JP2004501991A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2004501991A5 JP2004501991A5 JP2002505863A JP2002505863A JP2004501991A5 JP 2004501991 A5 JP2004501991 A5 JP 2004501991A5 JP 2002505863 A JP2002505863 A JP 2002505863A JP 2002505863 A JP2002505863 A JP 2002505863A JP 2004501991 A5 JP2004501991 A5 JP 2004501991A5
- Authority
- JP
- Japan
- Prior art keywords
- fluoropolymer
- formula
- iii
- weight
- carbon atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
【0001】
発明の技術分野
本発明は、(i)テトラフルオロエチレン(TFE)、(ii)ビニリデンフルオリド(VDF)、(iii)式CF2=CFRfの少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rf及びR’fは、下記定義のとおりである)のペルフルオロビニルエーテル、から由来するフルオロポリマーに関する。
発明の技術分野
本発明は、(i)テトラフルオロエチレン(TFE)、(ii)ビニリデンフルオリド(VDF)、(iii)式CF2=CFRfの少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rf及びR’fは、下記定義のとおりである)のペルフルオロビニルエーテル、から由来するフルオロポリマーに関する。
【0009】
発明の要約
本発明は、TFE、VDF、少なくとも1種のペフルオロ化エチレン系不飽和モノマー及びペルフルオロビニルエーテルを含む、フルオロポリマーを提供する。本発明のこのポリマーは、広範囲の組成にわたって優れた物理的特性を示す。そのポリマーは、又、極めて優れた柔軟性を示す。
発明の要約
本発明は、TFE、VDF、少なくとも1種のペフルオロ化エチレン系不飽和モノマー及びペルフルオロビニルエーテルを含む、フルオロポリマーを提供する。本発明のこのポリマーは、広範囲の組成にわたって優れた物理的特性を示す。そのポリマーは、又、極めて優れた柔軟性を示す。
【0010】
本発明にしたがって、(i)TFE、(ii)VDF、(iii)式CF2=CFRf(式中、Rfは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロアルキルでり、R’fは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロ脂肪族基、好ましくはペルフルオロアルキル又はペルフルオロアルコキシであり、又、aは、0〜3の値を有する)のペルフルオロビニルエーテル、のインターポリマー化単位から由来するフルオロポリマーが提供される。
本発明にしたがって、(i)TFE、(ii)VDF、(iii)式CF2=CFRf(式中、Rfは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロアルキルでり、R’fは、1〜8個、好ましくは1〜3個の炭素原子を有するペルフルオロ脂肪族基、好ましくはペルフルオロアルキル又はペルフルオロアルコキシであり、又、aは、0〜3の値を有する)のペルフルオロビニルエーテル、のインターポリマー化単位から由来するフルオロポリマーが提供される。
Claims (23)
- (i)テトラフルオロエチレン、(ii)ビニリデンフルオリド、(iii)式CF2=CFRf(式中、Rfは、1〜8個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、(iii)に記載したとおりであり、R’fは、1〜8個の炭素原子を有するペルフルオロ脂肪族基であり、又aは、0〜3の値を有する)のペルフルオロビニルエーテル、から由来するインターポリマー化単位を含むフルオロポリマー。
- R’fは、ペルフルオロアルキル又はペルフルオロアルコキシである、請求項1に記載のフルオロポリマー。
- フルオロポリマーが半結晶性である、請求項2に記載のフルオロポリマー。
- フルオロポリマーがエラストマーである、請求項2に記載のフルオロポリマー。
- aが1〜3の値である、請求項1に記載のフルオロポリマー。
- (i)テトラフルオロエチレン30〜85重量%、(ii)ビニリデンフルオリド5〜55重量%、(iii)式CF2=CFRf(式中、Rfは、1〜8個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー5〜50重量%、及び(iv)式CF2=CF−(OCF2CF(CF3))aOR’f(式中、aは、0〜3の値であり、又R’fは、1〜8個の炭素原子を有するペルフルオロ脂肪族基である)のペルフルオロビニルエーテル残量から由来するインターポリマー化単位を含むフルオロポリマー。
- 請求項6に記載のフルオロポリマーであって、テトラフルオロエチレン40〜80重量%、ビニリデンフルオリド10〜30重量%、式CF2=CFRfで表されるモノマー5〜40重量%、及びペルフルオロビニルエーテル0.1〜15重量%、から由来するインターポリマー化単位を含む、半結晶性フルオロポリマー。
- ペルフルオロビニルエーテルに対する式中のaが0〜2の値を有する、請求項7に記載の半結晶性フルオロポリマー。
- テトラフルオロエチレン20〜50重量%、ビニリデンフルオリド10〜35重量%、式CF2=CFRfで表されるモノマー20〜50重量%、及びペルフルオロビニルエーテル0.1〜15重量%、から由来するインターポリマー化単位を含む、請求項6に記載のエラストマーフルオロポリマー。
- ペルフルオロビニルエーテルに対する式中のaが0〜2の値を有する、請求項9に記載のエラストマーフルオロポリマー。
- (i)テトラフルオロエチレン、(ii)ビニリデンフルオリド、(iii)式CF2=CFRf(式中、Rfは、1〜8個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、(iii)に記載したとおりであり、R’fは、1〜8個の炭素原子を有するペルフルオロ脂肪族基であり、又aは、0〜3の値を有する)のペルフルオロビニルエーテル、から由来するインターポリマー化単位を含むポリマーを含む第1層、及び
熱可塑性ポリマー及びエラストマーポリマーから選択されるポリマーを含む第2層
を有する多層物品。 - 請求項13に記載の成形多層物品。
- 炭化水素流体に対する耐性を有する、請求項14に記載の成形多層物品。
- 第1層を形成するポリマーとして、(i)テトラフルオロエチレン、(ii)ビニリデンフルオリド、(iii)式CF2=CFRf(式中、Rfは、1〜8個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、及び(iv)式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、(iii)に記載したとおりであり、R’fは、1〜8個の炭素原子を有するペルフルオロ脂肪族基であり、又aは、0〜3の値を有する)のペルフルオロビニルエーテル、から由来するインターポリマー化単位で構成されたフルオロポリマーを用いた請求項13に記載の成形多層物品。
- ポリマー光ファイバーを含む、請求項13に記載の成形多層物品。
- 静電気消散性の、請求項13に記載の成形多層物品。
- (i)テトラフルオロエチレン、(ii)ビニリデンフルオリド、(iii)式CF2=CFRf(式中、Rfは、1〜8個の炭素原子を有するペルフルオロアルキルである)の少なくとも一種のエチレン系不飽和モノマー、から由来するインターポリマー化単位から本質的に構成されるポリマーの柔軟性改善方法であって、モノマー(i)、(ii)及び(iii)を式CF2=CF−(OCF2CF(Rf))aOR’f(式中、Rfは、(iii)に記載したとおりであり、R’fは、1〜8個の炭素原子を有するペルフルオロ脂肪族基であり、1〜8の値を有し、又aは、1〜3の値を有する)のペルフルオロビニルエーテルと共重合させる工程を含む、方法。
- ポリマーが熱可塑性である、請求項19に記載の方法。
- 請求項10に記載のエラストマーフルオロポリマー及びそのエラストマーフルオロポリマー用架橋剤を含む架橋性組成物。
- 更に充填材を含む、請求項21に記載の架橋性組成物。
- フルオロポリマーが多分散分子量分布を有する、請求項1に記載のフルオロポリマー。