CN108706875A - 双层蓝色流晶釉及其制作方法 - Google Patents
双层蓝色流晶釉及其制作方法 Download PDFInfo
- Publication number
- CN108706875A CN108706875A CN201810772861.XA CN201810772861A CN108706875A CN 108706875 A CN108706875 A CN 108706875A CN 201810772861 A CN201810772861 A CN 201810772861A CN 108706875 A CN108706875 A CN 108706875A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- ground
- coat enamel
- deck
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种双层蓝色流晶釉及其制作方法,双层蓝色流晶釉含有底釉和面釉;其中,所述底釉使用的底釉料中含有的组分及各组分质量份如下:钾长石30~35份;方解石8~10份;氧化锌20~23份;白云石10~15份;碳酸锂3~5份;石英12~15份;氧化铁2~4份;氧化钴2~4份;所述面釉使用的面釉料中含有的组分及各组分质量份如下:钾长石30~35份;钠长石15~20份;氧化锌10~12份;方解石8~12份;锂辉石8~12份;碳酸锂2~5份;氧化钛7~8份。本发明提高了面釉的流动性能,保证了双层釉之间的熔融效果。
Description
技术领域
本发明涉及一种双层蓝色流晶釉及其制作方法。
背景技术
目前,随着人们对古董收藏的热忱不断的增高,生活的各类家具,日用餐具都渐渐的趋近于古香古色,也将掀起一阵复古风。
发明内容
本发明所要解决的技术问题是克服现有技术的缺陷,提供一种双层蓝色流晶釉,它提高了面釉的流动性能,保证了双层釉之间的熔融效果。
为了解决以上技术问题,本发明的技术方案是:一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石30~35份;方解石8~10份;氧化锌20~23份;白云石10~15份;碳酸锂3~5份;石英12~15份;氧化铁2~4份;氧化钴2~4份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石30~35份;钠长石15~20份;氧化锌10~12份;方解石8~12份;锂辉石8~12份;碳酸锂2~5份;氧化钛7~8份。
本发明还提供了一种双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
进一步,面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。
采用了上述技术方案后,本发明以广大群众需求为背景,为广大群众提供喜爱的复古类的日用餐具产品,该釉在1270℃的抽屉窑中烧成,适应于大批量生产,因为无序排列的特性,所以成就了每个产品的单一性,深受广大客户的青睐,本发明提高了面釉的流动性能,保证了双层釉之间的熔融效果。
具体实施方式
为了使本发明的内容更容易被清楚地理解,下面根据具体实施例,对本发明作进一步详细的说明。
实施例一
一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石30份;方解石8份;氧化锌20份;白云石10份;碳酸锂3份;石英12份;氧化铁2份;氧化钴2份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石30份;钠长石15份;氧化锌10份;方解石8份;锂辉石8份;碳酸锂2份;氧化钛7份。
该双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。
实施例二
一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石35份;方解石10份;氧化锌23份;白云石15份;碳酸锂5份;石英15份;氧化铁4份;氧化钴4份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石35份;钠长石20份;氧化锌12份;方解石12份;锂辉石12份;碳酸锂5份;氧化钛8份。
该双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。
实施例三
一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石32份;方解石9份;氧化锌21份;白云石12份;碳酸锂4份;石英13份;氧化铁3份;氧化钴3份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石32份;钠长石17份;氧化锌11份;方解石10份;锂辉石10份;碳酸锂3份;氧化钛7份。
该双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。
比较例一
一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石30份;方解石8份;氧化锌20份;白云石10份;石英12份;氧化铁2份;氧化钴2份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石30份;钠长石15份;氧化锌10份;方解石8份;锂辉石8份;碳酸锂2份;氧化钛7份。
该双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。
比较例二
一种双层蓝色流晶釉,它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石30份;方解石8份;氧化锌15份;白云石10份;石英12份;氧化铁2份;氧化钴2份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石30份;钠长石15份;氧化锌10份;方解石8份;锂辉石8份;碳酸锂2份;氧化钛7份。
该双层蓝色流晶釉的制作方法,方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛。
比较例一:流动效果较弱,不能满足设计理念。
比较例二:结晶效果较弱,不能满足设计理念。
实施例一至实施例三:符合此研发的目的,为理想中的效果。
以上所述的具体实施例,对本发明所要解决的技术问题、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种双层蓝色流晶釉,其特征在于它含有底釉和面釉;其中,
所述底釉使用的底釉料中含有的组分及各组分质量份如下:
钾长石30~35份;方解石8~10份;氧化锌20~23份;白云石10~15份;碳酸锂3~5份;石英12~15份;氧化铁2~4份;氧化钴2~4份;
所述面釉使用的面釉料中含有的组分及各组分质量份如下:
钾长石30~35份;钠长石15~20份;氧化锌10~12份;方解石8~12份;锂辉石8~12份;碳酸锂2~5份;氧化钛7~8份。
2.一种如权利要求1所述的双层蓝色流晶釉的制作方法,其特征在于方法的步骤中含有:
S1:分别制备面釉料和底釉料;
S2:将干净的坯体上底釉料后烘干;
S3:将上好底釉料的坯体上面刷面釉料,在1270℃的抽屉窑中烧制而成。
3.根据权利要求2所述的制备方法,其特征在于:面釉料和底釉料的制备工艺为:按釉料︰球︰水的质量比=1︰1.7︰0.6,湿法球磨14~16小时,球磨后的釉料过200目筛后,调制成51~53波美浓度待用。