IN2014DN08225A - - Google Patents
Info
- Publication number
- IN2014DN08225A IN2014DN08225A IN8225DEN2014A IN2014DN08225A IN 2014DN08225 A IN2014DN08225 A IN 2014DN08225A IN 8225DEN2014 A IN8225DEN2014 A IN 8225DEN2014A IN 2014DN08225 A IN2014DN08225 A IN 2014DN08225A
- Authority
- IN
- India
- Prior art keywords
- less
- steel material
- mass
- hot stamped
- inclusions
- Prior art date
Abstract
This hot stamped steel material comprises a chemical composition including in mass% 0.18 0.26% of C more than 0.02% to 0.05% or less of Si 1.0 1.5% of Mn 0.03% or less of P 0.02% or less of S 0.001 0.5% of Al 0.1% or less of N 0.001 0.02% of O 0 2.0% of Cr 0 1.0% of Mo 0 0.5% of V 0 0.5% of W 0 5.0% of Ni 0 0.01% of B 0 0.5% of Ti 0 0.5% of Nb 0 1.0% of Cu and Fe and impurities as the remainder and is characterized in that: the concentration of Mn containing inclusions is 0.010 mass% or more to less than 0.25 mass%; and the percentage by number of Mn oxides in said inclusions with a maximum length of 1.0 4.0 µm is 10.0% or more. This hot stamped steel material ensures excellent resistance to hydrogen embrittlement even in cases where the steel material after having been hot stamped is subjected to processing in which stress remains such as perforation and the steel material can also be worked easily.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012050935 | 2012-03-07 | ||
PCT/JP2013/055992 WO2013133270A1 (en) | 2012-03-07 | 2013-03-05 | Steel sheet for hot stamping, method for producing same, and hot-stamped steel material |
Publications (1)
Publication Number | Publication Date |
---|---|
IN2014DN08225A true IN2014DN08225A (en) | 2015-05-15 |
Family
ID=49116745
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
IN8225DEN2014 IN2014DN08225A (en) | 2012-03-07 | 2013-03-05 |
Country Status (12)
Country | Link |
---|---|
US (2) | US10161023B2 (en) |
EP (1) | EP2824207A4 (en) |
JP (1) | JP5541421B2 (en) |
KR (1) | KR101629594B1 (en) |
CN (1) | CN104160050B (en) |
BR (1) | BR112014021801B1 (en) |
CA (1) | CA2865910C (en) |
IN (1) | IN2014DN08225A (en) |
MX (1) | MX366958B (en) |
RU (1) | RU2587106C2 (en) |
WO (1) | WO2013133270A1 (en) |
ZA (1) | ZA201406644B (en) |
Families Citing this family (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA2904122C (en) * | 2013-03-14 | 2018-07-10 | Nippon Steel & Sumitomo Metal Corporation | High strength steel sheet excellent in delayed fracture resistance and low temperature toughness, and high strength member manufactured using the same |
US20160145731A1 (en) * | 2014-11-26 | 2016-05-26 | GM Global Technology Operations LLC | Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components |
CN104846274B (en) | 2015-02-16 | 2017-07-28 | 重庆哈工易成形钢铁科技有限公司 | Hot press-formed use steel plate, hot press-formed technique and hot press-formed component |
RU2683397C1 (en) * | 2015-03-31 | 2019-03-28 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Steel sheet for hot stamping, method of manufacture steel sheet for hot stamping, and also hot formed by hot stamping body |
CN105420598A (en) * | 2015-12-14 | 2016-03-23 | 浙江海洋学院 | Low-carbon alloy steel for boat anchor and thermal treatment process of low-carbon alloy steel |
CN105546228A (en) * | 2016-01-20 | 2016-05-04 | 浙江海洋学院 | Seamless steel pipe for ship and preparing method of seamless steel pipe |
US10385415B2 (en) | 2016-04-28 | 2019-08-20 | GM Global Technology Operations LLC | Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure |
US10619223B2 (en) | 2016-04-28 | 2020-04-14 | GM Global Technology Operations LLC | Zinc-coated hot formed steel component with tailored property |
MX2019001760A (en) | 2016-08-16 | 2019-06-17 | Nippon Steel & Sumitomo Metal Corp | Hot press-formed member. |
CN106222556B (en) * | 2016-08-24 | 2018-03-16 | 武汉钢铁有限公司 | With the tensile strength >=1300MPa hot formings steel and production method of medium thin slab Direct Rolling |
CN106086685B (en) | 2016-08-24 | 2018-01-12 | 武汉钢铁有限公司 | With the thin hot forming steel of tensile strength >=1500MPa of sheet billet Direct Rolling and production method |
CN106119692B (en) * | 2016-08-24 | 2018-03-20 | 武汉钢铁有限公司 | With the tensile strength >=1500MPa hot formings steel and production method of medium thin slab Direct Rolling |
CN106222555B (en) * | 2016-08-24 | 2018-03-20 | 武汉钢铁有限公司 | With the thin hot forming steel of tensile strength >=1300MPa of sheet billet Direct Rolling and production method |
CN106119695B (en) * | 2016-08-24 | 2018-03-20 | 武汉钢铁有限公司 | With the tensile strength >=1100MPa hot formings steel and production method of medium thin slab Direct Rolling |
CN106086632B (en) * | 2016-08-24 | 2018-01-12 | 武汉钢铁有限公司 | With the thin hot forming steel of tensile strength >=1100MPa of sheet billet Direct Rolling and production method |
CN106086683B (en) * | 2016-08-24 | 2018-05-01 | 武汉钢铁有限公司 | With the thin hot forming steel of tensile strength >=1700MPa of sheet billet Direct Rolling and production method |
JP6572864B2 (en) * | 2016-10-18 | 2019-09-11 | Jfeスチール株式会社 | Hot-rolled steel sheet for manufacturing electrical steel sheet and method for manufacturing the same |
CN106636890B (en) * | 2016-11-11 | 2018-09-14 | 武汉钢铁有限公司 | Direct hot forming thin format hot rolled steel plate and its manufacturing method |
WO2018096387A1 (en) * | 2016-11-24 | 2018-05-31 | Arcelormittal | Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same |
JP6271067B1 (en) * | 2017-06-01 | 2018-01-31 | 日新製鋼株式会社 | High-strength Zn-Al-Mg-based surface-coated steel sheet and method for producing the same |
WO2018220412A1 (en) | 2017-06-01 | 2018-12-06 | Arcelormittal | Method for producing high-strength steel parts with improved ductility, and parts obtained by said method |
DE102017218704A1 (en) * | 2017-10-19 | 2019-04-25 | Thyssenkrupp Ag | Process for producing a steel component provided with a metallic, corrosion-protective coating |
MX2020005505A (en) | 2018-02-15 | 2020-09-03 | Nippon Steel Corp | Fe-Al PLATED HOT-STAMPED MEMBER AND METHOD FOR PRODUCING Fe-Al PLATED HOT-STAMPED MEMBER. |
US11285698B2 (en) * | 2018-03-20 | 2022-03-29 | Nippon Steel Corporation | Hot-stamped body |
WO2019180852A1 (en) * | 2018-03-20 | 2019-09-26 | 日本製鉄株式会社 | Hot stamp molded article |
JP7353768B2 (en) * | 2018-03-27 | 2023-10-02 | 株式会社神戸製鋼所 | Steel plate for hot stamping |
MX2020009944A (en) * | 2018-03-27 | 2020-10-16 | Kobe Steel Ltd | Steel plate for hot stamping. |
WO2019222950A1 (en) | 2018-05-24 | 2019-11-28 | GM Global Technology Operations LLC | A method for improving both strength and ductility of a press-hardening steel |
US11612926B2 (en) | 2018-06-19 | 2023-03-28 | GM Global Technology Operations LLC | Low density press-hardening steel having enhanced mechanical properties |
US11530469B2 (en) | 2019-07-02 | 2022-12-20 | GM Global Technology Operations LLC | Press hardened steel with surface layered homogenous oxide after hot forming |
CN112326551B (en) * | 2020-11-13 | 2023-07-18 | 江苏省沙钢钢铁研究院有限公司 | Test method for performance of composite steel plate |
CN114807739A (en) | 2021-01-28 | 2022-07-29 | 宝山钢铁股份有限公司 | Aluminum-plated steel plate, hot-formed part and manufacturing method |
Family Cites Families (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3292671B2 (en) * | 1997-02-10 | 2002-06-17 | 川崎製鉄株式会社 | Hot-rolled steel strip for cold-rolled steel sheet with good deep drawability and aging resistance |
CA2231760A1 (en) | 1998-03-11 | 1999-09-11 | Nisshin Steel Co., Ltd. | Cold-rolled steel strip and hot-dip coated cold-rolled steel strip for use as building material and manufacturing method thereof |
JP3410970B2 (en) * | 1998-07-02 | 2003-05-26 | 日本冶金工業株式会社 | Method for producing Fe-Ni alloy excellent in punching workability |
JP3990554B2 (en) * | 2000-06-30 | 2007-10-17 | 新日本製鐵株式会社 | Steel sheet with excellent shape freezing property and method for producing the same |
CA2422753C (en) | 2000-09-21 | 2007-11-27 | Nippon Steel Corporation | Steel plate excellent in shape freezing property and method for production thereof |
RU2197542C1 (en) * | 2001-06-28 | 2003-01-27 | Открытое акционерное общество "Северсталь" | Method of making sheet steel |
BRPI0212499B1 (en) | 2001-09-14 | 2015-12-08 | Nucor Corp | process for producing continuous casting steel strip and thin steel strip produced by the same |
JP3924159B2 (en) * | 2001-11-28 | 2007-06-06 | 新日本製鐵株式会社 | High-strength thin steel sheet with excellent delayed fracture resistance after forming, its manufacturing method, and automotive strength parts made from high-strength thin steel sheet |
JP2004068128A (en) | 2002-08-09 | 2004-03-04 | Daido Steel Co Ltd | Steel for machine structural use having excellent chip crushability |
DE602004021802D1 (en) * | 2003-04-23 | 2009-08-13 | Sumitomo Metal Ind | HOTPRESSED PRODUCT AND MANUFACTURING METHOD THEREFOR |
JP4443910B2 (en) | 2003-12-12 | 2010-03-31 | Jfeスチール株式会社 | Steel materials for automobile structural members and manufacturing method thereof |
JP4317491B2 (en) | 2004-06-29 | 2009-08-19 | 新日本製鐵株式会社 | Steel sheet for hot press |
JP4370991B2 (en) | 2004-07-15 | 2009-11-25 | Jfeスチール株式会社 | Method for evaluating delayed fracture resistance of steel for automotive structural members and steel for automotive structural members excellent in delayed fracture resistance |
JP4500124B2 (en) | 2004-07-23 | 2010-07-14 | 新日本製鐵株式会社 | Manufacturing method of hot-pressed plated steel sheet |
SI2266722T1 (en) * | 2004-09-15 | 2012-07-31 | Nippon Steel Corp | Method of production of a high strength part |
CN100507053C (en) * | 2004-11-29 | 2009-07-01 | 宝山钢铁股份有限公司 | 800MPa cold rolled and hot zinc plated double phase steel and its producing method |
RU2277594C1 (en) * | 2005-03-30 | 2006-06-10 | Открытое акционерное общество "Северсталь" | Cold rolled sheets for deep drawing making method |
KR100878614B1 (en) * | 2005-12-01 | 2009-01-15 | 주식회사 포스코 | Quenched steel sheet having ultra high strength, parts made of it and the method for manufacturing thereof |
WO2007064172A1 (en) * | 2005-12-01 | 2007-06-07 | Posco | Steel sheet for hot press forming having excellent heat treatment and impact property, hot press parts made of it and the method for manufacturing thereof |
EP1832667A1 (en) * | 2006-03-07 | 2007-09-12 | ARCELOR France | Method of producing steel sheets having high strength, ductility and toughness and thus produced sheets. |
KR101118852B1 (en) | 2006-11-28 | 2012-03-16 | 신닛뽄세이테쯔 카부시키카이샤 | Free-cutting steel excellent in manufacturability |
JP4846550B2 (en) * | 2006-12-12 | 2011-12-28 | 新日本製鐵株式会社 | Steel plate for galvannealed alloy and galvannealed steel plate |
JP5079795B2 (en) * | 2007-04-11 | 2012-11-21 | 新日本製鐵株式会社 | Hot-dip hot-dip steel sheet for press working with excellent low-temperature toughness and method for producing the same |
CA2729942C (en) * | 2008-07-11 | 2013-08-06 | Nippon Steel Corporation | Aluminum plated steel sheet for rapid heating hot-stamping, production method of the same and rapid heating hot-stamping method by using this steel sheet |
JP5126844B2 (en) * | 2008-08-19 | 2013-01-23 | 新日鐵住金株式会社 | Steel sheet for hot pressing, manufacturing method thereof, and manufacturing method of hot pressed steel sheet member |
JP5316025B2 (en) | 2009-01-28 | 2013-10-16 | Jfeスチール株式会社 | Die quench steel plate with excellent hot punchability |
KR101141015B1 (en) | 2009-06-26 | 2012-05-02 | 현대제철 주식회사 | Steel sheet having excellent hydrogen delayed fracture resistance quality, and method for producing the same |
JP5457840B2 (en) * | 2010-01-07 | 2014-04-02 | 株式会社神戸製鋼所 | High strength cold-rolled steel sheet with excellent elongation and stretch flangeability |
JP5064525B2 (en) * | 2010-02-18 | 2012-10-31 | 新日本製鐵株式会社 | High carbon steel sheet with low anisotropy and excellent hardenability and method for producing the same |
JP5327106B2 (en) | 2010-03-09 | 2013-10-30 | Jfeスチール株式会社 | Press member and manufacturing method thereof |
JP5466576B2 (en) * | 2010-05-24 | 2014-04-09 | 株式会社神戸製鋼所 | High strength cold-rolled steel sheet with excellent bending workability |
MX360249B (en) | 2011-03-09 | 2018-10-26 | Nippon Steel & Sumitomo Metal Corp | Steel sheets for hot stamping, method for manufacturing same, and method for manufacturing high-strength parts. |
-
2013
- 2013-03-05 RU RU2014140161/02A patent/RU2587106C2/en not_active IP Right Cessation
- 2013-03-05 IN IN8225DEN2014 patent/IN2014DN08225A/en unknown
- 2013-03-05 CA CA2865910A patent/CA2865910C/en not_active Expired - Fee Related
- 2013-03-05 KR KR1020147027737A patent/KR101629594B1/en active IP Right Grant
- 2013-03-05 CN CN201380012499.1A patent/CN104160050B/en active Active
- 2013-03-05 JP JP2013542282A patent/JP5541421B2/en active Active
- 2013-03-05 WO PCT/JP2013/055992 patent/WO2013133270A1/en active Application Filing
- 2013-03-05 US US14/382,704 patent/US10161023B2/en active Active
- 2013-03-05 BR BR112014021801-3A patent/BR112014021801B1/en not_active IP Right Cessation
- 2013-03-05 EP EP13757523.9A patent/EP2824207A4/en not_active Withdrawn
- 2013-03-05 MX MX2014010602A patent/MX366958B/en active IP Right Grant
-
2014
- 2014-09-10 ZA ZA2014/06644A patent/ZA201406644B/en unknown
-
2018
- 2018-08-23 US US16/110,069 patent/US20180363109A1/en not_active Abandoned
Also Published As
Publication number | Publication date |
---|---|
RU2014140161A (en) | 2016-04-27 |
BR112014021801B1 (en) | 2019-10-29 |
US10161023B2 (en) | 2018-12-25 |
JPWO2013133270A1 (en) | 2015-07-30 |
EP2824207A4 (en) | 2016-03-09 |
KR20140138829A (en) | 2014-12-04 |
ZA201406644B (en) | 2016-09-28 |
MX366958B (en) | 2019-08-01 |
JP5541421B2 (en) | 2014-07-09 |
WO2013133270A1 (en) | 2013-09-12 |
CN104160050B (en) | 2016-05-18 |
EP2824207A1 (en) | 2015-01-14 |
KR101629594B1 (en) | 2016-06-13 |
MX2014010602A (en) | 2014-09-18 |
US20180363109A1 (en) | 2018-12-20 |
RU2587106C2 (en) | 2016-06-10 |
CN104160050A (en) | 2014-11-19 |
US20150024237A1 (en) | 2015-01-22 |
CA2865910A1 (en) | 2013-09-12 |
CA2865910C (en) | 2017-10-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2014DN08225A (en) | ||
MY153634A (en) | Ferritic stainless steel | |
MY196356A (en) | Austenitic Stainless Steel Sheet and Method for Producing High Elastic Limit Nonmagnetic Steel Material Using the Same | |
MY153580A (en) | Ferritic stainless steel | |
MX2017012873A (en) | Heat-treated steel sheet member, and production method therefor. | |
MY175890A (en) | Ferritic stainless steel | |
MX352103B (en) | Lean austenitic stainless steel. | |
MX2016001050A (en) | High-strength steel material for oil well use, and oil well pipe. | |
SG11201901278XA (en) | Austenitic stainless steel | |
MX355892B (en) | Duplex stainless steel, and process for production thereof. | |
MX2019001947A (en) | Ferritic stainless steel. | |
MY176531A (en) | Austenitic stainless clad steel plate and method for producing thereof | |
MX346491B (en) | Hot-rolled or cold-rolled steel plate, method for manufacturing same, and use thereof in the automotive industry. | |
MX2013005094A (en) | Ferritic stainless steel with excellent oxidation resistance. | |
MX2013008518A (en) | Duplex stainless steel. | |
MX363869B (en) | Ferrite-based stainless steel plate having excellent resistance against scale peeling, and method for manufacturing same. | |
MX2017001943A (en) | Austenitic stainless steel sheet and metal gasket. | |
MY153707A (en) | Steel material having excellent atmospheric corrosion resistance | |
IN2014KN00959A (en) | ||
BR112015030008A2 (en) | heat treated steel material and production method thereof | |
MY182247A (en) | Ferritic stainless steel sheet | |
MY171873A (en) | Corrosion-resistant micro-alloyed steel and steel rail, and preparation method thereof | |
IN2015DN00283A (en) | ||
MX2016013634A (en) | Martensitic stainless-steel sheet and metal gasket. | |
MY165138A (en) | Ferritic stainless steel excellent in heat resistance property and formability |