JP2002543225A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2002543225A5 JP2002543225A5 JP2000614307A JP2000614307A JP2002543225A5 JP 2002543225 A5 JP2002543225 A5 JP 2002543225A5 JP 2000614307 A JP2000614307 A JP 2000614307A JP 2000614307 A JP2000614307 A JP 2000614307A JP 2002543225 A5 JP2002543225 A5 JP 2002543225A5
- Authority
- JP
- Japan
- Prior art keywords
- rigid foam
- polyol
- optionally present
- group
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
【特許請求の範囲】
【請求項1】 ウレタン基および/またはイソシアヌレート基および/またはウレア基を有し、
a)ジ−またはポリイソシアネートを、
b)イソシアネートに対して反応性である基を平均して少なくとも2個有するポリオール成分、
c)水および/または1種またはそれ以上の物理的発泡剤、
d)必要により存在する、触媒、
e)必要により存在する、付加的な助剤および添加剤
と反応させて得られうる連続気泡硬質発泡体であって、
成分b)が、3〜90のヒドロキシル価を有し、15mmole・kg−1以下の炭素−炭素二重結合を有する少なくとも1種のポリ(オキシアルキレン)ポリオールを含有することを特徴とする硬質発泡体。
【請求項2】 ウレタン基および/またはイソシアヌレート基および/またはウレア基を有する主に連続気泡の硬質発泡体の製造方法であって、
a)ジ−またはポリイソシアネートを、
b)イソシアネートに対して反応性である基を平均して少なくとも2個有するポリオール成分、
c)水および/または1種またはそれ以上の物理的発泡剤、
d)必要により存在する、触媒、
e)必要により存在する、付加的な助剤および添加剤
と反応させ、
成分b)が、3〜90のヒドロキシル価を有し、15mmole・kg−1以下の炭素−炭素二重結合を有する少なくとも1種のポリ(オキシアルキレン)ポリオールを含有することを特徴とする方法。
【請求項1】 ウレタン基および/またはイソシアヌレート基および/またはウレア基を有し、
a)ジ−またはポリイソシアネートを、
b)イソシアネートに対して反応性である基を平均して少なくとも2個有するポリオール成分、
c)水および/または1種またはそれ以上の物理的発泡剤、
d)必要により存在する、触媒、
e)必要により存在する、付加的な助剤および添加剤
と反応させて得られうる連続気泡硬質発泡体であって、
成分b)が、3〜90のヒドロキシル価を有し、15mmole・kg−1以下の炭素−炭素二重結合を有する少なくとも1種のポリ(オキシアルキレン)ポリオールを含有することを特徴とする硬質発泡体。
【請求項2】 ウレタン基および/またはイソシアヌレート基および/またはウレア基を有する主に連続気泡の硬質発泡体の製造方法であって、
a)ジ−またはポリイソシアネートを、
b)イソシアネートに対して反応性である基を平均して少なくとも2個有するポリオール成分、
c)水および/または1種またはそれ以上の物理的発泡剤、
d)必要により存在する、触媒、
e)必要により存在する、付加的な助剤および添加剤
と反応させ、
成分b)が、3〜90のヒドロキシル価を有し、15mmole・kg−1以下の炭素−炭素二重結合を有する少なくとも1種のポリ(オキシアルキレン)ポリオールを含有することを特徴とする方法。
連続気泡の体積パーセントを、DIS ISO 4590−86にしたがって決定した。本発明のポリオール混合物を使用した際に、得られる硬質発泡体の連続気泡の体積パーセントが著しく上昇することが本発明の実施例によって確認される。
本発明の好ましい態様は次のとおりである。
A. 密度が5〜500kg・m −3 である請求項1に記載の硬質発泡体。
B. 使用される触媒が、N−(ジメチルアミノエチル)−N−メチルエタノールアミンであることを特徴とする請求項3に記載の方法。
C. 真空パネルのための断熱充填基材として、家庭用冷蔵庫用または冷凍・冷蔵室の発泡充填キャビティー用および容器構造物における断熱材料としての請求項1またはA項に記載の硬質発泡体の使用。
D. 自動車におけるエネルギー吸収材料としての請求項1またはA項に記載の硬質発泡体の使用。
E. 自動車内装における請求項1またはA項に記載の硬質発泡体の使用。
F. 花栽培のための親水性基材としての請求項1またはA項に記載の硬質発泡体の使用。
本発明の好ましい態様は次のとおりである。
A. 密度が5〜500kg・m −3 である請求項1に記載の硬質発泡体。
B. 使用される触媒が、N−(ジメチルアミノエチル)−N−メチルエタノールアミンであることを特徴とする請求項3に記載の方法。
C. 真空パネルのための断熱充填基材として、家庭用冷蔵庫用または冷凍・冷蔵室の発泡充填キャビティー用および容器構造物における断熱材料としての請求項1またはA項に記載の硬質発泡体の使用。
D. 自動車におけるエネルギー吸収材料としての請求項1またはA項に記載の硬質発泡体の使用。
E. 自動車内装における請求項1またはA項に記載の硬質発泡体の使用。
F. 花栽培のための親水性基材としての請求項1またはA項に記載の硬質発泡体の使用。