ES2038400T3 - Procedimiento de fosfatado. - Google Patents

Procedimiento de fosfatado.

Info

Publication number
ES2038400T3
ES2038400T3 ES198989201935T ES89201935T ES2038400T3 ES 2038400 T3 ES2038400 T3 ES 2038400T3 ES 198989201935 T ES198989201935 T ES 198989201935T ES 89201935 T ES89201935 T ES 89201935T ES 2038400 T3 ES2038400 T3 ES 2038400T3
Authority
ES
Spain
Prior art keywords
zinc
magnesium
calculated
weight ratio
range
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES198989201935T
Other languages
English (en)
Inventor
Klaus Bittner
Gerhard Muller
Werner Dr. Rausch
Klaus Dr. Wittel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GEA Group AG
Original Assignee
Metallgesellschaft AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Metallgesellschaft AG filed Critical Metallgesellschaft AG
Application granted granted Critical
Publication of ES2038400T3 publication Critical patent/ES2038400T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

PARA FOSFATAR SUPERFICIES GALVANIZADAS (ACEROS GALVANIZADOS) SE TRATA LA SUPERFICIE A FOSFATAR DURANTE 10 SEGUNDOS Y POR CONTACTO CON UNA SOLUCION DE FOSFATACION, QUE CONTIENE UN ACELERADOR (NITRATO), DE 0,5 A 5,0 G/L DE CINC, DE 3 A 20 G/L DE FOSFATO (P2O5), DE 0,3 A 3 G/L DE MAGNESIO Y CON UNA RELACION DE MG (MAGNESIO)/ZN (CINC) ENTRE C0,5 A 10/1; PRESENTA UN VALOR S ENTRE 0,1 A 0,4 Y SE COMPLETA CON UN CONCENTRADO CON UNA RELACION EN PESO DE ZN/FOSFATO ENTRE 0 A 1/8. ES VENTAJOSO EL EMPLEO DE SOLUCIONES DE FOSFATACION QUE CONTIENEN DE 0,5 A 1 G/L DE ZINC EN UNA RELACION EN PESO DE MAGNESIO/ZINC DE (0,5 A 3)/1, CON UNA CANTIDAD DE IONES NIQUEL MAXIMA DE 1,5 G/L CON UNA CANTIDAD EN FLUOROS COMPLEJOS O SENCILLOS ENTRE 0,1 Y 1,5 G/L. SE EMPLEA SOBRE BANDAS DE ACERO GALVANIZADAS EN FORMA DE LACA O CON RECUBRIMIENTO CON LAMINAS ORGANICAS.
ES198989201935T 1988-08-24 1989-07-22 Procedimiento de fosfatado. Expired - Lifetime ES2038400T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE3828676A DE3828676A1 (de) 1988-08-24 1988-08-24 Phosphatierverfahren

Publications (1)

Publication Number Publication Date
ES2038400T3 true ES2038400T3 (es) 1993-07-16

Family

ID=6361479

Family Applications (1)

Application Number Title Priority Date Filing Date
ES198989201935T Expired - Lifetime ES2038400T3 (es) 1988-08-24 1989-07-22 Procedimiento de fosfatado.

Country Status (8)

Country Link
US (1) US5152849A (es)
EP (1) EP0359296B1 (es)
JP (1) JP2770860B2 (es)
AT (1) ATE85817T1 (es)
CA (1) CA1332560C (es)
DE (2) DE3828676A1 (es)
ES (1) ES2038400T3 (es)
GB (1) GB2223239B (es)

Families Citing this family (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH03107469A (ja) * 1989-09-21 1991-05-07 Nippon Parkerizing Co Ltd 裸耐食性に優れたりん酸塩化成皮膜を有する亜鉛系めっき材料
JP3219453B2 (ja) * 1992-03-17 2001-10-15 日本パーカライジング株式会社 耐黒変性に優れた亜鉛系めっき鋼板の製造方法
DE4326388A1 (de) * 1993-08-06 1995-02-09 Metallgesellschaft Ag Verfahren zur phosphatierenden Behandlung von einseitig verzinktem Stahlband
JP3479609B2 (ja) * 1999-03-02 2003-12-15 日本パーカライジング株式会社 スラッジ発生のないリン酸亜鉛処理液およびリン酸亜鉛処理方法
JP4630326B2 (ja) * 1999-08-09 2011-02-09 新日本製鐵株式会社 加工性に優れたリン酸塩処理亜鉛系めっき鋼板の製造方法
KR100523715B1 (ko) * 1999-08-26 2005-10-26 제이에프이 스틸 가부시키가이샤 표면처리강판
JP3872621B2 (ja) * 1999-11-05 2007-01-24 新日本製鐵株式会社 自動車車体用亜鉛系メッキ鋼板
JP4267213B2 (ja) 2001-03-27 2009-05-27 新日本製鐵株式会社 耐食性および色調に優れたリン酸亜鉛処理亜鉛系メッキ鋼板
JP4868748B2 (ja) * 2005-03-01 2012-02-01 日新製鋼株式会社 リン酸塩処理鋼板
KR101106516B1 (ko) * 2006-10-31 2012-01-20 제이에프이 스틸 가부시키가이샤 인산염 처리 아연계 도금 강판 및 그 제조 방법
JP5119864B2 (ja) * 2006-10-31 2013-01-16 Ｊｆｅスチール株式会社 リン酸塩処理亜鉛系めっき鋼板及びその製造方法
JP4992385B2 (ja) * 2006-10-31 2012-08-08 Ｊｆｅスチール株式会社 有機樹脂被覆リン酸塩処理亜鉛系めっき鋼板及びその製造方法
JP5462467B2 (ja) * 2008-10-31 2014-04-02 日本パーカライジング株式会社 金属材料用化成処理液および処理方法
JP6927146B2 (ja) * 2018-05-25 2021-08-25 Ｊｆｅスチール株式会社 化成処理めっき鋼板の製造方法
CN113930096A (zh) * 2020-06-29 2022-01-14 Ａｇｃ株式会社 复合材料、其制造方法和用途
CN113881934B (zh) * 2021-11-04 2023-04-21 湖南金化科技集团有限公司 一种少渣少灰的锌系磷化液

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB648888A (en) * 1947-04-25 1951-01-17 Walterisation Company Ltd Improvements in the production of phosphate coatings on metal surfaces
US3597283A (en) * 1969-10-08 1971-08-03 Lubrizol Corp Phosphating solutions for use on ferrous metal and zinc surfaces
US3676224A (en) * 1970-10-16 1972-07-11 Lubrizol Corp Phosphating solution with scale suppressing characteristics
JPS5165041A (en) * 1974-12-04 1976-06-05 Nippon Packaging Kk Kinzokuno rinsanenhimakukeiseihoho
JPS5357142A (en) * 1976-11-05 1978-05-24 Nippon Packaging Kk Process for forming black coating on aluminum or aluminum alloy
DE3245411A1 (de) * 1982-12-08 1984-07-05 Gerhard Collardin GmbH, 5000 Köln Verfahren zur phosphatierung elektrolytisch verzinkter metallwaren
US4529451A (en) * 1983-01-03 1985-07-16 Detrex Chemical Industries, Inc. Zinc phosphate coated metal and process of producing same
EP0172806A4 (en) * 1984-01-06 1986-05-16 Ford Motor Co ALKALINE RESISTANCE PHOSPHATE CONVERSION COATING.
DE3636390A1 (de) * 1986-10-25 1988-04-28 Metallgesellschaft Ag Verfahren zur erzeugung von phosphatueberzuegen auf metallen
US4717431A (en) * 1987-02-25 1988-01-05 Amchem Products, Inc. Nickel-free metal phosphating composition and method for use
DE3871031D1 (de) * 1987-08-19 1992-06-17 Metallgesellschaft Ag Verfahren zur phosphatierung von metallen.
EP0370535B1 (de) * 1988-11-25 1992-11-11 Metallgesellschaft Aktiengesellschaft Verfahren zum Aufbringen von Phosphatüberzügen

Also Published As

Publication number Publication date
ATE85817T1 (de) 1993-03-15
GB2223239B (en) 1992-09-23
EP0359296A1 (de) 1990-03-21
DE3828676A1 (de) 1990-03-01
JP2770860B2 (ja) 1998-07-02
GB2223239A (en) 1990-04-04
US5152849A (en) 1992-10-06
GB8919200D0 (en) 1989-10-04
CA1332560C (en) 1994-10-18
JPH02101175A (ja) 1990-04-12
DE58903562D1 (de) 1993-03-25
EP0359296B1 (de) 1993-02-17

Similar Documents

Publication Publication Date Title
ES2038400T3 (es) Procedimiento de fosfatado.
DK0633949T3 (es)
ES8302794A1 (es) "procedimiento de fosfatacion de metales".
ES2081420T3 (es) Procedimiento para el fosfatado de superficies metalicas.
PT74310A (fr) Procede de phosphatation de metaux
BR9004439A (pt) Processo para revestimento protetor de uma superficie de um aco revestido com zinco ou revestido com uma liga de zinco e processo para a formacao de um revestimento de conversao contendo fosfatos de zinco,manganes e niquel
DE3869455D1 (de) Verfahren zur phosphatierung vor der elektrotauchlackierung.
KR920702731A (ko) 망간 및 마그네슘 함유 아연 포스페이트 코팅의 형성방법
TW363089B (en) Aqueous solution and process for phosphatizing metallic surfaces
ES540769A0 (es) Procedimiento para la fosfatacion de superficies metalicas atemperatura de tratamiento baja
DE3378481D1 (en) Process for phosphatizing zinc-electroplated metal objects
EP0219779A3 (en) Phosphatizing process for electrolytically galvanized metal objects
ES2071110T3 (es) Procedimiento para la obtencion de capas de fosfato de cinc que contienen manganeso sobre acero galvanizado.
ES2081224T3 (es) Procedimiento para facilitar la conformacion en frio.
ES8607423A1 (es) Procedimiento para fosfatar una superficie metalica basada en hierro o zinc
ATE253651T1 (de) Verfahren zur phosphatierung von zink- oder aluminiumoberflächen
GB2003192A (en) Metal phosphating process
Ken NEW TECHNOLOGIES FOR ZINC PHOSPHATING BEFORE CATAPHORETIC PAINTING
GB1214607A (en) Phosphate coating of iron or steel surfaces
JPS55125279A (en) Chromate-treating method for zinc-plated steel sheet
GB852226A (en) Process for phosphating metals
JPS5770280A (en) Pretreatment in painting polyolefine powder

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 359296

Country of ref document: ES