JP2010528959A - ガラス組成物、それを用いた光学部材及び光学機器 - Google Patents
ガラス組成物、それを用いた光学部材及び光学機器 Download PDFInfo
- Publication number
- JP2010528959A JP2010528959A JP2009552228A JP2009552228A JP2010528959A JP 2010528959 A JP2010528959 A JP 2010528959A JP 2009552228 A JP2009552228 A JP 2009552228A JP 2009552228 A JP2009552228 A JP 2009552228A JP 2010528959 A JP2010528959 A JP 2010528959A
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass composition
- content ratio
- range
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(A)TeO2の含有比率が50〜95モル%の範囲にあること、
(B)B2O3の含有比率が1〜33モル%の範囲にあること、
(C)ZnOの含有比率が1〜37モル%の範囲にあること、
(D)Bi2O3の含有比率が1〜18モル%の範囲にあること、
(E)P2O5の含有比率が0〜15モル%の範囲にあること、
(F)R2O(式中、RはLi、Na及びKの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(G)MO(式中、MはMg、Ca、Sr及びBaの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(H)TiO2の含有比率が0〜13モル%の範囲にあること、
(I)Nb2O5の含有比率が0〜10モル%の範囲にあること、
(J)Ta2O5の含有比率が0〜13モル%の範囲にあること、
(K)L2O3(式中、Lはイットリウム及びランタノイドの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜11モル%の範囲にあること、
(L)上記(E)〜(K)に示すP2O5、R2O、MO、TiO2、Nb2O5、Ta2O5及びL2O3の総量の含有比率が0〜15モル%の範囲にあること;
に示す条件を満たす、ガラス組成物。
Description
(A)TeO2の含有比率が50〜95モル%の範囲にあること、
(B)B2O3の含有比率が1〜33モル%の範囲にあること、
(C)ZnOの含有比率が1〜37モル%の範囲にあること、
(D)Bi2O3の含有比率が1〜18モル%の範囲にあること、
(E)P2O5の含有比率が0〜15モル%の範囲にあること、
(F)R2O(式中、RはLi、Na及びKの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(G)MO(式中、MはMg、Ca、Sr及びBaの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(H)TiO2の含有比率が0〜13モル%の範囲にあること、
(I)Nb2O5の含有比率が0〜10モル%の範囲にあること、
(J)Ta2O5の含有比率が0〜13モル%の範囲にあること、
(K)L2O3(式中、Lはイットリウム及びランタノイドの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜11モル%の範囲にあること、
(L)上記(E)〜(K)に示すP2O5、R2O、MO、TiO2、Nb2O5、Ta2O5及びL2O3の総量の含有比率が0〜15モル%の範囲にあること;
に示す条件を満たす、ものである。
表1〜3に示す組成のガラス組成物をそれぞれ製造した。すなわち、先ず、それぞれ表1〜3に示す化合物(原料)を、それぞれ表1〜3に示す組成比で白金るつぼに入れ、800〜950℃の温度条件で10分加熱して熔解させた後、前記温度条件下で攪拌、清澄し、各化合物が均一に分散したガラス融液を得た。その後、前記ガラス融液を、温度300〜350℃に加熱した型(縦40mm、横40mm、厚み20mm)に鋳込んだ後、20時間かけて室温(25℃)まで徐冷することによって、本発明のガラス組成物をそれぞれ得た。
表4〜5に示す化合物(原料)を用い、表4〜5に示す組成比となるようにした以外は実施例1と同様にして、比較のためのガラス組成物をそれぞれ得た。
〈熔解安定性の測定〉
各実施例及び各比較例において、製造時のガラス融液中に前記化合物(原料)の熔け残りがあるかを目視にて観察するとともに、冷却後のガラス組成物中に結晶相が残っているかを目視にて観察して、各実施例及び各比較例で得られたガラス組成物の熔解安定性を評価した。なお、熔解安定性の評価では、ガラス融液中に熔け残りがなく且つガラス組成物中に結晶相が残らなかったものを良好であると判定し、前記熔け残り又は前記結晶相が残るものを熔解安定性が不良であると判定した。結果を表1〜5に示す。
各実施例及び各比較例で得られたガラス組成物の屈折率及びアッベ数を測定した。すなわち、先ず、各実施例及び各比較例で得られたガラス組成物を用いて、底面の一辺の長さが40mm、高さが15mmの正三角柱(プリズム)形状の試料をそれぞれ調製した。次に、各試料に対して株式会社ニコン製のスペクトメータを用いて最小偏角法を採用して、各実施例及び各比較例で得られたガラス組成物の屈折率を求めた。また、アッベ数は、このようにして測定された屈折率の値から計算して求めた。得られた結果を表1〜5に示す。なお、表1〜5に示す屈折率は、波長587.562nmの光(d線)に対する屈折率ndである。
各実施例及び各比較例で得られたガラス組成物の可視光透過率を測定した。すなわち、先ず、各実施例及び各比較例で得られたガラス組成物を用いて、縦30mm、横20mm、厚さが7mmの試料及び、縦30mm、横20mm、厚さ2mmの試料を調製した。次に、前記試料と、透過率測定機器(バリアン社製の商品名「CARY500」)とを用いて、可視光透過率を測定した。なお、透過率の評価に際しては、波長700〜300nmの範囲の光に対する透過率を測定し、波長450nmの光の透過率が75%以上のものを良好と判定し、75%未満となるものを不良と判定した。このような透過率の判定結果及び波長450nmの光に対する各ガラス組成物の透過率(%)の値を表1〜5に示す。また、実施例1、4、9、11及び14で得られたガラス組成物並びに比較例14及び15で得られたガラス組成物の可視光透過率のグラフを図1に示す。
Claims (7)
- 下記(A)〜(L):
(A)TeO2の含有比率が50〜95モル%の範囲にあること、
(B)B2O3の含有比率が1〜33モル%の範囲にあること、
(C)ZnOの含有比率が1〜37モル%の範囲にあること、
(D)Bi2O3の含有比率が1〜18モル%の範囲にあること、
(E)P2O5の含有比率が0〜15モル%の範囲にあること、
(F)R2O(式中、RはLi、Na及びKの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(G)MO(式中、MはMg、Ca、Sr及びBaの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜13モル%の範囲にあること、
(H)TiO2の含有比率が0〜13モル%の範囲にあること、
(I)Nb2O5の含有比率が0〜10モル%の範囲にあること、
(J)Ta2O5の含有比率が0〜13モル%の範囲にあること、
(K)L2O3(式中、Lはイットリウム及びランタノイドの中から選択される少なくとも1種の元素を示す。)の含有比率が0〜11モル%の範囲にあること、
(L)上記(E)〜(K)に示すP2O5、R2O、MO、TiO2、Nb2O5、Ta2O5及びL2O3の総量の含有比率が0〜15モル%の範囲にあること;
に示す条件を満たす、ガラス組成物。 - 前記TeO2の含有比率が75〜95モル%である、請求項1に記載のガラス組成物。
- 前記B2O3の含有比率が3〜15モル%である、請求項1に記載のガラス組成物。
- 前記ZnOの含有比率が3〜15モル%である、請求項1に記載のガラス組成物。
- 前記Bi2O3の含有比率が1〜10モル%である、請求項1に記載のガラス組成物。
- 請求項1〜5のうちのいずれか一項に記載のガラス組成物からなる、光学部材。
- 請求項1〜5のうちのいずれか一項に記載のガラス組成物からなる光学部材を備える、光学機器。