JPH0796697A - 装飾板 - Google Patents

装飾板

Info

Publication number
JPH0796697A
JPH0796697A JP5545394A JP5545394A JPH0796697A JP H0796697 A JPH0796697 A JP H0796697A JP 5545394 A JP5545394 A JP 5545394A JP 5545394 A JP5545394 A JP 5545394A JP H0796697 A JPH0796697 A JP H0796697A
Authority
JP
Japan
Prior art keywords
transfer
layer
inorganic
polyol
decorative plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP5545394A
Other languages
English (en)
Inventor
Keiji Sakamoto
恵治 坂本
Yoshio Takahashi
芳男 高橋
Yasukichi Ogasawara
安吉 小笠原
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toyo Ink Mfg Co Ltd
Original Assignee
Toyo Ink Mfg Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Ink Mfg Co Ltd filed Critical Toyo Ink Mfg Co Ltd
Priority to JP5545394A priority Critical patent/JPH0796697A/ja
Priority to DE69406379T priority patent/DE69406379T2/de
Priority to EP19940112215 priority patent/EP0637518B1/en
Priority to US08/285,703 priority patent/US5562969A/en
Priority to KR1019940019336A priority patent/KR950005546A/ko
Publication of JPH0796697A publication Critical patent/JPH0796697A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 （修正有） 【目的】転写性が良好でなおかつ耐水性が良好という、
高度に意匠性と性能を合わせ持つ装飾板を提供するこ
と。 【構成】表面に有機質層あるいは無機質層の施された、
金属、ガラス以外の無機質基材１上に、透明あるいは着
色剤を配合して隠蔽性を有する任意の色相にしたポリオ
ール硬化ポリウレタン樹脂塗料よりなる転写ベース層２
と、転写により所望の図柄層を設けた転写印刷層３、さ
らにポリオール硬化ポリウレタン樹脂塗料よりなるトッ
プコート層４を積層してなる装飾板。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、屋内外の壁、パネル材
あるいは屋内外装飾等に用いられる高度に意匠性、耐水
性に富む装飾板に関する。
【０００２】
【従来の技術】従来、屋内の壁、天井等のパネル材ある
いは室内装飾等に用いられる装飾板としては、例えば、
特公昭 59-1111号公報、特公昭60-58717号公報にポリオ
ール硬化ポリウレタン樹脂塗料を用いた、転写による化
粧板の製造方法が開示されている。かかる技術によれば
装飾板として、鮮明かつ繊細な着色図柄パターンが得ら
れるので、装飾的価値は高いものである。しかしなが
ら、この方法を基材としてけい酸カルシウム板（スレー
ト板）等の金属、ガラス以外の無機質基材に応用する
と、基材が非常にポーラスであるためポリオール硬化ポ
リウレタン樹脂塗料を部分的に吸い込み、転写時に転写
インキが充分に転移せず、不鮮明な図柄となりやすく、
得られた塗板の耐水試験（５０℃２４０時間浸漬）後に
基材の凝集破壊による塗膜剥離が起こるという欠点があ
った。
【０００３】
【発明が解決しようとする課題】本発明は、これら金
属、ガラス以外の無機質基材での従来の欠点を解決し、
転写性が良好でなおかつ耐水性が良好という、高度に意
匠性と性能を合わせ持つ装飾板を提供することを目的と
する。
【０００４】
【課題を解決するための手段】すなわち、表面に有機質
層あるいは無機質層の施された無機質基材上に、透明あ
るいは着色剤を配合して隠蔽性を有する任意の色相にし
たポリオール硬化ポリウレタン樹脂塗料よりなる転写ベ
ース層と、転写により所望の図柄層を設けた転写印刷
層、さらにポリオール硬化ポリウレタン樹脂塗料よりな
るトップコート層を積層することで、転写性、耐水性を
付与したものである。本発明の概要を、まず図面に基づ
いて説明する。
【０００５】図１は本発明により製造された装飾板の断
面図を示す。表面に有機質層あるいは無機質層を施した
無機質基材（１）、転写ベース層（２）、転写印刷層
（３）およびトップコート層（４）とからなる装飾板で
ある。
【０００６】無機質基材（１）は、金属、ガラス以外の
無機質材でスレート板、セメントけい酸カルシウム板、
石膏ボード、コンクリート板、煉瓦や瓦などで、厚さは
特に限定されないが、実用上は１〜１０ｍｍの厚さのも
のが好ましく使用される。基材は、表面に有機質層ある
いは無機質層を形成させることで、転写ベースが内部へ
吸い込むのを防ぎ転写性を確保すると同時に、基材内部
への水の侵入を防ぐことで耐水性も確保しているもので
ある。スレート板やセメントけい酸カルシウム板は安全
衛生面から石綿を使用していないものを使用する事が好
ましい。
【０００７】基材には、有機物などが付着している場合
があるので、適宜アルカリによる脱脂を行う。そしてよ
り付着性を向上させ、耐水性をよくするため、必要に応
じてシランカップリング剤による表面処理を行う。シラ
ンカップリング剤としては、エポキシ系、アミノ系、ビ
ニル系、メタクリル系、メルカプト系等のシランカップ
リング剤を用い、適宜アルコールで希釈してエアースプ
レー、ロールコート、カーテンコート、ディッピング等
公知の方法により塗装し、必要に応じて加熱して乾燥す
る。
【０００８】転写ベース層（２）およびトップコート層
（４）は、基材によく密着し転写印刷層を固定させ、各
種の性能を出現させるためのもので、ポリオール硬化ポ
リウレタン樹脂塗料が使用される。ポリオール硬化ポリ
ウレタン樹脂塗料としては、自体公知のポリオール成分
とポリイソシアネート成分とからなり、使用時に混合し
て用いられるものである。ポリオール成分としては、フ
ッ素ポリオール、アクリルポリオール、ポリエステルポ
リオール、ポリエーテルポリオールがある。フッ素ポリ
オールとしては、フルオロオレフィン単位に基づくフッ
素含有量１０重量％以上で且つ溶剤に可溶なヒドロキシ
ル基を有する含フッ素共重合体があげられる。アクリル
ポリオールとしてはヒドロキシアルキルアクリレートも
しくはメタクリレートを単量体成分として公知の方法で
得られた重合体があげられる。ポリエステルポリオール
としては、ポリカルボン酸あるいはその無水物とポリオ
ールとの縮合によって得られるもの、ポリエーテルポリ
オールとしては、ポリオールのポリオキシアルキル化に
よって得られるものがあげられる。ポリイソシアネート
成分としては、Ｐ−フェニレンジイソシアネート、ビフ
ェニルジイソシアネート、トリレンジイソシアネート、
３・３’−ジメチル−４・４’ビフェニレンジイソシア
ネート、１・４−テトラメチレンジイソシアネート、ヘ
キサメチレンジイソシアネート、、２・２・４−トリメ
チル−１・６−ヘキシレンジイソシアネート、メチレン
ビス（フェニルイソシアネート）、リジンメチルエステ
ルジイソシアネート、イソホロンジイソシアネート、メ
チルシクロヘキシルジイソシアネート、ポリフェニレン
ポリメチレンジイソシアネート、あるいは末端イソシア
ネート基を有するプレポリマーやケイ素原子に直接結合
したイソシアネート基を有する多官能性有機ケイ素化合
物などがあげられるが、特に無黄変性ポリイソシアネー
ト化合物が好ましい。また、ブロック化されたイソシア
ネート樹脂も使用できる。これらのポリオール成分とポ
リイソシアネート成分を、当量比（イソシアネート基／
ヒドロキシル基）が０．９〜１．４の範囲となるよう配
合して用いる。この範囲からはずれると充分な硬化塗膜
が得られず、耐水性、付着性、塗膜硬度、耐候性等種々
の性能に不具合をきたす。転写ベース層に用いる場合
は、適宜公知の手段により、顔料、充てん剤、溶剤、そ
の他の添加剤を使用して塗料化し、所望の色相にするこ
とができる。これらの塗料は、公知の塗装方法、たとえ
ば、カーテンフローコーター、ロールコーター、スプレ
ー、ハケ塗り、ディッピング等により、適宜溶剤で粘度
を調整して塗装する。転写ベースおよびトップコートの
膜厚は１０〜６０ミクロンで、乾燥は短時間で溶剤除去
および硬化を行わせるため、好ましくは加熱乾燥処理を
施す。
【０００９】転写印刷層には、溶剤可溶型のフッ素共重
合体、ビニル系樹脂、熱可塑性アクリル樹脂、熱可塑性
ポリエステル樹脂、オレフィン系樹脂、前記ポリオール
樹脂などのバインダーを単独あるいは適宜混合し、顔料
を分散させたインキが使用される。また本発明の転写印
刷層は、予めポリエステルフィルムなどの基体シートに
グラビア印刷方式、スクリーン印刷方式、オフセット印
刷方式等により任意の模様を形成した印刷画像を転写ベ
ース層の表面に転写したものである。
【００１０】
【実施例】以下実施例を挙げて本発明を説明する。実施
例で使用した基材、転写ベース、転写印刷層に使用する
転写フィルム、トップコートは下記に示す。尚、例中
「％」はすべて「重量％」を表す。又実施例で行った各
種試験は、次の通り行った。
【００１１】 〔基材〕 基材１ 表面に無機質塗料層およびガラス質層を形成させた セメントけい酸カルシウム板 厚み ５mm 基材２ 表面に紫外線硬化型塗料層を形成させた スレート板 厚み ５mm 基材３ ケイ酸カルシウム板（未処理） 厚み ５mm
【００１２】 〔転写ベース〕 転写ベースＡ ％ 備考 チタンホワイト 15.00 溶剤可溶型フッ素樹脂 40.00 旭硝子（株）社製 ルミフロン LF-100 ヘキサメチレンジイソ 住友バイエルウレタン（株）社製 シアネート 3.60 スミジュールＮ−３５００ キシレン 23.40 トルエン 18.00 100.00 主剤と硬化剤を８／１で混合して上記配合とした。
【００１３】当量比（イソシアネート／ヒドロキシル
基）＝１．０
【００１４】 転写ベースＢ ％ 備考 チタンホワイト 15.00 アクリルポリオール 40.00 大日本インキ化学工業（株）社製アクリデ ックA-801 ヘキサメチレンジイソ 旭化成工業（株）社製 シアネート 6.37 デュラネート２４Ａ−１００ 酢酸ブチル 23.63 トルエン 15.00 100.00 主剤と硬化剤を６／１で混合して上記配合とした。
【００１５】当量比（イソシアネート／ヒドロキシル
基）＝１．０
【００１６】 転写ベースＣ ％ 備考 チタンホワイト 14.38 アクリルポリオール 38.36 大日本インキ化学工業（株）社製アクリデ ックA-801 ヘキサメチレンジイソ 旭化成工業（株）社製 シアネート 7.94 デュラネート２４Ａ−１００ 酢酸ブチル 22.52 トルエン 16.80 100.00 主剤と硬化剤を６／１．３で混合して上記配合とした。
【００１７】当量比（イソシアネート／ヒドロキシル
基）＝１．３
【００１８】 転写ベースＤ ％ 備考 チタンホワイト 15.44 アクリルポリオール 41.18 大日本インキ化学工業（株）社製アクリデ ックA-801 ヘキサメチレンジイソ デュラネート２４Ａ−１００ シアネート 6.55 酢酸ブチル 21.16 トルエン 15.67 100.00 主剤と硬化剤を６／０．８で混合して上記配合とした。
【００１９】当量比（イソシアネート／ヒドロキシル
基）＝０．８
【００２０】 〔転写フィルム〕 名 称 フィルムの種類 インキの種類 印刷柄 転写フィルム Ａ ポリエチレンテ フッ素系＊1 御影石模様 レフタレート 転写フィルム Ｂ ポリエチレンテ 塩酢ビ系 御影石模様 レフタレート 注； ＊1 ：フルオロオレフィン単位に基づくフッ素共重合体
【００２１】 〔トップコート〕 トップコートＡ ％ 備考 溶剤可溶型フッ素樹脂 50.00 旭硝子（株）製 ルミフロン LF-302 ヘキサメチレンジイソ 住友バイエルウレタン（株）社製 シアネート 4.16 スミジュールＮ−３５００ キシレン 23.54 トルエン 12.30 酢酸ブチル 10.00 100.00 主剤と硬化剤を１０／１で混合して上記配合とした。
【００２２】当量比（イソシアネート／ヒドロキシル
基）＝１．０
【００２３】 トップコートＢ ％ 備考 アクリルポリオール 50.00 日立化成工業（株）社製 ヒタロイド３００８ ヘキサメチレンジイソ 11.34 住友バイエルウレタン（株）社製 シアネート スミジュールＮ−７５ オクチックス錫 0.10 日本化学産業（株）社製 メチルエチルケトン 14.56 トルエン 14.00 酢酸ブチル 10.00 100.00 主剤と硬化剤を４／１で混合して上記配合とした。
【００２４】当量比（イソシアネート／ヒドロキシル
基）＝１．０
【００２５】〔転写性試験〕基材に転写ベースを塗装焼
き付け後、基材温度を例中条件に保ちながら、転写フィ
ルムをラミネーターを用いて張り付けた後、ＰＥＴフィ
ルムを剥がしてインキを転移させた時のインキの転移性
を確認した。
【００２６】〔耐沸水試験〕試験片の裏面および側面
を、転写ベースに使用したものと同じ塗料でシールした
後、沸水中に浸漬し８時間煮沸後、取り出し室温で２時
間放置して、表面塗膜にカッターナイフで碁盤目状の切
りすじ（１ｍｍ四方×１００個）を入れた後、セロテー
プを強く押しつける。その後、セロテープを引き剥が
し、塗膜の残ったますめの数Ｘを数え、Ｘ／１００とし
た。
【００２７】〔耐水性試験〕同様にシール処理を施した
試験片を５０℃の温水中に１０日間浸漬後、取り出し室
温で２時間放置して、塗膜にカッターナイフで碁盤目状
の切りすじ（１ｍｍ四方×１００個）を入れた後、セロ
テープを強く押しつける。その後、セロテープを引き剥
がし、塗膜の残ったますめの数Ｘを数え、Ｘ／１００と
した。
【００２８】実施例１ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材１（東レグ
ラサル（株）社製 グラサル板）に、４０℃の５％カセ
イソーダ水溶液を１分間シャワーした後、イオン交換水
を３０秒間噴霧し、表面に残るアルカリ液を洗い流し、
ついで１００℃の熱風中で３０分間乾燥させた。しかる
後にエポキシシランカップリング剤をスプレーし、８０
℃の熱風中で１分間乾燥させた。次に転写ベースＡを、
エアースプレーにて乾燥塗膜厚が２０〜３０μとなるよ
うに塗装し、９０℃の熱風中で１０分間乾燥させて白色
の転写ベース層を形成させた。その後グラサル板を９０
℃まで加熱してから、転写フィルムＡをＪＩＳ硬度６０
のゴムロールを用いて、圧着温度８５℃、圧力４Ｋｇ／
ｃｍ2 で圧着せしめ、４０℃まで冷却し、ポリエチレン
テレフタレートフィルムを剥がして転写ベース上に御影
石模様の図柄を転写し、転写印刷層を形成させた。さら
に主剤／硬化剤＝１０／１に混合したトップコートＡ
を、エアースプレーにて乾燥塗膜が３０μとなるよう塗
装し、１００℃の熱風中で４０分間乾燥させ、トップコ
ート層を形成させた。このようにして作製した装飾板
は、御影石模様の図柄が鮮明かつ綺麗に仕上がり、装飾
的価値の高いものであった。また、このものの耐沸水
性、耐水性は良好であった。
【００２９】実施例２ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材１に、実施
例１と同様の処理を行い、エアースプレーにて転写ベー
スＢを乾燥塗膜厚が２０〜３０μとなるよう塗装し、８
０℃の熱風中で１０分間乾燥させて白色の転写ベース層
を形成させた。その後基材を８０℃まで加熱してから、
転写フィルムＢをＪＩＳ硬度６０のゴムロールを用い
て、圧着温度８０℃、圧力４Ｋｇ／ｃｍ2 で圧着せし
め、４０℃まで冷却し、ポリエチレンテレフタレートフ
ィルムを剥がして転写ベース上に御影石模様の図柄を転
写し、転写印刷層を形成させた。さらに主剤／硬化剤＝
４／１に混合して作製したトップコートＢを、エアース
プレーにて乾燥塗膜が３０μとなるよう塗装し、１００
℃の熱風中で４０分間乾燥させ、トップコート層を形成
させた。このようにして作製した装飾板は、転写性が良
く、御影石模様の図柄が鮮明かつ綺麗に仕上がり装飾的
価値の高いものであった。このものの耐沸水性、耐水性
は良好であった。
【００３０】実施例３ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材１に、実施
例１と同様の処理を行い、エアースプレーにて転写ベー
スＣを乾燥塗膜厚が２０〜３０μとなるよう塗装し、８
０℃の熱風中で１０分間乾燥させて白色の転写ベース層
を形成させた。その後基材を８０℃まで加熱してから、
転写フィルムＢをＪＩＳ硬度６０のゴムロールを用い
て、圧着温度８０℃、圧力４Ｋｇ／ｃｍ2 で圧着せし
め、４０℃まで冷却し、ポリエチレンテレフタレートフ
ィルムを剥がして転写ベース上に御影石模様の図柄を転
写し、転写印刷層を形成させた。さらに主剤／硬化剤＝
４／１に混合して作製したトップコートＢを、エアース
プレーにて乾燥塗膜が３０μとなるよう塗装し、１００
℃の熱風中で４０分間乾燥させトップコート層を形成さ
せた。このようにして作製した装飾板は、転写性が良
く、御影石模様の図柄が鮮明かつ綺麗に仕上がり、装飾
的価値の高いものであった。このものの耐沸水性、耐水
性は良好であった。
【００３１】実施例４ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材１に、実施
例１と同様の処理を行い、エアースプレーにて転写ベー
スＤを乾燥塗膜厚が２０〜３０μとなるよう塗装し、８
０℃の熱風中で１０分間乾燥させて白色の転写ベース層
を形成させた。その後基材を８０℃まで加熱してから、
転写フィルムＢをＪＩＳ硬度６０のゴムロールを用い
て、圧着温度８０℃、圧力４Ｋｇ／ｃｍ2 で圧着せし
め、４０℃まで冷却し、ポリエチレンテレフタレートフ
ィルムを剥がして転写ベース上に御影石模様の図柄を転
写し、転写印刷層を形成させた。さらに主剤／硬化剤＝
４／１に混合して作製したトップコートＢを、エアース
プレーにて乾燥塗膜が３０μとなるよう塗装し、１００
℃の熱風中で４０分間乾燥させ、トップコート層を形成
させた。このようにして作製した装飾板は、転写性が良
く、御影石模様の図柄が鮮明かつ綺麗に仕上がり装飾的
価値の高いものであった。このものの耐沸水性、耐水性
は良好であった。
【００３２】実施例５ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材２に、エポ
キシシランカップリング剤をスプレーし、８０℃の熱風
中で１分間乾燥させた。その後、エアースプレーにて転
写ベースＢを乾燥塗膜厚が２０〜３０μとなるように塗
装し、８０℃の熱風中で１０分間乾燥させて白色の転写
ベース層を形成させた。その後基材を８０℃まで加熱し
てから、転写フィルムＢをＪＩＳ硬度６０のゴムロール
を用い、圧着温度８０℃、圧力４Ｋｇ／ｃｍ2 で圧着せ
しめ、４０℃まで冷却し、ポリエチレンテレフタレート
フィルムを剥がして転写ベース上に御影石模様の図柄を
転写し、転写印刷層を形成させた。さらに主剤／硬化剤
＝４／１に混合して作製したトップコートＢを、エアー
スプレーにて乾燥塗膜が３０μとなるよう塗装し、１０
０℃の熱風中で４０分間乾燥させ、トップコート層を形
成させた。このようにして作製した装飾板は、転写性が
良く、御影石模様の図柄が鮮明かつ綺麗に仕上がり、装
飾的価値の高いものであった。このものの耐沸水性、耐
水性は良好であった。
【００３３】比較例１ 縦横３００×３００ｍｍ、厚さ５ｍｍの基材３に、転写
ベースＢをエアースプレーにて乾燥塗膜厚が２０〜３０
μとなるように塗装し８０℃の熱風中で１０分間乾燥さ
せて白色の転写ベース層を形成させた。その後、基材を
８０℃まで加熱してから、転写フィルムＢを、ＪＩＳ硬
度６０のゴムロールを用いて、圧着温度８０℃、圧力４
Ｋｇ／ｃｍ2 で圧着せしめ、４０℃まで冷却しポリエチ
レンテレフタレートフィルムを剥がして転写ベース上に
御影石模様の図柄を転写し、転写印刷層を形成させた。
次に、主剤／硬化剤＝４／１に混合して作製したトップ
コートＢをエアースプレーにて乾燥塗膜が３０μとなる
よう塗装し、１００℃の熱風中で４０分間乾燥させ、ト
ップコート層を形成させた。このようにして作製した装
飾板は、転写ベースの基材への吸い込みにより、一部転
写不良があり御影石模様の図柄が不鮮明であり装飾的価
値の低いものであった。また、このものの耐沸水性、耐
水性試験ではいずれもブリスターが認められ、付着も０
／１００と基材の凝集破壊による剥離が認められた。
【００３４】実施例１〜４および比較例１で得られた装
飾板についての転写性試験、耐沸水試験、耐水性試験の
結果を表５に示した。試験結果は、実施例では全て良好
で装飾板として有用であったが、比較例では外観、耐水
性が不良であり、装飾板として使用できないものであっ
た。
【００３５】
【表１】
【００３６】
【発明の効果】本発明により、屋内外の壁、パネル材あ
るいは屋内外装飾等に用いられる高度に意匠性、耐水性
に富む装飾板を提供することができた。
【図面の簡単な説明】
【図１】は、本発明による装飾板の断面図を示す。
【符号の説明】
１・・無機質基材 ４・・トップコート層 ２・・転写ベース層 ３・・転写印刷層
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｅ０４Ｆ 13/08 Ｅ 9127−2Ｅ Ａ 9127−2Ｅ

Claims (2)

    【特許請求の範囲】
  1. 【請求項１】 表面に有機質層あるいは無機質層の施さ
    れた、金属、ガラス以外の無機質基材上に、透明あるい
    は着色剤を配合して隠蔽性を有する任意の色相にしたポ
    リオール硬化ポリウレタン樹脂塗料よりなる転写ベース
    層と、転写により所望の図柄層を設けた転写印刷層、さ
    らにポリオール硬化ポリウレタン樹脂塗料よりなるトッ
    プコート層を積層してなる装飾板。
  2. 【請求項２】 無機質基材として、表面に無機質塗料層
    およびガラス質層を施したセメントけい酸カルシウム板
    を用いることを特徴とする請求項１記載の装飾板。
JP5545394A 1993-08-06 1994-03-25 装飾板 Pending JPH0796697A (ja)