DE2543082A1 - Cyanidischer silberelektrolyt zur galvanischen abscheidung von silber-graphit-dispersionsueberzuegen - Google Patents

Cyanidischer silberelektrolyt zur galvanischen abscheidung von silber-graphit-dispersionsueberzuegen

Info

Publication number
DE2543082A1
DE2543082A1 DE19752543082 DE2543082A DE2543082A1 DE 2543082 A1 DE2543082 A1 DE 2543082A1 DE 19752543082 DE19752543082 DE 19752543082 DE 2543082 A DE2543082 A DE 2543082A DE 2543082 A1 DE2543082 A1 DE 2543082A1
Authority
DE
Germany
Prior art keywords
silver
graphite
electrolyte
cyanidic
graphite dispersion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19752543082
Other languages
English (en)
Other versions
DE2543082C3 (de
DE2543082B2 (de
Inventor
Georg Behringer
Hans Dr Laub
Sjouke Zjilstra
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Original Assignee
Siemens AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens AG filed Critical Siemens AG
Priority to DE2543082A priority Critical patent/DE2543082C3/de
Priority to CH840976A priority patent/CH622032A5/de
Priority to NL7608919A priority patent/NL7608919A/xx
Priority to GB33828/76A priority patent/GB1534429A/en
Priority to FR7628496A priority patent/FR2325735A1/fr
Publication of DE2543082A1 publication Critical patent/DE2543082A1/de
Publication of DE2543082B2 publication Critical patent/DE2543082B2/de
Application granted granted Critical
Publication of DE2543082C3 publication Critical patent/DE2543082C3/de
Expired legal-status Critical Current

Description

2543Ü82
SIEMENS AKTIENGESELLSCHAFT Erlangen, den 24. 9. 1975 Berlin und München <* Werner-von-Siemens-Str. 50
Unser Zeichen: VPA 75 P 7565 BRD/Td 18 Hag
Cyanidischer Silberelektrolyt zur galvanischen Abscheidung von Silber-Graphit-Dispersionsüberzügen
Kontaktschichten aus Silber oder einer Silber-Kupferlegierung z.B. AgCu3, beispielsweise für Relais können auf pulvermetallurgischem oder auf galvanischem Wege hergestellt werden. Solche Schichten sind in arbeitenden Relais eines starken mechanischen Verschleiß unterworfen. Es ist bekannt, daß der Verschleiß von mechanisch, z.B. durch Reibung beanspruchten Oberflächenschichten durch Graphit herabgesetzt werden kann. Aus einem von Loffler, D., in Galvanotechnik (65)1974, Nr.5, S. 36Overöffentlichten Aufsatz sind graphithaltige Nickel- und Eisenüberzüge bekannt. Diese Nickel- bzw. Eisendispersionsüberzüge, sind galvanisch erzeugte Metallüberzüge, die eine nichtmetallische Phase in feiner, möglichst gleichmäßiger Verteilung, hier Graphit, enthalten und aus sauren Bädern zur Abscheidung gebracht werden.
Da es schwierig ist, dünne, graphithaltige Oberflächenschichten (Dicke "^ 20 /um),z.B. für Relaiskontakte auf pulvermetallurgischem Wege herzustellen, war es Aufgabe der Erfindung Silberbäder zu entwickeln, die die Herstellung verschleißfester Silber-Graphit-Dispersionsüberzüge auf galvanischem Wege gestatten.
Diese Aufgabe findet ihre Lösung gemäß der Erfindung in einem cyanidischen Silberelektrolyten, der 10 bis 100 g/l Graphit der Korngröße 1 bis 10 /um, 0,02 bis 0,5 g/l eines für Silberbäder geeigneten Glai Zusatzes und 0,05 bis 2 g/l eines für alkalische Elektrolyte geeigneten Netzmittels enthält. Die aus dem erfinlungsgemäßen Bad auf galvanischem Wege hergestellten graphithaltigen Oberflächenschichten sind glatt und gleichmäßig. Der Grap.J.t liegt
7098 1 3/0866
VPA 75 P 7565 BRD
in dem Silber-Graphit-Dispersionsüberzug in außerordentlich feiner und gleichmäßiger Verteilung vor. Der Graphitgehalt der Überzüge kann entsprechend dem jeweiligen Verwendungszweck 0,1 bis 3 Gew.~% betragen. Die Härte der Silber-Graphit-Überzüge (HV 0,05) liegt in einem Bereich von 700 bis 1000 N/mm .
Silber-Graphit-Dispersionsüberzüge gemäß der Erfindung weisen eine hervorragende Ahriebbeständigkeit auf. Abriebversucle mit Ag/Graphitüberzügen, die ca. 1,0 - 1,5 Gew.-% Graphit enthalten, haben beispielsweise gezeigt, daß der Verschleiß derartiger Dispersionsschichten 1/10 oder sogar weniger des Verschleißes von reinen Silber- oder Silber-Kupfer-Schichten unter denselben Bedingungen beträgt.
Zur Herstellung der Silber/Graphit-Dispersionsüberzüge wird ein Bad gemäß der Erfindung bei einer Temperatur von 25 bis 30°C und einer Stromdichte von 1 bis 5 A/dm betrieben.
Ein für die vorliegende Erfindung besonders geeigneter Silberelektrolyt enthält Kaliumsübercyanid, Kaliumcyanid und Kaliumcarbonat. Ferner ist in dem Silberelektrolyten feinkörniger Graphit enthalten, der während des Abseheidungsvorganges durch Umpumpen des Bades in Schwebe gehalten wird.
Geeignete Glanzbildner sind z.B. Türkis.chrotöl, Schwefelkohlenstoff, Natriumxanthogenat, Dithiocarbamat, Thiothiazolidin, Natriumthiosulfat, Ammoniumthiosulfat, Natriumselenit. Besonders geeignet ist Uatriumxanthogenat oder Watriumselenit.
Geeignete Netzmittel sind Türkischrotöle, sulfonierte Oleatester, Fettalkoholsulfonate, z.B. Natriumlaurylsulfat, Alkylarylsulfonate, z.B. Dlbutyl-Natriuranaphtalinsulfonat. Als besonders geeignet . hat sich rlatriumlaurylsulfat erwiesen.
Die aus einem Bad gemäß der Erfindung erhaltenen Silber/Graphit-Di spersionsubermge können nach entsprechender Vorbehandlung - evtl.
70981 3/0866
VPA 75 P 7565 BRD
unter Verwendung von Zwischenschichten - auf Stahl, Kupfer- oder Kupferlegierungen, Aluminium, Nickel, Molybdän oder Wolf ram niedergeschlagen werden.
Graphithaltige Oberflächenschichten finden vielfach als Kontaktschichten Verwendung. Sie können z.B. für Relaiskontakte oder auch für andere Zwecke, etwa zur Auskleidung von Lagern, eingesetzt werden.
Die Erfindung wird durch die folgenden Beispiele näher erläutert.
Beispiel 1
Metallgegenstände werden nach einer in der Galvanotechnik üblichen Vorbehandlung in einem Elektrolyten folgender Zusammensetzung mit einem Silber/Graphit-Dispersionsüberzug beschichtet.
Kaliumsilbercyanid K JAg(CN)2] 2co3 46 g/l
Kaliumcyanid KCN "~ 75 g/l
Kaliumcarbonat K 20 g/l
Graphit, Korngröße 1-5 /um 20 g/l
Natriumxanthogenat 0 ,075 g/l
Türkischrotöl 5 g/l
Natriumlaurylsulfat 0 ,17 g/l
Temperatur 3O°C
Stromdichte 2 A/dm ,4 Gew.%
Schichtdicke 15 /um
Graphitgehalt des Überzuges O
Beispiel 2
Metallgegenstände werden nach einer in der Galvanotechnik üblichen Vorbehandlung in einem Elektrolyten folgender Zusammensetzung mit einem Silber/Graphit-Dispersionsüberzug beschichtet:
709813/086'β
VPA 75 P 7565 BRD
Kaliumsilbercyanid 3a. 1-5 K(Ag(CN)2J 46 g/l
Kaliumcyanid KCN 75 g/l
Kaliumcarbonat K2CO3 20 g/l
Graphit, Korngröße ( 3C Cm. J
/um
/		 50 g/l
Dithiocarbamat A/dm2 . o, 1 g/l
Natriumlaurylsulfat /um o, 45 g/l
Temperatur 3OC Graphitgehalt des Überzuges
Stromdichte 2 Beispiel 3
Schichtdicke 15
1,0 Gew.%
Metallgegenstände werden nach einer in der Galvanotechnik üblichen Vorbehandlung in einem Elektrolyten folgender Zusammensetzung mit einem Silber/Graphit-Dispersionsüberzug beschichtet:
Kaliumsilbercyanid KpIg(CN)II 46 g/l
Kaliumcyanid KCN 75 g/l
Kaliumcarbonat K2CO, 20 g/l Graphit, Körngröße 1-5 /um 75 g/l
Natriumselenit '2 g/l
Natriumlaurylsulfat 0,7 g/l
Temperatur 30°C
Stromdichte 1 A/dm2
Schichtdicke 15 /Um
Graphitgehalt des Überzuges 2,3 Gew.%
5 Patentansprüche
0 Figuren
709813/0866

Claims (5)

VPA-75 P 7565 BRD Patentansprüche
1. Cyanidischer Silberelektrolyt zur galvanischen Abscheidung von Silber/Graphit-Dispersionsüberzügen, dadurch gekennzeichnet, daß er 10 bis 100 g/l Graphit der Korngröße 1 bis 10 /um, 0,02 bis 5 g/l eines für Silberbäder geeigneten Glanzzusatzes und 0,05 bis 2 g/l eines für alkalische Elektrolyte geeigneten Netzmittels enthält.
2. Cyanidischer Silberelektrolyt nach Anspruch 1, dadurch gekennzeichnet, daß er als Glanzbildner Natriumxanthogenat oder Natriumselenit enthält.
3. Cyanidischer Silberelektrolyt nach Anspruch 1, dadurch gekennzeichnet, daß er als Netzmittel Natriumlaurylsulfat enthält.
4. Verfahren zur Herstellung von Silber/Graphit-Dispersionsüberzügen mit einem Bad gemäß Anspruch 1 bis 3, dadurch gekennzeichnet, daß bei einer Temperatur von 25 bis 30 C und einer Stromdichte von 1 bis 5 A/dm abgeschieden wird.
5. Verwendung eines Bades nach Anspruch 1 bis 3 zur Herstellung von Silber/Graphit-Dispersionsüberzügen bei Relaiskontakten.
70981 3/0866
DE2543082A 1975-09-26 1975-09-26 Cyanidischer Silberelektrolyt und Verfahren zur galvanischen Abscheidung von Silber-Graphit-Dispersionsüberzügen und seine Anwendung Expired DE2543082C3 (de)