JP2010000238A - ゴルフボール - Google Patents
ゴルフボール Download PDFInfo
- Publication number
- JP2010000238A JP2010000238A JP2008161921A JP2008161921A JP2010000238A JP 2010000238 A JP2010000238 A JP 2010000238A JP 2008161921 A JP2008161921 A JP 2008161921A JP 2008161921 A JP2008161921 A JP 2008161921A JP 2010000238 A JP2010000238 A JP 2010000238A
- Authority
- JP
- Japan
- Prior art keywords
- molecular weight
- polyurethane
- polyol
- golf ball
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】コアと、前記コアを被覆するカバーとを有するゴルフボールであって、前記カバーが、ポリウレタンを樹脂成分として含有し、前記ポリウレタンが、ポリウレタンを構成する高分子量ポリオール成分として、分子量分布に多峰性を有する多峰性ポリオールを用いて得られたものである。
【選択図】図2
Description
y:濃度分率
x:分子量
装置:東ソー社製、HLC−8120GPC
溶離液:THF
温度:40℃
カラム:TSKgel SuperHM−M(東ソー社製)
ポリオール濃度:0.2質量%(ポリオール/(ポリオール+THF))
サンプル注入量:5μl
流速:0.5ml/min
分子量標準:ポリスチレン(東ソー社製、PStQuick Kit−H)
(1)センター硬度(ショアD硬度)
ASTM−D2240に規定するスプリング式硬度計ショアD型を備えた高分子計器社製自動ゴム硬度計P1型を用いて、センターを半球状に切断し、切断面の中心において測定したショアD硬度をコア中心硬度とした。
中間層用組成物を用いて、熱プレス成形により、厚み約2mmのシートを作製し、23℃で2週間保存した。このシートを、測定基板などの影響が出ないように、3枚以上重ねた状態で、ASTM−D2240に規定するスプリング式硬度計ショアD型を備えた高分子計器社製自動ゴム硬度計P1型を用いて測定した。
ポリオール成分について、下記の測定条件にてゲルパーミエーションクロマトグラフィ測定を行った。
測定条件
装置:東ソー社製、HLC−8120GPC
溶離液:THF
温度:40℃
カラム:TSKgel SuperHM−M(東ソー社製)
ポリオール濃度:0.2質量%(ポリオール/(ポリオール+THF))
サンプル注入量:5μl
流速:0.5ml/min
分子量標準:ポリスチレン(東ソー社製、PStQuick Kit−H)
ゴルフラボラトリー社製のスイングロボットに市販のサンドウエッジを取り付け、ヘッドスピードを36m/秒でボールの2箇所を各1回打撃し、各打撃部を観察して8段階で評価し、2箇所の平均値を求めた。なお、点数が低いほど耐擦過傷性が高いものであることを示している。
評価基準
0点:打撃痕が判別できない。
1点:点(最大3mm未満)でめくれがある。
2点:点(最大3mm以上)でめくれがある。
3点:線(最大5mm以上)でめくれがある。
4点:線(最大5mm以上)でしっかりとめくれがある。
5点:線(最大5mm以上)で深く、広くめくれがある。
6点:深く、広くめくれて、面になりかけている。
7点:面で削れている。
ゴルフラボラトリー社製スイングロボットに、アプローチウェッジ(SRIスポーツ社製、SRIXON I−302)を取り付け、ヘッドスピード21m/秒でゴルフボールを打撃し、打撃されたゴルフボールを連続写真撮影することによってスピン速度(rpm)を測定した。測定は、各ゴルフボールについて10回ずつ行い、その平均値をスピン速度とした。
表3に示す配合となるように、ポリイソシアネート成分としての80℃に加熱した4,4’−ジシクロヘキシルメタンジイソシアネート(住化バイエルウレタン社製、「デスモジュール(登録商標)W」)に、高分子量ポリオール成分としての80℃に加熱したPTMG2000(保土谷化学工業社製、「PTG−2000SN」(数平均分子量:2000))、および/または、80℃に加熱したPTMG1000(保土谷化学工業社製、「PTG−1000SN」(数平均分子量:1000))を投入した。そして、これらの全質量100質量部に対して、0.005質量部のジブチルチンジラウリレートを添加して、窒素気流下にて、80℃で2時間撹拌を行った。
(1)センターの作製
表1に示す配合のセンター用ゴム組成物を混練し、半球状キャビティを有する上下金型内で、170℃で15分間加熱プレスすることにより直径38.5mm、質量34.9gの球状のセンターを得た。
アクリル酸亜鉛:日本蒸溜工業製、「ZNDA−90S」
酸化亜鉛:東邦亜鉛製、「銀嶺(登録商標)R」
ジクミルパーオキサイド:日本油脂製、「パークミル(登録商標)D」
ジフェニルジスルフィド:住友精化製
次に、表2および表3に示した配合の中間層材料およびカバー用組成物を、二軸混練型押出機によりミキシングして、ペレット状の中間層材料およびカバー用組成物を調製した。押出は、スクリュー径45mm、スクリュー回転数200rpm、スクリューL/D=35で行った。配合物は、押出機のダイの位置で150〜230℃に加熱された。
ハイミランAM7329:三井デュポンポリケミカル社製、亜鉛イオン中和エチレン−メタクリル酸共重合体系アイオノマー樹脂
ハーフシェルの圧縮成形は、前述のようにして得たペレット状のカバー用組成物をハーフシェル成形用金型の下型の凹部ごとに1つずつ投入し、加圧してハーフシェルを成形した。圧縮成形は、成形温度160℃、成形時間5分、成形圧力2.94MPaの条件で行った。
(2)で得られたコアを(3)で得られた2枚のハーフシェルで同心円状に被覆して、圧縮成形によりカバー(厚み0.5mm)を成形した。圧縮成形は、成形温度150℃、成形時間2分、成形圧力9.8MPaの条件で行った。
PTMG2000:保土谷化学工業社製、PTG−2000SN
Claims (5)
- コアと、前記コアを被覆するカバーとを有するゴルフボールであって、
前記カバーが、ポリウレタンを樹脂成分として含有し、
前記ポリウレタンが、ポリウレタンを構成する高分子量ポリオール成分として、分子量分布に多峰性を有する多峰性ポリオールを用いて得られたものであることを特徴とするゴルフボール。 - 前記多峰性ポリオールが、分子量分布に二峰性を有する二峰性ポリテトラメチレンエーテルグリコールである請求項1に記載のゴルフボール。
- 前記二峰性ポリテトラメチレンエーテルグリコールが、数平均分子量が900〜1100であるポリテトラメチレンエーテルグリコール(PTMG1000)と、数平均分子量が1800〜2200であるポリテトラメチレンエーテルグリコール(PTMG2000)とを、モル比(PTMG1000/PTMG2000)2/8〜7/3で混合したものである請求項2に記載のゴルフボール。
- 前記ポリウレタンが、ポリウレタンを構成するポリイソシアネート成分として、4,4’−ジシクロヘキシルメタンジイソシアネートを含有するものである請求項1〜3のいずれか一項に記載のゴルフボール。
- 前記ポリウレタンが、ポリウレタンを構成する鎖長延長剤成分として、1,4−ブタンジオールを含有するものである請求項1〜4のいずれか一項に記載のゴルフボール。