JP6030814B1 - ポリカーボネート樹脂組成物及び成形品 - Google Patents
ポリカーボネート樹脂組成物及び成形品 Download PDFInfo
- Publication number
- JP6030814B1 JP6030814B1 JP2016538111A JP2016538111A JP6030814B1 JP 6030814 B1 JP6030814 B1 JP 6030814B1 JP 2016538111 A JP2016538111 A JP 2016538111A JP 2016538111 A JP2016538111 A JP 2016538111A JP 6030814 B1 JP6030814 B1 JP 6030814B1
- Authority
- JP
- Japan
- Prior art keywords
- polycarbonate resin
- group
- resin composition
- weight
- transmittance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
ポリカーボネート樹脂(A)と、リン系酸化防止剤(B)と、脂肪酸エステル(C)とを含有してなり、
前記リン系酸化防止剤(B)の量が、前記ポリカーボネート樹脂(A)100重量部に対して0.04〜0.1重量部であり、
前記脂肪酸エステル(C)の量が、前記ポリカーボネート樹脂(A)100重量部に対して0.03〜0.5重量部であり、
前記リン系酸化防止剤(B)が、2種の化合物で、該2種の化合物のうちの1種が、一般式(1):
で表される化合物であり、
前記リン系酸化防止剤(B)の他の1種が、一般式(3)で表される化合物であり、
前記一般式(1)で表される化合物の量が、リン系酸化防止剤(B)全量の42〜70重量%であるものである。
実施の形態1に係るポリカーボネート樹脂組成物は、ポリカーボネート樹脂(A)と、リン系酸化防止剤(B)と、脂肪酸エステル(C)とを含有したものである。なお、本発明のポリカーボネート樹脂組成物は、必要に応じて、その他の成分を含有していてもよい。
なくとも2種の化合物が含有される。少なくとも2種の化合物のうちの1種は、一般式(1):
で表される化合物である。
で表される化合物が挙げられる。
フォスファイト基の酸素原子と結合していることを示す。
で表される化合物が挙げられる。
デカスタブ」は登録商標)が商業的に入手可能である。これらの中でも3,9−ビス(2,6−ジ−t−ブチル−4−メチルフェノキシ)−2,4,8,10−テトラオキサ−3,9−ジフォスファスピロ[5,5]ウンデカンが好適である。
で表される化合物が挙げられる。
で表される化合物等が挙げられる。
いてもよい。
実施の形態2に係る成形品は、前記のごとく得られる実施の形態1に係るポリカーボネート樹脂組成物を成形して得られるものである。
って、該導光フィルムは、600μm程度以下の厚さであっても、色相が変化して外観が低下することや、高温成形を経て樹脂そのものが劣化することが少なく、輝度、光線透過率及び色相安定性のバランスが良好であるとともに、押出成形性にも優れるため、工業的利用価値が極めて高い。
1.ポリカーボネート樹脂(A)
ビスフェノールAと塩化カルボニルとから合成されたポリカーボネート樹脂
カリバー200−30
(商品名、住化スタイロンポリカーボネート(株)製、「カリバー」はスタイロン ユーロップ ゲーエムベーハーの登録商標、粘度平均分子量:18000、以下「PC」という)
(商品名、(株)ADEKA製、以下「B2」という)
グリセリンモノステアレート
リケマールS−100A
(商品名、理研ビタミン(株)製、以下「GM」という)
実施例1−1〜1−3及び比較例1−1〜1−2
前記各原料を、表1に示す割合にて一括してタンブラーに投入し、10分間乾式混合した後、二軸押出機((株)日本製鋼所製、TEX30α)を用いて、溶融温度240℃にて溶融混練し、ポリカーボネート樹脂組成物のペレットを得た。
長さ 断面楕円の長径 断面楕円の短径
実施例1−1 約5.0 約3.9 約2.6
1−2 約5.1 約4.1 約2.4
1−3 約5.1 約4.0 約2.8
比較例1−1 約5.0 約4.0 約2.5
1−2 約5.2 約4.3 約2.9
得られたペレットを120℃で4時間以上乾燥した後、射出成形機(ファナック(株)製、ROBOSHOT S2000i100A)を用い、成形温度280℃、金型温度80℃にて、JIS K 7139「プラスチック−試験片」にて規定の多目的試験片A型(全長168mm×厚さ4mm)を作製した。この168mm長光路試験片の端面を切削し、切削端面について、樹脂板端面鏡面機(メガロテクニカ(株)製、プラビューティーPB−500)を用いて鏡面加工した。
源として50Wハロゲンランプを用い、光源前マスク5.6mm×2.8mm、試料前マスク6.0mm×2.8mmを使用した状態で、波長380〜780nmの領域で1nm毎の、試験片の分光透過率を全長方向について、標準光源D65を用い、10度視野にて測定した。測定した分光透過率に基づき、各々の黄色度を求め、これを168mm長の初期色相YIとした。なお、YIが13以下を良好(表中、○で示す)、13を超えると不良(表中、×で示す)とした。
溶融ペレットを前記(ア)初期色相で用いた射出成形機のシリンダ内にて280℃で15分間滞留させた後、前記(ア)と同様にして168mm長光路試験片を作製した。
前記(ア)と同様にして168mm長光路試験片を作製した。分光光度計((株)日立製作所製、UH4150)に長光路測定付属装置を設置し、光源として50Wハロゲンランプを用い、光源前マスク5.6mm×2.8mm、試料前マスク6.0mm×2.8mmを使用した状態で、波長380〜780nmの領域で1nm毎の、試験片の分光透過率を全長方向について測定した。測定した分光透過率を積算し、十の位を四捨五入することにより、試験前積算透過率を求めた。
実施例2−1〜2−4及び比較例2−1〜2−4
前記各原料を、表2に示す割合にて一括してタンブラーに投入し、第1実施態様と同様の方法にてポリカーボネート樹脂組成物のペレットを得た。なお、実施例2−1〜2−4及び比較例2−1〜2−4で得られたペレットは、いずれも、ほぼ楕円柱状であり、ペレット100個からなる集合体のサイズ(平均値(mm))は、各々以下のとおりである。
長さ 断面楕円の長径 断面楕円の短径
実施例2−1 約5.0 約3.9 約2.6
2−2 約5.1 約4.1 約2.4
2−3 約5.0 約4.0 約2.5
2−4 約5.2 約4.3 約2.8
比較例2−1 約5.2 約4.3 約2.9
2−2 約5.3 約3.8 約2.8
2−3 約5.0 約3.9 約2.4
2−4 約5.0 約3.9 約2.6
得られたペレットを120℃で4時間以上乾燥した後、射出成形機(ファナック(株)製、ROBOSHOT S2000i100A)を用い、成形温度280℃、金型温度80℃にて、JIS K 7139「プラスチック−試験片」にて規定の多目的試験片A型(全長168mm×厚さ4mm)を作製した。この168mm長光路試験片の端面を切削し、切削端面について、樹脂板端面鏡面機(メガロテクニカ(株)製、プラビューティーPB−500)を用いて鏡面加工した。
溶融ペレットを前記(ア)初期色相で用いた射出成形機のシリンダ内にて280℃で15分間滞留させた後、前記(ア)と同様にして168mm長光路試験片を作製した。
押出シート成形機(田辺プラスチックス機械(株)製、単軸40mmシート押出機)を用い、スクリュウ回転数90rpm、溶融温度260℃の条件にて、得られたペレットから、幅250mm、厚さ0.5mmのシートを成形した。得られたシートの外観及び成形時の揮発成分によるロール表面の汚れを目視にて観察し、以下の評価基準に基づいて評価した。なお、評価が優良又は良好であれば、実用上問題がないレベルである。
(評価基準)
優良(表中、◎で示す):
シート表面に筋状のマークが全くなく、ロール表面の汚れもない。
良好(表中、○で示す):
シート表面に筋状のマークが殆どなく、ロール表面の汚れも殆どない。
普通(表中、△で示す):
シート表面に筋状のマークがあり、ロール表面の汚れもある。
不良(表中、×で示す):
シート表面に筋状のマークが多く、ロール表面の汚れも著しい。
第1実施態様と同様の方法にて長期信頼性の評価を行った。
全量の40〜80重量%の範囲内に調整されている。したがって、これらのポリカーボネート樹脂組成物から成形された168mm長光路試験片は、いずれも、黄色度が小さく、初期色相に優れるだけでなく、280℃で15分間滞留させた後に成形された168mm長光路試験片であっても、黄変が充分に抑制されており、熱安定性に優れる。さらに、これらのポリカーボネート樹脂組成物は、シートに成形する際の押出成形性に優れる。しかも、これらのポリカーボネート樹脂組成物から成形された168mm長光路試験片は、温度90℃、相対湿度90%の条件下で500時間に渡って加水分解試験を行った後でも、光線透過率の低下が非常に少なく、長期信頼性にも優れている。
Claims (7)
- ポリカーボネート樹脂(A)と、リン系酸化防止剤(B)と、脂肪酸エステル(C)とを含有してなり、
前記リン系酸化防止剤(B)の量が、前記ポリカーボネート樹脂(A)100重量部に対して0.04〜0.1重量部であり、
前記脂肪酸エステル(C)の量が、前記ポリカーボネート樹脂(A)100重量部に対して0.03〜0.5重量部であり、
前記リン系酸化防止剤(B)が、2種の化合物で、該2種の化合物のうちの1種が、一般式(1):
で表される化合物であり、
前記リン系酸化防止剤(B)の他の1種が、一般式(3)で表される化合物であり、
前記一般式(1)で表される化合物の量が、リン系酸化防止剤(B)全量の42〜70重量%である、ポリカーボネート樹脂組成物。 - 一般式(1)で表される化合物が、トリス(2,4−ジ−t−ブチルフェニル)フォスファイトである、請求項1に記載のポリカーボネート樹脂組成物。
- それを成形してなる168mm長光路試験片の、以下の式に基づいて算出されるΔ積算透過率が、5000未満である、請求項1に記載のポリカーボネート樹脂組成物:
Δ積算透過率=試験前積算透過率−試験後積算透過率
ここで、
試験前積算透過率:温度90℃、相対湿度90%の条件下で500時間、加水分解試験に供する前の試験片について、波長380〜780nmの領域で1nm毎に測定した全長方向の分光透過率を積算した値、及び
試験後積算透過率:前記加水分解試験に供した後の試験片について、波長380〜780nmの領域で1nm毎に測定した全長方向の分光透過率を積算した値
である。 - それを成形してなる168mm長光路試験片の、波長380〜780nmの領域で1nm毎に測定した全長方向の分光透過率から求めた初期色相YIが、13以下である、請求項1に記載のポリカーボネート樹脂組成物。
- 請求項1に記載のポリカーボネート樹脂組成物を成形してなる成形品。
- 車両ランプ用ライトガイドである、請求項5に記載の成形品。
- 導光フィルムである、請求項5に記載の成形品。