CN111234167A - 一种高稳定型有机硅改性型水性聚氨酯的制备方法 - Google Patents
一种高稳定型有机硅改性型水性聚氨酯的制备方法 Download PDFInfo
- Publication number
- CN111234167A CN111234167A CN202010257329.1A CN202010257329A CN111234167A CN 111234167 A CN111234167 A CN 111234167A CN 202010257329 A CN202010257329 A CN 202010257329A CN 111234167 A CN111234167 A CN 111234167A
- Authority
- CN
- China
- Prior art keywords
- modified
- waterborne polyurethane
- stability
- stirring
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)