JP2020193546A - 骨材美観を生かした水硬性プレミックス目地材及びその製造方法 - Google Patents
骨材美観を生かした水硬性プレミックス目地材及びその製造方法 Download PDFInfo
- Publication number
- JP2020193546A JP2020193546A JP2019109075A JP2019109075A JP2020193546A JP 2020193546 A JP2020193546 A JP 2020193546A JP 2019109075 A JP2019109075 A JP 2019109075A JP 2019109075 A JP2019109075 A JP 2019109075A JP 2020193546 A JP2020193546 A JP 2020193546A
- Authority
- JP
- Japan
- Prior art keywords
- water
- premix
- cement
- joint
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
表−1に示す実施例1〜3及び、比較例1〜2の配合において、使用するセメントの量を変化させ、それに伴う性能評価を行った。
(実施例4〜5及び比較例3〜4)
表−1に示す実施例4〜5及び、比較例3〜4の配合において、使用する粉末樹脂の量を変化させ、それに伴う性能評価を行った。
(実施例6〜7及び比較例5〜6)
表−1に示す実施例6〜7及び、比較例5〜6において、使用する水溶性液体の量を変化させ、それに伴う性能評価を行った。
(比較例7)
表−1に示す比較例7において、使用する水溶性液体の種類を変えて、それに伴う性能評価を行った。
セメント:
普通ポルトランドセメント・・・宇部三菱セメント社製 JIS規格品
超速硬セメント・・・DENKA社製 スーパーセメントS−5
粉末樹脂:
粉末樹脂A・・・日本酢ビポバール社製 JP18S
粉末樹脂B・・・三菱ケミカル社製 GL−03
水溶性液体:
水溶性液体A・・・日本触媒社製 ジエチレングリコール
水溶性液体B・・・旭硝子社製 プロピレングリコール
水溶性液体C・・・青木油脂工業社製 PEG−12
珪砂:
トーヨーマテラン社製 愛知県産天然珪砂5号及び7号
添加剤:
曽我社製 防カビ剤バイオテック2P
(1)硬さ評価
試験用水硬性プレミックス目地材の施工2日後、材料の終結時間が過ぎた後、インターロッキングブロックの施工経験熟練者が、目地部の硬化体を指で削って硬さを調査した。
○:十分に硬い。
△:指で削り取れる。
×:簡単に指で削り取れる。
(2)舗装材の汚れ評価
試験用水硬性プレミックス目地材の施工2日後、材料の終結時間が過ぎた後、インターロッキングブロックの施工経験熟練者及び40代の健全な一般女性が、舗装材表面の汚れを目視にて評価した。
○:2名とも汚れが無くきれいと評価
△:1名もしくは2名が、少し汚れていると評価
×:1名もしくは2名が、汚れていると評価。
(3)施工作業性評価
ビニル製の袋に20kgで充填された、試験用水硬性プレミックス目地材の施工を、インターロッキングブロックの施工経験熟練者が行い、施工作業性の評価を行った。
○:材料分離等無く、簡単に目地部に材料を充填できる。
△:材料分離傾向、目地部に材料を充填するために少し工夫がいる。
×:材料分離、目地部に材料を充填する事が困難。
(4)生産性評価
ダルトン社製容量50リットルのプラネタリーミキサを用いて、1バッチの質量30kgの、試験用水硬性プレミックス目地材の製造を行い、均一な製品になるために必要な混合時間を測定し、評価を行った。
○:材料投入の順序に問わず、混合時間が3分以内で完成する。
△:骨材に水溶性液体を投入混合した後、その他の材料を投入混合し、合計混合時間が 3分以内で完成する。
×:材料の投入の工夫の有無に関わらず、混合時間が3分より長い時間で完成する。
(5)材料コスト
試験材料のコストを比較した。
○:性能に対して安価
△:性能に対して同等価
×:性能に対して高価
Claims (5)
- 当該水硬性プレミックス目地材組成物を、コンクリートブロック、コンクリート平板、レンガ、舗石等の舗装材の目地部分に充填する工程と、当該水硬性プレミックス目地材組成物の、表面に水を散水する工程とを備えた事を特徴とする材料及び目地部の施工方法。
- 請求項1記載の、水硬性プレミックス目地材組成物が、セメント、粉末樹脂、水溶性液体、骨材を含有する事を特徴とする材料及び舗装材目地部の施工方法。
- 請求項2記載の水硬性プレミックス目地材料組成物100質量部中、セメント粉末体が2〜15質量部、水溶性液体が0.3〜2質量部、粉末樹脂が、セメント粉末体100質量部に対して5〜120質量部に、本発明の効果を実質的に阻害しない範囲の公知の混和材及び混和剤、及び、施工箇所にあった風合いを出すためと、強度特性を補助するための、粒度調整された骨材からなる事を特徴とする、請求項1記載の材料及び舗装材目地部の施工方法。
- 請求項3記載の水硬性プレミックス目地材料組成物のうち、水溶性液体が、水溶液中の水分含有量が極めて少なく、5%以下かつ不揮発性のものからなる事を特徴とする、請求項3記載の材料及び舗装材目地部の施工方法。
- 請求項4記載の水溶性液体が、エチレングリコール類、ポリエチレングリコール類、プロピレングリコール類、ポリエーテル類からなる事を特徴とする、請求項4記載の材料及び舗装材目地部の施工方法。