JP7298477B2 - 積層体、包装体及び包装物品 - Google Patents
積層体、包装体及び包装物品 Download PDFInfo
- Publication number
- JP7298477B2 JP7298477B2 JP2019546535A JP2019546535A JP7298477B2 JP 7298477 B2 JP7298477 B2 JP 7298477B2 JP 2019546535 A JP2019546535 A JP 2019546535A JP 2019546535 A JP2019546535 A JP 2019546535A JP 7298477 B2 JP7298477 B2 JP 7298477B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- adhesive
- laminate
- sealant
- sealant layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の第2側面によると、医薬品、化粧品又は食品を収容する包装体において包装材料として使用するための積層体であって、基材層と、厚さが0.1μm乃至1.0μmの範囲内にある接着剤層と、厚さが10μm乃至40μmの範囲内にあり、樹脂として環状オレフィン系樹脂のみを含んだ未延伸のシーラント層と、前記基材層と前記接着剤層との間に介在したバリア層とを具備した積層体であって、前記シーラント層の一方の主面は前記積層体の最表面を構成し、前記シーラント層の他方の主面は前記接着剤層を介して前記バリア層に貼り合わされており、前記バリア層と前記シーラント層との間の接着強度は0.8N/15mm以上であり、前記接着剤層は2液型ポリウレタン系接着剤からなり、前記バリア層はアルミニウム層を含み、前記アルミニウム層は前記接着剤層と直接接しており、前記シーラント層の前記他方の主面は、オゾン処理された表面であり、前記接着剤層と直接接している積層体が提供される。
本発明の第3側面によると、医薬品、化粧品又は食品を収容するための包装体であって、第1又は第2側面に係る積層体を、前記シーラント層が内容物を収容する空間と接するように含んだ包装体が提供される。
本発明の第4側面によると、第3側面に係る包装体と、これに収容された内容物とを含み、前記内容物は、医薬品、化粧品又は食品を含んだ包装物品が提供される。
図1に示す積層体1は、例えば、包装材料として使用する。この積層体は、包装材料以外の用途、例えば、電子機器の押し釦などの表面を覆うカバーフィルムとして使用することも可能である。
透明蒸着フィルムの樹脂フィルムとしては、アルミニウム蒸着フィルムの樹脂フィルムについて例示したものと同じフィルムを使用することができる。
シーラント層15は、陽電子消滅寿命測定法により求められる高分子自由体積Vfが、0.10nm3以下であることが好ましい。本発明者らは、陽電子消滅寿命測定法により求められる高分子自由体積と非吸着性とが相関していることを見出している。陽電子消滅寿命測定法により求められる高分子自由体積Vfが0.10nm3を超える場合、所望の非吸着性を得られない可能性がある。陽電子消滅寿命測定法については、後で詳述する。
接着剤は、アンカーコート剤及びドライラミネート接着剤の少なくとも一方であってもよい。アンカーコート剤の粘性は、ドライラミネート接着剤の粘性よりも低い。従って、アンカーコート剤を用いた場合、ドライラミネート接着剤を用いた場合と比較して、接着剤層14の厚さを小さくすることができる。
図2に示す方法では、ロールツーロール方式で積層体を製造する。
具体的には、先ず、巻出ロール16は基材層11を巻き出す。巻き出された基材層11は、ガイドロール17a、17b及び17cによって、巻出ロール16から接着剤塗布部18へと案内され、接着剤塗布部18を通過する。
積層体1は、その後、ガイドロール17fによって巻取ロール23へと案内される。巻取ロール23は、積層体1を巻き取る。
また、ラミネート前に押出されるシーラント層15の材料に対し、O3処理を行うことが好ましい。
先ず、基材層11を準備し、その一方の主面に2液型ポリウレタン系接着剤を塗布して、接着層を形成する。
次いで、接着剤層14上に、押出ラミネート法により、シーラント層15を形成する。このとき、ラミネート前に押出される環状オレフィン系樹脂に対し、O3処理を行うことが好ましい。
以上のようにして、積層体1を得る。
(1)本発明の一実施形態は、基材層と、厚さが0.1μm乃至1.0μmの範囲内にある接着剤層と、厚さが10μm乃至40μmの範囲内にあり、環状オレフィン系樹脂からなる未延伸のシーラント層とを具備した積層体であって、前記シーラント層の一方の主面は前記積層体の最表面を構成し、前記シーラント層の他方の主面は前記接着剤層を介して前記基材層に貼り合わされており、前記基材層と前記シーラント層との間の接着強度は0.8N/15mm以上である積層体に係る。
(2)本発明の他の実施形態は、前記基材層と前記接着剤層との間にバリア層を更に具備する(1)に記載の積層体に係る。
(3)本発明の更に他の実施形態は、前記バリア層はアルミニウム層又は無機酸化物薄膜を含んだ層を具備する(2)に記載の積層体に係る。
(4)本発明の更に他の実施形態は、前記基材層と前記バリア層との間に接着性樹脂層を更に具備する(2)又は(3)に記載の積層体に係る。
(5)本発明の更に他の実施形態は、前記接着性樹脂層がポリエチレンを含む(4)に記載の積層体に係る。
(6)本発明の更に他の実施形態は、前記シーラント層は樹脂として環状オレフィン系樹脂のみを含む(1)乃至(5)の何れか1つに記載の積層体に係る。
(7)本発明の更に他の実施形態は、前記シーラント層は環状オレフィン系樹脂及び任意の添加剤のみを含む(1)乃至(5)の何れか1つに記載の積層体に係る。
(8)本発明の更に他の実施形態は、前記添加剤は、滑剤、酸化防止剤、紫外線吸収剤、光安定剤、帯電防止剤、アンチブロッキング剤、難燃化剤、架橋剤、及び着色剤の1以上である(7)に記載の積層体に係る。
(9)本発明の更に他の実施形態は、前記滑材は、高級脂肪酸金属塩、脂肪族アルコール、ポリグリコール、トリグリセリド、ワックス、フェノール系化合物、又は、それらの1以上を含んだ混合物である(8)に記載の積層体に係る。
(10)本発明の更に他の実施形態は、前記シーラント層は環状オレフィン系樹脂のみを含む(1)乃至(5)の何れか1つに記載の積層体に係る。
(11)本発明の更に他の実施形態は、前記接着剤層は接着剤からなり、前記接着剤は溶剤系接着剤、水性系接着剤、反応系接着剤、及びホットメルト系接着剤の1以上である(1)乃至(10)の何れか1つに記載の積層体に係る。
(12)本発明の更に他の実施形態は、前記接着剤層は反応系接着剤からなり、前記反応系接着剤は、エポキシ樹脂系接着剤及びポリウレタン系接着剤の少なくとも一方である(1)乃至(10)の何れか1つに記載の積層体に係る。
(13)本発明の更に他の実施形態は、前記反応系接着剤は前記ポリウレタン系接着剤であり、前記ポリウレタン系接着剤は2液型ポリウレタン系接着剤である(12)に記載の積層体に係る。
(14)本発明の更に他の実施形態は、前記基材層は二軸延伸ポリエチレンテレフタレートフィルムである(1)乃至(13)の何れか1つに記載の積層体に係る。
(15)本発明の更に他の実施形態は、前記シーラント層の前記他方の主面は前記接着剤層と直接接触している(1)乃至(14)の何れか1つに記載の積層体に係る。
(16)本発明の更に他の一実施形態は、(1)乃至(15)の何れか1つに記載の積層体を、前記シーラント層が内容物を収容する空間と接するように含んだ包装体に係る。
(17)本発明の更に他の一実施形態は、(16)に記載の包装体と、これに収容された内容物とを含んだ包装物品に係る。
(1)本発明の一実施形態は、基材層の上に、厚さが0.1μm乃至1.0μmの範囲内にある接着剤層を形成することと、
厚さが10μm乃至40μmの範囲内にあり、環状オレフィン系樹脂からなる未延伸のシーラント層を、前記接着剤層の上に押出ラミネートにより形成することとを含み、
前記シーラント層の一方の主面は前記積層体の最表面を構成し、
前記基材層と前記シーラント層との間の接着強度は0.8N/15mm以上である積層体の製造方法に係る。
(2)本発明の他の実施形態は、前記接着剤層の形成と前記シーラント層の形成とを含むプロセスをロールツーロール方式によって行う(1)に記載の積層体の製造方法に係る。
(3)本発明の更に他の実施形態は、前記基材層の上に前記接着剤層を形成する前に、前記基材層の上にバリア層を設けることを更に含み、前記接着剤層は前記バリア層の上に形成することを含む(1)又は(2)に記載の積層体の製造方法に係る。
(4)本発明の更に他の実施形態は、前記バリア層はアルミニウム層又は無機酸化物薄膜を含んだ層を具備する(3)に記載の積層体の製造方法に係る。
<実施例1>
以下の方法により、基材層とバリア層と接着剤層とシーラント層とを含んだ積層体を製造した。
次いで、接着剤層上にシーラント層を形成した。具体的には、接着剤層上に、押出ラミネート法により、未延伸のCOC樹脂層を形成した。また、押出ラミネート法において、ラミネート前にO3処理を行った。
また、シーラント層の厚さは、30μmとした。
以上のようにして、積層体を得た。
2液型ポリウレタン系接着剤(アンカーコート剤B)を用いて接着剤層を形成したこと以外は、実施例1と同様の方法により積層体を製造した。
ポリオレフィン系接着剤(アンカーコート剤C)を用いて接着剤層を形成したこと以外は、実施例1と同様の方法により積層体を製造した。
ポリオレフィン系接着剤(アンカーコート剤C)を用いて接着剤層を形成したこと、及び、押出ラミネート法においてO3処理を行わなかったこと以外は、実施例1と同様の方法により積層体を製造した。
シーラント層の厚さを40μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
シーラント層の厚さを10μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ0.1μm及び40μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ0.1μm及び30μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ0.1μm及び10μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ1.0μm及び40μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ1.0μm及び30μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層及びシーラント層の厚さをそれぞれ1.0μm及び10μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
基材層に2液型ポリウレタン系接着剤を塗布しなかったこと、並びに、接着性樹脂層及びバリア層を設けなかったこと以外は、実施例1と同様の方法により積層体を製造した。
押出ラミネート法においてO3処理を行わなかったこと以外は、実施例1と同様の方法により積層体を製造した。
シーラント層の厚さを50μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
シーラント層の厚さを5μmとしたこと以外は、実施例1と同様の方法により積層体を製造した。
接着剤層の厚さを0.1μm未満としたこと以外は、実施例1と同様の方法により積層体を製造した。
基材層及びバリア層を実施例1と同様に準備した。次に、基材層の一方の主面に2液型ポリウレタン系接着剤を塗布し、続いて、この主面とバリア層とが向き合うように、基材層とバリア層とをラミネートした。
シーラント層の原料として、実施例1で使用したCOC樹脂とLDPEとを9:1の質量比で含んだ混合物を使用したこと以外は、実施例1と同様の方法により積層体を製造した。LDPEは、温度が190℃であり、荷重が21.168N(=2.16kgf)である場合のメルトフローレートが7.0g/10分であり、密度が0.918g/cm3であり、融点が約106℃であった。
以下のように、2層構造を有するシーラント層を形成したこと以外は、実施例1と同様の方法により積層体を製造した。即ち、接着剤層上に、押出ラミネート法により、LLDPEからなる厚さが10μmの層と、その上に設けられた、COC樹脂からなる厚さが20μmの層とを含んだシーラント層を形成した。LLDPEは、温度が190℃であり、荷重が21.168N(=2.16kgf)である場合のメルトフローレートが9.0g/10分であり、密度が0.912g/cm3であり、融点が120℃であった。COC樹脂の原料は、実施例1と同様のものを使用した。
以下のように、2層構造を有するシーラント層を形成したこと以外は、実施例1と同様の方法により積層体を製造した。即ち、接着剤層上に、押出ラミネート法により、LLDPEからなる厚さが10μmの層と、その上に設けられた、COC樹脂からなる厚さが5μmの層とを含んだシーラント層を形成した。LLDPEは、比較例7と同様のものを使用した。COC樹脂の原料は、実施例1と同様のものを使用した。
以下のように、2層構造を有するシーラント層を形成したこと以外は、実施例1と同様の方法により積層体を製造した。即ち、接着剤層上に、押出ラミネート法により、COC樹脂からなる厚さが20μmの層と、その上に設けられ、LLDPEからなる厚さが10μmの層とを備えるシーラント層を形成した。LLDPEは、比較例7と同様のものを使用した。COC樹脂の原料は、実施例1と同様のものを使用した。
基材層及びバリア層を実施例1と同様に準備した。次に、基材層の一方の主面に2液型ポリウレタン系接着剤を塗布し、続いて、この主面とバリア層とが向き合うように、基材層とバリア層とをラミネートした。
実施例1乃至13及び比較例1乃至10に係る積層体から、縦が10cm及び横が10cmの寸法を有している袋を製造した。次に、これら袋に貼付剤を充填し、これらをヒートシールによって封止した。次いで、このようにして得られた包装物品を室温で一定期間放置し、その後、貼付剤の有効成分が積層体のシーラント層へ吸着しているか否かを確認した。
結果を以下の表1及び表2に纏める。
以下に、当初の特許請求の範囲に記載していた発明を付記する。
[1]
基材層と、
厚さが0.1μm乃至1.0μmの範囲内にある接着剤層と、
厚さが10μm乃至40μmの範囲内にあり、環状オレフィン系樹脂からなる未延伸のシーラント層と
を具備した積層体であって、
前記シーラント層の一方の主面は前記積層体の最表面を構成し、前記シーラント層の他方の主面は前記接着剤層を介して前記基材層に貼り合わされており、前記基材層と前記シーラント層との間の接着強度は0.8N/15mm以上である積層体。
[2]
前記基材層と前記接着剤層との間にバリア層を更に具備する項1に記載の積層体。
[3]
前記バリア層はアルミニウム層又は無機酸化物薄膜を含んだ層を具備する項2に記載の積層体。
[4]
項1乃至3の何れか1項に記載の積層体を、前記シーラント層が内容物を収容する空間と接するように含んだ包装体。
[5]
項4に記載の包装体と、これに収容された内容物とを含んだ包装物品。
Claims (4)
- 医薬品、化粧品又は食品を収容する包装体において包装材料として使用するための積層体であって、
基材層と、
厚さが0.1μm乃至1.0μmの範囲内にある接着剤層と、
厚さが10μm乃至40μmの範囲内にあり、樹脂として環状オレフィン系樹脂のみを含んだ未延伸のシーラント層と
を具備した積層体であって、
前記シーラント層の一方の主面は前記積層体の最表面を構成し、前記シーラント層の他方の主面は前記接着剤層を介して前記基材層に貼り合わされており、前記基材層と前記シーラント層との間の接着強度は0.8N/15mm以上であり、
前記接着剤層は2液型ポリウレタン系接着剤からなり、
前記基材層はポリエチレンテレフタレートフィルムを含み、前記ポリエチレンテレフタレートフィルムは前記接着剤層と直接接しており、
前記シーラント層の前記他方の主面は、オゾン処理された表面であり、前記接着剤層と直接接している積層体。 - 医薬品、化粧品又は食品を収容する包装体において包装材料として使用するための積層体であって、
基材層と、
厚さが0.1μm乃至1.0μmの範囲内にある接着剤層と、
厚さが10μm乃至40μmの範囲内にあり、樹脂として環状オレフィン系樹脂のみを含んだ未延伸のシーラント層と、
前記基材層と前記接着剤層との間に介在したバリア層と
を具備した積層体であって、
前記シーラント層の一方の主面は前記積層体の最表面を構成し、前記シーラント層の他方の主面は前記接着剤層を介して前記バリア層に貼り合わされており、前記バリア層と前記シーラント層との間の接着強度は0.8N/15mm以上であり、
前記接着剤層は2液型ポリウレタン系接着剤からなり、
前記バリア層はアルミニウム層を含み、前記アルミニウム層は前記接着剤層と直接接しており、
前記シーラント層の前記他方の主面は、オゾン処理された表面であり、前記接着剤層と直接接している積層体。 - 医薬品、化粧品又は食品を収容するための包装体であって、
請求項1又は2に記載の積層体を、前記シーラント層が内容物を収容する空間と接するように含んだ包装体。 - 請求項3に記載の包装体と、これに収容された内容物とを含み、前記内容物は、医薬品、化粧品又は食品を含んだ包装物品。