JP6270844B2 - 耐粒界腐食性アルミニウム合金ストリップ、およびその製造方法 - Google Patents
耐粒界腐食性アルミニウム合金ストリップ、およびその製造方法 Download PDFInfo
- Publication number
- JP6270844B2 JP6270844B2 JP2015527925A JP2015527925A JP6270844B2 JP 6270844 B2 JP6270844 B2 JP 6270844B2 JP 2015527925 A JP2015527925 A JP 2015527925A JP 2015527925 A JP2015527925 A JP 2015527925A JP 6270844 B2 JP6270844 B2 JP 6270844B2
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- alloy strip
- rolled
- weight
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Si≦0.2%、
Fe≦0.35%、
0.04%≦Cu≦0.08%、
0.2% ≦Mn≦0.5%、
4.35%≦Mg≦4.8%、
Cr≦0.1%、
Zn≦0.25%、
Ti≦0.1%、
残部はAl、および個別に最大0.05重量%、そして合計で最大0.15重量%になる不可避不純物である、
を有するアルミニウム合金ストリップにより達成される。
アルミニウム合金ストリップの降伏点Rp0.2は確実に110MPa超にすることができる。この場合、ストリップの引張強さは通常255MPa超である。
Si≦0.2%、
Fe≦0.35%、
0.04%≦Cu≦0.08%、
0.2% ≦Mn≦0.5%、
4.45%≦Mg≦4.8%、
Cr≦0.1%、
Zn≦0.25%、
Ti≦0.1%、
残部はAl、および個別に最大0.05重量%、そして合計で最大0.15重量%になる不可避不純物である、を有することで達成される。Mg範囲を4.45重量%〜4.8重量%に限定することにより、中程度の粒度の非常に優れた強度が同様に得られる。
− 本発明によるアルミニウム合金組成からなる圧延インゴットを鋳造する工程;
− 480℃〜550℃で少なくとも0.5時間の圧延インゴットの均質化工程;
− 280℃〜500℃の温度での圧延インゴットの熱間圧延工程;
− 圧延率が40%未満、好ましくは最大30%、特に好ましくは最大25%の最終厚さまでのアルミニウム合金ストリップの冷間圧延工程;
− 仕上げ圧延されたアルミニウム合金ストリップの300℃〜500℃での軟化焼鈍工程;
を含む方法により達成される。
− 少なくとも30%、好ましくは少なくとも50%の圧延率による、熱間圧延されたアルミニウム合金ストリップの冷間圧延工程;
− 300℃〜500℃でのアルミニウム合金ストリップの中間焼鈍工程;
− 40%未満、好ましくは最大30%、特に好ましくは最大25%の圧延率で最終厚さまでその後冷間圧延する工程;
− 最終圧延されたアルミニウム合金ストリップの300℃〜500℃での軟化焼鈍工程;
を行う。
Claims (11)
- Alおよび不可避不純物のほかに少なくとも4重量%のMg含有量を有するAA 5xxx系アルミニウム合金からなるアルミニウム合金ストリップであって、前記アルミニウム合金ストリップは再結晶微細組織を有し、前記微細組織の粒度(KG)は、重量%単位の前記Mg含有量(c_Mg)に対して以下の依存関係を満たすことを特徴とし:
Si≦0.2%、
Fe≦0.35%、
0.04%≦Cu≦0.08%、
0.2% ≦Mn≦0.5%、
4.35%≦Mg≦4.8%、
Cr≦0.1%、
Zn≦0.25%、
Ti≦0.1%、
残部はAl、および個別に最大0.05重量%、そして合計で最大0.15重量%になる不可避不純物である、
を有し、
前記アルミニウム合金ストリップは120MPaを超える降伏点R p0.2 および260MPaを超える引張強さR m を有することを特徴とするアルミニウム合金ストリップ。 - 前記アルミニウム合金ストリップの前記アルミニウム合金は4.45%≦Mg≦4.8%を有することを特徴とする請求項1または2に記載のアルミニウム合金ストリップ。
- 前記粒度は最大40μmであることを特徴とする請求項1〜3の何れか1項に記載のアルミニウム合金ストリップ。
- 前記アルミニウム合金ストリップは0.5mm〜5mmの厚さを有することを特徴とする請求項1〜4の何れか1項に記載のアルミニウム合金ストリップ。
- 前記アルミニウム合金ストリップは冷間圧延され、軟化焼鈍されることを特徴とする請求項1〜5の何れか1項に記載のアルミニウム合金ストリップ。
- 請求項1〜6の何れか1項に記載のアルミニウム合金ストリップを製造するための方法であって、以下のプロセス工程:
− 圧延インゴットを鋳造する工程;
− 480℃〜550℃での少なくとも0.5時間の前記圧延インゴットの均質化工程;
− 280℃〜500℃の温度での前記圧延インゴットの熱間圧延工程;
− 圧延率が40%未満の、最終厚さを有する仕上げ圧延されたアルミニウム合金ストリップまでの前記アルミニウム合金ストリップの冷間圧延工程;
− 前記仕上げ圧延されたアルミニウム合金ストリップの300℃〜500℃での軟化焼鈍工程;
を含む方法。 - 前記熱間圧延後、代わりに以下のプロセス工程:
− 少なくとも30%の圧延率の、前記熱間圧延されたアルミニウム合金ストリップの冷間圧延工程;
− 300℃〜500℃での前記アルミニウム合金ストリップの中間焼鈍工程;
− 圧延率が40%未満の、最終厚さを有する前記仕上げ圧延されたアルミニウム合金ストリップまでのその後の冷間圧延工程;
− 前記仕上げ圧延されたアルミニウム合金ストリップの300℃〜500℃での軟化焼鈍工程;
が行われる請求項7に記載の方法。 - 前記中間焼鈍および/または前記軟化焼鈍はバッチ炉または連続炉にて行われることを特徴とする請求項7または8に記載の方法。
- 少なくとも一部が請求項1〜6の何れか1項に記載のアルミニウム合金ストリップからなる自動車用の部材。
- 前記部材は自動車の車体部品または車体付属品であることを特徴とする請求項10に記載の部材。