CN109735113A - 一种液晶屏贴合用透明硅凝胶 - Google Patents
一种液晶屏贴合用透明硅凝胶 Download PDFInfo
- Publication number
- CN109735113A CN109735113A CN201811646793.9A CN201811646793A CN109735113A CN 109735113 A CN109735113 A CN 109735113A CN 201811646793 A CN201811646793 A CN 201811646793A CN 109735113 A CN109735113 A CN 109735113A
- Authority
- CN
- China
- Prior art keywords
- general formula
- liquid crystal
- crystal display
- silicone gel
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种液晶屏贴合用透明硅凝胶，原料配方包括组分A35‑55份；组分B10‑25份；组分C2‑15份；粘结促进剂5份；组分E5‑25份；催化剂0.1‑5份；抑制剂0.1‑1.0份；所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：所述组分C为乙烯基MQ硅树脂，M:Q比值为0.8‑1.5；所述组分E为符合通式(3)的端侧氢聚硅氧烷。本发明制得的液晶屏贴合用透明硅凝胶，具有粘度低、脱泡时间短、固化成型快、硬度适中的优点。
Description
技术领域
本发明涉及一种液晶屏贴合用透明硅凝胶，属于胶粘材料技术领域。
背景技术
传统的液晶屏贴合过程中存在以下问题：一方面，光线在显示屏内传播过程中，存在介质折光率不匹配而产生的炫光问题；另一方面，触摸屏三个模组需要经过两次贴合，成本高，工序多，造成的不良也相对较多。
通常情况下有机硅体系硅凝胶作为屏幕贴合用液态光学胶，由于固化后的折射率与玻璃几乎一致，且贴合后的厚度通常控制在0.1mm～0.2mm左右，所以采用此技术的屏幕具有轻盈、纤薄、显示效果好等优点。同时，硅凝胶具有一定的韧性、高断裂伸长率及阻尼减震等优势，但通常用于液晶屏贴合用硅凝胶粘度较高(＞1000厘泊)，而随着粘度变低，交联密度增加，固化后硅凝胶硬度较硬，贴合后存在粘性下降、冷热冲击效果差及阻尼效果衰减等问题。
发明内容
本发明的目的在于提供一种液晶屏贴合用透明硅凝胶。
为实现上述目的及其他相关目的，本发明提供的技术方案是：一种液晶屏贴合用透明硅凝胶，所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝100-300；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝50-200；
所述组分C为乙烯基MQ硅树脂，M:Q比值为0.8-1.5；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝50-200、y＝10-50。
优选的技术方案为：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为200-500厘泊。
优选的技术方案为：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为100-300厘泊。
优选的技术方案为：所述组分C的粘度范围为5000-8000厘泊。
优选的技术方案为：所述粘接促进剂为γ-缩水甘油醚氧丙基三甲氧基硅烷、2-(3，4-环氧环己烷基)乙基三甲氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷中的至少一种。
优选的技术方案为：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为50-500厘泊。
优选的技术方案为：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为3000-5000ppm。
优选的技术方案为：所述铂金属用量为原料配方混合总量的2-20ppm。
优选的技术方案为：所述抑制剂为3-甲基-1-丁炔-3-醇、1-乙炔基环己醇和四乙烯基环四硅氧烷中的至少一种。
由于上述技术方案运用，本发明与现有技术相比具有的优点是：
本发明制得的液晶屏贴合用透明硅凝胶，一方面具有粘度低(混合粘度低于500厘泊)、脱泡时间短、固化成型快、硬度适中的优点；另一方面，柔性聚醚链节的引入提供硅凝胶柔曲性、延伸性、抗冲击、阻尼减震及高的剥离和撕裂强度，克服传统低粘度硅凝胶固化硬度高的缺点，可广泛用于不同工艺、多种尺寸的液晶屏贴合使用。
具体实施方式
以下由特定的具体实施例说明本发明的实施方式，熟悉此技术的人士可由本实施例所揭露的内容轻易地了解本发明的其他优点及功效。
本文中使用的术语的目的仅在于说明特别实施例，并不意图对本发明做限制。除非上下文明确显示，否则本文中使用的单数形式“一”、“一个”亦包括复数形式。
在说明较佳实施例时，可能基于清楚的目的而使用特别的术语；然而，本说明书所揭露者并不意图被限制在所选择的该特别术语；并且应当理解，每一个特定元件包括具有相同功能、以相似方式操作并达成相似效果的所有等效技术。
实施例1：一种液晶屏贴合用透明硅凝胶
一种液晶屏贴合用透明硅凝胶，所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝1200；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝120；
所述组分C为乙烯基MQ硅树脂，M:Q比值为1.2；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝120、y＝30。
优选的实施方式为：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为350厘泊。
优选的实施方式为：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为200厘泊。
优选的实施方式为：所述组分C的粘度范围为6500厘泊。
优选的实施方式为：所述粘接促进剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷。
优选的实施方式为：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为270厘泊。
优选的实施方式为：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为4000ppm。
优选的实施方式为：所述铂金属用量为原料配方混合总量的10ppm。
优选的实施方式为：所述抑制剂为1-乙炔基环己醇。
液晶屏贴合用透明硅凝胶的制备方法：上述组合物按照比例，在不锈钢、搪瓷或玻璃容器内混合均匀后，过滤灌装在指定规格包装容器内即可。经检测，液晶屏贴合用透明硅凝胶的粘度为350厘泊。
实施例2：一种液晶屏贴合用透明硅凝胶
一种液晶屏贴合用透明硅凝胶，所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝100；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝50；
所述组分C为乙烯基MQ硅树脂，M:Q比值为0.8；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝50、y＝10。
优选的实施方式为：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为200厘泊。
优选的实施方式为：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为100厘泊。
优选的实施方式为：所述组分C的粘度范围为5000厘泊。
优选的实施方式为：所述粘接促进剂为γ-缩水甘油醚氧丙基三甲氧基硅烷、2-(3，4-环氧环己烷基)乙基三甲氧基硅烷按照1：5的质量比例构成的混合物。
优选的实施方式为：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为50厘泊。
优选的实施方式为：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为3000ppm。
优选的实施方式为：所述铂金属用量为原料配方混合总量的2ppm。
优选的实施方式为：所述抑制剂为1-乙炔基环己醇和四乙烯基环四硅氧烷按照1：1的质量比例构成的混合物。
经检测，液晶屏贴合用透明硅凝胶的粘度为220厘泊。
实施例3：一种液晶屏贴合用透明硅凝胶
一种液晶屏贴合用透明硅凝胶，所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝300；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝200；
所述组分C为乙烯基MQ硅树脂，M:Q比值为1.5；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝200、y＝50。
优选的实施方式为：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为500厘泊。
优选的实施方式为：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为300厘泊。
优选的实施方式为：所述组分C的粘度范围为8000厘泊。
优选的实施方式为：所述粘接促进剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷。
优选的实施方式为：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为500厘泊。
优选的实施方式为：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为5000ppm。
优选的实施方式为：所述铂金属用量为原料配方混合总量的20ppm。
优选的实施方式为：所述抑制剂为四乙烯基环四硅氧烷。
经检测，液晶屏贴合用透明硅凝胶的粘度为150厘泊。
实施例4：一种液晶屏贴合用透明硅凝胶
一种液晶屏贴合用透明硅凝胶，所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝190；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝70；
所述组分C为乙烯基MQ硅树脂，M:Q比值为1.2；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝170、y＝43。
优选的实施方式为：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为290厘泊。
优选的实施方式为：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为300厘泊。
优选的实施方式为：所述组分C的粘度范围为7800厘泊。
优选的实施方式为：所述粘接促进剂为2-(3，4-环氧环己烷基)乙基三甲氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三甲氧基硅烷按照1：1：1的质量比例构成的混合物。
优选的实施方式为：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为500厘泊。
优选的实施方式为：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为4500ppm。
优选的实施方式为：所述铂金属用量为原料配方混合总量的17ppm。
优选的实施方式为：所述抑制剂为1-乙炔基环己醇。
经检测，液晶屏贴合用透明硅凝胶的粘度为400厘泊。
以上所述者仅为用以解释本发明之较佳实施例，并非企图具以对本发明做任何形式上之限制，是以，凡有在相同之发明精神下所作有关本发明之任何修饰或变更，皆仍应包括在本发明意图保护之范畴。
Claims (9)
1.一种液晶屏贴合用透明硅凝胶，其特征在于：所述液晶屏贴合用透明硅凝胶的原料配方包括下列重量份的原料：
所述组分A为符合通式(1)的乙烯基封端的聚硅氧烷：
(CH3)2(CH2＝CH)SiO1/2[(CH3)2SiO2/2]n (1)；
通式(1)中，n＝100-300；
所述组分B为符合通式(2)的端烯丙氧基聚氧化丙烯：
CH2＝CHCH2O(C3H6O)mCH2CH＝CH2 (2)；
通式(2)中，m＝50-200；
所述组分C为乙烯基MQ硅树脂，M:Q比值为0.8-1.5；
所述组分E为符合通式(3)的端侧氢聚硅氧烷：
R(CH3)2SiO1/2[(CH3)2SiO2/2]x[CH3RSiO2/2]y (3)
通式(3)中，R＝H、x＝50-200、y＝10-50。
2.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述符合通式(1)的乙烯基封端的聚硅氧烷的粘度范围为200-500厘泊。
3.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述符合通式(2)的端烯丙氧基聚氧化丙烯的粘度范围为100-300厘泊。
4.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述组分C的粘度范围为5000-8000厘泊。
5.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述粘接促进剂为γ-缩水甘油醚氧丙基三甲氧基硅烷、2-(3，4-环氧环己烷基)乙基三甲氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷中的至少一种。
6.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述符合通式(3)的端侧氢聚硅氧烷的粘度范围为50-500厘泊。
7.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述催化剂为铂金属络合物，所述铂金属络合物中铂金属的质量浓度为3000-5000ppm。
8.根据权利要求7所述的液晶屏贴合用透明硅凝胶，其特征在于：所述铂金属用量为原料配方混合总量的2-20ppm。
9.根据权利要求1所述的液晶屏贴合用透明硅凝胶，其特征在于：所述抑制剂为3-甲基-1-丁炔-3-醇、1-乙炔基环己醇和四乙烯基环四硅氧烷中的至少一种。