JP5138482B2 - ロジンエマルションサイズ剤用分散剤 - Google Patents
ロジンエマルションサイズ剤用分散剤 Download PDFInfo
- Publication number
- JP5138482B2 JP5138482B2 JP2008175365A JP2008175365A JP5138482B2 JP 5138482 B2 JP5138482 B2 JP 5138482B2 JP 2008175365 A JP2008175365 A JP 2008175365A JP 2008175365 A JP2008175365 A JP 2008175365A JP 5138482 B2 JP5138482 B2 JP 5138482B2
- Authority
- JP
- Japan
- Prior art keywords
- parts
- rosin
- sizing agent
- dispersant
- emulsion sizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
a)成分はa)成分〜c)成分のモノマー類の合計、すなわち100重量部のうち6〜40重量部の量で使用できる。さらに好ましくは6〜30重量部である。6重量部未満の場合、ロジン系物質と分散剤との親和性が低下し、40重量部以上の場合はロジン系物質との親和性が良好になるものの水性分散媒への親和性が低下し、良好な乳化性の分散剤が得られなくなる。
本発明で使用できるロジン系物質には、ロジン類、強化ロジン類、ロジンエステル類及び強化ロジンエステル類等があり、これらの1種又は2種以上併用できる。ロジン系物質の配合割合及び配合成分については、ロジンエマルションサイズ剤が使用される抄紙工程の条件により適宜変更することができる。例えば、抄紙工程のpHが4.5〜5.0程度である場合は、強化ロジン類の配合量を50重量%〜100重量%、ロジンエステル類及び/又は強化ロジンエステル類を0〜50重量%配合して使用することが好ましく、抄紙工程のpHが5.5〜7.0程度である場合は、強化ロジン類を10〜60重量%、ロジンエステル類及び/又は強化ロジンエステル類を10〜60重合%配合し使用することが好ましい。
カラム:(株)東ソーGPWXL
測定温度:40℃
検出器:示差屈折計
また、粘度の測定にはB型粘度計(株式会社東京計器製 形式:BM)を使用した。
(製造例1)
温度計、冷却器、攪拌機、窒素導入管を備えた五つ口フラスコに、疎水性ビニル系モノマーとしてスチレンを120部、n−ブチルメタアクリレートを28.6部、アニオン性水溶性ビニル系モノマーとしてメタアクリル酸を114.3部、非イオン性水溶性ビニル系モノマーとして40%アクリルアミド水溶液を50部、テルピノレンを5.7部、ノルマルドデシルメルカプタンを2.9部、多価メルカプト化合物としてペンタエリスリトールテトラキスチオグリコレートを2.9部仕込んだ。その後、水を390.0部、イソプロピルアルコールを280.0部加え80℃まで加熱を行った。重合開始剤として過硫酸アンモニウムを5.7部添加し、4時間重合を行った。その後、イソプロピルアルコールの留去を行い、水を添加し、濃度30%、重量平均分子量(Mw)87000、粘度800mPa・sの分散剤1を得た。
製造例1と同様の装置に、スチレンを76.0部、ノルマルブチルメタクリルアクリレートを76.0部、2−エチルヘキシルアクリレートを23.4部、アクリル酸を87.8部、40%アクリルアミド水溶液を58.5部、α−メチルスチレンダイマーを5.8部、多価メルカプト化合物としてエチレングリコールビスチオグリコレートを1.5部仕込んだ。その後水を385部、イソプロピルアルコールを280部、重合開始剤としてアゾイソブチロニトリルを5.8部加え溶解し、80℃まで加熱し、同温度で4時間保持した。その後、実施例1と同様にイソプロピルアルコールの留去を行い、水を添加し、濃度30%、Mw85000、粘度920mPa・sの分散剤2を得た。
製造例1と同様の反応装置に、スチレンを58.3部、シクロヘキシルメタクリレートを58.3部、ノルマルブチルメタクリレートを58.3部、メタクリル酸を99.1部、40%アクリルアミド水溶液を15部、テルピノレンを5.8部、α−メチルスチレンダイマーを5.8部、多価メルカプト化合物としてペンタエリスリトールテトラキスチオグリコレートを2.9部仕込んだ。水を411部、イソプロピルアルコールを280部仕込み80℃で溶解を行った。重合開始剤として過硫酸アンモニウムを5.8部添加し、4時間重合を行った。その後、イソプロピルアルコールの留去を行い、水を添加し、濃度30%、Mw96000、粘度750mPa・sの分散剤3を得た。
製造例1と同様の反応装置に、スチレンを41.3部、シクロヘキシルメタクリレートを41.3部、n−ブチルアクリレートを41.3部、メタクリル酸を82.6部、40%アクリルアミド水溶液を172.3部、テルピノレンを13.8部、n−ドデシルメルカプタンを2.7部、多価メルカプト化合物としてブタンジオールビスチオグリコレートを2.5部仕込んだ。その後、水を316.7部、イソプロピルアルコールを280部、アゾビスイソブチロニトリルを5.8部加え40℃で溶解を行った。溶解確認後、80℃まで加熱し4時間温度を維持した後、イソプロピルアルコールを留去し、水を加え濃度30%、Mw88000、粘度1050mPa・sの分散剤4を得た。
製造例1と同様の反応装置に、シクロヘキシルメタクリレートを100.5部、2−エチルヘキシルアクリレートを28.7部、メタクリル酸を71.7部、40%アクリルアミド水溶液を215.3部、テルピノレンを1部、メルカプトプロピオン酸−2−エチルヘキシルを0.5部、多価メルカプト化合物としてペンタエリスリトールテトラキスチオグリコレートを1.5部仕込んだ。さらに、水を290.9部、イソプロピルアルコールを280部仕込み、重合開始剤としてアゾビスイソブチロニトリルを5.8部加え、実施例4と同様の操作で濃度30%、Mw101000、粘度960mPa・sの分散剤5を得た。
製造例1と同様の反応装置に、シクロヘキシルメタクリレートを57.2部、n−ブチルアクリレートを57.2部、メタクリル酸を85.8部、40%アクリルアミド水溶液を214.5部、ターピノーレンを2.9部、α−メチルスチレンダイマーを2.9部、多価メルカプト化合物としてトリメチロールプロパントリスチオグリコレートを2.6部仕込んだ。さらに、水を291.3部、イソプロパノールを280部仕込み、80℃まで加熱を行った。その後、重合開始剤として過硫酸アンモニウムを5.7部添加し4時間反応を行った。その後イソプロパノールを留去し、さらに水で濃度調製することで濃度30%、Mw89000、粘度860mPa・sの分散剤6を得た。
製造例1と同様の反応装置に、シクロヘキシルメタクリレートを56.7部、n−ブチルメタクリレートを28.4部、2−エチルヘキシルアクリレートを28.4部、40%アクリルアミド水溶液を248部、イタコン酸を56.7部、p−スチレンスルホン酸ナトリウムを8.5部、ビニルスルホン酸ナトリウムを5.7部、ターピノーレンを2.8部、α−メチルスチレンダイマーを2.8部、2−メルカプトエタノールを2.8部、多価メルカプト化合物としてペンタエリスリトールテトラキスチオグリコレートを1.2部、水を271.2部、イソプロピルアルコールを280部加えた。80℃まで加熱を行い重合開始剤として過硫酸アンモニウムを5.7部添加し、同温度で4時間反応を行った。その後、イソプロピルアルコールを留去し、水で濃度調整を行うことで、固形分30%、Mw120000、粘度800mPa・Sの分散剤7を得た。
製造例1と同様の反応装置に、シクロヘキシルメタクリレートを34.2部、2−エチルヘキシルアクリレートを22.8部、40%アクリルアミド水溶液を320.3部、イタコン酸を71.2部、メタアリルスルホン酸ナトリウムを14.2部、ビニルスルホン酸ナトリウムを14.2部、テルピノレンを0.6部、2−メルカプトエタノールを5.7部、多価メルカプト化合物としてペンタエリスリトールテトラキスチオプロピオネートを1.0部、水を227.9部、イソプロピルアルコールを280部加え、重合開始剤としてアゾイソブチロニトリルを5.7部添加し40℃で溶解した。その後80℃に加熱し重合を4時間行った後、イソプロピルアルコールを留去し、水で濃度調整を行うことで、固形分30%、Mw140000、粘度700mPa・sの分散剤8を得た。
多価メルカプト化合物を使用しない以外は製造例1〜7と同様の操作でそれぞれ比較分散剤1〜7を得た。
ペンタエリスリトールテトラキスチオプロピオネートを使用せず、テルピノレンを1.6部とした以外は製造例8と同様の操作で比較分散剤8を得た。
(製造例17:ロジンフマル酸強化物)
ガムロジン920部を1L四つ口フラスコに仕込み、200℃で加熱溶融させ、その後フマル酸を80部添加し、同温度で3時間保持し、SV(ケン化価)233の反応生成物R1を得た。
ガムロジン920部を1L四つ口フラスコに仕込み200℃で加熱溶融させる。その後無水マレイン酸を80部添加し、同温度で3時間保持し、SV246の反応生成物R2を得た。
ガムロジン600部とグリセリン55部とを1L四つ口フラスコに仕込み、窒素気流下で200℃まで加熱し脱水反応を行った。その後さらに270℃で14時間脱水反応を行いAV30の反応生成物R3を得た。
実施例19で得た反応生成物950部を1L四つ口フラスコに仕込み200℃で加熱溶融させる。その後無水マレイン酸50部を添加し、同温度で3時間保持し、SV85の反応生成物R4を得た。
1Lオートクレーブに製造例17で得たフマル化ロジン100部を仕込み、150℃に加熱溶融し、これに製造例1で得た分散剤30部に48%苛性ソーダを3.3部加えたものを添加混合し、さらに熱水を85部加えながら転相させ、固形分50%のロジンエマルションサイズ剤を得た。
実施例1と同様にして上記分散剤2〜8、比較分散剤1〜8の分散剤を用い、製造例17〜20で得たロジン系物質をそれぞれ表2に示した組成比で用いて、それぞれ固形分50%のロジンエマルションサイズ剤を得た。
島津製作所製レーザー回折/散乱式粒度分布測定装置SALD−2100で測定した。測定した粒子径はメディアン径である。
実施例あるいは比較例のサイズ剤50gをカップに入れ、25℃、荷重20kg、回転数1000rpmにて10分間マーロン式安定性試験を行った。生成した凝集物を200メッシュでろ過し全固形分に対する凝集量を百分率で示した。
サイズ剤の風乾物1gと水道水50gを試験管に取り、軽く攪拌してその分乾物の再分散性を観察した。容易に分散するものを3、十回前後攪拌することにより分散するものを2、そして全く分散しないものを1とし3段階評価で行った。
長さ100cm、内径3cmの試験管に実施例あるいは比較例のサイズ剤を500cc入れ、冷暗所に室温で2ヶ月静置した。底部に沈降した沈殿物の高さ(mm)を測定した。
カナディアン・スタンダード・フリーネス400ccに叩解したパルプ(LBKP/NBKP=8/2)を2.0%のパルプスラリーとし、これに対パルプ固形分15%の炭酸カルシウム(奥多摩工業社製TP−121)、1%の硫酸バンド、0.5%のカチオン化澱粉(日本NSC社Cato3210)及び2%の実施例および比較例で得たそれぞれのサイズ剤を添加し、100ドイツ硬度に調整した塩化カルシウム水溶液でパルプ濃度0.2%まで希釈し、箱型容器に入れた。パルプスラリーをポンプで循環してこれを30cmの高さから容器中に落下させ、10分後の液面に蓄積する泡の面積を液面全体面積に対する百分率で示した。
灰分を15%含有した炭酸カルシウムを10%含有するカナディアン・スタンダード・フリーネス400ccまで叩解したダンボール古紙パルプを絶乾固形分2%のパルプスラリーとし、全紙用薬品添加後のパルプスラリーがpH6.5となるような量の水酸化ナトリウムを添加した。このパルプスラリーに絶乾パルプに対して1.5%の硫酸バンド、0.5%の日本NSC社製カチオン化澱粉Cato3210、0.4%または0.5%の上記実施例および比較例で得たそれぞれのサイズ剤を添加し、パルプ濃度0.2%まで希釈するとともに、パルプスラリーの水硬度を塩化カルシウムで100ドイツ硬度に調製した。JIS丸型抄紙機でJIS P8222に準拠して坪量80g/m2となるように抄紙した。湿紙の乾燥はドラムドライヤーを用いて90℃で2分間乾燥させた。得られたサイジング紙をJIS P8111に準拠して調湿し、JIS P8122に準拠して試験紙のステキヒトサイズ度を測定した。
Claims (4)
- a)少なくとも1種の疎水性ビニル系モノマー類;
b)少なくとも1種のアニオン性水溶性ビニル系モノマー類;及び
c)少なくとも1種のノニオン性水溶性ビニル系モノマー類
からなるビニル系モノマーと、
d)少なくとも1種の多価メルカプト化合物と
を必須成分として重合させてなるロジン系エマルションサイズ剤用分散剤。 - a)成分6〜40重量部、b)成分6〜40重量部、及びc)成分6〜70重量部からなるモノマーの総計100重量部に対してd)成分を0.01〜3重量部の量で使用することを特徴とする、請求項1に記載のロジン系エマルションサイズ剤用分散剤。
- 請求項1の重合物をさらに無機及び/又は有機アルカリにより完全及び/又は部分中和させてなることを特徴とする、請求項1又は2に記載のロジン系エマルションサイズ剤用分散剤。
- ロジン類及び強化ロジン類の少なくとも1種及び/又はロジンエステル類及び強化ロジンエステル類の少なくとも1種を含むロジン系物質を、請求項1〜3のいずれか記載の分散剤で分散させてなるロジンエマルションサイズ剤。