JP6462185B2 - 硬化性樹脂の硬化物の剥離剤、硬化性樹脂の硬化物の膨潤剤及び硬化性樹脂の硬化フォームの減容剤 - Google Patents
硬化性樹脂の硬化物の剥離剤、硬化性樹脂の硬化物の膨潤剤及び硬化性樹脂の硬化フォームの減容剤 Download PDFInfo
- Publication number
- JP6462185B2 JP6462185B2 JP2018513679A JP2018513679A JP6462185B2 JP 6462185 B2 JP6462185 B2 JP 6462185B2 JP 2018513679 A JP2018513679 A JP 2018513679A JP 2018513679 A JP2018513679 A JP 2018513679A JP 6462185 B2 JP6462185 B2 JP 6462185B2
- Authority
- JP
- Japan
- Prior art keywords
- curable resin
- cured product
- cured
- release agent
- ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
R1O−CH2CH2CON(CH3)2 (1)
〔式中、R1は炭素原子数1〜4のアルキル基である〕
[2]前記アミド化合物(A)からなる、[1]の剥離剤。
[3]さらに、エステル系化合物、グリコールエーテル系化合物、アミン系化合物及びハロゲン化炭化水素化合物からなる群から選ばれる少なくとも1種の有機化合物(B)を含む、[1]の剥離剤。
[4]前記アミド化合物(A)が、3−メトキシ−N,N−ジメチルプロパンアミド及び3−ブトキシ−N,N−ジメチルプロパンアミドの少なくとも一方である、[1]〜[3]のいずれかの剥離剤。
[5]前記エステル系化合物が、カルボニル基を二つ有するエステル化合物及び環状エステルの少なくとも一方である、[3]又は[4]の剥離剤。
[6]成分(A)及び成分(B)の合計100重量部に対して、成分(B)が90重量部未満である、[3]〜[5]のいずれかの剥離剤。
[7]さらに、シリカ(C)を含み、前記アミド化合物(A)及び前記シリカ(C)の合計100重量部に対して、前記シリカ(C)の含有量が3.5〜23重量部である、[1]、[3]〜[6]のいずれかの記載の剥離剤。
[8]さらに、シリカ(C)を含み、20℃での粘度が12〜2,000,000mPa・sである、[1]、[3]〜[7]のいずれかの記載の剥離剤。
[9]前記硬化性樹脂が、ウレタン樹脂である、[1]〜[8]のいずれかの剥離剤。
[10]硬化性樹脂の硬化物を介して2以上の基材が貼り合された接着体から、該2以上の基材を分離するための、[1]〜[9]のいずれかの剥離剤。
[11]一般式(1)で表されるアミド化合物(A)を含む、硬化性樹脂の硬化フォームの減容剤。
R1O−CH2CH2CON(CH3)2 (1)
〔式中、R1は炭素原子数1〜4のアルキル基である〕
[12]一般式(1)で表されるアミド化合物(A)を含む、硬化性樹脂の硬化物の膨潤剤。
R1O−CH2CH2CON(CH3)2 (1)
〔式中、R1は炭素原子数1〜4のアルキル基である〕
剥離剤は、一般式(1)で表されるアミド化合物を含む。
R1O−CH2CH2CON(CH3)2 (1)
〔式中、R1は炭素原子数1〜4のアルキル基である〕
一般式(1)で表されるアミド化合物(以下「成分(A)」ともいう。)は、化審法、労働安全衛生法及び大気汚染防止法(以下、「化審法等」ともいう。)の規制対象に非該当である。よって、一般式(1)で表されるアミド化合物を含む剥離剤は、低毒性であり、安全性に優れる。
本発明の剥離剤は、成分(A)に加えて、エステル系化合物、グリコールエーテル系化合物、アミン系化合物及びハロゲン化炭化水素化合物からなる群から選ばれる少なくとも1種の有機化合物(以下「成分(B)」ともいう。)を含むことが好ましい。
本発明の剥離剤は、成分(A)に加えて、シリカ(以下「成分(C)」ともいう。)を含むことが好ましい。
剥離剤は、硬化性樹脂の硬化物の種類に応じて、本発明の効果を損なわない範囲で、成分(A)、成分(B)及び成分(C)以外の更なる成分を含むことができる。このような成分として、ジメチルスルホキシド、炭化水素系溶剤等の溶剤、並びに防錆剤、界面活性剤、紫外線吸収剤、酸化防止剤、シリカ以外の増粘剤等の添加剤が挙げられる。これらの具体例は、剥離剤の添加剤として当業者に知られており、市販品を用いることができる。
剥離剤において、一般式(1)で表されるアミド化合物の含有量は、10重量%超、20重量%以上、30重量%以上、50重量%以上、70重量%以上、80重量%以上の順に増加するほど好ましく、より好ましくは90重量%以上であり、特に好ましくは100重量%である。このような範囲であれば、硬化性樹脂の硬化物に対する剥離性がより高くなる。
剥離剤が成分(C)を含む場合、剥離剤の20℃での粘度が、12mPa・s以上であることが好ましく、12mPa・s〜2,000,000mPa・sであることがより好ましく、14〜20,000mPa・sであることが特に好ましい。このような範囲であれば、硬化性樹脂の硬化物に対する剥離性を十分に発揮することができる。粘度が12mPa・s以上であると、剥離剤の粘度が低すぎず、浸漬できない被剥離物に対しても剥離効果により優れる。また、粘度が2,000,000mPa・s以下であると、剥離効果は維持できるが、シリカの量に対して、(A)の含有量が低くなりすぎず、浸漬できない被剥離物に対しても剥離効果により優れる。これらの粘度範囲になるように、成分(A)及び成分(C)の含有量を調整することが好ましい。
剥離剤は、原料成分である一般式(1)で表されるアミド化合物を単独で用いることができる。また、剥離剤が成分(B)、成分(C)及び/又は前記更なる成分を含む場合、剥離剤は、原料成分である一般式(1)で表されるアミド化合物及び場合により更に含まれる成分(B)、成分(C)及び/又は前記更なる成分を混合することにより製造することができる。
硬化性樹脂の硬化物には、硬化性樹脂の硬化物、及び、硬化性樹脂に配合される添加剤を含む硬化性樹脂組成物の硬化物が含まれる。また、硬化性樹脂の硬化物には、硬化性樹脂の硬化反応が促進することにより硬化する硬化物のほかに、反応希釈剤等の硬化性樹脂に配合された添加剤が揮発し、粘度が上昇するによって固化した固化物も含まれる。
硬化性樹脂としては、ウレタン樹脂、エポキシ樹脂、アクリル樹脂及びスチロール樹脂等が挙げられ、ウレタン樹脂が好ましい。
固体基材として、有機の基材、無機の基材及びそれらの組合せが挙げられ、例えば、金属(例えば、銅、鉄、ステンレス、アルミニウム等)、ガラス、セラミック(例えば、タイル、レンガ、石等)、プラスチック(例えば、シリコーン基材等)又はそれらの組み合わせが挙げられる。
硬化性樹脂の硬化物が付着した固体基材から、硬化性樹脂の硬化物を除去する方法は、剥離剤を、前記固体基材と接触させる工程を含む。本発明において、剥離剤を基材に接触させる工程において、固体基材に付着した硬化性樹脂の硬化物は、固体基材から除去される。
減容剤は、一般式(1)で表されるアミド化合物(A)を含む。減容剤は、フォーム状である硬化性樹脂の硬化物、即ち、硬化フォームを減容するために用いられる。ここで、減容とは、硬化性樹脂の硬化フォームの一部が溶解及び/又は膨潤することにより、その形状を保持することができなくなり、硬化フォームの体積が減少することを意味する。本発明において、剥離剤は、硬化性樹脂の硬化物の全部又は一部を、溶解及び/又は膨潤できるため、一般式(1)で表されるアミド化合物を含む溶剤組成物は、硬化性樹脂の硬化フォームの減容剤として用いることができる。溶解させる硬化フォームの量が、硬化性樹脂の硬化フォーム減容剤の飽和溶解量を超える場合に、硬化フォームの一部が溶解せずに残ってもよい。
減容剤を用いた硬化性樹脂の硬化フォームを減容する方法は、減容剤を、硬化性樹脂の硬化フォームと接触させる工程を含む。減容剤が硬化性樹脂の硬化フォームと接触すると、硬化性樹脂の硬化フォームの全部又は一部が、溶解及び/又は膨潤し、硬化性樹脂の硬化フォームは減容する。減容剤と硬化フォームとを接触させる条件は、剥離剤の使用方法において前記した条件が挙げられる。
膨潤剤は、一般式(1)で表されるアミド化合物(A)を含む。本発明において、剥離剤は、硬化性樹脂の硬化物の全部又は一部を膨潤できるため、一般式(1)で表されるアミド化合物を含む溶剤組成物は、硬化性樹脂の硬化物の膨潤剤として用いることができる。
膨潤剤を用いた硬化性樹脂の硬化物を膨潤させる方法は、膨潤剤を、硬化性樹脂の硬化物と接触させる工程を含む。膨潤剤が硬化性樹脂の硬化物と接触すると、硬化性樹脂の硬化物の全部又は一部が膨潤し、これにより、硬化性樹脂の硬化物は軟化し得る。例えば、硬化性樹脂の硬化物が固体基材に付着している場合は、膨潤剤を用いることで、硬化物の全部又は一部を膨潤させて、軟化させることができる。これにより、硬化性樹脂の硬化物と基材との密着力を低下させることにより、基材から硬化性樹脂の硬化物を除去できる。また、膨潤剤は、硬化性樹脂の硬化物の全部又は一部を膨潤させることができるため、硬化性樹脂の硬化物のみからなる成型物に膨潤剤を適用し、その一部のみを膨潤させることにより除去することもできる。膨潤剤と硬化性樹脂の硬化物とを接触させる条件は、剥離剤の使用方法において前記した条件が挙げられる。
減容剤において、成分(B)が二塩基酸エステルであり、剥離剤がエポキシ樹脂の硬化物を介して2以上の基材が貼り合された接着体から、該2以上の基材を分離するための方法に用いられる場合は、成分(B)である二塩基酸エステルの含有量は、成分(A)及び成分(B)の合計100重量部に対して、成分(B)が90重量部未満であることが好ましく、70重量部以下がより好ましく、50重量部以下がさらに好ましく、30重量部以下が特に好ましい。
(ウレタン樹脂の硬化物が付着した固体基材の作製)
光製SUS430板を10mm×40mm×厚さ0.5mmに切断し、脱脂洗浄のために1−ブロモプロパン中に1時間浸漬させた後、取り出して1時間乾燥させた。SUS板にウレタン接着剤(ヘンケル製ロックタイトスーパークリア DSC−050)を約10mm×30mmになるように板の表面に垂らして、硬化させて、試験片1(ウレタン樹脂の硬化物が付着した固体基材)を得た。更に、2日間放置したものを使用した。なお、ウレタン樹脂の硬化物は白色であった。
(膨潤及び除去試験)
PPカップ(旭化成パックス株式会社製、230ml)に、溶剤組成物20gを入れた。その後、試験片1を入れて、室温(25℃)で1時間放置した。試験片1を取出し、以下の基準で評価した。
<実施例1及び2並びに比較例1及び2の評価>
◎:ウレタン樹脂の硬化物が基材に付着していたが膨潤して透明になっており、ティッシュで拭くことにより、ウレタン樹脂の硬化物を除去できた。
○:ウレタン樹脂の硬化物は形状を保って基材に付着しており、基材とウレタン樹脂の硬化物との界面にヘラを入れた場合に、ウレタン樹脂の硬化物を剥離できた。また、剥離したウレタン樹脂の硬化物をティッシュで拭いたとき、ティッシュにウレタン樹脂の硬化物の膨潤物が付着した。
×:ウレタン樹脂の硬化物は形状を保って基材に付着しており、色も白色のままで、基材とウレタン樹脂の硬化物との界面にヘラを入れた場合でも、ウレタン樹脂の硬化物を剥離できなかった。また、ウレタン樹脂の硬化物をティッシュで拭いたとき、ティッシュにウレタン樹脂の硬化物の膨潤物が付着していなかった。
<実施例3〜27及び比較例3〜7の評価>
◎:ウレタン樹脂の硬化物が基材に付着していたが膨潤して透明になっており、ティッシュで拭くことにより、ウレタン樹脂の硬化物を全て除去できた。
○:ウレタン樹脂の硬化物は基材に付着しており、大半は膨潤して透明になっていたが、一部白い部分が残っていた。ウレタン樹脂の硬化物をティッシュで拭くと、拭取ることができた。
△:ウレタン樹脂の硬化物は基材に付着しており、一部は膨潤して透明になっていたが、白い部分が多く残っていた。ウレタン樹脂の硬化物をティッシュで拭いても、拭き取ることができなかった。
×:ウレタン樹脂の硬化物は形状を保って基材に付着しており、色も白色のままで、膨潤していなかった。ウレタン樹脂の硬化物をティッシュで拭いても、拭き取ることができなかった。
(ウレタン樹脂の硬化物を介して2つの基材が貼り合わせられた接着体の作製)
光製SUS430板を10mm×40mm×厚さ0.5mmに切断した板を2枚用意した。用意した2枚の板を、脱脂洗浄のために1−ブロモプロパンで1時間浸漬させた後、取り出して1時間乾燥させた。ウレタン接着剤(ヘンケルロックタイトスーパークリア DSC−050)を約10mm×40mmになるように板の表面に垂らして、2枚の板を貼り合せて、試験片2(ウレタン樹脂の硬化物を介して2つの基材が貼り合わせられた接着体)を得た。更に、2日間放置したものを使用した。
(分離試験)
PPカップ(旭化成パックス株式会社製、230ml)に、溶剤組成物20gを入れた。その後、試験片2を入れて、室温で2時間放置した。試験片2を取出し、以下の基準で評価した。
○:基材とウレタン樹脂の硬化物との界面にヘラを入れた場合に2つの板を分離できた。
×:基材とウレタン樹脂の硬化物との界面にヘラを入れた場合でも、2つの板を剥離できなかった。
(対象物の作製)
光製SUS430板を10mm×40mm×厚さ0.5mmに切断し、脱脂洗浄のために1−ブロモプロパン中に1時間浸漬させた後、取り出して1時間乾燥させた。SUS板にエポキシ接着剤(ハンツマン・ジャパン製アラルダイト ST170)を、ヘラを用いて約10mm×30mmになるように板の表面に塗布し、硬化させて、試験片3(エポキシ樹脂の硬化物が付着した基材)を得た。更に、2日間放置したものを使用した。なお、エポキシ樹脂の硬化物は硬く、手で折り曲げることは困難である。
(溶解試験)
100mlビーカーに溶剤組成物20gを入れ、試験片3を入れた。アルミホイルでフタをして、実施例21〜24及び比較例7では液温60℃で放置し、その他の実施例及び比較例では液温約70℃で放置した。5時間経過まで1時間毎に、試験片3を取出し、以下の基準により評価し、◎又は○となった時間を記載した。
◎:エポキシ樹脂の硬化物が基材から除去されていた。また、エポキシ樹脂の硬化物は溶剤組成物中に膨潤していた。
○:エポキシ樹脂の硬化物は形状を保っており、基材とエポキシ樹脂の硬化物との界面にヘラを入れた場合に、エポキシ樹脂の硬化物を剥離できた。剥がしたエポキシ樹脂の硬化物は、手で折り曲げられるほど軟化していた。
×:エポキシ樹脂の硬化物は形状を保っており、基材とエポキシ樹脂の硬化物との界面にヘラを入れた場合でも、エポキシ樹脂の硬化物を剥離できなかった。
(ウレタン樹脂の硬化フォームの作製)
ウレタンフォーム(ヘンケル社製、du fi x 発泡ウレタン グリーンフォーム)をPP(ポリプロピレン)製プラカップ(旭化成パックス株式会社製、230ml)に入れ、1週間以上放置して、ウレタン樹脂のフォームを硬化させた。さらに、6ヶ月間放置して、ウレタン樹脂の硬化フォームを得た。プラカップからウレタン樹脂の硬化フォームを取り出して、1/4にカットし、1g(±0.3g)(3cm×3cm×4.5cmの大きさ)の試験片4を得た。
PP製プラカップ(旭化成パックス株式会社製、230ml)に、溶剤組成物20gを入れ、試験片4を1個入れて、ラップ(リケンファブロ株式会社製)でフタをして、室温で放置した。0.5時間ごとにガラス棒で突っついて、状態を確かめた。目視で、試験片が膨潤しゼリー状態になること確認して終了した。試験片がゼリー状になるまでの時間を測定した。表3〜8において、6時間以内に試験片がゼリー状態になった場合はその時間を記載し、6〜24時間以内に試験片がゼリー状態になった場合を*とし、24時間を経過しても試験片がゼリー状態にならなかった場合を×とした。
[試験例5:エポキシ樹脂の硬化物を介して2つの基材が貼り合わされた接着体の分離]
(エポキシ樹脂の硬化物を介して2つの基材が貼り合わせられた接着体の作製)
光製SUS430板を10mm×40mm×厚さ0.5mmに切断した板を2枚用意した。用意した2枚の板を、脱脂洗浄のために1−ブロモプロパンで1時間浸漬させた後、取り出して1時間乾燥させた。エポキシ接着剤(ハンツマン・ジャパン製アラルダイト ST170)を約10mm×40mmになるように板の表面に垂らして、2枚の板を貼り合せて、試験片5(エポキシ樹脂の硬化物を介して2つの基材が貼り合わせられた接着体)を得た。更に、2日間放置したものを使用した。
(分離試験)
100mlビーカーに溶剤組成物20gを入れ、試験片5を入れた。アルミホイルでフタをして、実施例21〜24及び比較例7では液温60℃で放置し、その他の実施例及び比較例では液温約70℃で放置した。5時間経過まで1時間毎に、試験片5を取出し、以下の基準により評価し、◎又は○となった時間を記載した。
◎:基材とエポキシ樹脂の硬化物とが、界面にヘラを入れなくても分離した。
○:基材とエポキシ樹脂の硬化物との界面にヘラを入れた場合に2つの板を分離できた。
×:基材とエポキシ樹脂の硬化物との界面にヘラを入れた場合でも、2つの板を剥離できなかった。
ウレタン樹脂の硬化物で被覆された銅線(礎電線株式会社製マグネットワイヤー、UEW 0.30MMカラー300G(2種)の赤色。直径0.30mm。)を80mmに切断したものを試験片6(ウレタン樹脂の硬化物が付着した固体基材)とした。
規格瓶(アズワン製 広口 No.4 37.5ml)に、溶剤組成物10gを入れた。その後、先端40mmが溶剤組成物に接触するように試験片6を入れて、室温(25℃)で0.5時間放置した。試験片6を取出し、以下の基準で評価した。
◎:溶剤組成物と接触していたウレタン樹脂の硬化物の被覆の全てが除去されていた。
○:溶剤組成物と接触していたウレタン樹脂の硬化物の被覆の一部が除去されていた。
×:溶剤組成物と接触していたウレタン樹脂の硬化物の被覆を除去できなかった。また、ティッシュで拭いた場合であっても、溶剤組成物と接触していたウレタン樹脂の硬化物の被覆を除去できなかった。
試験例7では、シリカを含む剥離剤が傾斜を有する被剥離物に対する剥離効果を試験した。
粘度は、回転粘度計(VISCO Cat.No.6800、株式会社アタゴ製)を用い、表11に示す温度及び測定条件で測定した。なお、表11における「測定不可」とは、剥離剤の粘度が2,000,000mPa・s超であることを意味する。
光製SUS430板を縦30mm×横50mm×厚さ0.5mmに切断し、脱脂洗浄のために1−ブロモプロパン中に1時間浸漬させた後、取り出して1時間乾燥させた。ウレタン接着剤(ロックタイトスーパークリア DSC−050(ヘンケルジャパン株式会社製))の0.5gを、約10mm×30mmになるようにステンレス板の表面に垂らして、硬化させて、試験片7(ウレタン樹脂の硬化物が付着した固体基材)を得た。更に、2日間放置したものを使用した。なお、ウレタン樹脂の硬化物は白色であった。
試験片7に対して、剥離剤0.5gをパスツールピペット及びスパチュラーのヘラ部分によって塗布した。試験片7の一方の縦の端の下に、高さ3mmの割り箸によるスペーサーを入れ、試験片7が斜めになるように立てかけた。即ち、試験片7は、斜辺距離50mmに対して垂直距離3mmの勾配を有する。室温(25℃)で1時間放置した後、試験片7について、以下の基準で評価した。
ヘラは、ステンレス製ヘラ(株式会社大創産業、ヘラ幅25mm)を用いた。
○:ウレタン樹脂の硬化物は形状を保って基材に付着しており、基材とウレタン樹脂の硬化物との界面にヘラを入れた場合に、ウレタン樹脂の硬化物を剥離できた。
×:ウレタン樹脂の硬化物は形状を保って基材に付着しており、色も白色のままで、基材とウレタン樹脂の硬化物との界面にヘラを入れた場合でも、ウレタン樹脂の硬化物を剥離できなかった。
ティッシュは、ネピアティシュ200W(王子ネピア株式会社製)を用いた。
○:ウレタン樹脂の硬化物が基材に付着していたが膨潤して透明になっており、1/8に折ったティッシュで拭くことにより、ウレタン樹脂の硬化物を全て除去できた。
×:ウレタン樹脂の硬化物は形状を保って基材に付着しており、色も白色のままで、膨潤していなかった。ウレタン樹脂の硬化物を1/8に折ったティッシュで拭いた場合であっても、拭き取ることができなかった。
3−ブトキシ−N,N−ジメチルプロパンアミド:KJケミカルズ株式会社製
N−メチル−2−ピロリドン:BASF社製
2−ヒドロキシイソ酪酸メチル:三菱ガス化学株式会社製
二塩基酸エステル:三協化学株式会社製 No.23エステル(コハク酸ジメチル21.6重量%、グルタル酸ジメチル59.3重量%及びアジピン酸ジメチル18.3重量%の混合物)
γ−ブチロラクトン:BASF社製
ジエチレングリコールジエチルエーテル:関東化学株式会社製
ジベンジルアミン:広栄化学工業株式会社製
アセト酢酸エチル:関東化学株式会社社製
エチレングリコールジメチルエーテル:三協化学株式会社製
シリカ:AEROSIL RY 200(日本アエロジル株式会社製、疎水性シリカ、BET比表面積100±20m2/g)
また、表1の試験例1及び3の結果により、3−メトキシ−N,N−ジメチルプロパンアミドは、ウレタン樹脂及びエポキシ樹脂の硬化物の全部を膨潤させることができ、3−ブトキシ−N,N−ジメチルプロパンアミドは、ウレタン樹脂及びエポキシ樹脂の硬化物の全部又は一部を膨潤させることができた。よって、一般式(1)で表されるアミド化合物は、硬化性樹脂の膨潤性に優れた硬化性樹脂の硬化物の膨潤剤である。
一方、比較例2は、ウレタン樹脂及びエポキシ樹脂の硬化物に対する剥離性及び膨潤性が劣っており、ウレタン樹脂の硬化フォームと接触させた場合、24時間経過しても、ウレタンフォームの減容剤として用いることができなかった。
表2〜8より、3−メトキシ−N,N−ジメチルプロパンアミドに、二塩基酸エステル、ジエチレングリコールジエチルエーテル、γ−ブチロラクトン、ジベンジルアミン、アセト酢酸エチル又は1−ブロモプロパンを加えた組成物は、硬化性樹脂の硬化物の剥離性及び膨潤性、並びに硬化性樹脂の硬化フォームの減容性の効果を奏することがわかる。特に、これらの効果は二塩基酸エステル、ジエチレングリコールジエチルエーテル、γ−ブチロラクトン、ジベンジルアミン、アセト酢酸エチル及び1−ブロモプロパンの合計が90重量部未満であるときに、十分な効果を奏しているということができる。
表2より、二塩基酸エステルを加えた組成物は、二塩基酸エステルが30重量部以下の実施例で、良好な硬化性樹脂の硬化物の剥離性及び膨潤性を示すことがわかる。また二塩基酸エステルが90重量部未満であれば、硬化性樹脂の硬化物の剥離性及び膨潤性、並びに硬化性樹脂の硬化フォームの減容性の効果を十分に奏していることがわかる。
表3より、γ−ブチロラクトンを加えた組成物は、γ−ブチロラクトンが50重量部付近以外では、3−メトキシ−N,N−ジメチルプロパンアミドの塩基性とγ−ブチロラクトンの酸性が強く作用せず、硬化性樹脂の硬化物の剥離性及び膨潤性、並びに硬化性樹脂の硬化フォームの減容性の効果を十分に奏していることがわかる。特に、γ−ブチロラクトンが10重量部以下の実施例で、良好な硬化性樹脂の硬化物の剥離性及び膨潤性並びに硬化性樹脂の硬化フォームの減容性の効果を示すことがわかる。
表4より、ジエチレングリコールジエチルエーテルを加えた組成物は、硬化性樹脂の硬化物の剥離性及び膨潤性、並びに硬化性樹脂の硬化フォームの減容性の効果を奏することがわかる
表5より、ジベンジルアミンを加えた組成物は、硬化性樹脂の硬化物の剥離性及び膨潤性が良好であり、さらに、ジベンジルアミンが20重量部以下であると、3−メトキシ−N,N−ジメチルプロパンアミド単独の実施例1よりも優れた硬化性樹脂の硬化フォームの減容性の効果を奏することがわかる。3−メトキシ−N,N−ジメチルプロパンアミドとジベンジルアミンはいずれも塩基であるので、相乗効果が図れるものと考えられる
表6より、アセト酢酸エチルを加えた組成物は、優れたエポキシ樹脂の剥離性及び膨潤性を奏することがわかる。
表7より、1−ブロモプロパンを加えた組成物は、1−ブロモプロパンが70重量部以下の実施例で良好な硬化性樹脂の硬化フォームの減容性の効果を奏し、硬化性樹脂の硬化物の剥離性及び膨潤性も良好であることがわかる。
表8より、3−メトキシ−N,N−ジメチルプロパンアミドに、二塩基酸エステル、ジエチレングリコールジエチルエーテル及びジベンジルアミンからなる群から選ばれる2種を加えた組成物も、硬化性樹脂の硬化物の剥離性及び膨潤性、並びに硬化性樹脂の硬化フォームの減容性の効果を奏することがわかる。
表9より、3−メトキシ−N,N−ジメチルプロパンアミドに、エチレングリコールジメチルエーテルを加えた組成物も、硬化性樹脂の硬化物の剥離性の効果を奏することがわかる。
表10及び11より、3−メトキシ−N,N−ジメチルプロパンアミドに、シリカを加えた組成物も、硬化性樹脂の硬化物の剥離性の効果を奏することがわかる。また、アミド化合物の含有量及び剥離剤の粘度が好ましい範囲である場合、ステンレス製ヘラによって、ウレタン樹脂の硬化物を剥離できた。これにより、ティッシュによる手拭きの場合は、除去範囲が手の届く部分と限られるが、ヘラ等を用いることが出来れば、長い棒にヘラをつけることによって、除去範囲を広げることが可能である。また、実施例29〜35の剥離剤の粘度は、いずれも20℃以上で測定されているが、実施例29〜35の剥離剤の20℃での粘度は、いずれも12mPa・s以上であった。
Claims (11)
- アミド化合物(A)を含む、硬化性樹脂の硬化物が付着した固体基材から、硬化性樹脂の硬化物を除去するための、剥離剤であって、
前記アミド化合物(A)が、3−メトキシ−N,N−ジメチルプロパンアミド及び3−ブトキシ−N,N−ジメチルプロパンアミドの少なくとも一方であり、
さらに、カルボニル基を二つ有するエステル化合物、グリコールエーテル系化合物及びハロゲン化炭化水素化合物からなる群から選ばれる少なくとも1種の有機化合物(B)を含み、
前記グリコールエーテル系化合物は、エチレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、ジエチレングリコールジエチルエーテル、トリエチレングリコールジメチルエーテル、ジエチレングリコールジブチルエーテル、ジメトキシテトラエチレングリコール及びジプロピレングリコールジメチルエーテルらなる群から選ばれる少なくとも1種であり、
前記剥離剤において、前記アミド化合物(A)の含有量は、50重量%以上100重量%未満であり、前記硬化性樹脂が、ウレタン樹脂又はエポキシ樹脂である、剥離剤(但し、2−ピロリドンを含む剥離剤を除き、及び、ウレタン樹脂を含む剥離剤を除く)。 - 成分(A)及び成分(B)の合計100重量部に対して、成分(B)が0重量部超50重量部以下である、請求項1に記載の剥離剤。
- さらに、シリカ(C)を含み、前記アミド化合物(A)及び前記シリカ(C)の合計100重量部に対して、前記シリカ(C)の含有量が3.5〜23重量部である、請求項1又は2に記載の剥離剤。
- さらに、シリカ(C)を含み、20℃での粘度が12〜2,000,000mPa・sである、請求項1又は2に記載の剥離剤。
- アミド化合物(A)からなる、硬化性樹脂の硬化物が付着した固体基材から、硬化性樹脂の硬化物を除去するための、剥離剤であって、
前記アミド化合物(A)が、3−メトキシ−N,N−ジメチルプロパンアミド及び3−ブトキシ−N,N−ジメチルプロパンアミドの少なくとも一方であり、
前記硬化性樹脂が、ウレタン樹脂又はエポキシ樹脂である、剥離剤。 - さらに、シリカ(C)のみを含み、前記アミド化合物(A)及び前記シリカ(C)の合計100重量部に対して、前記シリカ(C)の含有量が3.5〜23重量部である、請求項5に記載の剥離剤。
- さらに、シリカ(C)のみを含み、20℃での粘度が12〜2,000,000mPa・sである、請求項5に記載の剥離剤。
- 前記硬化性樹脂が、ウレタン樹脂である、請求項1〜7のいずれか1項に記載の剥離剤。
- 硬化性樹脂の硬化物を介して2以上の基材が貼り合された接着体から、該2以上の基材を分離するための、請求項1〜8のいずれか一項記載の剥離剤。
- アミド化合物(A)を含む、硬化性樹脂の硬化フォームの減容剤であって、
前記アミド化合物(A)が、3−メトキシ−N,N−ジメチルプロパンアミド及び3−ブトキシ−N,N−ジメチルプロパンアミドの少なくとも一方であり、
さらに、カルボニル基を二つ有するエステル化合物、グリコールエーテル系化合物及びハロゲン化炭化水素化合物からなる群から選ばれる少なくとも1種の有機化合物(B)を含み、
前記グリコールエーテル系化合物は、エチレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、ジエチレングリコールジエチルエーテル、トリエチレングリコールジメチルエーテル、ジエチレングリコールジブチルエーテル、ジメトキシテトラエチレングリコール及びジプロピレングリコールジメチルエーテルらなる群から選ばれる少なくとも1種であり、
前記減容剤において、前記アミド化合物(A)の含有量は、50重量%以上100重量%未満であり、前記硬化性樹脂が、ウレタン樹脂である、
硬化性樹脂の硬化フォームの減容剤(但し、2−ピロリドンを含む減容剤を除き、及び、ウレタン樹脂を含む減容剤を除く)。 - アミド化合物(A)を含む、硬化性樹脂の硬化物の膨潤剤であって、
前記アミド化合物(A)が、3−メトキシ−N,N−ジメチルプロパンアミド及び3−ブトキシ−N,N−ジメチルプロパンアミドの少なくとも一方であり、
さらに、カルボニル基を二つ有するエステル化合物、グリコールエーテル系化合物及びハロゲン化炭化水素化合物からなる群から選ばれる少なくとも1種の有機化合物(B)を含み、
前記グリコールエーテル系化合物は、エチレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、ジエチレングリコールジエチルエーテル、トリエチレングリコールジメチルエーテル、ジエチレングリコールジブチルエーテル、ジメトキシテトラエチレングリコール及びジプロピレングリコールジメチルエーテルらなる群から選ばれる少なくとも1種であり、
前記膨潤剤において、前記アミド化合物(A)の含有量は、50重量%以上100重量%未満であり、前記硬化性樹脂が、ウレタン樹脂又はエポキシ樹脂である、
硬化性樹脂の硬化物の膨潤剤(但し、2−ピロリドンを含む膨潤剤を除き、及び、ウレタン樹脂を含む膨潤剤を除く)。