JP5669308B2 - ポリビニルアミンの安定な油中水型エマルジョンの製造方法 - Google Patents
ポリビニルアミンの安定な油中水型エマルジョンの製造方法 Download PDFInfo
- Publication number
- JP5669308B2 JP5669308B2 JP2011011488A JP2011011488A JP5669308B2 JP 5669308 B2 JP5669308 B2 JP 5669308B2 JP 2011011488 A JP2011011488 A JP 2011011488A JP 2011011488 A JP2011011488 A JP 2011011488A JP 5669308 B2 JP5669308 B2 JP 5669308B2
- Authority
- JP
- Japan
- Prior art keywords
- polyvinylamine
- oil emulsion
- water
- producing
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
NaOH(aq):水酸化ナトリウム水溶液、HCl(aq):塩酸水溶液
HN3(g):アンモニアガス、HCl(g):塩化水素ガス
固有粘度:1mol/L NaCl水溶液中25℃において測定(単位:dL/g)
水溶液pH:1.0重量%水溶液に30分溶解した溶液のpH
Claims (6)
- 乳化重合法により得られたN−ビニルカルボン酸アミド重合物水溶液の油中分散液を酸又は塩基の存在下加水分解する方法において、HLB8.0〜14.0の範囲のポリオキシアルキレンアルキルエーテルの共存下で加水分解を行うことを特徴とする、ポリビニルアミンの安定な油中水型エマルジョンの製造方法。
- 塩基の存在下加水分解することを特徴とする、請求項1に記載のポリビニルアミンの安定な油中水型エマルジョンの製造方法。
- 前記N−ビニルカルボン酸アミド重合物水溶液の油中分散液を前記ポリオキシアルキレンアルキルエーテルの共存下、前記塩基で加水分解を行った後、酸を添加することを特徴とする、請求項2に記載のポリビニルアミンの安定な油中水型エマルジョンの製造方法。
- 前記ポリオキシアルキレンアルキルエーテルをN−ビニルカルボン酸アミドの重合後、加水分解工程の前に添加することを特徴とする、請求項1〜3のいずれかに記載のポリビニルアミンの安定な油中水型エマルジョンの製造方法。
- 1mol/L濃度のNaCl水溶液中での25℃におけるポリビニルアミンの固有粘度が、0.5〜10.0(dL/g)の範囲であることを特徴とする、請求項1〜4のいずれかに記載のポリビニルアミンの安定な油中水型エマルジョンの製造方法。
- 前記油中水型エマルジョンの1質量%水溶液のpHが6.0〜14.0の範囲であることを特徴とする、請求項1〜4のいずれかに記載のポリビニルアミンの安定な油中水型エマルジョンの製造方法。