JP5626488B2 - 酸素吸収剤の製造方法 - Google Patents
酸素吸収剤の製造方法 Download PDFInfo
- Publication number
- JP5626488B2 JP5626488B2 JP2013557976A JP2013557976A JP5626488B2 JP 5626488 B2 JP5626488 B2 JP 5626488B2 JP 2013557976 A JP2013557976 A JP 2013557976A JP 2013557976 A JP2013557976 A JP 2013557976A JP 5626488 B2 JP5626488 B2 JP 5626488B2
- Authority
- JP
- Japan
- Prior art keywords
- oxygen
- component
- alloy
- salt
- acid salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、酸素吸収剤の製造方法に関し、より詳細には、大気雰囲気下での過度な発熱を抑え、安定して酸素吸収性能を維持できる酸素吸収剤を製造する方法に関する。
食品や医薬品などの保存技術の一つとして、酸素吸収剤(脱酸素剤)による保存技術がある。具体的には、雰囲気中の酸素を除去する脱酸素剤を対象物と共に密閉包装体の内部に入れて、密閉包装体の内部を無酸素状態にすることによって、対象物の酸化劣化、カビ、変色などを抑制する技術である。
これまでに雰囲気中の酸素を除去する脱酸素剤として、各種無機系材料からなるもの及び有機系材料からなるものが提案されている。例えば、無機系主剤として鉄などの金属粉、亜硫酸塩、亜硫酸水素塩、亜ニチオン酸塩などを用いたもの、有機系主剤としてL−アスコルビン酸、エリソルビン酸及びそれらの塩、グルコースなどの糖類、カテコール、ピロガロールなどの還元性多価アルコール類を用いたものなどが挙げられる。
しかしながら、これら従来の脱酸素剤は、使用時に水もしくは水分を供給するものがないと実用的な脱酸素能を得ることができないという問題点があった。すなわち、従来の脱酸素剤は、使用する際に水もしくは水分を保持させた物質、例えば、結晶水を持った化合物を混合するか、あるいは保存しようとする食品などから出てくる水蒸気を利用することによってはじめて実用的な脱酸素能を得ることができるものであった。このため、従来の脱酸素剤を、乾燥条件下にて使用または保存する必要のある医薬品または乾燥食品や、水もしくは水分の存在を嫌う金属製品の防錆保存について適用することは困難であった。
このため、これらの用途においては、酸素吸収の際に水分を必要としない酸素吸収剤が求められていた。このような要求に応え得る酸素吸収剤としては、例えば、酸素欠陥を利用した酸化セリウムを主剤とした脱酸素剤(特開2007−185653号公報)、酸素欠陥を有した酸化チタンを主剤とした脱酸素剤(特開2005−104064号公報)、水素還元を行った金属を主剤とした脱酸素剤(特開昭62−277148号公報)、および有機物の自動酸化を利用した脱酸素剤などが報告されている。
しかしながら、上記した脱酸素剤のうち、特開2007−185653号公報や特開2005−104064号公報に開示された脱酸素剤は、その原料となる金属がレアメタルであるため、希少で高価である。また海外からの輸入に頼らざるを得ず、情勢によっては仕入れが変動し安定した生産量が望めなくなる場合もある。このため、コストと安定供給の観点から必ずしも満足し得るものとは言えなかった。また、特開昭62−277148号公報に開示された脱酸素剤は、製造に際して大がかりな水素還元設備を付帯する必要があるため、簡便な手法ではなく、大気中での取り扱い性が良いとも言えない。さらに、上記した有機物の自動酸化を利用した脱酸素剤においては、主剤として有機物の酸化反応を利用しているため、酸素吸収後に発生する副生成物の問題がある。
このため、水分が無いか殆ど無い雰囲気下であっても雰囲気中の酸素を吸収する能力をもつ酸素吸収剤であって、原料が安価で安定しており、副生成物の問題も殆ど無く、水素還元を行う場合のような大規模な装置を付帯する必要のないものが、依然として望まれていた。
本発明者らは、アルミニウムと鉄とからなる合金、または、アルミニウムとニッケルとからなる合金から水酸化ナトリウム水溶液を用いてアルミニウムのみを取り除いた金属が、30%RH(25℃)以下であるような水分が無いか殆ど無い雰囲気中であっても、雰囲気中の酸素を、従来の脱酸素剤と同等のレベルで、吸収・除去し得るとともに、このような金属であれば、水素還元を行う場合のような大規模な装置を用いなくても簡易かつ安価に製造することができることを見出し、この金属を脱酸素剤として使用すれば、水分が殆ど無い雰囲気中でも酸素を吸収することができるとの知見を得た。
しかしながら、上記した金属は酸素吸収活性が非常に高く、大気雰囲気中でも酸素と反応して発熱する場合があり、酸素吸収剤を発熱させずに使用するような場合は、酸素吸収剤を特定の環境下(例えば、無酸素雰囲気下)で使用する必要がある。その場合、特定の環境にするには設備等を要するため、取扱いが煩雑になるとともに、取扱いコストの上昇を招く。
そして、本発明者らは、今般、上記金属を、金属と塩を形成し得る特定の溶液で処理して金属表面の一部に金属塩を形成することにより、酸素吸収活性を制御できることに気付き、この方法によれば、大気雰囲気下での過度な発熱を抑え、安定して酸素吸収性能を維持できる酸素吸収剤を製造することができるとの知見を得た。本発明はかかる知見によるものである。
したがって、本発明の目的は、大気雰囲気下での過度な発熱を抑え、安定して酸素吸収性能を維持できる酸素吸収剤が得られる方法を提供することである。
本発明による酸素吸収剤の製造方法は、
(A)マンガン族、鉄族、白金族および銅族からなる群より選択される少なくとも1種の遷移金属と、(B)アルミニウム、亜鉛、スズ、鉛、マグネシウムおよびケイ素からなる群より選択される少なくとも1種の金属と、を含む合金(X)を、酸またはアルカリの水溶液処理に供して、前記成分(B)の少なくとも一部を溶出除去し、
前記成分(B)の少なくとも一部が除去された合金(Y)を、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、前記合金(Y)の表面の少なくとも一部に金属塩を形成させる、
ことを含んでなるものである。
(A)マンガン族、鉄族、白金族および銅族からなる群より選択される少なくとも1種の遷移金属と、(B)アルミニウム、亜鉛、スズ、鉛、マグネシウムおよびケイ素からなる群より選択される少なくとも1種の金属と、を含む合金(X)を、酸またはアルカリの水溶液処理に供して、前記成分(B)の少なくとも一部を溶出除去し、
前記成分(B)の少なくとも一部が除去された合金(Y)を、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、前記合金(Y)の表面の少なくとも一部に金属塩を形成させる、
ことを含んでなるものである。
本発明の態様によれば、前記成分(A)が、鉄、コバルト、ニッケル、および銅からなる群より選択されるものであってよい。
また、本発明の態様によれば、前記成分(B)がアルミニウムであってもよい。
また、本発明の態様によれば、前記合金(Y)に含まれる成分(B)の含有率が0.01〜50質量%となるまで、前記成分(B)の溶出除去を行ってもよい。
また、本発明の態様によれば、前記酸またはアルカリの水溶液が水酸化ナトリウム水溶液であってもよい。
また、本発明の態様によれば、前記成分(A)と前記成分(B)とを含む合金(X)の粉末を、酸またはアルカリの水溶液処理に供して、前記成分(B)の少なくとも一部を溶出除去して、粉末状の合金(Y)を得てもよい。
また、本発明の態様によれば、前記無機酸塩または有機酸塩が、無機酸および有機酸から選択される少なくとも1種類の弱酸と強塩基との塩であってもよい。
また、本発明の態様によれば、前記無機酸塩または有機酸塩が、リン酸塩、炭酸塩、およびシュウ酸塩からなる群より選択される少なくとも1種の塩であってもよい。
本発明の別の態様によれば、上記した方法により得られた酸素吸収剤も提供される。
また、本発明の態様による酸素吸収剤は、前記成分(B)の少なくとも一部を溶出除去して得られる合金(Y)が、多孔質形状であってもよい。
また、本発明による酸素吸収剤は、前記成分(B)の少なくとも一部を溶出除去して得られる合金(Y)の、BET法により測定される比表面積が、少なくとも10m2/gであってもよい。
本発明の別の態様によれば、上記した酸素吸収剤を、通気性包装材を全部または一部に用いた包装材で包装してなる酸素吸収性包装体や、酸素吸収剤と熱可塑性樹脂とを含んでなる酸素吸収性樹脂組成物も提供される。
また、本発明の別の態様によれば、上記酸素吸収性樹脂組成物からなる酸素吸収性樹脂シートまたはフィルムも提供される。
本発明による酸素吸収剤の製造方法によれば、特定の遷移金属(A)と特定の金属(B)とを含む合金(X)から成分(B)の少なくとも一部を溶出除去して合金(Y)を得た後、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で合金(Y)を処理して、合金(Y)の表面の少なくとも一部に金属塩を形成させることにより、大気雰囲気下での過度な発熱を抑え、安定して酸素吸収性能を維持できる酸素吸収剤を得ることができる。
<酸素吸収剤の製造方法>
本発明による酸素吸収剤の製造方法は、(1)特定の遷移金属(A)と特定の金属(B)とを含む合金(X)から成分(B)の少なくとも一部を溶出除去して合金(Y)を得る工程と、(2)合金(Y)を、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、合金(Y)の表面の少なくとも一部に金属塩を形成させる工程とを含むものである。以下、酸素吸収剤を製造する方法の各工程について説明する。なお、なお、本明細書において、「酸素吸収剤」とは、かかる剤を設置した周囲の雰囲気中から酸素を選択的に吸収することができるものをいう。
本発明による酸素吸収剤の製造方法は、(1)特定の遷移金属(A)と特定の金属(B)とを含む合金(X)から成分(B)の少なくとも一部を溶出除去して合金(Y)を得る工程と、(2)合金(Y)を、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、合金(Y)の表面の少なくとも一部に金属塩を形成させる工程とを含むものである。以下、酸素吸収剤を製造する方法の各工程について説明する。なお、なお、本明細書において、「酸素吸収剤」とは、かかる剤を設置した周囲の雰囲気中から酸素を選択的に吸収することができるものをいう。
成分(A)
酸素吸収剤を構成する成分(A)として使用可能な遷移金属は、マンガン族(マンガン、テクネチウム、レニウム)、鉄族(鉄、コバルト、ニッケル)、白金族(ルテニウム、ロジウム、パラジウム、オスミウム、イリジウム、白金)、銅族(銅、銀、金)から選択されるものである。上記した遷移金属は、単独でも2種以上を組み合わせて用いても良く、例えば、鉄とニッケルが選択される場合、成分(A)として、Fe−Ni合金を使用しても良い。
酸素吸収剤を構成する成分(A)として使用可能な遷移金属は、マンガン族(マンガン、テクネチウム、レニウム)、鉄族(鉄、コバルト、ニッケル)、白金族(ルテニウム、ロジウム、パラジウム、オスミウム、イリジウム、白金)、銅族(銅、銀、金)から選択されるものである。上記した遷移金属は、単独でも2種以上を組み合わせて用いても良く、例えば、鉄とニッケルが選択される場合、成分(A)として、Fe−Ni合金を使用しても良い。
成分(A)としては、好ましくは、マンガン、鉄、コバルト、ニッケル、または銅であり、より好ましくは、鉄、コバルト、ニッケル、または銅であり、さらに好ましくは、鉄、またはニッケルであり、特に好ましくは、鉄である。このうち、鉄は、安全性が高く安価であるため好ましい。
成分(B)
酸素吸収剤を構成する成分(B)としては、アルミニウム、亜鉛、スズ、鉛、マグネシウムおよびケイ素から選択されるものを使用する。これらは単独でも2種以上を組み合わせて用いても良い。成分(B)として例示したなかでも、アルミニウム、亜鉛、マグネシウムまたはケイ素から選択されるものが好ましく、より好ましくは、アルミニウム、亜鉛、マグネシウムまたはケイ素であり、さらに好ましくはアルミニウムである。このうち、アルミニウムは安価であるため好ましい。
酸素吸収剤を構成する成分(B)としては、アルミニウム、亜鉛、スズ、鉛、マグネシウムおよびケイ素から選択されるものを使用する。これらは単独でも2種以上を組み合わせて用いても良い。成分(B)として例示したなかでも、アルミニウム、亜鉛、マグネシウムまたはケイ素から選択されるものが好ましく、より好ましくは、アルミニウム、亜鉛、マグネシウムまたはケイ素であり、さらに好ましくはアルミニウムである。このうち、アルミニウムは安価であるため好ましい。
本発明による酸素吸収剤は、上記した成分(A)と成分(B)とを含む合金(X)を調製するが、このとき、合金(X)には、添加金属として、さらに、モリブデン、クロム、チタン、バナジウム、タングステンなどを加えても良い。シアン酸類等の添加成分をさらに含有していても良い。
上記したような成分(A)と成分(B)とを含む合金(X)は、溶融法により調製することができる。このとき、成分(A)と成分(B)との組成の割合は、好ましくは、成分(A)が20〜80質量%であるとき、成分(B)は20〜80質量%であり、より好ましくは、成分(A)が30〜70質量%であるとき、成分(B)は30〜70質量%である。より具体的な例を挙げると、成分(A)が鉄またはニッケル、成分(B)がアルミニウムである場合、鉄またはニッケルの割合は30〜55質量%、アルミニウムの割合は45〜70質量%であることが好ましい。
得られる合金(X)は、そのまま、酸またはアルカリの水溶液処理に供してもよいが、通常は、微粉砕した後に、酸またはアルカリの水溶液処理に供する。なお、本明細書において「合金」とは、特定の結晶構造を有している単一組成のもののみならず、それらの混合物及び金属自体の混合物を含むものとする。
合金(X)を微粉砕する方法としては、慣用の金属の解砕・粉砕のための方法を適宜使用することができ、例えば、ジョークラッシャーや、ロールクラッシャー、ハンマーミル等で粉砕し、さらに必要に応じてボールミルで微粉砕することができる。あるいは、前記合金の溶湯をアトマイズ法等の急冷凝固法により微粉化してもよい。ここでアトマイズ法による場合には、アルゴンガス等の不活性ガス中で行なうのが好ましい。アトマイズ法としては、例えば特開平5−23597号公報に記載の方法を使用することができる。
得られる合金粉末の粒径は、5〜200μmの範囲内となることが好ましく、またこの粒径分布はできるだけ狭いことが好ましい。粒径の大きなものを排除したり、粒径分布をそろえたりする観点から、市販のメッシュ篩(例えば、200メッシュ篩など)を使用して篩い分け(分級)を適宜行っても良い。なお、アトマイズ法による場合、粉末は球状に近くなる傾向にあり、また、粒径分布を狭くできる傾向にある。
次いで、上記のようにして得られた合金(X)またはその粉末を、酸またはアルカリの水溶液処理に供して、合金(X)から、成分(B)の少なくとも一部を溶出させ除去する。すなわち、本発明においては、上記合金(X)から成分(B)の少なくとも一部を溶出させ除去した後に得られる合金(Y)が酸素吸収剤として使用される。酸またはアルカリの水溶液としては、成分(A)が溶解しないか殆ど溶解せず、かつ、成分(B)が主として溶解するもの、あるいは、成分(A)および(B)のいずれもが溶解するが、成分(B)の溶解速度が成分(A)よりも高いものであれば特に制限はなく使用することができる。酸水溶液における酸としては、例えば、塩酸、硫酸、硝酸などを使用することができ、アルカリ水溶液におけるアルカリとしては、例えば、水酸化ナトリウム、水酸化カリウム、水酸化カルシウム、水酸化テトラメチルアンモニウム(TMAH)、Na2CO3、K2CO3、アンモニアなどを使用することができる。これら酸およびアルカリ水溶液についてはそれぞれついて、必要に応じて2種以上を組み合わせて用いても良い。
本発明の好ましい態様によれば、酸またはアルカリの水溶液としてアルカリ水溶液を用いることが好ましく、より好ましくは、水酸化ナトリウム水溶液である。例えば、成分(B)としてアルミニウムを用いた場合、アルカリ水溶液として水酸化ナトリウムを用いると、水洗により過剰量の水酸化ナトリウムを除去し、また溶出したアルミニウムを除去することが容易であり、このため、水洗回数を削減できるという効果が期待できる。
酸またはアルカリの水溶液処理において、通常は、合金粉末であれば、合金粉末を酸またはアルカリの水溶液中へ攪拌しながら少しずつ投入するが、合金粉末を水中にいれておき、ここに濃厚な酸またはアルカリを滴下しても良い。
酸またはアルカリの水溶液処理において、使用する酸またはアルカリ水溶液の濃度は、例えば、5〜60質量%であり、より具体的には、例えば水酸化ナトリウムの場合、10〜40質量%が好ましい。
酸またはアルカリの水溶液処理においては、該水溶液の温度は、例えば、20〜120℃程度であることが好ましい。より好ましい温度は25〜100℃である。
合金または合金粉末を酸またはアルカリの水溶液処理に供しておく処理時間は、使用する合金の形状、状態、およびその量、酸またはアルカリの水溶液の濃度、処理する際の温度等により変化し得るが、通常は、30〜300分間程度で良い。処理時間を調整することで、合金からの成分(B)の溶出量を調節することもできる。
本発明においては、酸またはアルカリの水溶液処理によって、合金(X)から、成分(B)の少なくとも一部を溶出除去する。ここで、「成分(B)の少なくとも一部」を溶出除去するとは、成分(A)および成分(B)を含む合金(X)から、成分(B)の一部を溶出させ除去することに加えて、成分(B)の全部を合金(X)から溶出させ除去する場合も包含する意味である。したがって、本発明において「合金(Y)」とは、成分(B)の全部が溶出した金属(すなわち、成分(A)のみからなる金属)も包含する概念である。なお、成分(B)の溶出の過程では、結果として成分(A)の一部が溶解する可能性も否定できないので、「成分(B)の少なくとも一部」には、成分(B)のみが酸またはアルカリの水溶液処理によって溶出される場合に限定して解釈する必要はない。
酸またはアルカリの水溶液処理によって、成分(B)(例えば、アルミニウム)の少なくとも一部、好ましくはその大部分が合金(X)から溶出する。合金(X)からの成分(B)の溶出の割合は、溶出除去によって得られる合金(Y)における成分(B)の含有率(質量基準)(残存率)で示すことができる。
酸素吸収剤として用いられる金属(即ち、成分(B)を溶出した後の合金(Y))において、成分(B)の含有率は、好ましくは0.01〜50質量%であり、より好ましくは0.1〜40質量%である。より具体的には、例えば、合金(X)が、Al−Fe合金である場合、酸またはアルカリの水溶液処理によるアルミニウムの溶出除去によって得られる合金(Y)におけるアルミニウムの含有率は、好ましくは0.01〜50質量%であり、より好ましくは0.1〜40質量%、さらに好ましくは1〜5質量%である。なお、酸素吸収剤に用いられる合金(Y)中の成分(B)(例えば、アルミニウム)の含有量は、例えば、ICP法により測定することができる。
次に、成分(B)の少なくとも一部が溶出除去された合金(Y)を、成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、金属表面の少なくとも一部に金属塩を形成させる。成分(B)の金属の少なくとも一部が溶出した合金(Y)は、酸素吸収活性が非常に高く、大気雰囲気中でも酸素と反応して発熱する場合がある。上記のように、成分(B)の金属を溶出した後の合金(Y)の表面を特定の水溶液で処理することにより、合金(Y)の表面の一部に金属塩を形成させて、酸素との反応による発熱を抑制し、酸素吸収性能を制御することができる。合金(Y)の表面に金属塩を形成させることにより酸素との反応による発熱が抑制される理由は定かではないが、以下のように考えられる。
合金(Y)を、無機酸塩または有機酸塩の水溶液で処理することにより、合金(Y)の表面に金属塩の被膜が形成される。この被膜により合金(Y)の細孔中への酸素の拡散が阻害され急激な酸化反応が起こらなくなり、その結果、発熱が抑制されるものと考えられる。
遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液としては、無機酸および有機酸から選択される少なくとも1種類の弱酸と強塩基との塩水溶液が挙げられる。無機酸としてはリン酸や炭酸等が挙げられ、有機酸としてはシュウ酸等が挙げられる。これらの弱酸と反応して有機酸塩または無機酸塩を形成する強塩基としては、水酸化ナトリウム、水酸化カリウム等、特に制限なく使用することができる。
上記した無機酸塩または有機酸塩のなかでも、リン酸塩、炭酸塩、およびシュウ酸塩を好ましく使用することができ、例えば、リン酸水素ナトリウム、リン酸2水素ナトリウム、炭酸水素ナトリウム、シュウ酸ナトリウム等が挙げられる。
例えば、合金が、Al−Fe合金から成分(B)であるアルミニウムを溶出除去した金属を、上記した無機酸塩または有機酸塩水溶液で処理した場合、金属(即ち、Fe)表面に金属塩を形成して、リン酸鉄(II)八水和物、リン酸鉄(III)二水和物、炭酸鉄(II)、炭酸鉄(II)一水和物、シュウ酸鉄(II)二水和物、シュウ酸鉄(III)五水和物等の塩からなる被膜が形成される。また、Al−Ni合金から成分(B)であるアルミニウムを溶出除去した金属を、上記した無機酸塩または有機酸塩水溶液で処理した場合、金属(即ち、Ni)表面に金属塩を形成して、リン酸ニッケル(II)八水和物、炭酸ニッケル(II)、シュウ酸ニッケル(II)二水和物等の塩からなる被膜が形成される。これらの塩も酸素と反応するものの鉄やニッケルよりも酸化活性が低いため、結果として、酸素吸収剤の大気雰囲気下での過度な発熱が抑えられ、安定した酸素吸収性能を維持することができる。
成分(B)の金属を溶出除去した合金(Y)の無機酸塩または有機酸塩の水溶液処理は、溶出除去後の金属を乾燥させた後に行ってもよく、また、乾燥することなく、溶出除去後に続けて行ってもよい。
無機酸塩または有機酸塩の水溶液の濃度は、表面処理を行う金属の量にもよるが、0.1M以上、飽和濃度以下であることが好ましい。飽和濃度とは、ある温度条件下で一定量の水に対して最大限溶け得る溶質の濃度を意味する。塩水溶液の濃度が低すぎると、合金表面に金属塩を形成できない場合がある。
金属塩被膜が形成されているかどうかを確認するには、例えば、X線回折分析や電子顕微鏡観察等により行うことができる。
上記のようにして得られる酸素吸収剤は、大気雰囲気下での過度な発熱が抑えられ、安定して酸素吸収性能を維持できる。酸素吸収剤の使用用途にもよるが、大気中に酸素吸収剤を取り出した際の表面温度は、250℃以下であることが好ましく、200℃以下がより好ましく、150℃以下がさらに好ましく、100℃以下であることが特に好ましい。例えば、酸素吸収剤を無酸素環境下から大気中へ取り出して、熱可塑性樹脂等と混練して使用する場合、酸素吸収剤の表面温度が低い方が、耐熱性の低い熱可塑性樹脂との混練が可能となる。
上記のようにして得られた合金(Y)は、多孔質形状(または多孔体)を有している。ここで、多孔質形状とは、電子顕微鏡にて確認できる程度の多数の細孔を表面および内部に有している状態をいう。本発明においては、合金(Y)が有する多孔質形状の程度は、その比表面積にて表すことができる。具体的には、本発明の酸素吸収剤に用いられる合金(Y)のBET法による比表面積は少なくとも10m2/gであり、好ましくは、少なくとも20m2/g、より好ましくは、少なくとも40m2/gである。
例えば、本発明において、成分(A)として鉄を用い、成分(B)としてアルミニウムを用いた場合、得られる多孔質形状の合金(Y)の比表面積(BET法によるもの)は、20〜40m2/g程度である一方で、多孔質ではない通常の鉄粉(還元鉄粉またはアトマイズ鉄粉)の場合、その比表面積は0.07〜0.13m2/g程度であり、多孔質形状であるか否かは明らかである。
また、合金(Y)が有する多孔質形状の程度は、かさ密度で表すこともできる。本発明の酸素吸収剤に用いられる合金(Y)のかさ密度は、2g/cm3以下であり、好ましくは、1.5g/cm3以下である。因みに、多孔質ではない通常の鉄粉(還元鉄粉またはアトマイズ鉄粉)の場合、そのかさ密度は、2〜3g/cm3程度である。
本発明において、酸素吸収剤として用いられる多孔質の合金(Y)は、高い酸素吸収活性を有しているため、低湿度条件(例えば、30%RH(相対湿度)(25℃)以下の条件)の雰囲気下であっても、酸素吸収剤として好適に使用することができる。無論、高湿度条件(例えば、100%RH(相対湿度)(25℃)の条件)の雰囲気下であっても、酸素吸収剤として好適に使用できることは言うまでもない。
したがって、上記のようにして得られた合金(Y)は、30%RH(相対湿度)(25℃)以下の低湿度の雰囲気において、少なくとも5mL/gの酸素、より好ましくは10mL/gの酸素、を吸収し得る。また、当該合金(Y)を酸素吸収剤として使用した場合の酸素吸収量は、例えば、30%RH(相対湿度)(25℃)以下の低湿度の雰囲気において、5〜150mL/gとなる。
<酸素吸収剤の使用>
上記したように、酸素吸収剤に使用される多孔質の金属は、大気中では酸化し劣化し易いものであることから、使用に際しては、この金属を熱可塑性樹脂に混合(混練)して得られる酸素吸収性樹脂の形態で使用することができる。この酸素吸収性樹脂は、混練した後に押出延伸させることでフィルム化又はシート化し、酸素吸収性のフィルム又はシートとすることもできる。
上記したように、酸素吸収剤に使用される多孔質の金属は、大気中では酸化し劣化し易いものであることから、使用に際しては、この金属を熱可塑性樹脂に混合(混練)して得られる酸素吸収性樹脂の形態で使用することができる。この酸素吸収性樹脂は、混練した後に押出延伸させることでフィルム化又はシート化し、酸素吸収性のフィルム又はシートとすることもできる。
使用される熱可塑性樹脂としては、その種類に特に制限はないが、例えば、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、エラストマー、またはこれらの混合物が使用できる。
また、酸素吸収剤を、通気性包装材を全部または一部に用いた包装材で包装した酸素吸収剤包装体としてもよい。包装材としては、2枚の通気性包装材を貼り合わせて袋状としたものや、1枚の通気性包装材と1枚の非通気性包装材とを貼り合わせて袋状としたもの、1枚の通気性包装材を折り曲げ、折り曲げ部を除く縁部同士をシールして袋状としたものが挙げられる。また、通気性包装材としては、酸素と二酸化炭素とを透過する包装材を使用できる。このような通気性包装材としては、紙や不織布の他、従来公知のプラスチックフィルムに通気性を付与したものが挙げられる。
本発明による酸素吸収剤は、水分活性に無関係に酸素吸収を行い、水分活性の高い領域から低い領域まで適用可能である。また、水分活性が低く、低湿度の乾燥条件での保存が必要とされる物品に好適に適用できる。なお、水分活性とは物品中の自由水含有量を示す尺度で、0〜1の数字で示され、水分のない物品は0、純水は1となる。すなわち、ある物品の水分活性Awは、その物品を密封し平衡状態に到達した後の空間内の水蒸気圧をP、純水の水蒸気圧をP0、同空間内の相対湿度をRH(%)、とした場合、
Aw=P/P0=RH/100
と定義される。
Aw=P/P0=RH/100
と定義される。
低湿度の保存条件を必要とする低水分含有物品を保存するためには、低水分含有物品を保存する雰囲気の相対湿度(RH)は、好ましくは20〜70%、より好ましくは20〜50%である。低水分含有物品の水分含有率は、好ましくは50質量%以下、より好ましくは30質量%以下、特に好ましくは10質量%以下のものが全て該当する。低湿度の保存条件を必要とする低水分含有物品(被包装物)として、例えば、粉末、顆粒食品類(粉末スープ、粉末飲料、粉末菓子、調味料、穀物粉、栄養食品、健康食品、着色料、着香料、香辛料)、粉末、顆粒薬品(散薬類、粉石鹸、歯磨粉、工業薬品)、これらの成形体(錠剤型)などの、水分の増加を嫌い、異物の混入を避ける必要のある食品、薬品等を例示することができる。特に、後記するような酸素吸収性包装体に、これら被包装物を充填した場合、水分が無いか殆ど無い雰囲気中であっても、雰囲気中の酸素を、従来の脱酸素剤と同等のレベルで、吸収・除去し得ることが可能である。したがって、従来の脱酸素剤の適用の難しかった水分を嫌う乾燥食品、医薬品、電子材料のパッケージの雰囲気中を脱酸素状態にするなどの用途に好適に使用することができる。例えば、粉末調味料、粉末コーヒー、コーヒー豆、米、茶、豆、おかき、せんべい等の乾燥食品や医薬品、ビタミン剤等の健康食品に好適に使用することができる。
以下、本発明を実施例によりさらに具体的に説明するが、本発明は以下の実施例により特に限定されるものではない。
実施例1
Al(アルミニウム)粉とNi(ニッケル)粉をそれぞれ50重量%の割合で混合し、窒素中で溶解して、Al−Ni合金を得た。得たAl−Ni合金はジョークラッシャー、ロールクラッシャー及びボールミルを用いて粉砕し、粉砕物を目開き200メッシュ(0.075mm)の網を用いて分級し、200メッシュ以下のAl−Ni合金を得た。得られたAl−Ni合金粉100gを90℃の25重量%水酸化ナトリウム水溶液中で1時間攪拌混合した後、混合溶液を静置し、上層液を取り除いた。残った沈殿物をpHが10以下になるまで蒸留水で洗浄し、Al−Ni多孔質合金粉を得た。したがって、多孔質合金粉は、酸素に接触させることを回避すべく、水溶液中での反応により得た。
Al(アルミニウム)粉とNi(ニッケル)粉をそれぞれ50重量%の割合で混合し、窒素中で溶解して、Al−Ni合金を得た。得たAl−Ni合金はジョークラッシャー、ロールクラッシャー及びボールミルを用いて粉砕し、粉砕物を目開き200メッシュ(0.075mm)の網を用いて分級し、200メッシュ以下のAl−Ni合金を得た。得られたAl−Ni合金粉100gを90℃の25重量%水酸化ナトリウム水溶液中で1時間攪拌混合した後、混合溶液を静置し、上層液を取り除いた。残った沈殿物をpHが10以下になるまで蒸留水で洗浄し、Al−Ni多孔質合金粉を得た。したがって、多孔質合金粉は、酸素に接触させることを回避すべく、水溶液中での反応により得た。
得られたAl−Ni多孔質合金粉を、200Pa以下、60℃で2時間真空乾燥してAl−Ni多孔質合金粉乾燥物を得た。得られた合金粉のかさ密度は1.4g/cm3であった(JIS Z2504に準拠して測定)。また、多孔質合金粉0.3gを、通気性小袋内に包装し、乾燥剤と共にガスバリア袋(Al箔ラミネートプラスチック袋)に入れ、500mLの空気(酸素濃度20.9%)を充填して密封し、25℃で1日保存した後の酸素濃度は15.0%であり、ガスバリア袋内の減少した酸素濃度から酸素吸収量を算出した結果、酸素吸収量は115.7mL/gであった。
また、得られたAl−Ni多孔質合金粉の平均粒径を、粒度・形状分布測定器(株式会社セイシン企業製「PITA−2」)を使用して測定したところ、平均粒径は30μmであった。さらに、得られたAl−Ni多孔質合金粉の比表面積を、自動比表面積測定装置(株式会社島津製作所製「ジェミニVII2390」を使用して測定したところ、比表面積は90m2/gであった。
次いで、0.5Mの濃度のリン酸水素2ナトリウム水溶液61mLと、0.5Mの濃度のリン酸2水素ナトリウム水溶液39mLとを混合することにより、0.5Mの濃度の酸塩水溶液を調製した。調製した酸塩水溶液に、真空乾燥(80℃で2時間)したAl−Ni多孔質合金粉2.8gを浸漬し、5時間後に酸素吸収剤をスパチュラで緩衝溶液中から取り出し、200Pa、60℃で2時間真空乾燥を行った。その後、リン酸緩衝液に浸漬して得られたAl−Ni多孔質合金粉を上記と同様にして酸素吸収量を算出した。
また、リン酸緩衝液に浸漬して得られたAl−Ni多孔質合金粉1gを、窒素雰囲気中でグラスフィルターに包んで、ガスバリア袋(Al箔ラミネートプラスチック袋)に入れた後、大気中に取り出した。合金粉が入ったグラスフィルターの上に熱電対を置き、合金粉の温度変化を温度データロガーにて測定した。結果は下記の表1に示される通りであった。
実施例2
Al(アルミニウム)粉とFe(鉄)粉をそれぞれ50質量%の割合で混合し、窒素中で溶解して、Al−Fe合金を得た。得たAl−Fe合金はジョークラッシャー、ロールクラッシャー及びボールミルを用いて粉砕し、粉砕物を目開き200メッシュ(0.075mm)の網を用いて分級し、200メッシュ以下のAl−Fe合金を得た。得られたAl−Fe合金粉100gを、50℃の25質量%水酸化ナトリウム水溶液中で1時間攪拌混合した後、混合溶液を静置し、上層液を取り除いた。残った沈殿物をpHが10以下になるまで蒸留水で洗浄し、Al−Fe多孔質合金粉を得た。したがって、多孔質合金粉は、酸素に接触させることを回避すべく、水溶液中での反応により得た。
Al(アルミニウム)粉とFe(鉄)粉をそれぞれ50質量%の割合で混合し、窒素中で溶解して、Al−Fe合金を得た。得たAl−Fe合金はジョークラッシャー、ロールクラッシャー及びボールミルを用いて粉砕し、粉砕物を目開き200メッシュ(0.075mm)の網を用いて分級し、200メッシュ以下のAl−Fe合金を得た。得られたAl−Fe合金粉100gを、50℃の25質量%水酸化ナトリウム水溶液中で1時間攪拌混合した後、混合溶液を静置し、上層液を取り除いた。残った沈殿物をpHが10以下になるまで蒸留水で洗浄し、Al−Fe多孔質合金粉を得た。したがって、多孔質合金粉は、酸素に接触させることを回避すべく、水溶液中での反応により得た。
得られたAl−Fe多孔質合金粉を、200Pa以下、50℃で水分量1質量%以下まで真空乾燥してAl−Fe多孔質合金粉乾燥物を得た。得られたAl−Fe多孔質合金粉のかさ密度は1.4g/cm3であった(JIS Z2504に準拠して測定)。また、Al−Fe多孔質合金粉の酸素吸収量、平均粒径、および比表面積を実施例1と同様にして測定したところ、それぞれ、61.9mL/g、約30μm、24.0m2/gであった。
また、実施例1で用いた酸塩水溶液に代えて、2Mの炭酸ナトリウム水溶液20mLを用い、浸漬時間を0.5時間に変更した以外は実施例1と同様にして酸塩水溶液処理を行い、酸素吸収量および温度変化を測定した。結果は下記の表1に示される通りであった。
比較例1
実施例1において、酸塩水溶液処理を行わなかった以外は実施例1と同様にして酸素吸収量および温度変化を測定した。結果は下記の表1に示される通りであった。
実施例1において、酸塩水溶液処理を行わなかった以外は実施例1と同様にして酸素吸収量および温度変化を測定した。結果は下記の表1に示される通りであった。
比較例2
実施例2において、酸塩水溶液処理を行わなかった以外は実施例2と同様にして酸素吸収量および温度変化を測定した。結果は下記の表1に示される通りであった。
実施例2において、酸塩水溶液処理を行わなかった以外は実施例2と同様にして酸素吸収量および温度変化を測定した。結果は下記の表1に示される通りであった。
Claims (12)
- 酸素吸収剤を製造する方法であって、
(A)鉄、コバルト、ニッケル、および銅からなる群より選択される少なくとも1種の遷移金属と、(B)アルミニウムと、を含む合金(X)を、アルカリの水溶液処理に供して、前記成分(B)の少なくとも一部を溶出除去し、
前記成分(B)の少なくとも一部が除去された合金(Y)を、前記成分(A)の遷移金属と塩を形成し得る無機酸塩または有機酸塩の水溶液で処理して、前記合金(Y)の表面の少なくとも一部に金属塩を形成させる、
ことを含んでなる、酸素吸収剤の製造方法。 - 前記合金(Y)に含まれる成分(B)の含有率が0.01〜50質量%となるまで、前記成分(B)の溶出除去を行う、請求項1に記載の方法。
- 前記アルカリの水溶液が水酸化ナトリウム水溶液である、請求項1または2に記載の方法。
- 前記成分(A)と前記成分(B)とを含む合金(X)の粉末を、アルカリの水溶液処理に供して、前記成分(B)の少なくとも一部を溶出除去して、粉末状の合金(Y)を得ることを含む、請求項1〜3のいずれか一項に記載の方法。
- 前記無機酸塩または有機酸塩が、無機酸および有機酸から選択される少なくとも1種類の弱酸と強塩基との塩である、請求項1〜4のいずれか一項に記載の方法。
- 前記無機酸塩または有機酸塩が、リン酸塩、炭酸塩、およびシュウ酸塩からなる群より選択される少なくとも1種の塩である、請求項1〜5のいずれか一項に記載の方法。
- 請求項1〜6のいずれか一項に記載の方法により得られた酸素吸収剤。
- 前記成分(B)の少なくとも一部を溶出除去して得られる合金(Y)が、多孔質形状である、請求項7に記載の酸素吸収剤。
- 前記成分(B)の少なくとも一部を溶出除去して得られる合金(Y)の、BET法により測定される比表面積が、少なくとも10m2/gである、請求項7または8に記載の酸素吸収剤。
- 請求項7〜9のいずれか一項に記載の酸素吸収剤を、通気性包装材を全部または一部に用いた包装材で包装してなる、酸素吸収性包装体。
- 請求項7〜9のいずれか一項に記載の酸素吸収剤と熱可塑性樹脂とを含んでなる、酸素吸収性樹脂組成物。
- 請求項11に記載の酸素吸収性樹脂組成物からなる酸素吸収性樹脂シートまたはフィルム。