JP2023015094A - フッ素化フィルター膜、フィルターおよび方法 - Google Patents
フッ素化フィルター膜、フィルターおよび方法 Download PDFInfo
- Publication number
- JP2023015094A JP2023015094A JP2022168583A JP2022168583A JP2023015094A JP 2023015094 A JP2023015094 A JP 2023015094A JP 2022168583 A JP2022168583 A JP 2022168583A JP 2022168583 A JP2022168583 A JP 2022168583A JP 2023015094 A JP2023015094 A JP 2023015094A
- Authority
- JP
- Japan
- Prior art keywords
- filtration membrane
- membrane
- fluoropolymer
- ionic groups
- filtration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
負荷電AMPSモノマーで改質されたPTFE表面
本実施例は、負荷電モノマーである2-アクリルアミド-2-メチル-1-プロパンスルホン酸(AMPS)によるPTFE膜の表面改質を実証する。このモノマーの負荷電イオン基は、図2において熱安定でないことが示される。
負荷電PTFE膜の色素結合能の決定
本実施例は、正荷電色素分子、メチレンブルーの吸収を測定することにより、処理された多孔質フルオロポリマー膜に存在する負電荷の量を近似することができる方法を実証する。
負荷電PTFE膜の熱安定性の決定
改質された膜試験片を加熱し、昇温曝露前後の色素結合能の変化を測定することにより、表面改質されたPTFEの熱安定性を決定した。
負荷電SVSモノマーで改質されたPTFE表面
本実施例は、負荷電モノマーであるビニルスルホン酸ナトリウム(SVS)によるPTFE膜の表面改質、およびSVSによってもたらされる荷電官能基の熱安定性(図3を参照されたい)を実証する。
負荷電VPAモノマーで改質されたPTFE表面
本実施例は、負荷電モノマーであるビニルホスホン酸(VPA)によるPTFE膜の表面改質、およびVPAによってもたらされる荷電官能基の熱安定性(図4を参照されたい)を実証する。
正荷電APTAC/DADMACモノマーで改質されたPTFE表面
本実施例は、正荷電モノマーである(3-アクリルアミドプロピル)トリメチルアンモニウムクロリド(APTAC)およびジアリルジメチルアンモニウムクロリド(DADMAC)によるPTFE膜の表面改質を実証する。
正荷電PTFE膜の色素結合能の決定
本実施例は、負荷電色素分子、ポンソーSの吸収を測定することにより、正電荷の量を近似することができる方法を実証する。
正荷電PTFE膜の熱安定性の決定
改質された膜試験片を加熱し、昇温曝露前後の色素結合能の変化を測定することにより、表面改質されたPTFEの熱安定性を決定した。
正荷電(1-ビニルイミダゾール)モノマーで改質されたPTFE表面
本実施例は、正荷電モノマー、(1-ビニルイミダゾール)によるPTFE膜の表面改質、および1-ビニルイミダゾールによってもたらされる、正荷電官能基の熱安定性(図6を参照されたい)を実証する。
熱安定な負荷電モノマーSVSで改質されたPTFE膜を用いた濾過による、イソプロパノールからの金属の除去
本実施例は、熱安定な負荷電モノマーSVSで改質されたPTFE膜の、濾過中にイソプロパノールの金属を減少させる能力を実証する。実施例4と同様の方法を使用して負荷電PTFE膜を調製し、47mmの膜試験片へと切断した。これらの膜試験片を、10%HClで数回洗浄した後10%HClに一晩漬け、脱イオン水で平衡化することによって調整し、清潔な47mmフィルターアセンブリ(Savillex)に固定した。膜およびフィルターアセンブリを、塗布溶媒でもあるIsopropanol Gigabit(KMG)でフラッシュした。また、対照試料として、未処理の未改質PTFEを同じ方法を使用して調製および調整し、フィルターアセンブリに固定した。塗布溶媒に、各金属5ppbの目標濃度でCONOSTAN Oil Analysis Standard S-21(SCP Science)をスパイクした。濾過金属除去効率を決定するために、金属でスパイクした塗布溶媒を、各フィルターを含有する対応する47mmフィルターアセンブリに10mL/分で通過させ、濾液を50、100および150mLの清潔なPFAジャーに収集した。金属でスパイクした塗布溶媒および各濾液試料の金属濃度をICP-MSを使用して決定した。結果を、表6の合計金属除去(%)、および図7の100mL濾過での個別の金属除去%に提示する。熱安定な負荷電モノマーSVSで改質されたPTFE膜は、未改質膜と比べて、イソプロパノールから金属(リチウム、ナトリウム、マグネシウム、アルミニウム、カルシウム、チタン、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、銀、カドミウム、スズ、バリウムおよび鉛を含む)を除去する向上した能力を示す。
熱安定な負荷電モノマーSVSで改質されたPTFE膜、および熱安定な正荷電(1-ビニルイミダゾール)モノマーで改質されたPTFE表面を用いた濾過による、nBAからの金属の除去
本実施例は、熱安定な負荷電モノマーSVSまたは熱安定な正荷電モノマー(1-ビニルイミダゾール)で改質された2種のPTFE膜の、濾過中にイソプロパノールの金属を減少させる能力を実証する。実施例4および実施例9と同様の方法を使用して荷電PTFE膜を調製し、47mmの膜試験片へと切断した。これらの膜試験片を、10%HClで数回洗浄した後10%HClに一晩漬け、脱イオン水で平衡化することによって調整して、清潔な47mmフィルターアセンブリ(Savillex)に固定した。膜およびフィルターアセンブリを、Isopropanol Gigabit(KMG)でフラッシュし、続いて酢酸n-ブチル(nBA)でフラッシュした。また、対照試料として、未処理の未改質PTFEを同じ方法を使用して調製および調整し、フィルターアセンブリに固定した。塗布溶媒に、各金属5ppbの目標濃度でCONOSTAN Oil Analysis Standard S-21(SCP Science)をスパイクした。濾過金属除去効率を決定するために、金属でスパイクした塗布溶媒を、各フィルターを含有する対応する47mmフィルターアセンブリに10mL/分で通過させ、濾液を50、100および150mLの清潔なPFAジャーに収集した。金属でスパイクした塗布溶媒および各濾液試料の金属濃度をICP-MSを使用して決定した。結果を、表7の合計金属除去(%)、および図8の100mL濾過での個別の金属除去%に示す。熱安定な負荷電モノマーSVSで改質されたPTFE膜、および熱安定な正荷電モノマー(1-ビニルイミダゾール)で改質されたPTFEは、未改質膜と比べて、nBAから金属(ホウ素、ナトリウム、マグネシウム、アルミニウム、カルシウム、チタン、バナジウム、クロム、マンガン、鉄、ニッケル、銅、亜鉛、モリブデン、銀、カドミウム、スズ、バリウムおよび/または鉛を含む)を除去する向上した能力を示す。
熱安定な負荷電モノマーSVSで改質されたPTFE膜、および熱安定な正荷電(1-ビニルイミダゾール)モノマーで改質されたPTFE表面を用いた、フィルターのG25ビーズ保持率
フィルターのG25ビーズ(0.025μmの緑色蛍光ポリマーミクロスフェア、Fluoro-Max)保持率を、熱安定な負荷電モノマーSVSで改質されたPTFE膜、および熱安定な正荷電(1-ビニルイミダゾール)モノマーで改質されたPTFE表面について決定し、未改質PTFE膜と比較した。8ppbのG25ビーズと0.1%のトリトンX(Sigma)の供給溶液を脱イオン水中で調製した。膜ロールから47mmのサイズの膜試験片を切断し、イソプロパノールで濡らし、膜をフィルターアセンブリに固定した。濡れた膜を含有する膜アセンブリを脱イオン水でフラッシュし、続いて脱イオン水中0.1%のトリトンXでフラッシュした。0.5、1、2、3および4%単層の計算されたビーズ添加量で、G25およびトリトンXを用いて調製した溶液を膜に通して濾過し、濾液を収集した。蛍光分光光度計を使用してG25ビーズの濃度を計算することにより、収集した濾液試料を8ppbのG25ビーズと0.1%トリトンXとの供給溶液と比較する。種々の単層での膜の除去パーセントを図9にグラフ化した。熱安定な負荷電モノマーSVSで改質されたPTFE膜、および熱安定な正荷電モノマー、(1-ビニルイミダゾール)で改質されたPTFEは両方とも、未改質膜と比べて向上したG25ビーズ保持率を示す。
Claims (38)
- 多孔質フルオロポリマー膜、
熱安定なイオン基、および
縁部
を含む濾過膜と;
フルオロポリマー端板と
を含むフィルター構成要素であって、
濾過膜の縁部が端板にポッティングされ、縁部に沿って流体密シールをもたらす、フィルター構成要素。 - 濾過膜を、濾過膜の縁部が端板にポッティングされるように、フルオロポリマーの溶融加工性フルオロポリマーを軟化させるために十分な時間にわたり、少なくとも摂氏240度の温度に曝露した時、濾過膜が、曝露前に濾過膜に存在したイオン基の量の少なくとも50パーセントを含有する、請求項1に記載のフィルター構成要素。
- 濾過膜を、濾過膜の縁部が端板にポッティングされるように、フルオロポリマーの溶融加工性フルオロポリマーを軟化させるために十分な時間にわたり、少なくとも摂氏280度の温度に曝露した時、濾過膜が、曝露前に濾過膜に存在したイオン基の量の少なくとも50パーセントを含有する、請求項1に記載のフィルター構成要素。
- 溶融加工性フルオロポリマーが、濾過膜に接着した貼り合わせ用フィルム、端板の表面およびポッティング化合物から選択される、請求項2または3に記載のフィルター構成要素。
- イオン基が、負荷電イオン基を含む、請求項1から4のいずれか一項に記載のフィルター構成要素。
- イオン基が、イオン性硫黄含有基およびイオン性リン含有基から選択される、請求項5に記載のフィルター構成要素。
- イオン基が、ホスホン酸およびスルホネートから選択される、請求項6に記載のフィルター構成要素。
- イオン基が、正荷電イオン基を含む、請求項1から4のいずれか一項に記載のフィルター構成要素。
- イオン基がイミダゾールである、請求項8に記載のフィルター構成要素。
- 濾過膜が、多孔質フルオロポリマー膜、および熱安定なイオン基を含む多孔質フルオロポリマー膜の表面上のコーティングを備える、請求項1から9のいずれか一項に記載のフィルター構成要素。
- コーティングが、
液体コーティング溶液の反応性化合物の合計重量に対して、
25~90重量部のイオン基含有反応性化合物、および
10~75重量部のイオン基不含反応性化合物
を含む液体コーティング溶液から得られる、請求項10に記載のフィルター構成要素。 - イオン基含有反応性化合物が、1-ビニルイミダゾール、ビニルピリジン、ビニルスルホン酸、ビニルスルホン酸ナトリウム、ビニルホスホン酸および4-ビニルベンゼンスルホン酸ナトリウムから選択される、請求項9に記載のフィルター構成要素。
- イオン基不含反応性化合物が、メチレンビスアクリルアミド、メタクリル酸2-(ジメチルアミノ)エチルおよび1,4-ブタンジオールジビニルエーテルから選択される、請求項11または12に記載のフィルター構成要素。
- 濾過膜が、多孔質フルオロポリマー膜、および多孔質フルオロポリマー膜にグラフトされた熱安定なイオン基を含む、請求項1から13のいずれか一項に記載のフィルター構成要素。
- 多孔質フルオロポリマー膜が、ポリ(テトラフルオロエチレン)(PTFE)、ポリ(テトラフルオロエチレン-co-ヘキサフルオロプロピレン)(FEP)およびポリ(テトラフルオロエチレン-co-ペルフルオロ(アルキルビニルエーテル))(FPA)から選択されるペルフルオロポリマーを含む、請求項1から14のいずれか一項に記載のフィルター構成要素。
- フルオロポリマー膜がポリテトラフルオロエチレン(PTFE)を含む、請求項1から14のいずれか一項に記載のフィルター構成要素。
- フルオロポリマー膜が、シート、プリーツシートまたは中空糸である、請求項1から16のいずれか一項に記載のフィルター構成要素。
- 端板が溶融加工性フルオロポリマーを含む、請求項1から17のいずれか一項に記載のフィルター構成要素。
- 膜を取り囲むフルオロポリマーハウジング、
流体がフルオロポリマーハウジングの中へ流れることを可能にする入口、
流体が膜を通過した後に、ハウジングから流れ出ることを可能にする出口
を備える、請求項1から18のいずれか一項に記載のフィルター構成要素を含むフィルター。 - 入口と出口の間を流れる流体が接触する表面によって画定される流路をさらに備え、流路のすべての表面がフルオロポリマー材料で作製されている、請求項19に記載のフィルター。
- 請求項1から18のいずれか一項に記載のフィルター構成要素、または請求項19もしくは20に記載のフィルターを使用する方法であって、流体に濾過膜を通過させることを含む方法。
- 流体が、酢酸n-ブチル(nBA)、イソプロピルアルコール(IPA)、酢酸2-エトキシエチル(2EEA)、キシレン、シクロヘキサノン、乳酸エチル、メチルイソブチルカルビノール(MIBC)、メチルイソブチルケトン(MIBK)、酢酸イソアミル、ウンデカン、プロピレングリコールメチルエーテル(PGME)およびプロピレングリコールモノメチルエーテルアセテート(PGMEA)から選択される溶媒を含む、請求項21に記載の方法。
- 溶融加工性フルオロポリマーと接触している濾過膜を含むフィルター構成要素を調製する方法であって、
濾過膜が、
多孔質フルオロポリマー膜、
熱安定なイオン基、および
縁部
を含み;
方法が、
濾過膜および溶融加工性フルオロポリマーを加熱して、溶融加工性フルオロポリマーを軟化させることを含む、方法。 - 濾過膜が、加熱後に、加熱する工程の前に濾過膜に存在したイオン基の量の少なくとも50パーセントを含有する、請求項23に記載の方法。
- 溶融加工性フルオロポリマーが、濾過膜に接着した貼り合わせ用フィルム、端板およびポッティング化合物から選択される、請求項23または24に記載の方法。
- 濾過膜の縁部を端板にポッティングすることを含む、請求項23から25のいずれか一項に記載の方法。
- 多孔質フルオロポリマー膜、および
多孔質フルオロポリマー膜の表面のコーティングであって、熱安定なイオン基を含むコーティング
を備える濾過膜。 - 濾過膜の一部としての熱安定なイオン基が、摂氏240度の温度に5分間加熱可能であり、イオン基の50モルパーセント以下が化学的に劣化する、請求項27に記載の濾過膜。
- イオン基が、負荷電イオン基を含む、請求項27または28に記載の濾過膜。
- イオン基が、イオン性硫黄含有基およびイオン性リン含有基から選択される、請求項27から29のいずれか一項に記載の濾過膜。
- イオン基が、ホスホン酸およびスルホネートから選択される、請求項27から29のいずれか一項に記載の濾過膜。
- イオン基が、正荷電イオン基を含む、請求項27または28に記載の濾過膜。
- イオン基がイミダゾールである、請求項32に記載の濾過膜。
- コーティングが、
液体コーティング溶液の反応性化合物の合計重量に対して、
25~90重量部のイオン基含有反応性化合物、および
10~75重量部のイオン基不含反応性化合物
を含む液体コーティング溶液から得られる、請求項27から33のいずれか一項に記載の濾過膜。 - イオン基含有反応性化合物が、1-ビニルイミダゾール、ビニルピリジン、ビニルスルホン酸、ビニルホスホン酸および4-ビニルベンゼンスルホン酸ナトリウムから選択される、請求項34に記載の濾過膜。
- イオン基不含反応性化合物が、メチレンビスアクリルアミド、メタクリル酸2-(ジメチルアミノ)エチルおよび1,4-ブタンジオールジビニルエーテルから選択される、請求項34または35に記載の濾過膜。
- 多孔質フルオロポリマー膜が、ポリ(テトラフルオロエチレン)(PTFE)、ポリ(テトラフルオロエチレン-co-ヘキサフルオロプロピレン)(FEP)およびポリ(テトラフルオロエチレン-co-ペルフルオロ(アルキルビニルエーテル))(FPA)から選択されるペルフルオロポリマーを含む、請求項27から36のいずれか一項に記載の濾過膜。
- フルオロポリマー膜がポリテトラフルオロエチレン(PTFE)を含む、請求項27から37のいずれか一項に記載の濾過膜。