CN1225566C - 用作排放汽车废气的管道构件的铁素体不锈钢 - Google Patents
用作排放汽车废气的管道构件的铁素体不锈钢 Download PDFInfo
- Publication number
- CN1225566C CN1225566C CNB02813138XA CN02813138A CN1225566C CN 1225566 C CN1225566 C CN 1225566C CN B02813138X A CNB02813138X A CN B02813138XA CN 02813138 A CN02813138 A CN 02813138A CN 1225566 C CN1225566 C CN 1225566C
- Authority
- CN
- China
- Prior art keywords
- quality
- steel
- stainless steel
- ferritic stainless
- formability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
号 | 合金化元素(质量%) | |||||||||||||
C | Si | Mn | Ni | Cr | Nb | Ti | Mo | Cu | Al | B | V | N | [Nb] | |
1 | 0.015 | 0.31 | 0.15 | 0.10 | 17.09 | 0.35 | _ | 0.01 | 0.85 | 0.01 | _ | 0.10 | 0.009 | 0.16 |
2 | 0.010 | 0.28 | 0.17 | 0.11 | 17.13 | 0.36 | _ | 0.01 | 1.50 | 0.01 | _ | 0.11 | 0.008 | 0.22 |
3 | 0.008 | 0.32 | 0.05 | 0.10 | 17.02 | 0.33 | _ | 0.01 | 1.93 | 0.01 | _ | 0.10 | 0.010 | 0.19 |
4 | 0.012 | 0.33 | 0.22 | 0.09 | 10.71 | 0.35 | _ | _ | 1.42 | 0.01 | _ | 0.12 | 0.011 | 0.17 |
5 | 0.011 | 0.39 | 0.50 | 0.09 | 14.01 | 0.38 | _ | _ | 1.45 | 0.01 | 30 | 0.12 | 0.006 | 0.24 |
6 | 0.007 | 0.21 | 0.16 | 0.21 | 19.52 | 0.33 | _ | _ | 1.51 | 0.01 | 20 | 0.11 | 0.008 | 0.21 |
7 | 0.007 | 0.81 | 0.18 | 0.12 | 12.03 | 0.31 | 0.15 | 0.04 | 1.50 | 0.03 | 10 | 0.06 | 0.006 | 0.21 |
8 | 0.011 | 0.30 | 1.21 | 0.10 | 17.44 | 0.36 | 0.20 | 0.03 | 1.53 | 0.03 | 50 | 0.03 | 0.009 | 0.20 |
9 | 0.011 | 0.36 | 0.12 | 0.11 | 17.42 | 0.21 | 0.11 | 0.09 | 1.51 | 0.02 | 150 | 0.04 | 0.007 | 0.07 |
10 | 0.028 | 0.33 | 0.31 | 0.11 | 17.40 | 0.45 | 0.07 | 0.02 | 1.48 | 0.01 | 20 | 0.04 | 0.021 | 0.06 |
号 | 合金化元素(质量%) | |||||||||||||
C | Si | Mn | Ni | Cr | Nb | Ti | Mo | Cu | Al | B | V | N | [Nb] | |
11 | 0.008 | 0.30 | 0.28 | 0.14 | 17.00 | 0.37 | _ | 0.02 | 0.60 | 0.03 | _ | _ | 0.011 | 0.22 |
12 | 0.010 | 0.36 | 0.28 | 0.17 | 16.99 | 0.38 | _ | 0.01 | 4.08 | 0.01 | _ | 0.04 | 0.012 | 0.20 |
13 | 0.008 | 1.38 | 0.26 | 0.17 | 17.06 | 0.41 | 0.01 | 0.01 | 1.48 | _ | _ | _ | 0.013 | 0.24 |
14 | 0.009 | 0.35 | 0.32 | 0.31 | 17.24 | 0.74 | _ | 0.01 | 2.48 | 0.02 | _ | 0.01 | 0.013 | 0.56 |
15 | 0.020 | 0.42 | 0.39 | 0.10 | 12.16 | 0.01 | 0.23 | 0.02 | _ | 0.02 | _ | - | 0.014 | -0.26 |
16 | 0.011 | 1.10 | 0.98 | 0.10 | 14.75 | 0.50 | _ | 0.01 | 0.03 | _ | _ | _ | 0.012 | 0.31 |
17 | 0.012 | 0.40 | 0.70 | 0.22 | 18.28 | 0.50 | _ | 1.94 | 0.24 | 0.01 | 20 | 0.04 | 0.011 | 0.32 |
18 | 0.011 | 0.82 | 0.25 | 0.11 | 17.42 | 0.45 | 0.01 | 0.02 | 1.69 | 0.34 | 20 | 0.01 | 0.021 | 0.19 |
19 | 0.012 | 0.31 | 0.29 | 0.11 | 19.55 | 0.20 | 0.01 | _ | 0.82 | _ | _ | 0.02 | 0.008 | 0.04 |
号 | 800℃时0.2%屈服应力(N/mm2) | 非正常氧化的极限温度(℃) | 锻造后的延伸率(%) | 转变温度(℃) | 极限应变 | |
1 | 35454743444445433635 | 1000100010008509001000950100010001000 | 34323134333232343532 | -50-50-50-50-50-50-50-50-50-50 | ○○○○○○○○○○ | 本发明实施例 |
2 | ||||||
3 | ||||||
4 | ||||||
5 | ||||||
6 | ||||||
7 | ||||||
8 | ||||||
9 | ||||||
10 | ||||||
11 | 2450454718 25354030 | 100095011001000850950100010001000 | 3429 28303735323132 | -50-250 0-75-50-250-25 | ○× × ×○○○○○ | 对比例 |
12 | ||||||
13 | ||||||
14 | ||||||
15 | ||||||
16 | ||||||
17 | ||||||
18 | ||||||
19 |
Claims (3)