CN110272552A - 一种石墨烧结用聚酰亚胺薄膜的制备方法 - Google Patents
一种石墨烧结用聚酰亚胺薄膜的制备方法 Download PDFInfo
- Publication number
- CN110272552A CN110272552A CN201910537474.2A CN201910537474A CN110272552A CN 110272552 A CN110272552 A CN 110272552A CN 201910537474 A CN201910537474 A CN 201910537474A CN 110272552 A CN110272552 A CN 110272552A
- Authority
- CN
- China
- Prior art keywords
- kapton
- preparation
- heat conduction
- sintering
- conduction material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)