JP6132465B2 - 樹脂シート及びその製造方法、この樹脂シートからなる太陽電池封止用樹脂シート、並びに、この樹脂シートを用いた太陽電池モジュール - Google Patents
樹脂シート及びその製造方法、この樹脂シートからなる太陽電池封止用樹脂シート、並びに、この樹脂シートを用いた太陽電池モジュール Download PDFInfo
- Publication number
- JP6132465B2 JP6132465B2 JP2012019716A JP2012019716A JP6132465B2 JP 6132465 B2 JP6132465 B2 JP 6132465B2 JP 2012019716 A JP2012019716 A JP 2012019716A JP 2012019716 A JP2012019716 A JP 2012019716A JP 6132465 B2 JP6132465 B2 JP 6132465B2
- Authority
- JP
- Japan
- Prior art keywords
- resin sheet
- ethylene
- solar cell
- resin
- roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の樹脂シートは、表面にはエンボスが形成され、裏面には微細な窪みが形成されたシートである。このような樹脂シートは、公知の成形方法で得ることが出来る。成形方法としては、例えば、押出成形法、カレンダ成形法がある。
バックアップロールは、エンボスロールが樹脂シートの表面側にエンボスパターンを転写するに際し、樹脂シートをエンボスロールに押し付ける作用を有する。バックアップロールとしては、ゴム製弾性ロールが好適である。またバックアップロールとしては、樹脂シートの裏面に微細な窪みを形成する為に、例えばロール表層(ゴムからなる弾性層)に無機微粒子等の微粒子を含む。これにより、樹脂シートの裏面に微粒子のサイズに応じた微小な窪みを形成できる。
エンボスロールは、ロール表面にエンボスパターン(凹凸形状パターン)を有する。凹凸形状パターンに特に制限はなく、樹脂シートの表面に形成するエンボスパターンに応じた形状にすれば良い。例えば、エンボスロール表面に、所望形状の凸部を、所望間隔をあけて配置しても良い。凸部の形状としては、例えば、ドーム状、半ドーム状、錘状(円錐状、多角錘状等)、ストライプ状、波状、メッシュ状、格子状がある。また、エンボスロール表面に、所望形状の凹部を、所望間隔をあけて配置しても良い。凹部の形状としては、例えば、逆ドーム、逆錘状(逆円錐状、逆多角錘状等)、ストライプ状、波状、メッシュ状、格子状がある。
本発明の樹脂シートは、エチレン系樹脂からなる。エチレン系樹脂のショアA硬度は50〜85であり、、好ましくは60〜80である。ショアA硬度は、エンボスの無いシートを試料として用い、ASTM D2240に準拠して測定する。
本発明の樹脂シートは、表面にはエンボスが形成され、裏面には微細な窪みが形成されている。
本発明の太陽電池モジュールは、本発明の樹脂シートの裏面にバックシートが接するように積層されたものである。すなわち、この樹脂シートを太陽電池封止材として用いたことを特徴とする太陽電池モジュールである。この太陽電池モジュールは、例えば、保護部材(保護ガラス等)、樹脂シート、太陽電池セル、樹脂シート及びバックシートをこの順に積層した構成を有する。このような太陽電池モジュールは、例えば加圧、加熱下にて各部材を真空ラミネートすることにより製造できる。その際の樹脂シートの表面側(エンボス側)は太陽電池セルと接し、裏面側(微細窪み側)はバックシートや保護部材(保護ガラス等)と接するように積層すれば良い。
エチレン・酢酸ビニル共重合体(酢酸ビニル含量=28%、190℃、2160g荷重でのMFR=20g/10分、Mw/Mn=2.19)100部に、2,5−ジメチル−2,5−ビス(t−ブチルパーオキシ)ヘキサン0.1部と、t−ブチルパーオキシ−2−エチルヘキシルカーボネート0.2部と、トリアリルイソシアヌレート0.4部と、γ−メタクリロキシプロピルトリメトキシシラン0.5部とを配合して樹脂組成物を得た。この樹脂組成物をTダイ付押出機にて押し出し、1.4mm間隔でダイヤ形状のエンボス形成したエンボスロールと、シリコンラバー層に約50μm未満の粒子径を持つアルミナ粒子を含有させた層を表層に有するバックアップロールとで加圧してエンボスを施したシートとし、厚さ約600μmのエンボス付樹脂シートを成形した。このときのバックアップロールの平均表面粗度は4.7μmであり、得られた樹脂シート裏面の平均表面粗度は2.4μm、ショアA硬度は82、表面のエンボスの深さは0.43mm、エンボスの周期は1.4mmであった。
バックアップロールのシリコンラバー層として、約10μm未満の粒子径を持つアルミナ粒子を含有させたシリコンラバー層を用いたこと以外は、実施例1と同様にして樹脂シートを得た。このときのバックアップロールの平均表面粗度は2.1μmであり、得られた樹脂シート裏面の平均表面粗度は1.1μmであった。
Claims (7)
- ショアA硬度が50〜85のエチレン系樹脂からなり、表面にはエンボスが形成された樹脂シートであって、
裏面には微細な窪みが形成され、裏面の平均表面粗度が1.5〜10μmであり、
裏面には、表面のエンボスと略同一の周期で形成された波形の凹凸形状を有し、かつ該波形状の凸部付近における平均表面粗度が1.5〜10μmであることを特徴とする樹脂シート。 - 表面に形成されたエンボスの深さが0.1mm以上であり、かつ該エンボスの周期が0.1mm〜5mmである請求項1記載の樹脂シート。
- エチレン系樹脂が、エチレン・酢酸ビニル共重合体である請求項1又は2記載の樹脂シート。
- エチレン・酢酸ビニル共重合体の酢酸ビニル含有量が21〜40質量%であり、かつ有機過酸化物を含有する請求項3記載の樹脂シート。
- 請求項1〜4の何れか一項記載の樹脂シートからなる太陽電池封止用樹脂シート。
- 請求項1〜4の何れか一項記載の樹脂シートの製造方法であって、
ダイから溶融押出されたエチレン・酢酸ビニル樹脂からなる樹脂シートを、凹凸形状パターンを有するエンボスロールと、該エンボスロールに対向配置されたバックアップロールとの間で加圧することにより、前記樹脂シート表面に前記エンボスロールの凹凸形状パターンを転写する工程を含み、
前記バックアップロールとして、表層に無機微粒子を含むゴム製弾性ロールを用いることを特徴とする樹脂シートの製造方法。 - 請求項5記載の樹脂シートの裏面にバックシートが接するように積層された太陽電池モジュール。