CN1210883A - 一种润滑油催化脱蜡催化剂 - Google Patents
一种润滑油催化脱蜡催化剂 Download PDFInfo
- Publication number
- CN1210883A CN1210883A CN 97116407 CN97116407A CN1210883A CN 1210883 A CN1210883 A CN 1210883A CN 97116407 CN97116407 CN 97116407 CN 97116407 A CN97116407 A CN 97116407A CN 1210883 A CN1210883 A CN 1210883A
- Authority
- CN
- China
- Prior art keywords
- catalyzer
- zsm
- molecular sieve
- lubricating oil
- aluminum oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
氧化铝 | CO2法氧化铝 | 普通氧化铝 |
弱酸,% | 62 | 40~60 |
中强酸,% | 30 | 25~40 |
强酸,% | 8 | 15~25 |
组成和性质 | 指标 |
组分含量: | |
H-ZSM-5,w% | 55~75 |
Al2O3,w% | 20~30 |
WO3,w% | 10~18 |
NiO,w% | 2~5 |
物化性质: | |
孔容,cm3/g | 0.10~0.30 |
比表面,m2/g | 180~300 |
堆积密度,g/cm3 | 0.88~0.95 |
NH3-TPD总酸量 | 0.30~0.40 |
强酸量比率,% | 2~6 |
催化剂 | 本发明 | 参比剂A | 参比剂B | |
沸石种类 | ZSM-5 | ZSM-5 | ZSM-8 | |
氧化铝 | CO2法 | 小孔Al2O3 | Al2O3+无定型Si-Al | |
NiO,w% | 4.82 | 3 | 6.4 | |
WO3,w% | 15.25 | 10 | ||
孔容,cm3/g | 0.157 | 0.18 | 0.184 | |
比表面,m2/g | 206 | >250 | 292 | |
平均孔径,nm | 2.26 | 2.0 | 2.5 | |
工艺条件 | ||||
压力,MPa | 4.0 | 8.0 | 4.0 | 8.0 |
温度,℃ | 300 | 330 | 390 | 290 |
空速,h-1 | 1.0 | 1.0 | 1.0 | 1.0 |
氢油比(v) | 500 | 800 | 500 | 800 |
产品分布,w% | ||||
>320℃ | 79.8 | 76.1 | 70.7 | 77.1 |
总液收,w% | 85.3 | 80.4 | 83.6 | 82.2 |
>320℃馏分油性: | ||||
倾点,℃ | -17 | -35 | -15 | -23 |
粘度,mm2/s 40℃ | 54.74 | 56.20 | 59.7 | 54.86 |
粘度指数(Ⅵ) | 69 | 68 | 70 | 70 |
名称 | 盘锦VGO加氢尾油 |
密度,kg/m3馏程,℃IBP/10%30%/50%70%/90%95%/EBP硫,μg/g氮,μg/g运动粘度,mm2/s100℃倾点,℃残炭,w%蜡含量,w% | 866.4323/377401/412427/450463/4814.53.05.54350.0215.60 |
Claims (7)