JP4604090B2 - 透明性固形粉末化粧料 - Google Patents
透明性固形粉末化粧料 Download PDFInfo
- Publication number
- JP4604090B2 JP4604090B2 JP2007534462A JP2007534462A JP4604090B2 JP 4604090 B2 JP4604090 B2 JP 4604090B2 JP 2007534462 A JP2007534462 A JP 2007534462A JP 2007534462 A JP2007534462 A JP 2007534462A JP 4604090 B2 JP4604090 B2 JP 4604090B2
- Authority
- JP
- Japan
- Prior art keywords
- powder
- elastic
- mass
- silicone
- cosmetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、更に(A)弾性粉末混合物30〜55質量%、(B)平均粒子径が0.1〜50μmの範囲にある非弾性球状シリコーン樹脂粉末25〜40質量%および(C)油剤20〜45質量%を必須成分とし、(A)弾性粉末混合物は、(A1)弾性粉末と、(A2)弾性粉末の周囲を非弾性物質で被覆した複合粉体、それぞれ1種以上を含むことを特徴とし、これら必須成分と、必要に応じて任意成分の混合組成物を固化して得られる固形粉末化粧料に関する。
(A1)弾性粉末とは、電子顕微鏡を用いた観察による平均粒子径が0.01〜1000μm、好ましくは0.1〜50μmの一次粒子の凝集体であるゴム弾性を有する粉末であって、JIS−K−6301に従って測定されるJIS−A硬度が15〜80の範囲の数字を示すものである。このような弾性粉末の具体的な例としては、シリコーンエラストマー、フルオロシリコーンエラストマー、変性シリコーンエラストマー、アクリル系エラストマー、ポリウレタン系エラストマー等の合成エラストマー、天然エラストマー等の粉末が挙げられるが、中でもシリコーンエラストマー粉末が最も好ましい。該シリコーンエラストマー粉末は、ジメチルポリシロキサン等のシリコーン油を含有していても構わない。市販品としては、東レ・ダウ・コーニング社製のトレフィルEシリーズ、例えば、トレフィルE−506C(粉末分100%)、トレフィルE−507(粉末分70%)、トレフィルE−508(粉末分70%)等が挙げられる。
本発明で用いる(B)非弾性球状シリコーン樹脂粉末としては、メチルシロキサン網状重合体またはポリオルガノシルセスキオサン(ポリメチルシルセスキオサン)硬化物等のシリコーン樹脂粉末を用いることができる。その具体例としてはGE東芝シリコーン社製のトスパールシリーズが挙げられる。
(B)成分の平均粒子径は、化粧料の肌上での「のび」・「肌への付着性」等を考慮した結果、平均粒子径が0.1〜50μmであることが必要であり、好ましくは1〜20μmである。
なお、本発明でいう「透明性」を有する化粧料とは、金皿の底面に白地に所定の大きさの黒文字を記した紙を置き、さらにその上に混合組成物を入れ、厚さ3mmになるように成型したとき、真上から見たときに底面の文字を目視認識できるものをさす。
上述した条件で試料の透明性を目視で観察し、以下の判断基準により透明性を評価した。
金皿の底面の文字(16ポイント)が認識できた場合:◎
金皿の底面の文字(26ポイント)が認識できた場合:○
金皿の底面の文字が認識できなかった場合 :×
(1)の透明性の評価において外観の透明性が◎または○と評価された試料のみ(比較例4,5以外)を20名の被験者に対してブラシを用いて使用させ官能評価を行った。使用時の「とれ」に関するスコアは、良い(5点)、やや良い(4点)、普通(3点)、やや悪い(2点)、悪い(1点)の5段階で評価し、使用時の「感触」に関するスコアは、さらさら感、さっぱり感について、感じる(5点)、やや感じる(4点)、普通(3点)、やや感じない(2点)、感じない(1点)の5段階で評価した。さらに20名のスコアの平均値を求め、表1に示す評価基準で判定した。
本発明の化粧料に関する実施例では表2に示す処方で、比較例では表3に示す処方でプレストパウダーを作製した。
実施例および比較例のプレストパウダーを製造するために、粉末成分を均一に混合した後、油剤成分を徐々に加え、更に均一状態になるまでカッターミルを用いて混合を行った。得られた混合粉末を直径55mm、高さ3mmの丸状金皿に試料の厚さ2mmになるようプレス充填した。打型圧力は2kg/cm2で内容量は3.0〜3.5g程度とした。
なお、上記実施例および比較例で使用したトレフィルE−508の平均粒子径は3μm;トレフィルE−506Cの平均粒子径は3μm;KSP−102の平均粒子径は30μm;トスパール130の平均粒子径は3μmであった。
下記に示す組成のプレストパウダーを常法により作製した。上記外観の透明性、使用性(とれ,感触)に関して上記と同じ方法で評価したところ、優れた透明性を有し、使用性も良好であることが確認された。
(プレストパウダー) (質量%)
シリコーンエラストマー(粉末分) 26
[トレフィルE−508:東レダウコーニング社製]
複合粉体 6
[KSP−102:信越化学工業社製]
非弾性球状シリコーン樹脂粉末 26
[トスパール145A:GE東芝シリコーン社製]
ジメチルポリシロキサン 30
ジメチルポリシロキサン(トレフィルE含有分) 11
無水珪酸 1
−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−
100
実施例10
下記に示す組成のプレストパウダーを常法により作製した。上記外観の透明性、使用性(とれ,感触)に関して上記と同じ方法で評価したところ、優れた透明性を有し、使用性も良好であることが確認された。
(プレストパウダー) (質量%)
シリコーンエラストマー(粉末分) 26
[トレフィルE−508:東レダウコーニング社製]
複合粉体 6
[KSP−102:信越化学工業社製]
非弾性球状シリコーン樹脂粉末 26
[トスパール145A:GE東芝シリコーン社製]
ジメチルポリシロキサン 30
ジメチルポリシロキサン(トレフィルE−508含有分)11
アクリレーツクロスポリマー 1
−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−
100
Claims (4)
- (A)弾性粉末混合物30〜40質量%、(B)平均粒子径が0.1〜50μmの範囲にあるメチルシロキサン網状重合体またはポリオルガノシルセスキオサン硬化物から選択されるシリコーン樹脂粉末25〜40質量%および(C)屈折率が1.4〜1.6であるシリコーン化合物および/または炭化水素30〜55質量%を必須成分とし、(A)弾性粉末混合物は、(A1)シリコーンエラストマー粉末と、(A2)シリコーンエラストマー粉末の表面をシリコーン樹脂で被覆した複合シリコーン粉体、それぞれ1種以上を含むことを特徴とし、これら必須成分の混合組成物を固化して得られる固形粉末化粧料。
- 屈折率が1.3〜1.6の範囲にある粉末を更に含有する、請求項1記載の固形粉末化粧料。
- 光輝性粉体を更に含有する、請求項1または2記載の固形粉末化粧料。
- 成分(A)、成分(B)および成分(C)の合計配合量が、化粧料全体に対して90質量%以上である、請求項1〜3のいずれか1項に記載の固形粉末化粧料。