JP2012503343A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2012503343A5 JP2012503343A5 JP2011528274A JP2011528274A JP2012503343A5 JP 2012503343 A5 JP2012503343 A5 JP 2012503343A5 JP 2011528274 A JP2011528274 A JP 2011528274A JP 2011528274 A JP2011528274 A JP 2011528274A JP 2012503343 A5 JP2012503343 A5 JP 2012503343A5
- Authority
- JP
- Japan
- Prior art keywords
- capacitor
- valve metal
- anode
- agglomerate powder
- sintered body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
本発明の対象は、バルブメタル及び/又はバルブメタル亜酸化物のアノード体であり、好ましくはニオブ、タンタル、及びニオブ亜酸化物のアノード体、さらに好ましくは、式NbOx(ただし、0.7<x<1.3、特に好ましくは、0.8<x<1.1)のニオブ亜酸化物アノード体であり、見かけ密度が理論密度の88%超、好適には90%超、とりわけ好ましくは理論密度の92%超のものである。本発明によれば、最大94%の見かけ密度、及び(密な)アノード材料の理論密度を超える見かけ密度が達成可能である。本発明によるアノード体の場合、閉鎖孔の累積体積は、(密な)アノード材料の体積の12%未満、好適には10%未満、とりわけ好適には8%未満である。本発明の意味合いにおいてバルブメタルとは、ニオブ、タンタル、及びチタンの群の金属と理解される。
Claims (25)
- 見かけ密度が理論密度の88%超である、バルブメタル及び/又はバルブメタル亜酸化物のコンデンサアノード焼結体であって、前記バルブメタルが、Ti、Zr、Hf、V、Mo、W、Al、又はその混合物若しくは合金である、前記コンデンサアノード焼結体。
- 見かけ密度が理論密度の90%超、好適には92%超である、請求項1に記載のアノード体。
- 見かけ密度が理論密度の92%超である、タンタル金属のコンデンサアノード焼結体。
- 見かけ密度が理論密度の88%超である、ニオブ亜酸化物のコンデンサアノード焼結体。
- 組成が
NbOx
[式中、0.7<x<1.3]
である、請求項4に記載のアノード体。 - BET比表面積(m2/g)×滑り係数ηの積が0.33〜0.75、好適には0.45〜0.58である、ニオブ亜酸化物アグロメレート粉末。
- 圧縮係数が0.07超である、ニオブ亜酸化物アグロメレート粉末。
- BET比表面積(m2/g)×滑り係数ηの積が0.62〜0.95、好適には0.65〜0.86である、タンタルアグロメレート粉末。
- 圧縮係数が0.08超である、タンタルアグロメレート粉末。
- BET比表面積(m2/g)×滑り係数ηの積が0.38〜0.8、好適には0.42〜0.6である、ニオブアグロメレート粉末。
- 圧縮係数が0.08超である、ニオブアグロメレート粉末。
- プレス密度2.8g/cm3にプレスし、1340℃以上の温度で20分間の焼結後に、見かけ密度が88%超、好適には90%超、とりわけ好適には92%超のアノード体が製造可能な、ニオブ亜酸化物アグロメレート粉末を含有する、コンデンサアノード焼結体。
- プレス密度5g/cm3超にプレスし、1250℃以上の温度で20分間の焼結後に、見かけ密度が92%超のアノード体が製造可能な、タンタルアグロメレート粉末を含有する、コンデンサアノード焼結体。
- コンデンサアノード焼結体の製造に適したバルブメタル及び/又はバルブメタル酸化物のアグロメレート粉末の製造方法において、
アグロメレート粉末の前駆体粒子を微粒子状細孔形成剤と混合し、圧縮によって高多孔性の接着結合された前駆体粒子のアグロメレートを生成し、細孔形成剤を熱により除去し、接着結合されたアグロメレートを、焼結橋形成に充分な温度及び所要時間の温度処理に供し、この少なくとも部分的に焼結されたアグロメレートを、バルブメタル及び/又はバルブメタル亜酸化物のアグロメレート粉末にさらに加工することを特徴とする、前記製造方法。 - 細孔形成剤として、蒸発温度、昇華温度、又は分解温度が600℃未満のアンモニウム塩を使用することを特徴とする、請求項14に記載の方法。
- 細孔形成剤として、微粒子状の塩化アンモニウム及び/又はシュウ酸アンモニウムを使用することを特徴とする、請求項15に記載の方法。
- 細孔形成剤を、前駆体化合物の体積に対して10〜90体積%の量で使用することを特徴とする、請求項14から16のいずれか1項に記載の方法。
- コンデンサアノード焼結体の製造に適したバルブメタル及び/又はバルブメタル亜酸化物のアグロメレート粉末の製造方法において、
バルブメタルの、又はニオブ及び/又はタンタルの酸化物、水酸化物、及び水和五酸化物から成る群から選択されるアグロメレート粉末の前駆体粒子を、過酸化水素又は二酸化炭素含有水の中でスラリー化し、乾燥によって酸素ガス若しくは二酸化炭素を放出させながら水を除去し、その結果、高多孔性の接着結合された前駆体粒子のアグロメレートが生成され、この接着結合されたアグロメレートを、焼結橋形成に充分な温度及び所要時間の温度処理に供し、この少なくとも部分的に焼結されたアグロメレートを、バルブメタル及び/又はバルブメタル酸化物のアグロメレート粉末にさらに加工することを特徴とする、前記製造方法。 - 前駆体粒子が、80m2/g超、好適には100m2/g超の比表面積を有することを特徴とする、請求項14から18のいずれか1項に記載の方法。
- 請求項1から5までのいずれか1項に記載のコンデンサアノード焼結体の化成により製造される、コンデンサアノード。
- 請求項6から11までのいずれか1項に記載のアグロメレート粉末のプレスと焼結により製造される、コンデンサアノード。
- 請求項1から5までのいずれか1項に記載のバルブメタル及び/又はバルブメタル亜酸化物のコンデンサアノード焼結体を含む、コンデンサ。
- 請求項20に記載のコンデンサアノードを含む、コンデンサ。
- 請求項21に記載のコンデンサアノードを含む、コンデンサ。
- 電気的装置における、請求項22から24までのいずれか1項に記載のコンデンサの使用方法。