IN2014DN08225A - - Google Patents

Info

Publication number
IN2014DN08225A
IN2014DN08225A IN8225DEN2014A IN2014DN08225A IN 2014DN08225 A IN2014DN08225 A IN 2014DN08225A IN 8225DEN2014 A IN8225DEN2014 A IN 8225DEN2014A IN 2014DN08225 A IN2014DN08225 A IN 2014DN08225A
Authority
IN
India
Prior art keywords
less
steel material
mass
hot stamped
inclusions
Prior art date
Application number
Other languages
English (en)
Inventor
Hiroyuki Tanahashi
Toshimasa Tomokiyo
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of IN2014DN08225A publication Critical patent/IN2014DN08225A/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B1/24—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process
    • B21B1/26—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process by hot-rolling, e.g. Steckel hot mill
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0463—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Articles (AREA)
IN8225DEN2014 2012-03-07 2013-03-05 IN2014DN08225A (ru)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012050935 2012-03-07
PCT/JP2013/055992 WO2013133270A1 (ja) 2012-03-07 2013-03-05 ホットスタンプ用鋼板及びその製造方法並びにホットスタンプ鋼材

Publications (1)

Publication Number Publication Date
IN2014DN08225A true IN2014DN08225A (ru) 2015-05-15

Family

ID=49116745

Family Applications (1)

Application Number Title Priority Date Filing Date
IN8225DEN2014 IN2014DN08225A (ru) 2012-03-07 2013-03-05

Country Status (12)

Country Link
US (2) US10161023B2 (ru)
EP (1) EP2824207A4 (ru)
JP (1) JP5541421B2 (ru)
KR (1) KR101629594B1 (ru)
CN (1) CN104160050B (ru)
BR (1) BR112014021801B1 (ru)
CA (1) CA2865910C (ru)
IN (1) IN2014DN08225A (ru)
MX (1) MX366958B (ru)
RU (1) RU2587106C2 (ru)
WO (1) WO2013133270A1 (ru)
ZA (1) ZA201406644B (ru)

Families Citing this family (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5880777B2 (ja) * 2013-03-14 2016-03-09 新日鐵住金株式会社 耐遅れ破壊特性と低温靭性に優れた高強度鋼板、およびそれを用いて製造した高強度部材
US20160145731A1 (en) * 2014-11-26 2016-05-26 GM Global Technology Operations LLC Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components
CN104846274B (zh) * 2015-02-16 2017-07-28 重庆哈工易成形钢铁科技有限公司 热冲压成形用钢板、热冲压成形工艺及热冲压成形构件
CN107427889B (zh) * 2015-03-31 2019-10-25 日本制铁株式会社 热冲压用钢板及其制造方法、以及热冲压成型体
CN105420598A (zh) * 2015-12-14 2016-03-23 浙江海洋学院 一种船锚用低碳合金钢及其热处理工艺
CN105546228A (zh) * 2016-01-20 2016-05-04 浙江海洋学院 一种船舶用无缝钢管及其制备方法
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
CN109563575B (zh) * 2016-08-16 2021-03-05 日本制铁株式会社 热压成型构件
CN106119692B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1500MPa热成形钢及生产方法
CN106119695B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1100MPa热成形钢及生产方法
CN106086683B (zh) * 2016-08-24 2018-05-01 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1700MPa薄热成形钢及生产方法
CN106222556B (zh) * 2016-08-24 2018-03-16 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1300MPa热成形钢及生产方法
CN106086632B (zh) * 2016-08-24 2018-01-12 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1100MPa薄热成形钢及生产方法
CN106086685B (zh) 2016-08-24 2018-01-12 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1500MPa薄热成形钢及生产方法
CN106222555B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1300MPa薄热成形钢及生产方法
JP6572864B2 (ja) * 2016-10-18 2019-09-11 Ｊｆｅスチール株式会社 電磁鋼板製造用の熱延鋼板およびその製造方法
CN106636890B (zh) * 2016-11-11 2018-09-14 武汉钢铁有限公司 直接热成形用薄规格热轧钢板及其制造方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
JP6271067B1 (ja) * 2017-06-01 2018-01-31 日新製鋼株式会社 高強度Ｚｎ−Ａｌ−Ｍｇ系表面被覆鋼板およびその製造方法
WO2018220412A1 (fr) 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
DE102017218704A1 (de) * 2017-10-19 2019-04-25 Thyssenkrupp Ag Verfahren zur Herstellung eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils
EP3623493B1 (en) 2018-02-15 2023-12-20 Nippon Steel Corporation Fe-al plated hot-stamped member and method for producing fe-al plated hot-stamped member
MX2020009562A (es) * 2018-03-20 2020-10-05 Nippon Steel Corp Cuerpo estampado en caliente.
JP6443596B1 (ja) * 2018-03-20 2018-12-26 新日鐵住金株式会社 ホットスタンプ成形体
RU2766947C1 (ru) * 2018-03-27 2022-03-16 Кабусики Кайся Кобе Сейко Се (Кобе Стил, Лтд.) Стальной лист для горячей штамповки
JP7353768B2 (ja) * 2018-03-27 2023-10-02 株式会社神戸製鋼所 ホットスタンプ用鋼板
US11613789B2 (en) 2018-05-24 2023-03-28 GM Global Technology Operations LLC Method for improving both strength and ductility of a press-hardening steel
WO2019241902A1 (en) 2018-06-19 2019-12-26 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
CN112326551B (zh) * 2020-11-13 2023-07-18 江苏省沙钢钢铁研究院有限公司 一种复合钢板性能的测试方法
CN114807739A (zh) 2021-01-28 2022-07-29 宝山钢铁股份有限公司 一种镀铝钢板、热成形部件及制造方法

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3292671B2 (ja) * 1997-02-10 2002-06-17 川崎製鉄株式会社 深絞り性と耐時効性の良好な冷延鋼板用の熱延鋼帯
CA2231760A1 (en) 1998-03-11 1999-09-11 Nisshin Steel Co., Ltd. Cold-rolled steel strip and hot-dip coated cold-rolled steel strip for use as building material and manufacturing method thereof
JP3410970B2 (ja) 1998-07-02 2003-05-26 日本冶金工業株式会社 打抜き加工性に優れるＦｅ−Ｎｉ系合金の製造方法
JP3990554B2 (ja) 2000-06-30 2007-10-17 新日本製鐵株式会社 形状凍結性に優れた鋼板およびその製造方法
WO2002024968A1 (fr) 2000-09-21 2002-03-28 Nippon Steel Corporation Tole d'acier presentant de bonnes caracteristiques de gel de forme et procede permettant de produire cette tole
RU2197542C1 (ru) * 2001-06-28 2003-01-27 Открытое акционерное общество "Северсталь" Способ производства листовой стали
UA77001C2 (en) 2001-09-14 2006-10-16 Nucor Corp Method for production of steel strip and steel strip (variants)
JP3924159B2 (ja) * 2001-11-28 2007-06-06 新日本製鐵株式会社 成形加工後の耐遅れ破壊性に優れた高強度薄鋼板及びその製造方法並びに高強度薄鋼板により作成された自動車用強度部品
JP2004068128A (ja) 2002-08-09 2004-03-04 Daido Steel Co Ltd 切屑破砕性にすぐれた機械構造用鋼
DE602004021802D1 (de) * 2003-04-23 2009-08-13 Sumitomo Metal Ind Heisspressgeformtes produkt und herstellungsverfahren dafür
JP4443910B2 (ja) 2003-12-12 2010-03-31 Ｊｆｅスチール株式会社 自動車構造部材用鋼材およびその製造方法
JP4317491B2 (ja) 2004-06-29 2009-08-19 新日本製鐵株式会社 熱間プレス用鋼板
JP4370991B2 (ja) 2004-07-15 2009-11-25 Ｊｆｅスチール株式会社 自動車構造部材用鋼材の耐遅れ破壊特性評価方法および耐遅れ破壊特性に優れた自動車構造部材用鋼材
JP4500124B2 (ja) 2004-07-23 2010-07-14 新日本製鐵株式会社 ホットプレス用めっき鋼板の製造方法
PT1790422E (pt) * 2004-09-15 2012-05-25 Nippon Steel Corp Peça com elevada resistência, e processo para produção da mesma
CN100507053C (zh) * 2004-11-29 2009-07-01 宝山钢铁股份有限公司 一种800MPa冷轧热镀锌双相钢及其制造方法
RU2277594C1 (ru) * 2005-03-30 2006-06-10 Открытое акционерное общество "Северсталь" Способ производства холоднокатаных листов для глубокой вытяжки
KR100878614B1 (ko) * 2005-12-01 2009-01-15 주식회사 포스코 열처리 경화형 초고강도 강판, 이를 이용한 열처리 경화형부재와 그 제조방법
WO2007064172A1 (en) * 2005-12-01 2007-06-07 Posco Steel sheet for hot press forming having excellent heat treatment and impact property, hot press parts made of it and the method for manufacturing thereof
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP5212111B2 (ja) 2006-11-28 2013-06-19 新日鐵住金株式会社 製造性に優れた快削鋼
JP4846550B2 (ja) 2006-12-12 2011-12-28 新日本製鐵株式会社 合金化溶融亜鉛めっき用鋼板及び合金化溶融亜鉛めっき鋼板
TW200932926A (en) * 2007-04-11 2009-08-01 Nippon Steel Corp Hot-dip metal coated high-strength steel sheet for press working excellent in low-temperature toughness and process for production thereof
CA2729942C (en) * 2008-07-11 2013-08-06 Nippon Steel Corporation Aluminum plated steel sheet for rapid heating hot-stamping, production method of the same and rapid heating hot-stamping method by using this steel sheet
JP5126844B2 (ja) * 2008-08-19 2013-01-23 新日鐵住金株式会社 熱間プレス用鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
JP5316025B2 (ja) 2009-01-28 2013-10-16 Ｊｆｅスチール株式会社 熱間打抜き性に優れたダイクエンチ用鋼板
KR101141015B1 (ko) 2009-06-26 2012-05-02 현대제철 주식회사 수소지연파괴 저항성이 우수한 강판 및 그 제조방법
JP5457840B2 (ja) * 2010-01-07 2014-04-02 株式会社神戸製鋼所 伸びおよび伸びフランジ性に優れた高強度冷延鋼板
JP5064525B2 (ja) * 2010-02-18 2012-10-31 新日本製鐵株式会社 異方性が小さく焼入性に優れた高炭素鋼板及びその製造方法
JP5327106B2 (ja) 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5466576B2 (ja) * 2010-05-24 2014-04-09 株式会社神戸製鋼所 曲げ加工性に優れた高強度冷延鋼板
BR112013022953B1 (pt) 2011-03-09 2019-03-19 Nippon Steel & Sumitomo Metal Corporation Chapa de aço para o uso em estampagem a quente, bem como método para produção e uso da mesma

Also Published As

Publication number Publication date
KR101629594B1 (ko) 2016-06-13
ZA201406644B (en) 2016-09-28
RU2587106C2 (ru) 2016-06-10
CA2865910C (en) 2017-10-17
EP2824207A1 (en) 2015-01-14
RU2014140161A (ru) 2016-04-27
JP5541421B2 (ja) 2014-07-09
CN104160050B (zh) 2016-05-18
KR20140138829A (ko) 2014-12-04
WO2013133270A1 (ja) 2013-09-12
US20180363109A1 (en) 2018-12-20
MX366958B (es) 2019-08-01
EP2824207A4 (en) 2016-03-09
CA2865910A1 (en) 2013-09-12
US10161023B2 (en) 2018-12-25
JPWO2013133270A1 (ja) 2015-07-30
CN104160050A (zh) 2014-11-19
US20150024237A1 (en) 2015-01-22
BR112014021801B1 (pt) 2019-10-29
MX2014010602A (es) 2014-09-18

Similar Documents

Publication Publication Date Title
IN2014DN08225A (ru)
MY153634A (en) Ferritic stainless steel
MY196356A (en) Austenitic Stainless Steel Sheet and Method for Producing High Elastic Limit Nonmagnetic Steel Material Using the Same
MY153580A (en) Ferritic stainless steel
SG11201901278XA (en) Austenitic stainless steel
MX2017012873A (es) Miembro de lamina de acero con tratamiento termico y metodo para producirlo.
MY175890A (en) Ferritic stainless steel
MX352103B (es) Acero inoxidable austenítico delgado.
MX2016001050A (es) Material de acero de alta resistencia para pozo de petroleo y tuberias de pozo de petroleo.
MX355892B (es) Acero inoxidable dúplex y método para la producción del mismo.
MX2019001947A (es) Acero inoxidable ferritico.
MY176531A (en) Austenitic stainless clad steel plate and method for producing thereof
MX346491B (es) Placa de acero laminada en caliente o en frio, su proceso de fabricacion y su uso en la industria automotriz.
MX2013005094A (es) Acero inoxidable ferritico con excelente resistencia a la oxidacion.
MX351782B (es) Acero inoxidable duplex.
MX363869B (es) Placa de acero inoxidable de ferrita que tiene excelente resistencia contra desprendimiento de laminilla, y metodo para fabricarla.
IN2015DN01710A (ru)
MY153707A (en) Steel material having excellent atmospheric corrosion resistance
IN2014KN00959A (ru)
BR112015030008A2 (pt) material de aço tratado termicamente e método de produção do mesmo
MY182247A (en) Ferritic stainless steel sheet
MX2016014667A (es) Acero inoxidable ferritico.
IN2015DN00283A (ru)
MX2016013634A (es) Hoja de acero inoxidable martensitico y junta de metal.
MX2018003852A (es) Acero inoxidable ferritico.