JP2008080673A - 容器用積層シート - Google Patents
容器用積層シート Download PDFInfo
- Publication number
- JP2008080673A JP2008080673A JP2006263936A JP2006263936A JP2008080673A JP 2008080673 A JP2008080673 A JP 2008080673A JP 2006263936 A JP2006263936 A JP 2006263936A JP 2006263936 A JP2006263936 A JP 2006263936A JP 2008080673 A JP2008080673 A JP 2008080673A
- Authority
- JP
- Japan
- Prior art keywords
- styrene
- resin
- weight
- laminated sheet
- thermoplastic elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】スチレン系樹脂(A1)及びスチレン系熱可塑性エラストマー(A2)で構成されたコア層(A)の少なくとも一方の面に、オレフィン系樹脂(B1)及びスチレン系熱可塑性エラストマー(B2)で構成されたスキン層(B)が形成された積層シートであって、スチレン系熱可塑性エラストマー(A2)の割合が、スチレン系樹脂(A1)100重量部に対して1〜15重量部程度であり、かつスチレン系熱可塑性エラストマー(B2)の割合が、オレフィン系樹脂(B1)100重量部に対して5〜30重量部程度である積層シートを調製する。
【選択図】なし
Description
・食品に含まれる油により容器の材質が侵されること
・容器が蓋で嵌合され、冷却されると、気圧差により容器に歪みが生じること
・これらの現象が合わさって、容器底に亀裂が入り、食品に含まれる液体(汁など)が外部に漏れ出すこと
である。
0<[St−TPE]B−[St−TPE]A<15
で表される関係を充足していてもよい。前記スチレン系熱可塑性エラストマー(A2)及びスチレン系熱可塑性エラストマー(B2)は、それぞれ、テトラヒドロフランによる不溶分の割合が3重量%以下であってもよい。前記スチレン系熱可塑性エラストマー(A2)及びスチレン系熱可塑性エラストマー(B2)は、それぞれ、スチレン−ジエン系ブロック共重合体であってもよい。前記スチレン系樹脂(A1)は、ポリスチレン系樹脂とゴム含有スチレン系樹脂とで構成され、かつ両者の割合(重量比)が、ポリスチレン系樹脂/ゴム含有スチレン系樹脂=20/80〜80/20程度であってもよい。本発明の積層シートは、総厚みが0.25〜0.7mm程度であり、かつコア層(A)の厚みとスキン層(B)の厚みとの比率が、スキン層(B)/コア層(A)=1/10〜1/2.5程度であってもよい。本発明の積層シートは、密着力も強く、コア層(A)とスキン層(B)との層間強度は1.8N/15mm以上であってもよい。また、本発明の積層シートは、コア層(A)の両面にスキン層(B)が形成されていてもよい。さらに、スキン層(A)の上に、溶融ラミネートなどによって、さらにオレフィン系樹脂(特にポリプロピレン系樹脂)で構成されたカバー層が積層されていてもよい。このカバー層厚みは、15〜50μm程度であってもよい。
(A1)スチレン系樹脂
スチレン系樹脂(A1)としては、例えば、芳香族ビニル単量体を主構成単位として形成される単独又は共重合体が挙げられる。スチレン系樹脂を形成するための芳香族ビニル単量体としては、例えば、スチレン、アルキル置換スチレン(例えば、ビニルトルエン、ビニルキシレン、p−エチルスチレン、p−イソプロピルスチレン、ブチルスチレン、p−t−ブチルスチレンなど)、ハロゲン置換スチレン(例えば、クロロスチレン、ブロモスチレンなど)、α位にアルキル基が置換したα−アルキル置換スチレン(例えば、α−メチルスチレンなど)などが例示できる。これらの芳香族ビニル単量体は、単独で又は二種以上組み合わせて使用できる。これらの単量体のうち、通常、スチレン、ビニルトルエン、α−メチルスチレンなど、特にスチレンが使用される。
以下に示す溶液A〜Cを調製する。
B溶液:10%ヨウ化カリウム水溶液(ヨウ化カリウム100gを蒸留水900gに溶解させる)
C溶液:チオ硫酸ナトリウム水溶液(チオ硫酸ナトリウム45gを精秤し、これを蒸留水に溶解させ1000mlの溶液とする。前記溶液に0.3gの炭酸水素ナトリウムを添加し一晩放置する)
(2)チオ硫酸ナトリウム水溶液の標定
300mlの三角フラスコに、精秤した臭素酸カリウム0.1gと、100mlの蒸留水と、100mlのB溶液とを加え、混合溶液とする。この溶液に、10mlの濃塩酸を添加し、3分間放置する。この溶液をチオ硫酸ナトリウム水溶液(C溶液)で滴定し、水溶液が無色になったところで滴定を終了する。下記式により、C溶液の規定度(N)を算出する。
(3)ゴム含有スチレン系樹脂の溶解
300mlの三角フラスコに、精秤したゴム含有スチレン系樹脂1gと、75mlのテトラヒドロフラン(THF)とを加え、一晩放置し、ゴム含有スチレン系樹脂を溶解させる。
ゴム含有スチレン系樹脂のTHF溶液(前記(3))に、10mlのA溶液を添加し、15分間暗所に放置し、さらに100mlのB溶液を添加し、混合溶液(ゴム含有スチレン系樹脂溶液)とする。この溶液を、チオ硫酸ナトリウム水溶液(C溶液)で滴定し、水溶液が無色になったところで滴定を終了する。ブランクとして、ゴム含有スチレン系樹脂を含まない溶液(ブランク溶液)でも同様の操作を行う。下記式よりゴム含有量(RC)を算出する。
(式中、niは粒子径Diを有するゴム状重合体粒子の個数を示す)
また、ゴム状重合体のグラフト率は、5〜150%、好ましくは10〜150%程度である。
スチレン系熱可塑性エラストマー(A2)は、芳香族ビニル単位(例えば、スチレン系樹脂の項で例示された芳香族ビニルなど)と、ジエン系単位(例えば、ブタジエン、イソプレンなど)とで構成されており、通常、スチレン−ジエン系ブロック共重合体である。スチレン−ジエン系ブロック共重合体としては、例えば、スチレン−ブタジエン−スチレン共重合体(SBS)などのスチレン−ブタジエン共重合体、水添スチレン−ブタジエン−スチレン共重合体(SEBS)、スチレン−イソプレン共重合体、水添スチレン−イソプレン共重合体(SEP)、スチレン−イソプレン−スチレン共重合体(SIS)、水添スチレン−イソプレン−スチレン共重合体(SEPS)などが例示できる。これらのスチレン−ジエン系ブロック共重合体のうち、耐衝撃性の点から、水添されていないスチレン−ジエン系共重合体、特に、スチレン−ブタジエンブロック共重合体が好ましい。ブロック共重合体において、末端ブロックは、スチレン系ブロック又はジエン系ブロックのいずれで構成してもよい。
(1)50mLサンプル瓶に試料ペレット約1gを入れ、重量(WT1)を記録しておく。
(2)瓶に蓋をせず、恒温槽200℃下にて40分間放置する。
(3)THFを40mL入れ、シェーカーにて160rpmで約40分間攪拌する。
(4)スパチュラで掻き混ぜ、未溶分を溶解させる。
(5)予め重量(WT2)を測定した400メッシュ金網を用いて、不溶分を濾別する。
(6)濾別した金網を恒温槽60℃下にて1時間放置し、THFを蒸発させる。
(7)THF蒸発後の濾別した金網の重量(WT3)を測定し、WT3−WT2を算出することで、不溶分の重量(WT4)を測定する。
(8)(WT4/WT1)×100を算出し、THF不溶分発生率と規定する。
オレフィン系樹脂(A3)は、例えば、ポリエチレン系樹脂[例えば、低、中又は高密度ポリエチレン、直鎖状低密度ポリエチレン、エチレン−プロピレン共重合体、エチレン−ブテン−1共重合体、エチレン−プロピレン−ブテン−1共重合体、エチレン−(4−メチルペンテン−1)共重合体、エチレン−酢酸ビニル共重合体、エチレン−(メタ)アクリル酸共重合体又はそのアイオノマー、エチレン−アクリル酸エチル共重合体などのエチレン−(メタ)アクリレート共重合体など]やポリ(メチルペンテン−1)系樹脂などであってもよいが、耐熱性、成形性、耐油性などの点から、ポリプロピレン系樹脂が好ましい。
オレフィン系樹脂(B1)としては、前記コア層(A)の項で例示されたオレフィン系樹脂が例示できる。オレフィン系樹脂(B1)としても、前記コア層(A)のオレフィン系樹脂(A3)と同様の理由で、ポリプロピレンホモポリマー、ポリプロピレンブロック共重合体などのポリプロピレン系樹脂(特にリプロピレンブロック共重合体)が好ましい。ポリプロピレン系樹脂の融点及びMFRについてもコア層(A)のポリプロピレン系樹脂と同様である。
0<[St−TPE]B−[St−TPE]A<15
で表される関係を充足するのが好ましい。特に、両者の差([St−TPE]B−[St−TPE]A)は3〜14(例えば、5〜14,好ましくは7〜13)程度の範囲にあってもよい。両層に含まれるスチレン系熱可塑性エラストマーの割合の関係がこの範囲にあると、シートや容器などの成形品の外観が向上する。
本発明の積層シートは、前記コア層(A)の少なくとも一方の面に前記スキン層(B)が形成されているが、耐熱性及び耐油性の点から、前記コア層(A)の両面に前記スキン層(B)が形成されているのが好ましい。
(1)シート幅方向(TD方向)中央部において、長手がTD方向となるように、150mmX5mmのサンプルを作成する。
(2)サンプルの長手方向が垂直となるように、サンプルの長手方向の端部を固定し、サンプル長手中央部の両断面を50mmにわたって、油(日清オイリオグループ(株)製、日清サラダ油)を塗布する。
(3)油を塗布した直後に、15.3MPaの荷重となるように、サンプルの長手方向の他端に錘をつける。
(4)錘をつけてからサンプルが破断するまでの時間(単位:秒)を測定する。
(5)このような試験を温度20℃で行い、N=5の平均値を算出する。
本発明の積層シートは、成形性に優れるため、圧空成形(押出圧空成形、熱板圧空成形、真空圧空成形など)、自由吹込成形、真空成形、折り曲げ加工、マッチドモールド成形、熱板成形などの慣用の熱成形などで、簡便に二次成形することができる。
(スチレン系樹脂)
GP:一般用ポリスチレン(東洋スチレン(株)製、商品名「トーヨースチロールGP HRM63C」)
HI:耐衝撃性ポリスチレン(東洋スチレン(株)製、商品名「トーヨースチロールHI E640」)
(ポリプロピレン系樹脂:PP)
PP1:ポリプロピレンブロック共重合体((株)プライムポリマー製、商品名「プライムポリプロ F707V、MFR:6.5、融点:161℃)
PP2:ポリプロピレンブロック共重合体(サンアロマー(株)製、商品名「PB370A」、MFR:1.3、融点:161℃)
PP3:ポリプロピレンブロック共重合体(サンアロマー(株)製、商品名「PM870A」、MFR:17、融点:161℃)
PP4:ポリプロピレンホモポリマー(サンアロマー(株)製、商品名「PM600A」、MFR:7.5 融点:163℃)
PP5:ポリプロピレンランダム共重合体(サンアロマー(株)製、商品名「PF621S」、MFR:6.5、融点:146℃)
PP6:ポリプロピレンランダム共重合体(サンアロマー(株)製、商品名「PC540R」、MFR:5、融点:132℃)
(スチレン系熱可塑性エラストマー:St−TPE)
SBS1:SBSブロック共重合体(旭化成ケミカルズ(株)製、商品名「タフプレン126」、ゴム含有量:60重量%、THF不溶分発生率:0.07重量%)
SBS2:SBSブロック共重合体(JSR(株)製、商品名「TR2003」、ゴム含有量:57重量%、THF不溶分発生率:6.3重量%)
SEBS:スチレン−エチレン−ブチレン−スチレンブロック共重合体(旭化成ケミカルズ(株)製、商品名「タフテックH1041」、エチレン−ブチレン単位含有量:70重量%)
(カバー層)
PPフィルム:東洋紡績(株)製、商品名:「パイレン」フィルム−CT P1111、原料PP:プロピレンホモポリマー)。
実施例及び比較例で得られたシートについて、前述の方法で評価した。
実施例及び比較例で得られたシートを用いて、単発真空成形機((株)浅野研究所製)によって、縦140mm×横105mm×深さ20mmの直方体形状であり、フランジ部分(5mm幅)及び蓋部分を有するトレーを成形した。次に、空気攪拌付き恒温槽のストレート板上にトレーを置いて、125℃下3分間放置した。トレーを取り出した後、変形度合いを観察し、以下基準で評価した。
4:フランジのみがわずかに変形する
3:フランジが変形し、トレー全体もわずかに変形する
2:トレー全体が変形する
1:トレー形状が大きく崩れる。
実施例及び比較例で得られた各シートを用いて、JIS K 7113に準じた2号ダンベルを打抜き、サンプルシートを得た。このサンプルシートを用いて、テンシロン((株)東洋精機製作所製、商品名「RTA520」)により、試験スピード50mm/分で引張弾性率を測定した。測定した値は、シート流れ方向(MD方向)及び幅方向(TD方向)の平均値で示した。
実施例及び比較例で得られた各シートをJIS K 7211に準拠してデュポン衝撃強度を測定した。
実施例及び比較例で得られた各シートを用いて、シート中央部で長手がMD方向となるように、100mm×15mmのサンプルを作成した。テンシロン((株)東洋精機製作所製、商品名「RTA520」)により、試験スピード50mm/分でMD方向にスキン層(B)(スキン層(B)/コア層(A)/スキン層(B)の3層タイプの場合は、キャストロール側のスキン層(B))を角度180°で剥離させ、その強度を測定した。
実施例及び比較例で得られた各シートを目視で観察し、以下の評価基準で評価した。
4:凝視すれば、層間乱れがわずかに見られる
3:やや層間乱れがある
2:一目で層間乱れが確認できる
1:層間乱れが激しい。
実施例及び比較例で得られた各シートを用いて、単発真空成形機((株)浅野研究所製)によって、開口部径90mm、底部径80mm、高さ50mmのカップ状容器を成形し、容器と底面のコーナー(底面と側面との接する部分)との外観を目視観察し、以下の基準で評価した。
4:ほぼ均一に伸びて、均一な厚みに成形されている
3:底面またはコーナーの一部にややムラがある
2:底面またはコーナーの一部にムラがある
1:底面またはコーナーの一部に薄皮となっている部分がある。
実施例及び比較例で得られた各シートを用いて、耐熱性試験と同じ形状のトレーに成形した後、自動パンチャー((株)浅野研究所製)を用いて、自動パンチャー用打ち抜き刃で打ち抜いた。打ち抜き断面を目視で観察しヒゲ発生の有無を評価した。各トレーについて100枚打ち抜き、以下の基準で評価した。
4:ヒゲの発生したトレーの枚数が3〜7枚
3:ヒゲの発生したトレーの枚数が8〜16枚
2:ヒゲの発生したトレーの枚数が17〜33枚
1:ヒゲの発生したトレーの枚数が34枚以上。
実施例1、31及び32で得られた各シートを目視で観察し、シート10000m当たりの異物(ゲル)の発生率(個/10000m)を目視で測定した。
コア層(A)用材料として、表1〜4に示す組成の成分をブレンドし、フィードブロック方式の多層押出機(直径Φ90mm、直径Φ65mm)のΦ90mm押出機に供給した。さらに、スキン層(B)用材料として、表1〜4に示す組成の成分をブレンドし、Φ65mm押出機に供給した。それぞれの押出機内において、押出温度200℃で溶融混練した。この溶融混練物をT−ダイよりシート状に押出し、シート表面を80℃まで急冷し、引き取り速度を調整することにより積層シートを得た。なお、実施例18については、コア層(A)の一方の面にスキン層(B)が積層されるように調整した。さらに、実施例27の積層シートについては、0.03mmのPPフィルムをT−ダイより押出された溶融シートと冷却ロールとの間に挟み込む方法、いわゆる熱ラミネート法により、スキン層(B)の上に、さらにカバー層を積層した。得られたシートの評価結果を表1〜4に示す。
表4に示す組成の成分をブレンドし、押出機(直径Φ90mm)に供給し、押出温度200℃で溶融混練した。この溶融混練物をT−ダイよりシート状に押出し、シート表面を80℃まで急冷し、引き取り速度を調整することにより単層シートを得た。また、比較例22のシートについては、0.03mmのPPフィルムをT−ダイより押出された溶融シートと冷却ロールとの間に挟み込む方法、いわゆる熱ラミネート法により、さらにカバー層を積層した。得られたシートの評価結果を表4に示す。
Claims (15)
- スチレン系樹脂(A1)及びスチレン系熱可塑性エラストマー(A2)で構成されたコア層(A)の少なくとも一方の面に、オレフィン系樹脂(B1)、スチレン系熱可塑性エラストマー(B2)及びスチレン系樹脂(B3)で構成されたスキン層(B)が形成された積層シートであって、スチレン系熱可塑性エラストマー(A2)の割合が、スチレン系樹脂(A1)100重量部に対して1〜15重量部であり、かつスチレン系熱可塑性エラストマー(B2)の割合が、オレフィン系樹脂(B1)100重量部に対して5〜30重量部である積層シート。
- コア層(A)が、さらに、スチレン系樹脂(A1)100重量部に対して、0.001〜10重量部のオレフィン系樹脂(A3)を含む請求項1記載の積層シート。
- スキン層(B)が、さらに、オレフィン系樹脂(B1)100重量部に対して、0.1〜30重量部のスチレン系樹脂(B3)を含む請求項1記載の積層シート。
- コア層(A)が、さらに、スチレン系樹脂(A1)100重量部に対して、0.01〜5重量部のオレフィン系樹脂(A3)を含むとともに、オレフィン系樹脂(A3)及びオレフィン系樹脂(B1)が、それぞれ、3〜20g/10分のメルトフローレート(JIS K 7210)を有するポリプロピレン系樹脂である請求項1記載の積層シート。
- コア層(A)が、さらに、スチレン系樹脂(A1)100重量部に対して、0.1〜3重量部のオレフィン系樹脂(A3)を含むとともに、オレフィン系樹脂(A3)及びオレフィン系樹脂(B1)が、それぞれ、融点145℃以上のポリプロピレン系樹脂である請求項1記載の積層シート。
- コア層(A)中のスチレン系熱可塑性エラストマー(A2)の割合(重量%)を[St−TPE]A、スキン層(B)中のスチレン系熱可塑性エラストマー(B2)の割合(重量%)を[St−TPE]Bとしたとき、式:
0<[St−TPE]B−[St−TPE]A<15
で表される関係を充足する請求項1記載の積層シート。 - スチレン系熱可塑性エラストマー(A2)及びスチレン系熱可塑性エラストマー(B2)が、それぞれ、テトラヒドロフランによる不溶分の割合が3重量%以下である請求項1記載の積層シート。
- スチレン系熱可塑性エラストマー(A2)及びスチレン系熱可塑性エラストマー(B2)が、それぞれ、スチレン−ジエン系ブロック共重合体である請求項1記載の積層シート。
- スチレン系樹脂(A1)が、ポリスチレン系樹脂とゴム含有スチレン系樹脂とで構成され、かつ両者の割合(重量比)が、ポリスチレン系樹脂/ゴム含有スチレン系樹脂=20/80〜80/20である請求項1記載の積層シート。
- 総厚みが0.25〜0.7mmであり、かつコア層(A)の厚みとスキン層(B)の厚みとの比率が、スキン層(B)/コア層(A)=1/20〜1/2.5である請求項1記載の積層シート。
- コア層(A)とスキン層(B)との層間強度が1.8N/15mm以上である請求項1記載の積層シート。
- コア層(A)の両面にスキン層(B)が形成されている請求項1記載の積層シート。
- スキン層(A)の上に、さらにオレフィン系樹脂で構成されたカバー層が積層された請求項1記載の積層シート。
- カバー層がポリプロピレン系樹脂で構成され、かつその厚みが、15〜50μmである請求項13記載の積層シート。
- 請求項1記載の積層シートで構成された食品用容器。