JP6622714B2 - ゼオライト膜構造体の製造方法 - Google Patents
ゼオライト膜構造体の製造方法 Download PDFInfo
- Publication number
- JP6622714B2 JP6622714B2 JP2016561914A JP2016561914A JP6622714B2 JP 6622714 B2 JP6622714 B2 JP 6622714B2 JP 2016561914 A JP2016561914 A JP 2016561914A JP 2016561914 A JP2016561914 A JP 2016561914A JP 6622714 B2 JP6622714 B2 JP 6622714B2
- Authority
- JP
- Japan
- Prior art keywords
- zeolite membrane
- zeolite
- membrane
- sample
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ゼオライト膜構造体10は、多孔質支持体20と、第1ゼオライト膜30と、第2ゼオライト膜40とを備える。
ゼオライト膜構造体10の製造方法について説明する。
以上、本発明の一実施形態について説明したが、本発明は上記実施形態に限定されるものではなく、発明の要旨を逸脱しない範囲で種々の変更が可能である。
以下のようにして、サンプルNo.1に係るゼオライト膜構造体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
まず、サンプルNo.1と同じアルミナ支持体を作製した。
サンプルNo.1〜15について、調製した第2ゼオライト膜形成用ゾルのpHを測定したところ、サンプルNo.5以外は、pHが10以上であることを確認した。
サンプルNo.1〜15について、以下の手法によって第2ゼオライト膜の緻密性と第1ゼオライト膜と第2ゼオライト膜の密着性を定量的に測定した。
サンプルNo.1〜15について、以下の手法によって第2ゼオライト膜の主析出部を確認した。第2ゼオライト膜の成膜前後の重量差を「第2ゼオライト膜の重量」とした。また、第2ゼオライト膜合成によって溶液中に析出した粉末を遠心分離によって回収した後、洗浄して80℃で12時間以上乾燥させて得られた粉末の重量を「第2ゼオライト膜形成用溶液中に析出した第2ゼオライトの合計重量」とした。「第2ゼオライト膜の重量」>「第2ゼオライト膜形成用溶液中に析出した第2ゼオライトの合計重量」の場合に第2ゼオライト膜の主析出部を「膜」、そうでない場合に第2ゼオライト膜の主析出部を「溶液」とした。
Agを導入したサンプルNo.1,6,8について、エチレン/エタンの分離性能を評価した。エチレン(C2H4)とエタン(C2H6)の25℃の混合ガス(各ガスの体積比=50:50)を0.4MPaでセル内に導入し、第1ゼオライト膜と第2ゼオライト膜を透過したガスを、ガスクロマトグラフを用いて成分分析した。その結果、Agを導入したサンプルNo.1,6,8は、いずれもエチレンが選択透過することが分かった。
20 多孔質支持体
30 第1ゼオライト膜
40 第2ゼオライト膜
Claims (5)
- 多孔質支持体を第1ゼオライト膜形成用溶液に浸漬した状態で水熱合成することによって、前記多孔質支持体上に第1ゼオライト膜を形成する工程と、
前記第1ゼオライト膜が形成された前記多孔質支持体を10℃以上70℃以下かつpH10以上の第2ゼオライト膜形成用溶液に5分以上浸漬する工程と、
前記第1ゼオライト膜が形成された前記多孔質支持体を前記第2ゼオライト膜形成用溶液に浸漬した状態で水熱合成することによって、前記第1ゼオライト膜上に第2ゼオライト膜を形成する工程と、
を備え、
前記第1ゼオライト膜と前記第2ゼオライト膜は、骨格構造を構成する少なくとも1種のコンポジットビルディングユニットを共有しており、
前記第1ゼオライト膜の表面に付着された第2ゼオライト膜形成用種結晶の単位面積当たりの質量は0.01g/cm2以下である、
ゼオライト膜構造体の製造方法。 - 前記第2ゼオライト膜の形成後において、前記第2ゼオライト膜の重量は、前記第2ゼオライト膜形成用溶液中に析出した第2ゼオライトの合計重量よりも大きい、
請求項1に記載のゼオライト膜構造体の製造方法。 - 前記第1ゼオライト膜の骨格構造は、前記第2ゼオライト膜の骨格構造と同じである、
請求項1又は2に記載のゼオライト膜構造体の製造方法。 - 前記第1ゼオライト膜におけるSi/Al原子比は、前記第2ゼオライト膜におけるSi/Al原子比と異なる、
請求項3に記載のゼオライト膜構造体の製造方法。 - 前記第1ゼオライト膜及び前記第2ゼオライト膜の少なくとも一方の骨格構造は、MFI、DDR、MEL、BEA、CHA、MOR、FAU、LTA、FER、SODのいずれかである、
請求項1乃至4のいずれかに記載のゼオライト膜構造体の製造方法。