JP5215276B2 - ポリアミド逆浸透複合膜及びその製造方法 - Google Patents
ポリアミド逆浸透複合膜及びその製造方法 Download PDFInfo
- Publication number
- JP5215276B2 JP5215276B2 JP2009240856A JP2009240856A JP5215276B2 JP 5215276 B2 JP5215276 B2 JP 5215276B2 JP 2009240856 A JP2009240856 A JP 2009240856A JP 2009240856 A JP2009240856 A JP 2009240856A JP 5215276 B2 JP5215276 B2 JP 5215276B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene glycol
- reverse osmosis
- composite membrane
- osmosis composite
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の他の目的は、新規のポリアミド逆浸透複合膜を提供することにある。
本発明のさらに他の目的は、ポリアミド逆浸透複合膜を製造する新規の方法を提供することにある。
本発明はさらに、前記のタイプのポリアミド逆浸透複合膜の製造方法に関する。
本発明の他の目的、特性、特徴及び効果は、後述する発明の詳細な説明で明らかにされる。本発明の各実施例は、本発明の技術分野に属する者によって充分に実行できる程度に開示されており、本発明の範囲内の構造または変化を有する他の実施例も、充分に理解できる程度に開示されている。後述する発明の詳細な説明は、本発明の保護範囲を制限するものではなく、本発明の範囲は、特許請求の範囲によって規定される。
本発明によるポリアミド逆浸透複合膜は、多孔性支持体と、この多孔性支持体上に前記水溶液及び有機溶液を順次コーティングした界面重合によって得られる前記ポリアミド薄膜と、を含み、高い塩排除率及び高い透過流量性能を示している。
下記の実施例は、本発明を一層具体的に説明するものであり、本発明の保護範囲を制限するものではない。
不織布上にキャスティングされた140μm厚さの多孔性ポリスルホン支持体を2重量%のメタフェニレンジアミン(MPD)及び0.1重量%のジ(エチレングリコール)ヘキシルメチルエーテル(実施例1−a〜1−bで言及された方法によって製造)を含有する水溶液に30秒間浸し、支持体から余剰の前記水溶液を除去した後、前記支持体を、溶媒としてイソパー溶媒(Isopar solvent、Exxon Corp.)を用いた0.1重量%のトリメソイルクロライド有機溶液に1分間浸漬する。その後、余剰の有機溶液を除去し、1分間風乾した後、40〜60℃で0.2%の炭酸ナトリウム水溶液で30分間浸漬した。その後、再び純水で充分に水洗して目的とするポリアミド逆浸透複合膜を製造した。
150mlの水に水酸化ナトリウム60gを溶解した水溶液を撹拌しながらジ(エチレングリコール)ヘキシルエーテル120gを投入した後、硫酸ジメチル80gを水溶液に約2時間の間徐々に添加した。硫酸ジメチルを全て添加した後、窒素パージ条件で連続的に撹拌しながら50〜55℃で加熱して24時間反応し、放冷して常温に調節した後、前記有機層を分液漏斗を用いて分離した。この分離された有機溶液を150mmHgの減圧条件で148〜158℃で分別蒸溜し、ジ(エチレングリコール)ヘキシルメチルエーテルを約90g得た。
53mlの水に水酸化ナトリウム33gを窒素雰囲気下で溶解した水溶液にジ(エチレングリコール)メチルエーテル50gを撹拌しながら添加した後、窒素雰囲気下で60℃で1時間の間継続して撹拌し、1−ブロモヘキサン140gを3時間にかけて前記混合溶液に添加した後、温度を70〜80℃に上昇して24時間の間反応した。次いで、反応混合物を放冷して反応混合物を常温に調節し、有機層を分液漏斗で分離した後、まず、150mmHgの減圧条件で反応されてないジ(エチレングリコール)メチルエーテル及び1−ブロモヘキサンを分別蒸溜して148〜158℃で目的とするジ(エチレングリコール)ヘキシルメチルエーテル60gを得た。
実施例2〜12及び比較例A〜Lは、上述した実施例1の0.1重量%のジ(エチレングリコール)ヘキシルメチルエーテルの代りに、下記の表1及び表2に開示された極性化合物を用いたことを除けば、実施例1と同様に行った。実施例1〜12及び比較例A〜Lの多様な極性化合物によるポリアミド逆浸透複合膜の透過流量及び塩排除率は、下記の表1及び表2にそれぞれ記載した。
ジ(エチレングリコール)ヘキシルメチルエーテルを、MPDを含有する水溶液に添加する代りに、0.5重量%のジ(エチレングリコール)ジビニルエーテルをイソパー溶媒(Isopar(登録商標)solvent)中の0.1重量%のトリメソイルクロライド有機溶液に添加することを除けば、実施例1と同一方法で目的とするポリアミド逆浸透複合膜を製造した。前記表1から分かるように、透過流量は32.3gfdで、塩排除率は98.4%であった。
ジ(エチレングリコール)ヘキシルメチルエーテルを、MPDを含有する水溶液に添加する代りに、0.5重量%のトリ(エチレングリコール)ジビニルエーテルをイソパー溶媒(Isopar(登録商標)solvent)中の0.1重量%のトリメソイルクロライド有機溶液に添加することを除けば、実施例1と同一方法で目的とするポリアミド逆浸透複合膜を製造した。前記表1から分かるように、透過流量は33.1gfdで、塩排除率は98.2%であった。
本発明の詳細な説明で記載された製造方法及びケミカルは、単純な例示に過ぎなく、本発明が属する技術分野の技術者であれば、本発明の技術的思想内で多様な変形及び改善が可能である。また、このような変形及び改善は、特許請求の範囲によって本発明の保護範囲に属する。
Claims (13)
- (a)多孔性支持体;及び
(b)前記多孔性支持体上に形成されたポリアミド層;
を含むことを特徴とする逆浸透複合膜であって、
前記ポリアミド層が、
(i)多官能性アミンを含む水溶液;及び
(ii)多官能性アシルハライドを含む炭素数8〜12のイソパラフィン系有機溶液;
の界面縮重合による反応生成物を含み、
(iii)前記水溶液の少なくとも1つは、テトラ(エチレングリコール)ジメチルエーテル、ポリ(エチレングリコール)ジメチルエーテル、ジ(エチレングリコール)ジビニルエーテル、トリ(エチレングリコール)ジビニルエーテル、テトラ(エチレングリコール)ジビニルエーテル、ポリ(エチレングリコール)ジビニルエーテル、及びその混合物からなる群から選択される極性化合物をさらに含み、
2,000ppm塩化ナトリウム水溶液を25℃、225psiの圧力条件で交差流れ方式で透過させ測定した塩排除率が98.7%以上である、ポリアミド膜からなる、前記逆浸透複合膜。 - 前記極性化合物が、前記水溶液に存在し、前記水溶液の0.001〜5重量%である、請求項1に記載の逆浸透複合膜。
- 前記極性化合物が、前記水溶液の0.01〜3重量%である、請求項2に記載の逆浸透複合膜。
- 前記多官能性アミンが、芳香族1級ジアミン及びその置換された誘導体、アルカン1級ジアミン、脂環族1級ジアミン、脂環族2級ジアミン、芳香族2級ジアミン及びキシレンジアミンからなる群から選択される少なくとも1つである、請求項1に記載の逆浸透複合膜。
- 前記多官能性アミンが、メタフェニレンジアミンである、請求項4に記載の逆浸透複合膜。
- 前記多官能性アミンが、メタフェニレンジアミン脂環族2級ジアミンのピペラジンである、請求項4に記載の逆浸透複合膜。
- 前記多官能性アシルハライドが、イソフタロイルハライド、テレフタロイルハライド、トリメソイルハライド及びその混合物からなる群から選択される少なくとも1つである、請求項1に記載の逆浸透複合膜。
- 前記多官能性アシルハライドが、トリメソイルハライドである、請求項7に記載の逆浸透複合膜。
- 前記多孔性支持体が、ポリスルホン、ポリエーテルスルホン、ポリイミド、ポリアミド、ポリエチレン、ポリプロピレン、ポリアクリロニトリル、ポリビニリデンフロライド及びポリテトラフロライドからなる群から選択される物質によって形成されることを特徴とする請求項1〜8に記載の逆浸透複合膜。
- (a)多官能性アミンを含む水溶液で多孔性支持体をコーティングし、前記多孔性支持体上に液体層を形成する段階;
(b)前記液体層を、多官能性アシルハライドを含む炭素数8〜12のイソパラフィン系有機溶液に接触させ、前記多官能性アシルハライドが前記多官能性アミンと界面縮重合し、 前記多孔性支持体上に架橋されたポリアミド層を形成する段階;及び
(c)前記段階(b)の反応生成物を乾燥し、逆浸透複合膜を形成する段階;
(d)形成した逆浸透複合膜の2,000ppm塩化ナトリウム水溶液を25℃、225psiの圧力条件で交差流れ方式で透過させ測定した塩排除率が98.7%以上であることを確認する段階を含み、
前記水溶液の少なくとも1つは、
テトラ(エチレングリコール)ジメチルエーテル、ポリ(エチレングリコール)ジメチルエーテル、ジ(エチレングリコール)ジビニルエーテル、トリ(エチレングリコール)ジビニルエーテル、テトラ(エチレングリコール)ジビニルエーテル、ポリ(エチレングリコール)ジビニルエーテル、及びその混合物からなる群から選択される極性化合物をさらに含む、逆浸透複合膜の製造方法。 - 前記段階(c)の反応生成物を塩基性水溶液で洗浄する段階をさらに含む、請求項10に記載の逆浸透複合膜の製造方法。
- (a)多孔性支持体を、水及び少なくとも1つの極性化合物を含む混合溶媒でコーティングして前記多孔性支持体上に液体層を形成する段階であって、前記少なくとも1つの極性化合物が、
テトラ(エチレングリコール)ジメチルエーテル、ポリ(エチレングリコール)ジメチルエーテル、ジ(エチレングリコール)ジビニルエーテル、トリ(エチレングリコール)ジビニルエーテル、テトラ(エチレングリコール)ジビニルエーテル、ポリ(エチレングリコール)ジビニルエーテル、及びその混合物からなる群から選択される、前記段階;
(b)前記液体層を多官能性アミンを含む水溶液でコーティングして前記多孔性支持体上に二重コーティング液体層を形成する段階;
(c)前記二重コーティング液体層を、多官能性アシルハライドを含む炭素数8〜12のイソパラフィン系有機溶液に接触させ、前記多官能性アシルハライドを前記多官能性アミンと界面縮重合し、前記多孔性支持体上に架橋されたポリアミド層を形成する段階;及び
(d)前記段階(c)の反応生成物を乾燥し、逆浸透複合膜を形成する段階;
(e)形成した逆浸透複合膜の2,000ppm塩化ナトリウム水溶液を25℃、225psiの圧力条件で交差流れ方式で透過させ測定した塩排除率が98.7%以上であることを確認する段階を含む、逆浸透複合膜の製造方法。 - 前記段階(d)の反応生成物を塩基性水溶液で洗浄する段階をさらに含む、請求項12に記載の逆浸透複合膜の製造方法。