器では必然的に首部も大きくなり、取
扱いが不便であり、また大きなキヤツプを必要と
することから、コストアツプの要因ともなつてい
る。 以上の点に鑑み、種々検討した結果、予熱処理
された未延伸の首部片と、非晶性であつてかつ未
延伸の有底胴部片とをそれぞれ別個に成形し、次
い該首部片と非晶性の有底胴部片とを溶融接着し
て形成されたPET製のパリソンを用いて二軸延
伸中空成形を行うことにより、上記欠点を改善す
ることが可能であることを知つた。すなわち、本
発明によれば、胴部を白化させることなく、かつ
首部の強度が改善され、、しかも所望の大きさの
首部を有する大型容器が提供される。 本発明は、予熱処理された未延伸のPET製首
部片と、非晶性であつてかつ未延伸のPET製有
底胴部片の被着部とが溶融接着されていることを
特徴とするポリエチレンテレフタレート樹脂二軸
延伸中空成形体用パリソンが提供するものであ
る。 本発明に用いるポリエチレンテレフタレート樹
脂とは、通常ジカルボン酸成分の80モル%以上、
好ましくは90モル%以上がテレフタル酸であり、
グリコール成分の80ル%以上、好ましくは90モル
%以上がエチレングリコールである結晶性の熱可
塑性ポリエステル樹脂である。尚、残余の他のジ
カルボン酸としては、具体的には例えばイソフタ
ル酸、ジフエニルエーテル―4,4′―ジカルボン
酸、ナフタリン―1,4または2,6―ジカルボ
ン酸等の芳香族ジカルボン酸、シユウ酸、コハク
酸、アジビン酸、セバン酸、ウンデカジカルボン
酸等の脂肪族ジカルボン酸、ヘキサヒドロテレフ
タル酸等の脂環族ジカルボン酸等が挙げられ、他
のグリコール成分としては、プロピレングリコー
ル、1,4―ブタンジオール、ネオペンチルグリ
コール等の脂肪族グリコール、シクロヘキサンジ
メタノール等の脂環族グリコール、ビスフエノー
ル等の芳香族ジヒドロキシ化合物等が挙げられ
る。テレフタル酸及びエチレングリコールが上記
範囲であれば、共重合体でもPETと他のポリエ
ステルとの混合物であつてもよい。 本発明におけるパリソンは第1図に示す如く未
延伸の首部片1及び胴部片2はそれぞれ別個に成
形されるが、首部片の胴部側3は、胴部片と溶融
接着する為に、同一径である必要がある。未延伸
の首部片は通常射出成形により成形される。 胴部片2は必ずしも射出成形で成形する必要は
なく、押出成形により成形されたパイプの一端を
有底化したものでもよい。胴部片2は、前記首部
片1と溶融接着後二軸延伸中空成形を行う為、必
ず非晶性であらねばならない。非晶性の胴部片2
は例えばPETを溶融賦形し、急冷することによ
り得られる。 成形された未延伸の首部片1を非晶性の有底胴
部片2と溶融接着する前に未延伸の首部片1を加
熱処理して結晶化させておくと、首部の強度が改
善され、しかも胴部は従来の透明で優れた機械的
強度を備えたPETの二軸延伸中空成形体が得ら
れる。 また第2図に示す如く、非晶性の有底胴部片の
径に比べて小さな口径を有する首部片4を用いる
と、口径の小さな首部を有する大型容器が得られ
るので、キヤツプのコストダウン、或いは大容量
で任意の口径の容器が得られるので、その用途は
多岐に亙る。その際、前述の如く、首部片を結晶
化させておくと口部の強度が向上するので好まし
い。 また、首部片と非晶性の有底胴部片に添加する
顔料あるいは染料を異なつた色にすれば、口部と
本体とが異なつた中空体が得られ、デザイン上二
種の色づけが出来る利点がある。 未延伸の首部片と非晶性の有底胴部片との溶融
接着は、通常ポリオレフイン樹脂等に使用されて
いるバツト熔接等により容易に行い得る。その
際、首部片及び有底胴部片のいずれの被着部分も
溶融させねばならない。いずれか一方だけ溶融さ
せて接着させても、充分な接着力は得られない。 前記方法により得られた結晶化した首部あるい
は小口径の首部と非晶性の有底胴部とからなるパ
リソンは、公知の方法、例えば首部を把持した後
パリソンの有底胴部を90〜110℃に加熱した後、
二軸延伸中空金型内で縦方向に2〜2.5倍、横方
向に3〜5倍延伸することにより中空成形体とす
ることが出来る。 本発明の方法により得られたパリソンを用いる
ことにより前述の如く、例えば結晶化した首部を
有するパリソンからは、口部強度に優れた二軸延
伸中空成形体が、小口径の首部を有するパリソン
からは、口径が小さくしかも大容量の二軸延伸中
空成形体かが得られ、また首部と胴部で異なつた
色にもできるので、それぞれ高温充填の食品容器
(ジユース、ソース等)、大型貯蔵容器(生ビール
樽、酒樽等)に好適である。 次に実施例を挙げて本発明を更に具体的に説明
する。 実施例 1 IV=0.8のPETを用い首部片を射出成形して成
形し、これを130℃のオーブン中で約2時間熱処
理し、結晶化させた。一方、有底胴部片は金型温
度20℃の射出成形により急冷し、非晶性有底胴部
片を得た。次に両者を280℃にて10〜20秒の加熱
によりバツト熔接を行つた。この様にして得られ
たプリフオームを110℃に再加熱し、縦2.5倍、横
4.3倍の二軸延伸ボトルを得た。このボトルにつ
いてその強度を調べた結果は以下の通りである。 【表】
第1図は本発明に係わるパリソンの断面図、及
び第2図は本発明に係わる小口径首部片を有する
パリソンの断面図である。 1……首部片、2……有底胴部片、4……小口
径首部片。
び第2図は本発明に係わる小口径首部片を有する
パリソンの断面図である。 1……首部片、2……有底胴部片、4……小口
径首部片。
Claims (1)
- 【特許請求の範囲】 1 予熱処理され結晶化された未延伸のポリエチ
レンテレフタレート樹脂製首部片と非晶性であつ
てかつ未延伸のポリエチレンテレフタレート樹脂
製有底胴部片の被着部とが、溶融接着されてなる
ポリエチレンテレフタレート樹脂二軸延伸中空成
形体用パリソン。 2 前記首部片が有底胴部片の胴径に比べて小さ
い口径である特許請求の範囲第1項に記載のパリ
ソン。