CN1830344B - 一种抗菌海绵橡胶鞋用中底及其生产方法 - Google Patents

一种抗菌海绵橡胶鞋用中底及其生产方法 Download PDF

Info

Publication number
CN1830344B
CN1830344B CN2005100534762A CN200510053476A CN1830344B CN 1830344 B CN1830344 B CN 1830344B CN 2005100534762 A CN2005100534762 A CN 2005100534762A CN 200510053476 A CN200510053476 A CN 200510053476A CN 1830344 B CN1830344 B CN 1830344B
Authority
CN
China
Prior art keywords
rubber
antibacterial
antiseptic
spoonga
zinc oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2005100534762A
Other languages
English (en)
Other versions
CN1830344A (zh
Inventor
梁高勇
张建春
陈绮梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Quartermaster Research Institute of General Logistics Department of CPLA
Original Assignee
Quartermaster Research Institute of General Logistics Department of CPLA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quartermaster Research Institute of General Logistics Department of CPLA filed Critical Quartermaster Research Institute of General Logistics Department of CPLA
Priority to CN2005100534762A priority Critical patent/CN1830344B/zh
Publication of CN1830344A publication Critical patent/CN1830344A/zh
Application granted granted Critical
Publication of CN1830344B publication Critical patent/CN1830344B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种抗菌海绵橡胶鞋用中底及其生产方法，由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，所述鞋用中底的硬度为45-55，回弹性为50-55％，压缩永久变形5-15％，视密度为0.7-0.8，所述鞋用中底对金黄色葡萄球菌的抑菌宽度为10-20毫米，对大肠杆菌的抑菌宽度为10-25毫米，对枯草杆菌的抑菌宽度为9-13毫米。本发明具有较高的抗菌性能，可以明显的消除臭味，使用本发明制成的胶鞋具有穿着卫生、减轻重量、缓弹等优点。

Description

一种抗菌海绵橡胶鞋用中底及其生产方法
技术领域
本发明涉及一种抗菌海绵橡胶鞋用中底及其生产方法，该抗菌海绵橡胶鞋用中底，除具有较好的拉伸强度、弹性模量和弯曲强度以外还具有较高的抗菌性能。
背景技术
在已有技术中，海绵橡胶鞋用中底是具有多孔结构的橡胶发泡材料，也称之为微孔橡胶中底。通常，海绵橡胶鞋用中底大多以天然橡胶、合成橡胶为主要原料，加入发泡剂、硫化剂、促进剂、填充剂等辅料，经混炼工艺加工而成，海绵橡胶鞋用中底有一定的强度、硬度和刚度。因此，缓冲、减震一直是海绵橡胶鞋用中底的主要考核指标，而穿着的卫生性能并没有得到足够的重视，在实际的使用中，海绵橡胶鞋用中底会产生较大的臭味，特别是在胶鞋穿着过程中更为明显。目前，国内外还没有比较好的办法消除这种臭味。因此，需要开发出一种抗菌海绵橡胶鞋用中底及其生产方法。
发明内容
本发明的目的在于提供一种抗菌海绵橡胶鞋用中底及其生产方法，该生产方法采用新配方、特殊混炼工艺生产出了卫生性能良好的抗菌鞋用中底。
本发明的目的是由下述技术方案实现的：一种抗菌海绵橡胶鞋用中底，所述鞋用中底由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，所述鞋用中底的硬度为45-55，回弹性为50-55％，压缩永久变形5-15％，视密度为0.7-0.8，所述鞋用中底对金黄色葡萄球菌的抑菌宽度为10-20毫米，对大肠杆菌的抑菌宽度为10-25毫米，对枯草杆菌的抑菌宽度为9-13毫米。
一种抗菌海绵橡胶鞋用中底的生产方法，所述鞋用中底由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，所述混炼工艺为：使用炼胶机，辊温为45-55℃，加入橡胶后，压炼2-3分钟，加入氧化锌、硬脂酸、防老剂、抗菌剂，压炼2-5分钟，加二分之一填料，二分之一软化剂，压炼5-8分钟，再加入剩下的二分之一填料，二分之一软化剂，混炼5-8分钟，经薄通、停放，使用前在炼胶机上加入硫磺。
本发明与已有技术相比具有如下的优点：
1、本发明具有较好的拉伸强度、弹性模量、弯曲强度和压缩永久变形。
2、本发明具有广谱、有效的抗菌性能，可以明显的消除臭味，对人体安全。
3、使用本发明制成的胶鞋具有穿着卫生、减轻重量、缓弹等优点。
具体实施方式
实施例一：
一种抗菌海绵橡胶鞋用中底，由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，所述鞋用中底成份的重量比为：
天然橡胶      100    硫磺          1.5-2
氧化锌        3-5    硫化促进剂    1.2-2
硬脂酸        1-5    软化剂        12-25
防老剂        1-2    填料          90-100
抗菌剂        1-5
制成的鞋用中底的物理特性为：
邵A海绵硬度45-55      回弹性50-55％
压缩永久变形5-15％    视密度0.7-0.8
在本实施例中，所述鞋用中底对金黄色葡萄球菌的抑菌宽度为10-20毫米，对大肠杆菌的抑菌宽度为10-25毫米，对枯草杆菌的抑菌宽度为9-13毫米。
在本实施例中，所述抗菌剂可以是有机抗菌剂，也可以是无机抗菌剂，还可以有机、无机抗菌剂混用。要求抗菌剂在胶料中分散均匀，以免影响发泡质量。
在本实施例中，所述有机抗菌剂可以是多氯碳酸苯氨、双胍葡萄糖酸盐、异噻唑磷酮混合物、氟喹诺酮混合物、甲壳素、大麻粉体、活性炭中的一种，所述有机抗菌剂可以单用或多种并用。
在本实施例中，所述无机抗菌剂可以是氧化锌、氧化锌晶须、氯化钠、银粉或银系化合物中的一种，所述无机抗菌剂可以单用或多种并用。
在本实施例中，所述抗菌剂可以是无机抗菌剂和有机抗菌剂中的两种或多种混合并用。
在本实施例中，所述硫化促进剂可以是二苯胍、二硫化二苯丙噻唑、2-硫醇基本并噻唑中的一种，所述硫化促进剂可以单用或多种并用。
在本实施例中，所述软化剂可以是机油或石蜡。
在本实施例中，所述防老剂可以是聚羟基对苯基甲酸锌、聚羟基苯乙烯化二苯氨、双酚A、4-甲基-6-叔丁基苯酚锌盐中的一种，所述防老剂可以单用或多种并用。
在本实施例中，所述填料可以是陶土或碳酸钙。
本发明的抗菌海绵橡胶鞋用中底除了具有较好的拉伸强度、弹性模量和弯曲强度以外，最大的特点就是抗菌性能较高适于制作微孔、闭孔式的海绵橡胶，如制作各种抗菌鞋内底、中底或鞋垫等海绵橡胶制品。当然，本发明的抗菌海绵橡胶也可作鞋底，鞋底由密实橡胶和抗菌海绵橡胶组合而成，密实橡胶为外底，有防滑花纹，具有穿着卫生、减轻重量、缓弹等优点。
实施例二：
一种抗菌海绵橡胶鞋用中底的生产方法，由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，所述混炼工艺为：使用炼胶机，辊温为45-55℃，加入橡胶后，压炼2-3分钟，加入氧化锌、硬脂酸、防老剂、抗菌剂，压炼2-5分钟，加二分之一填料，二分之一软化剂，压炼5-8分钟，再加入剩下的二分之一填料，二分之一软化剂，混炼5-8分钟，经薄通、停放，使用前在炼胶机上加入硫磺。

Claims (5)

1.一种抗菌海绵橡胶鞋用中底，所述鞋用中底由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，其特征在于：所述鞋用中底成份的重量比为：
天然橡胶      100    硫磺          1.5-2
氧化锌        3-5    硫化促进剂    1.2-2.0
硬脂酸        1-5    软化剂        12-25
防老剂        1-2    填料          90-100
抗菌剂        1-5。
2.根据权利要求1所述的抗菌海绵橡胶鞋用中底，其特征在于：所述抗菌剂是氧化锌、氧化锌晶须、氯化钠、银粉或银系化合物中的一种或多种。
3.根据权利要求1所述的抗菌海绵橡胶鞋用中底，其特征在于：所述抗菌剂是多氯碳酸苯氨、双胍葡萄糖酸盐、异噻唑磷酮混合物、氟喹诺酮混合物、甲壳素、大麻粉体、活性炭中的一种或多种。
4.根据权利要求1所述的抗菌海绵橡胶鞋用中底，其特征在于：所述抗菌剂是无机抗菌剂和有机抗菌剂中的两种或多种混合并用。
5.权利要求1所述抗菌海绵橡胶鞋用中底的生产方法，所述鞋用中底由天然橡胶、氧化锌、硬脂酸、硫磺、硫化促进剂、软化剂、防老剂、填料、抗菌剂经过混炼、硫化、发泡制成，其特征在于：所述混炼工艺为：使用炼胶机，辊温为45-55℃，加入橡胶后，压炼2-3分钟，加入氧化锌、硬脂酸、防老剂、抗菌剂，压炼2-5分钟，加二分之一填料，二分之一软化剂，压炼5.8分钟，再加入剩下的二分之一填料，二分之一软化剂，混炼5-8分钟，经薄通、停放，使用前在炼胶机上加入硫磺。
CN2005100534762A 2005-03-11 2005-03-11 一种抗菌海绵橡胶鞋用中底及其生产方法 Expired - Fee Related CN1830344B (zh)