JP2019206450A - フェライト組成物および積層電子部品 - Google Patents
フェライト組成物および積層電子部品 Download PDFInfo
- Publication number
- JP2019206450A JP2019206450A JP2018101762A JP2018101762A JP2019206450A JP 2019206450 A JP2019206450 A JP 2019206450A JP 2018101762 A JP2018101762 A JP 2018101762A JP 2018101762 A JP2018101762 A JP 2018101762A JP 2019206450 A JP2019206450 A JP 2019206450A
- Authority
- JP
- Japan
- Prior art keywords
- compound
- sio
- phase
- content
- terms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【課題】インダクタンス特性が改善され、比抵抗および初透磁率μｉが高く、直流重畳特性および交流抵抗も良好となるフェライト組成物等を得る。【解決手段】 主成分と副成分とを有するフェライト組成物である。主成分が、Ｆｅ２Ｏ３換算で４４．０〜５０．０モル％（４４．０モル％を含まない）のＦｅの化合物、ＣｕＯ換算で５．５〜１４．０モル％のＣｕの化合物、ＺｎＯ換算で４．０〜３９．０モル％のＺｎの化合物、および、残部でありＮｉＯ換算で４０．０モル％未満であるＮｉの化合物で構成されている。主成分１００重量部に対して、副成分として、Ｓｉの化合物をＳｉＯ２換算で３．０〜１３．０重量部（３．０重量部を含まない）、Ｃｏの化合物をＣｏ３Ｏ４換算で２．０〜１０．０重量部（２．０重量部を含まない）、Ｂｉの化合物をＢｉ２Ｏ３換算で０．２５〜５．００重量部、含有する。Ｃｏ／Ｓｉが重量比で０．４〜２．９である。【選択図】図３Ａ
Description
本発明は、フェライト組成物および積層電子部品に関する。
近年、ＩＣＴ機器へのＮＦＣ技術や非接触給電などの採用に伴い、ＩＣＴ機器の回路に流れる交流電流の大電流化が進行している。そして、大電流に対応するノイズ除去製品が求められている。
ノイズ除去製品としては、巻線タイプのフェライトインダクタや積層タイプのフェライトインダクタなどが挙げられるが、上記のような大電流の使用環境では、ノイズ除去特性の高さから巻線タイプのフェライトインダクタが用いられてきた。しかし、積層タイプのフェライトインダクタでも巻線タイプのフェライトインダクタと同等以上のノイズ除去特性が求められてきた。
特許文献１および特許文献２では、組成を制御することで優れた特性を有するフェライト組成物および積層電子部品が記載されている。
しかし、現在ではさらに優れた特性を有するフェライト組成物および積層電子部品が求められている。
本発明は、このような実状に鑑みてなされ、その目的は、インダクタンス特性等が改善されたフェライト組成物等を得ることである。
上記目的を達成するために、本発明に係るフェライト組成物は、
主成分と副成分とを有するフェライト組成物であって、
前記主成分が、Ｆｅ２Ｏ３換算で４４．０〜５０．０モル％（４４．０モル％を含まない）のＦｅの化合物、ＣｕＯ換算で５．５〜１４．０モル％のＣｕの化合物、ＺｎＯ換算で４．０〜３９．０モル％のＺｎの化合物、および、残部でありＮｉＯ換算で４０．０モル％未満であるＮｉの化合物で構成されており、
前記主成分１００重量部に対して、前記副成分として、Ｓｉの化合物をＳｉＯ２換算で３．０〜１３．０重量部（３．０重量部を含まない）、Ｃｏの化合物をＣｏ３Ｏ４換算で２．０〜１０．０重量部（２．０重量部を含まない）、Ｂｉの化合物をＢｉ２Ｏ３換算で０．２５〜５．００重量部、含有し、
（前記Ｃｏの化合物のＣｏ３Ｏ４換算での含有量）／（前記Ｓｉの化合物のＳｉＯ２換算での含有量）が重量比で０．４〜２．９であることを特徴とする。
主成分と副成分とを有するフェライト組成物であって、
前記主成分が、Ｆｅ２Ｏ３換算で４４．０〜５０．０モル％（４４．０モル％を含まない）のＦｅの化合物、ＣｕＯ換算で５．５〜１４．０モル％のＣｕの化合物、ＺｎＯ換算で４．０〜３９．０モル％のＺｎの化合物、および、残部でありＮｉＯ換算で４０．０モル％未満であるＮｉの化合物で構成されており、
前記主成分１００重量部に対して、前記副成分として、Ｓｉの化合物をＳｉＯ２換算で３．０〜１３．０重量部（３．０重量部を含まない）、Ｃｏの化合物をＣｏ３Ｏ４換算で２．０〜１０．０重量部（２．０重量部を含まない）、Ｂｉの化合物をＢｉ２Ｏ３換算で０．２５〜５．００重量部、含有し、
（前記Ｃｏの化合物のＣｏ３Ｏ４換算での含有量）／（前記Ｓｉの化合物のＳｉＯ２換算での含有量）が重量比で０．４〜２．９であることを特徴とする。
本発明に係るフェライト組成物は、上記の特徴を有することで、インダクタンス特性が改善され、比抵抗および初透磁率μｉが高く、直流重畳特性および交流抵抗も良好となる。
本発明に係るフェライト組成物は、スピネルフェライトからなる主相と、Ｚｎ２ＳｉＯ４相からなる第１の副相と、ＳｉＯ２相からなる粒界相と、からなっていてもよい。
さらに、ＳｉＯ２相からなる第２の副相を含んでいてもよい。
本発明に係る積層電子部品は、コイル導体およびセラミック層が積層されて構成される積層電子部品であって、
前記セラミック層が上記のフェライト組成物で構成されていることを特徴とする。
前記セラミック層が上記のフェライト組成物で構成されていることを特徴とする。
セラミック層が上記のフェライト組成物で構成されていることにより、積層型であるにもかかわらず、巻線型のコイル部品と比較して同等以上のノイズ除去特性を発揮することが可能である。
以下、本発明を、図面に示す実施形態に基づき説明する。図１に示すように、本発明の一実施形態に係る電子部品としての積層チップコイル１は、セラミック層２と内部電極層３とがＹ軸方向に交互に積層してあるチップ本体４を有する。
各内部電極層３は、四角状環またはＣ字形状またはコ字形状を有し、隣接するセラミック層２を貫通する内部電極接続用スルーホール電極（図示略）または段差状電極によりスパイラル状に接続され、コイル導体３０を構成している。
チップ本体４のＹ軸方向の両端部には、それぞれ端子電極５，５が形成してある。各端子電極５には、積層されたセラミック層２を貫通する端子接続用スルーホール電極６の端部が接続してあり、各端子電極５，５は、閉磁路コイル（巻線パターン）を構成するコイル導体３０の両端に接続される。
本実施形態では、セラミック層２および内部電極層３の積層方向がＹ軸に一致し、端子電極５，５の端面がＸ軸およびＺ軸に平行になる。Ｘ軸、Ｙ軸およびＺ軸は、相互に垂直である。図１に示す積層チップコイル１では、コイル導体３０の巻回軸が、Ｙ軸に略一致する。
チップ本体４の外形や寸法には特に制限はなく、用途に応じて適宜設定することができ、通常、外形はほぼ直方体形状とし、たとえばＸ軸寸法は０．１５〜０．８ｍｍ、Ｙ軸寸法は０．３〜１．６ｍｍ、Ｚ軸寸法は０．１〜１．０ｍｍである。
また、セラミック層２の電極間厚みおよびベース厚みには特に制限はなく、電極間厚み（内部電極層３、３の間隔）は３〜５０μｍ、ベース厚み（端子接続用スルーホール電極６のＹ軸方向長さ）は５〜３００μｍ程度で設定することができる。
本実施形態では、端子電極５としては、特に限定されず、本体４の外表面にＡｇやＰｄなどを主成分とする導電性ペーストを付着させた後に焼付け、さらに電気めっきを施すことにより形成される。電気めっきには、Ｃｕ、Ｎｉ、Ｓｎなどを用いることができる。
コイル導体３０は、Ａｇ（Ａｇの合金含む）を含み、たとえばＡｇ単体、Ａｇ−Ｐｄ合金などで構成される。コイル導体の副成分として、Ｚｒ、Ｆｅ、Ｍｎ、Ｔｉ、およびそれらの酸化物を含むことができる。
セラミック層２は、本発明の一実施形態に係るフェライト組成物で構成してある。以下、フェライト組成物について詳細に説明する。
本実施形態に係るフェライト組成物は、主成分としてＦｅの化合物、Ｃｕの化合物、Ｚｎの化合物およびＮｉの化合物を含有する。Ｆｅの化合物としては、例えばＦｅ２Ｏ３を含んでもよい。Ｃｕの化合物としては、例えばＣｕＯを含んでもよい。Ｚｎの化合物としては、例えばＺｎＯを含んでもよい。Ｎｉの化合物としては、例えばＮｉＯを含んでもよい。
主成分１００モル％中、Ｆｅの化合物の含有量は、Ｆｅ２Ｏ３換算で、４４．０〜５０．０モル％（４４．０モル％を含まない）、好ましくは４４．１〜４９．２モル％である。Ｆｅの化合物の含有量が多い場合には直流重畳特性および比抵抗が低下しやすい。また、十分な焼結性が得られにくくなり、特に低温焼結時に密度が低下しやすい。さらに、交流抵抗が高くなりやすい。Ｆｅの化合物の含有量が少ない場合には、初透磁率μｉが低下しやすい。
主成分１００モル％中、Ｃｕの化合物の含有量は、ＣｕＯ換算で、５．５〜１４．０モル％、好ましくは６．０〜９．０モル％である。Ｃｕの化合物の含有量が多い場合には、直流重畳特性が低下しやすい。さらに、交流抵抗が高くなりやすく比抵抗が低くなりやすい。Ｃｕの化合物の含有量が少ない場合には、焼結性が劣化し、特に低温焼結時の焼結密度が低下しやすい。また、焼結性の劣化により比抵抗が低下しやすい。さらに、初透磁率μｉも低下しやすい。
主成分１００モル％中、Ｚｎの化合物の含有量は、ＺｎＯ換算で、４．０〜３９．０モル％、好ましくは４．５〜２５．０モル％である。Ｚｎの化合物の含有量が多い場合には、直流重畳特性が低下しやすい。Ｚｎの化合物の含有量が少ない場合には、初透磁率μiが低くなりやすい。また、焼結性が劣化し、特に低温焼結時の焼結密度が低下しやすい。
主成分の残部は、Ｎｉの化合物から構成されている。主成分１００モル％中、Ｎｉの化合物の含有量は、ＮｉＯ換算で、４０．０モル％未満である。好ましくは４．５〜３９．９モル％である。Ｎｉの化合物の含有量が多い場合には、初透磁率μｉが低下しやすい。また、低温焼結時に密度が低下しやすい。
本実施形態に係るフェライト組成物は、上記の主成分に加え、副成分として、Ｓｉの化合物、Ｃｏの化合物およびＢｉの化合物を含有している。
Ｓｉの化合物の含有量は、主成分１００重量部に対して、ＳｉＯ２換算で、３．０〜１３．０重量部（３．０重量部を含まない）、好ましくは５．０〜８．０重量部である。Ｓｉの化合物の含有量が多い場合には、焼結性が劣化し、初透磁率μｉが低下しやすい。Ｓｉの化合物の含有量が少ない場合には、直量重畳特性が低下しやすい。また、交流抵抗が高くなりやすい。
Ｃｏの化合物の含有量は、主成分１００重量部に対して、Ｃｏ３Ｏ４換算で、２．０〜１０．０重量部（２．０重量部を含まない）、好ましくは３．０〜８．０重量部である。Ｃｏの化合物の含有量が多い場合には、初透磁率μｉが低下しやすい。Ｃｏの化合物の含有量が少ない場合には、直流重畳特性が低下しやすい。また、交流抵抗が高くなりやすい。さらに、Ｃｏの化合物は高い振幅電流に対するＱ値の低下を抑制する効果を有する。
Ｂｉの化合物の含有量は、主成分１００重量部に対して、Ｂｉ２Ｏ３換算で、０．２５〜５．００重量部、好ましくは１．００〜４．００重量部である。Ｂｉの化合物の含有量が多い場合には、比抵抗が低くなりやすい。また、直流重畳特性が低下しやすく交流抵抗が高くなりやすい。Ｂｉの化合物の含有量が少ない場合には、比抵抗が低くなりやすい。また、十分な焼結性が得られにくくなり、特に低温焼結時に密度が低下しやすい。また、Ｂｉの化合物は焼結過程においてＺｎ２ＳｉＯ４の生成を促進させる作用も持つ。そして、仮焼材料の粉砕の際に酸化ビスマスを添加する場合に、特にＺｎ２ＳｉＯ４の生成を促進させる作用が大きくなる。
（Ｃｏの化合物のＣｏ３Ｏ４換算での含有量）／（Ｓｉの化合物のＳｉＯ２換算での含有量）（以下、単に「Ｃｏ／Ｓｉ」と記載する）は、重量比で０．４〜２．９である。好ましくは１．０〜２．５である。Ｃｏの化合物の含有量およびＳｉの化合物の含有量が上記の範囲内であっても、Ｃｏ／Ｓｉが高すぎる場合には、初透磁率μｉが低下しやすい。Ｃｏ／Ｓｉが低すぎる場合には、交流抵抗Ｒａｃが高くなりやすい。または、密度が低下しやすい。
なお、各主成分および各副成分の含有量は、フェライト組成物の製造時において、原料粉末の段階から焼成後までの各工程で実質的に変化しない。
本実施形態に係るフェライト組成物では、主成分の組成範囲が上記の範囲に制御されていることに加え、副成分として、Ｓｉの化合物、Ｃｏの化合物およびＢｉの化合物が上記の範囲内で含有されている。その結果、焼結性が良好であって比抵抗および初透磁率μｉが高く、直流重畳特性および交流抵抗も良好なフェライト組成物を得ることができる。加えて、本発明に係るフェライト組成物は、内部電極として用いられるＡｇの融点以下の９００℃程度で焼結することが可能である。そのため、種々の用途への適用が可能となる。
また、本実施形態に係るフェライト組成物は、上記副成分とは別に、さらにＭｎ３Ｏ４などのマンガン酸化物、酸化ジルコニウム、酸化錫、酸化マグネシウム、ガラス化合物などの付加的成分を本発明の効果を阻害しない範囲で含有してもよい。これらの付加的成分の含有量は、特に限定されないが、例えば主成分１００重量部に対して０．０５〜１．０重量部程度である。
特に、酸化マグネシウムの含有量は、０．５重量部以下（０を含む）とすることが好ましい。酸化マグネシウムの含有量を０．５重量部以下とすることで、ＭｇＯとＳｉＯ２との反応を抑制し、後述するＺｎ２ＳｉＯ４相からなる第１の副相を生成しやすくなる。
さらに、本実施形態に係るフェライト組成物には、不可避的不純物元素の酸化物が含まれ得る。
具体的には、不可避的不純物元素としては、Ｃ、Ｓ、Ｃｌ、Ａｓ、Ｓｅ、Ｂｒ、Ｔｅ、Ｉや、Ｌｉ、Ｎａ、Ｍｇ、Ａｌ、Ｃａ、Ｇａ、Ｇｅ、Ｓｒ、Ｃｄ、Ｉｎ、Ｓｂ、Ｂａ、Ｐｂ等の典型金属元素や、Ｓｃ、Ｔｉ、Ｖ、Ｃｒ、Ｙ、Ｎｂ、Ｍｏ、Ｐｄ、Ａｇ、Ｈｆ、Ｔａ等の遷移金属元素が挙げられる。また、不可避的不純物元素の酸化物は、フェライト組成物中に０．０５重量部以下程度であれば含有されてもよい。
特に、主成分１００重量部に対して、Ａｌの含有量をＡｌ２Ｏ３換算で０．０５重量部以下とすることにより、焼結性および比抵抗を向上させやすくなる。
本実施形態に係るフェライト組成物は、上記の組成を有し、かつ、図３Ａおよび図３Ｂに示すようなコンポジット構造を有することが好ましい。
図３Ａは本実施形態に係るフェライト組成物１１（後述するＮｏ．５）について倍率２００００倍でＳＴＥＭ−ＥＤＳにより観察した結果である。図３Ｂは図３Ａを模式図化したものである。好ましいフェライト組成物１１はスピネルフェライトからなる主相１２の他にＺｎ２ＳｉＯ４相からなる第１の副相１４ａおよびＳｉＯ２相からなる第２の副相１４ｂを含む。さらに、前記各相（主相１２と、第１の副相１４ａと、第２の副相１４ｂ）の間にＳｉＯ２相からなる粒界相１６を含む。ＳｉＯ２相からなる第２の副相１４ｂは含まれなくてもよいが、含まれることが好ましい。第１の副相１４ａには、Ｎｉ、Ｃｕ、Ｃｏなどのその他の元素が含まれていてもよく、Ｚｎ２ＳｉＯ４に固溶していてもよい。第２の副相１４ｂには例えば、Ｆｅ、Ｎｉなどのその他の元素が含まれていてもよい。また、粒界相１６にはＳｉＯ２の他に、Ｂｉ２Ｏ３も主相１２よりも多く含まれる。なお、図３Ａおよび図３Ｂにおいて第２の副相１４ｂと粒界相１６との区別は、暫定的に行ったものである。具体的には、モル比でＳｉＯ２の含有割合がＢｉ２Ｏ３の含有割合よりも大きな部分を第２の副相１４ｂ、ＳｉＯ２の含有割合がＢｉ２Ｏ３の含有割合以下である部分を粒界相１６としている。正確な区別は、後述するさらに高倍率のＳＴＥＭ−ＥＤＳ観察により行うことができる。
Ｚｎ２ＳｉＯ４相からなる第１の副相１４ａ、ＳｉＯ２を含む第２の副相１４ｂ、およびＳｉＯ２を含む粒界相１６は、熱膨張係数がスピネルフェライトからなる主相１２と比較して小さい。そのため、熱膨張係数の小さい各相が熱膨張係数の大きい主相１２に引張応力を印加している。引張応力を印加することで、フェライト組成物１１を用いたコイル部品のインダクタンス特性が向上する。
さらに、本実施形態に係るフェライト組成物１１は、主相１２と、主相１２とは組成の異なる副相１４と、粒界相１６と、の合計に占める副相１４の割合が従来のフェライト組成物よりも大きい。具体的には、２００００倍以上であり主相１２が観察できる倍率のＳＴＥＭ−ＥＤＳ画像において、主相１２と、副相１４と、粒界相１６との合計面積を１００％として副相１４の合計面積が５％以上３３％以下であることが好ましい。副相１４の合計面積が５％以上であることで、上記の引張応力が十分に印加される。引張応力が十分に印加されることで、フェライト組成物１１からなるコイル部品はインダクタンス特性が改善され、比抵抗および初透磁率μｉが高く、直流重畳特性および交流抵抗も良好となる。また、第１の副相１４ａの面積は１％以上３２％以下であることが好ましく、第２の副相１４ｂの面積は１％以上１６％以下であることが好ましい。なお、主相１２の面積は６６％以上８２％以下であることが好ましく、粒界相１６の面積は１％以上１５％以下であることが好ましい。
また、本実施形態では、Ｚｎ２ＳｉＯ４相とは、Ｚｎ２ＳｉＯ４を含む相のことを指す。ＳｉＯ２相とは、ＳｉＯ２の含有割合が主相よりも高い相のことを指す。Ｂｉ２Ｏ３相とは、Ｂｉ２Ｏ３の含有割合が主相よりも高い相のことを指す。なお、後述するようにＳｉＯ２相からなり、かつ、Ｂｉ２Ｏ３相からなる相があってもよい。
また、本実施形態に係るフェライト組成物１１（Ｎｏ．５）について倍率１０００００倍でＳＴＥＭ−ＥＤＳを用いて得られるＳｉ元素マッピング画像が図４である。また、図４を概略図としたものが図５である。
図４および図５の副相１４が第１の副相１４ａか第２の副相１４ｂかについては、任意の方法により確認できる。例えば、Ｚｎ元素マッピングが挙げられる。
図３Ａおよび図３Ｂと比較して観察倍率を高めた図４および図５より、前記各相（主相１２と、第１の副相１４ａと、第２の副相１４ｂ）の間にＳｉＯ２相からなる粒界相１６が存在し、主相または副相であるコアの周囲をＳｉＯ２を含むシェルで覆うコアシェル構造となっていることがわかる。
なお、上述の通り、粒界相１６にはＢｉ２Ｏ３も含まれている。粒界相１６がＢｉ２Ｏ３相かつＳｉＯ２相であることは、例えば、ＳＴＥＭ−ＥＤＳを用いて主相１２および粒界相１６を通過する部分を線分析することで確認することができる。
本実施形態に係るフェライト組成物１１はＳｉＯ２相である粒界相１６を含むことで、粒界相１６の割合が従来のフェライト組成物における粒界相の割合よりも大きくなる。これは、粒界相１６の厚みが従来のフェライト組成物よりも厚いことを意味している。そして、主相とは熱膨張率が異なるＳｉＯ２相からなる粒界相１６が含まれ、各相を覆うことで、粒界相１６から各相へ引張応力が印加される。引張応力が十分に印加されることで、フェライト組成物１１はインダクタンス特性が改善され、比抵抗および初透磁率μｉが高く、直流重畳特性および交流抵抗も良好となる。本実施形態では、２００００倍以上の主相１２が見える大きさのＳＴＥＭ−ＥＤＳ画像において、主相１２と、主相とは熱膨張率が異なる副相１４と、粒界相１６との合計面積を１００％として粒界相１６の面積が１％以上１５％以下であることが好ましい。
なお、本実施形態に係るフェライト組成物１１において主相１２および副相１４をそれぞれ結晶粒子とした場合の平均結晶粒子径は、好ましくは０．２〜１．５μｍである。平均結晶粒子径の測定方法は任意である。例えばＸＲＤを用いて測定する方法がある。
さらに、Ｚｎ２ＳｉＯ４相の存在は上記のＥＰＭＡやＳＴＥＭ−ＥＤＳでの元素分析解析の他、Ｘ線回折でも確認できる。
以下、Ｚｎ２ＳｉＯ４の含有量の定義および測定方法について説明する。
Ｘ線回折装置にてフェライト組成物のＸ線回折強度を測定し、フェライト組成物１１におけるスピネル型フェライトの（３１１）面のピーク強度ＩＡとＺｎ２ＳｉＯ４の（１１３）面のピークの強度ＩＢとを測定する。Ｚｎ２ＳｉＯ４相の含有量は、ＩＡでＩＢを割った値（ＩＢ／ＩＡ）とする。なお、Ｘ線回折装置により示される強度からバックグラウンドを引いた値を前記Ｘ線回折強度とする。
Ｚｎ２ＳｉＯ４の含有量（ＩＢ／ＩＡ）は、０．００６以上であることが好ましい。また、Ｚｎ２ＳｉＯ４の含有量の上限には特に限定はないが、ＩＢ／ＩＡが０．２００以下であることが好ましい。
次に、本実施形態に係るフェライト組成物の製造方法の一例を説明する。まず、出発原料（主成分の原料および副成分の原料）を、所定の組成比となるように秤量する。なお、平均粒径が０．０５〜１．０μｍの出発原料を用いることが好ましい。
主成分の原料としては、酸化鉄（α−Ｆｅ２Ｏ３）、酸化銅（ＣｕＯ）、酸化ニッケル（ＮｉＯ）、酸化亜鉛（ＺｎＯ）あるいは複合酸化物などを用いることができる。前記複合酸化物としては、例えば珪酸亜鉛（Ｚｎ２ＳｉＯ４）が挙げられる。さらに、その他、焼成により上記した酸化物や複合酸化物となる各種化合物等を用いることができる。焼成により上記した酸化物になるものとしては、たとえば、金属単体、炭酸塩、シュウ酸塩、硝酸塩、水酸化物、ハロゲン化物、有機金属化合物等が挙げられる。
副成分の原料としては、酸化珪素、酸化ビスマスおよび酸化コバルトを用いることができる。副成分の原料となる酸化物については特に限定はなく、複合酸化物などを用いることができる。前記複合酸化物としては、例えば珪酸亜鉛（Ｚｎ２ＳｉＯ４）が挙げられる。さらに、その他、焼成により上記した酸化物や複合酸化物となる各種化合物等を用いることができる。焼成により上記した酸化物になるものとしては、たとえば、金属単体、炭酸塩、シュウ酸塩、硝酸塩、水酸化物、ハロゲン化物、有機金属化合物等が挙げられる。
なお、酸化コバルトの一形態であるＣｏ３Ｏ４は、保管や取り扱いが容易であり、空気中でも価数が安定していることから、コバルト化合物の原料として好ましい。
次に、主成分の原料である酸化鉄、酸化銅、酸化ニッケル、酸化亜鉛を混合し、原料混合物を得る。さらに、上記の主成分の原料のうち、酸化亜鉛はこの段階では添加せず、原料混合物の仮焼後に珪酸亜鉛とともに添加してもよい。逆に、副成分の原料の一部をこの段階で主成分の原料と混合してもよい。原料混合物に含まれる原料の種類と割合、および、原料混合物の仮焼後に添加する原料の種類と割合を適宜制御することで、主相、第１の副相、第２の副相および粒界相の存在割合を制御することができる。
具体的には、仮焼後に添加するＺｎ２ＳｉＯ４の添加量が多いほど第１の副相の面積割合が大きくなる傾向にある。また仮焼後に添加するＳｉＯ２の添加量が多いほど第２の副相の面積割合が大きくなる傾向がある。さらに原料混合物におけるＺｎＯの含有量が少ないほど第２の副相もしくは粒界相の面積割合が大きくなる傾向にある。
混合する方法は任意である。例えば、ボールミルを用いて行う湿式混合や、乾式ミキサーを用いて行う乾式混合が挙げられる。
次に、原料混合物の仮焼を行い、仮焼材料を得る。仮焼は、原料の熱分解、成分の均質化、フェライトの生成、焼結による超微粉の消失と適度の粒子サイズへの粒成長を起こさせ、原料混合物を後工程に適した形態に変換するために行われる。仮焼時間および仮焼温度は任意である。仮焼は、通常、大気（空気）中で行うが、大気中よりも酸素分圧が低い雰囲気で行っても良い。
次に、副成分の原料となる酸化珪素、酸化ビスマス、酸化コバルトおよび珪酸亜鉛等を仮焼材料と混合し、混合仮焼材料を作製する。特にこの段階で添加する珪酸亜鉛が多いほどＺｎ２ＳｉＯ４相である第１の副相の存在割合が高くなりやすい。また、仮焼材料におけるＺｎが少ないほど、ＳｉＯ２相でありＢｉ２Ｏ３相でもある粒界相の存在割合が高くなりやすい。これは、仮焼材料におけるＺｎが少ない場合には、焼成時にＺｎ２ＳｉＯ４のＺｎが主相へ固溶しやすくなり、ＳｉＯ２が粒界相に生じるためである。さらに、この段階で添加する酸化珪素が多いほどＳｉＯ２相である第２の副相の存在割合が高くなりやすい。
次に、混合仮焼材料の粉砕を行い、粉砕仮焼材料を得る。粉砕は、混合仮焼材料の凝集をくずして適度の焼結性を有する粉体とするために行われる。混合仮焼材料が大きい塊を形成しているときには、粗粉砕を行ってからボールミルやアトライターなどを用いて湿式粉砕を行う。湿式粉砕は、粉砕仮焼材料の平均粒径が、好ましくは０．１〜１．０μｍ程度となるまで行う。
以下、上記の湿式粉砕後の粉砕材料を用いる図１に示す積層チップコイル１の製造方法について説明する。
図１に示す積層チップコイル１は、一般的な製造方法により製造することができる。すなわち、粉砕仮焼材料をバインダーと溶剤とともに混練して得たフェライトペーストを用いて、Ａｇなどを含む内部電極ペーストと交互に印刷積層した後に焼成することで、チップ本体４を形成することができる（印刷法）。あるいはフェライトペーストを用いてグリーンシートを作製し、グリーンシートの表面に内部電極ペーストを印刷し、それらを積層して焼成することでチップ本体４を形成してもよい（シート法）。いずれにしても、チップ本体を形成した後に、端子電極５を焼き付けあるいはメッキなどで形成すればよい。
フェライトペースト中のバインダーおよび溶剤の含有量は任意である。例えば、フェライトペースト全体を１００重量％としてバインダーの含有量は１〜１０重量％程度、溶剤の含有量は１０〜５０重量％程度の範囲で設定することができる。また、フェライトペースト中には、必要に応じて分散剤、可塑剤、誘電体、絶縁体等を１０重量％以下の範囲で含有させることができる。Ａｇなどを含む内部電極ペーストも同様にして作製することができる。また、焼成条件などは、特に限定されないが、内部電極層にＡｇなどが含まれる場合には、焼成温度は、好ましくは９３０℃以下、さらに好ましくは９００℃以下である。
なお、本発明は、上述した実施形態に限定されるものではなく、本発明の範囲内で種々に改変することができる。
たとえば、図２に示す積層チップコイル１ａのセラミック層２を上述した実施形態のフェライト組成物を用いて構成してもよい。図２に示す積層チップコイル１ａでは、セラミック層２と内部電極層３ａとがＺ軸方向に交互に積層してあるチップ本体４ａを有する。
各内部電極層３ａは、四角状環またはＣ字形状またはコ字形状を有し、隣接するセラミック層２を貫通する内部電極接続用スルーホール電極（図示略）または段差状電極によりスパイラル状に接続され、コイル導体３０ａを構成している。
チップ本体４ａのＹ軸方向の両端部には、それぞれ端子電極５，５が形成してある。各端子電極５には、Ｚ軸方向の上下に位置する引き出し電極６ａの端部が接続してあり、各端子電極５，５は、閉磁路コイルを構成するコイル導体３０ａの両端に接続される。
本実施形態では、セラミック層２および内部電極層３の積層方向がＺ軸に一致し、端子電極５，５の端面がＸ軸およびＺ軸に平行になる。Ｘ軸、Ｙ軸およびＺ軸は、相互に垂直である。図２に示す積層チップコイル１ａでは、コイル導体３０ａの巻回軸が、Ｚ軸に略一致する。
図１に示す積層チップコイル１では、チップ本体４の長手方向であるＹ軸方向にコイル導体３０の巻軸があるため、図２に示す積層チップコイル１ａに比較して、巻数を多くすることが可能であり、高い周波数帯までの高インピーダンス化が図りやすいという利点を有する。図２に示す積層チップコイル１ａにおいて、その他の構成および作用効果は、図１に示す積層チップコイル１と同様である。
また、本実施形態のフェライト組成物は、図１または図２に示す積層チップコイル以外の電子部品に用いることができる。例えば、コイル導体とともに積層されるセラミック層として本実施形態のフェライト組成物用いることができる。他にも、ＬＣ複合部品などのコイルと他のコンデンサ等の要素とを組み合わせた複合電子部品に本実施形態のフェライト組成物を用いることができる。
本実施形態のフェライト組成物を用いた積層チップコイルの用途は任意である。例えばＮＦＣ技術や非接触給電などが採用されたＩＣＴ機器（例えばスマートフォンなど）の回路など、特に高い交流電流が流れるために従来は巻線タイプのフェライトインダクタが用いられてきた回路にも好適に用いられる。
以下、本発明を、さらに詳細な実施例に基づき説明するが、本発明は、以下に示す実施例に限定されない。
（実験例１）
主成分の原料として、Ｆｅ２Ｏ３、ＮｉＯ、ＣｕＯ、ＺｎＯを準備した。副成分の原料として、ＳｉＯ２、Ｂｉ２Ｏ３、Ｃｏ３Ｏ４を準備した。なお、出発原料の平均粒径は０．０５〜１．００μｍであることが好ましい。
主成分の原料として、Ｆｅ２Ｏ３、ＮｉＯ、ＣｕＯ、ＺｎＯを準備した。副成分の原料として、ＳｉＯ２、Ｂｉ２Ｏ３、Ｃｏ３Ｏ４を準備した。なお、出発原料の平均粒径は０．０５〜１．００μｍであることが好ましい。
次に、準備した主成分原料の粉末および副成分原料の粉末を、焼結体として表１〜表６に記載の組成になるように秤量した。
秤量後に、準備した主成分原料のうち、Ｆｅ２Ｏ３、ＮｉＯ、ＣｕＯ、および必要に応じてＺｎＯの一部をボールミルで１６時間湿式混合して原料混合物を得た。なお、実験例１のＮｏ．５では、原料混合物におけるＺｎＯの含有量が１０モル％以下となるようにした。すなわち、後述する仮焼材料におけるＺｎＯの含有量も１０モル％以下となる。
次に、得られた原料混合物を乾燥した後に、空気中で仮焼して仮焼材料を得た。仮焼温度は原料混合物の組成に応じて５００〜９００℃の範囲で適宜選択した。その後、仮焼材料に前記湿式混合工程において混合しなかったＺｎＯの残部、およびＳｉＯ２をＺｎ２ＳｉＯ４の化合物の形で添加し、さらにその他の副成分等を添加しながらボールミルで粉砕して粉砕仮焼材料を得た。なお、実験例１のＮｏ．５では仮焼材料へはＺｎ２ＳｉＯ４の化合物およびＺｎＯを添加し、ＳｉＯ２は添加しなかった。
仮焼材料に添加するＺｎＯの残部の量については、仮焼材料に添加するＳｉＯ２の１．０〜３．０倍（モル換算）とすることが好ましい。
次に、この粉砕仮焼材料を乾燥した後、粉砕仮焼材料１００重量部に、バインダとして重量濃度６％のポリビニルアルコール水溶液を１０．０重量部添加して造粒して顆粒とした。この顆粒を、加圧成形して、トロイダル形状（寸法＝外径１３ｍｍ×内径６ｍｍ×高さ３ｍｍ）の成形体、およびディスク形状（寸法＝外径１２ｍｍ×高さ２ｍｍ）の成形体を得た。
次に、これら各成形体を、空気中において、Ａｇの融点（９６２℃）以下である８６０〜９００℃で２時間焼成して、焼結体としてのトロイダルコアサンプルおよびディスクサンプルを得た。さらに得られた各サンプルに対し以下の特性評価を行った。なお、秤量した原料粉末と焼成後の成形体とで組成がほとんど変化していないことを蛍光Ｘ線分析装置により確認した。
比抵抗ρ
ディスクサンプルの両面にＩｎ−Ｇａ電極を塗り、直流抵抗値を測定し、比抵抗ρを求めた（単位：Ω・ｍ）。測定はＩＲメーター（ＨＥＷＬＥＴＴ ＰＡＣＫＡＲＤ社製４３２９Ａ）を用いて行った。本実施例では、比抵抗ρは１０６Ω・ｍ以上を良好とした。
ディスクサンプルの両面にＩｎ−Ｇａ電極を塗り、直流抵抗値を測定し、比抵抗ρを求めた（単位：Ω・ｍ）。測定はＩＲメーター（ＨＥＷＬＥＴＴ ＰＡＣＫＡＲＤ社製４３２９Ａ）を用いて行った。本実施例では、比抵抗ρは１０６Ω・ｍ以上を良好とした。
初透磁率μ ｉ
トロイダルコアサンプルに銅線ワイヤを１０ターン巻きつけ、ＬＣＲメータ（アジレントテクノロジー社製４９９１Ａ）を使用して、初透磁率μｉを測定した。測定条件としては、測定周波数１ＭＨｚ、測定温度２５℃とした。初透磁率μｉが３．０以上である場合を良好とした。
トロイダルコアサンプルに銅線ワイヤを１０ターン巻きつけ、ＬＣＲメータ（アジレントテクノロジー社製４９９１Ａ）を使用して、初透磁率μｉを測定した。測定条件としては、測定周波数１ＭＨｚ、測定温度２５℃とした。初透磁率μｉが３．０以上である場合を良好とした。
直流重畳特性
トロイダルコアサンプルに銅線ワイヤを３０ターン巻きつけ、直流電流を印加したときの透磁率μを測定した。印加する直流電流を０〜８Ａまで変化させながら透磁率μを測定し、横軸に直流電流を、縦軸に透磁率をとってグラフ化した。直流電流０Ａのときの透磁率が初透磁率μｉである。そして、透磁率がμｉから１０％低下するときの電流値をＩｄｃとして求めた。
トロイダルコアサンプルに銅線ワイヤを３０ターン巻きつけ、直流電流を印加したときの透磁率μを測定した。印加する直流電流を０〜８Ａまで変化させながら透磁率μを測定し、横軸に直流電流を、縦軸に透磁率をとってグラフ化した。直流電流０Ａのときの透磁率が初透磁率μｉである。そして、透磁率がμｉから１０％低下するときの電流値をＩｄｃとして求めた。
印加する直流電流が８Ａ以下の段階で透磁率が１０％低下した場合は、透磁率が１０％低下したときの直流電流がＩｄｃである。印加する直流電流が８Ａの時点で透磁率が１０％低下しなかった場合は、直流電流８Ａでのグラフの傾きからＩｄｃを算出した。本実施例では、Ｉｄｃが８．０Ａ以上の場合に直流重畳特性が良好であるとした。
密度
前記焼結後のフェライト組成物の密度はトロイダルコアサンプルについて焼成後の焼結体の寸法および重量から算出した。密度が４．７０ｇ／ｃｍ３以上の場合に焼結性が良好であるとした。
前記焼結後のフェライト組成物の密度はトロイダルコアサンプルについて焼成後の焼結体の寸法および重量から算出した。密度が４．７０ｇ／ｃｍ３以上の場合に焼結性が良好であるとした。
フェライト組成物の観察
前記焼結後のフェライト組成物（トロイダルコアサンプル）について、ＥＰＭＡおよびＳＴＥＭ−ＥＤＳにより観察した。観察倍率は２００００倍以上とし、各実施例および比較例により適した観察倍率を適宜設定した。そして、各フェライト組成物がスピネルフェライト相からなる主相、Ｚｎ２ＳｉＯ４相からなる第１の副相、ＳｉＯ２相からなる第２の副相およびＳｉＯ２相とからなる粒界相を含むか否かについて確認した。さらに、主相、第１の副相、第２の副相および粒界相の面積割合をＳＴＥＭ−ＥＤＳの観察結果から算出した。表１〜表６の各実施例では、第１の副相の面積は４％以上１５％以下、第２の副相の面積は１％以上１０％以下、主相の面積は７５％以上９５％以下、粒界相の面積は５％以上２５％以下であった。
前記焼結後のフェライト組成物（トロイダルコアサンプル）について、ＥＰＭＡおよびＳＴＥＭ−ＥＤＳにより観察した。観察倍率は２００００倍以上とし、各実施例および比較例により適した観察倍率を適宜設定した。そして、各フェライト組成物がスピネルフェライト相からなる主相、Ｚｎ２ＳｉＯ４相からなる第１の副相、ＳｉＯ２相からなる第２の副相およびＳｉＯ２相とからなる粒界相を含むか否かについて確認した。さらに、主相、第１の副相、第２の副相および粒界相の面積割合をＳＴＥＭ−ＥＤＳの観察結果から算出した。表１〜表６の各実施例では、第１の副相の面積は４％以上１５％以下、第２の副相の面積は１％以上１０％以下、主相の面積は７５％以上９５％以下、粒界相の面積は５％以上２５％以下であった。
Ｚｎ ２ ＳｉＯ ４ の含有量
Ｚｎ２ＳｉＯ４の含有量については、前記焼結後のフェライト組成物についてＸ線回折装置（Ｐａｎａｌｙｔｉｃａｌ社製Ｘ‘Ｐｅｒｔ ＰＲＯ ＭＰＤ ＣｕＫα線）によりＩＢ／ＩＡを測定することで調べた。
Ｚｎ２ＳｉＯ４の含有量については、前記焼結後のフェライト組成物についてＸ線回折装置（Ｐａｎａｌｙｔｉｃａｌ社製Ｘ‘Ｐｅｒｔ ＰＲＯ ＭＰＤ ＣｕＫα線）によりＩＢ／ＩＡを測定することで調べた。
交流抵抗
交流抵抗（Ｒａｃ）については、トロイダルコアサンプルに銅線ワイヤを１次側に6ターン、２次側に3ターン巻つけ、Ｂ−Ｈアナライザ（岩通計測製ＳＹ−８２１８）およびアンプ（エヌエフ回路設計ブロック製４１０１−ＩＷ）を使用して、測定時の周波数を３ＭＨｚ、交流電流値を１．６Ａｒｍｓとした。交流抵抗Ｒａｃは２５ｍΩ以下を良好とした。
交流抵抗（Ｒａｃ）については、トロイダルコアサンプルに銅線ワイヤを１次側に6ターン、２次側に3ターン巻つけ、Ｂ−Ｈアナライザ（岩通計測製ＳＹ−８２１８）およびアンプ（エヌエフ回路設計ブロック製４１０１−ＩＷ）を使用して、測定時の周波数を３ＭＨｚ、交流電流値を１．６Ａｒｍｓとした。交流抵抗Ｒａｃは２５ｍΩ以下を良好とした。
表１では主にＦｅ２Ｏ３の含有量およびＮｉＯの含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、Ｆｅ２Ｏ３の含有量が小さすぎるＮｏ．１は初透磁率μｉが低すぎる結果となった。また、Ｆｅ２Ｏ３の含有量が大きすぎるＮｏ．７ａは焼結性が悪化し、直流重畳特性が悪化し、比抵抗ρが低すぎ、交流抵抗Ｒａｃが高すぎる結果となった。
表２では主にＺｎＯの含有量およびＮｉＯの含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、ＮｉＯの含有量が大きすぎるＮｏ．８は初透磁率μｉが低すぎる結果となった。
表３では主にＣｕＯの含有量およびＮｉＯの含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、ＣｕＯの含有量が小さすぎるＮｏ．１０ａは焼結性が悪化し、比抵抗ρが低すぎ、初透磁率μｉが低すぎる結果となった。ＣｕＯの含有量が大きすぎるＮｏ．１１ａは直流重畳特性が悪化し、比抵抗ρが低すぎ、交流抵抗Ｒａｃが高すぎる結果となった。
表４では主にＳｉＯ２の含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、ＳｉＯ２の含有量が小さすぎるＮｏ．１４ａは直流重畳特性が悪化し、交流抵抗Ｒａｃが高すぎる結果となった。ＳｉＯ２の含有量が大きすぎるＮｏ．１８ａは焼結性が悪化し、初透磁率μｉが低すぎる結果となった。
表５では主にＣｏ３Ｏ４の含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、Ｃｏ３Ｏ４の含有量が小さすぎるＮｏ．１９ａは直流重畳特性が悪化し、交流抵抗Ｒａｃが高すぎる結果となった。Ｃｏ３Ｏ４の含有量が大きすぎ、Ｃｏ／Ｓｉも大きすぎるＮｏ．２２ａは初透磁率μｉが低すぎる結果となった。また、Ｃｏ３Ｏ４の含有量が大きすぎるＮｏ．２２ｂも初透磁率μｉが低すぎる結果となった。
表６では主にＢｉ２Ｏ３の含有量を変化させている。全ての主成分および副成分が所定の範囲内である試料は全ての特性が良好となった。これに対し、Ｂｉ２Ｏ３の含有量が小さすぎるＮｏ．２３ ａは焼結性が悪化し、比抵抗ρが低すぎ、初透磁率μｉが低すぎる結果となった。Ｂｉ２Ｏ３の含有量が大きすぎるＮｏ．２４ａは比抵抗ρが低すぎ、直流重畳特性が悪化し、交流抵抗Ｒａｃが高すぎる結果となった。
（実験例２）
実験例２では、実験例１のＮｏ．５について、組成を変化させずに原料混合物の組成および仮焼後に添加する添加物の種類および／または添加量を変化させることで、ＥＰＭＡ観察時の主相、第１の副相、第２の副相および粒界相の面積割合を変化させた。結果を表７に示す。
実験例２では、実験例１のＮｏ．５について、組成を変化させずに原料混合物の組成および仮焼後に添加する添加物の種類および／または添加量を変化させることで、ＥＰＭＡ観察時の主相、第１の副相、第２の副相および粒界相の面積割合を変化させた。結果を表７に示す。
具体的には、Ｎｏ．５ａおよびＮｏ．５ｅでは、Ｎｏ．５と比較して原料混合物におけるＺｎＯの含有量を増加させ、仮焼材料にはＳｉＯ２および必要であればＺｎＯを添加した。Ｚｎ２ＳｉＯ４の化合物は添加しなかった。なお、原料混合物におけるＺｎＯの含有量は１０モル％超である。
Ｎｏ．５ｃでは、Ｎｏ．５と比較して原料混合物におけるＺｎＯの含有量を増加させ、仮焼材料には、Ｚｎ２ＳｉＯ４の化合物と、ＳｉＯ２および必要であればＺｎＯを添加した。なお、原料混合物におけるＺｎＯの含有量は１０モル％以下である。
Ｎｏ．５ｄでは、Ｎｏ．５にて仮焼材料に添加したＺｎ２ＳｉＯ４の化合物の代わりにＳｉＯ２およびＺｎＯを添加した。なお、原料混合物におけるＺｎＯの含有量は１０モル％以下である。
Ｎｏ．５ｇでは、Ｎｏ．５と比較して原料混合物におけるＺｎＯの含有量を増加させ、仮焼材料にはＺｎ２ＳｉＯ４の化合物およびＳｉＯ２を添加した。なお、原料混合物におけるＺｎＯの含有量は１０モル％超である。
表７より、主相、第１の副相、第２の副相および粒界相の面積割合が変化しても好適な結果が得られた。特に、Ｚｎ２ＳｉＯ４からなる第１の副相の面積割合が高いほど、インダクタンス特性が改善され、直流重畳特性および交流抵抗Ｒａｃも良好となる傾向であった。さらに、Ｂｉ２Ｏ３およびＳｉＯ２からなる粒界相の面積割合が高いほど、インダクタンス特性が改善され、直流重畳特性および交流抵抗Ｒａｃも良好となる傾向であった。
１，１ａ… 積層チップコイル
２… セラミック層
３，３ａ… 内部電極層
４，４ａ… チップ本体
５… 端子電極
６… 端子接続用スルーホール電極
６ａ… 引き出し電極
１１… フェライト組成物
１２… 主相（スピネルフェライト相）
１４… 副相（低α相）
１４ａ… 第１の副相（Ｚｎ２ＳｉＯ４相）
１４ｂ… 第２の副相（ＳｉＯ２相）
１６… 粒界相（Ｂｉ２Ｏ３相、ＳｉＯ２相）
３０，３０ａ… コイル導体
２… セラミック層
３，３ａ… 内部電極層
４，４ａ… チップ本体
５… 端子電極
６… 端子接続用スルーホール電極
６ａ… 引き出し電極
１１… フェライト組成物
１２… 主相（スピネルフェライト相）
１４… 副相（低α相）
１４ａ… 第１の副相（Ｚｎ２ＳｉＯ４相）
１４ｂ… 第２の副相（ＳｉＯ２相）
１６… 粒界相（Ｂｉ２Ｏ３相、ＳｉＯ２相）
３０，３０ａ… コイル導体
Claims (4)
- 主成分と副成分とを有するフェライト組成物であって、
前記主成分が、Ｆｅ２Ｏ３換算で４４．０〜５０．０モル％（４４．０モル％を含まない）のＦｅの化合物、ＣｕＯ換算で５．５〜１４．０モル％のＣｕの化合物、ＺｎＯ換算で４．０〜３９．０モル％のＺｎの化合物、および、残部でありＮｉＯ換算で４０．０モル％未満であるＮｉの化合物で構成されており、
前記主成分１００重量部に対して、前記副成分として、Ｓｉの化合物をＳｉＯ２換算で３．０〜１３．０重量部（３．０重量部を含まない）、Ｃｏの化合物をＣｏ３Ｏ４換算で２．０〜１０．０重量部（２．０重量部を含まない）、Ｂｉの化合物をＢｉ２Ｏ３換算で０．２５〜５．００重量部、含有し、
（前記Ｃｏの化合物のＣｏ３Ｏ４換算での含有量）／（前記Ｓｉの化合物のＳｉＯ２換算での含有量）が重量比で０．４〜２．９であることを特徴とするフェライト組成物。 - スピネルフェライトからなる主相と、Ｚｎ２ＳｉＯ４相からなる第１の副相と、ＳｉＯ２相からなる粒界相と、からなる請求項１に記載のフェライト組成物。
- さらに、ＳｉＯ２相からなる第２の副相を有する請求項２に記載のフェライト組成物。
- コイル導体およびセラミック層が積層されて構成される積層電子部品であって、
前記セラミック層が請求項１〜３のいずれかに記載のフェライト組成物で構成されている積層電子部品。