CN1080909A - 片状晶形轻质碳酸钙的制备方法 - Google Patents

片状晶形轻质碳酸钙的制备方法 Download PDF

Info

Publication number
CN1080909A
CN1080909A CN 93108625 CN93108625A CN1080909A CN 1080909 A CN1080909 A CN 1080909A CN 93108625 CN93108625 CN 93108625 CN 93108625 A CN93108625 A CN 93108625A CN 1080909 A CN1080909 A CN 1080909A
Authority
CN
China
Prior art keywords
calcium carbonate
preparation
light calcium
boride
control agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 93108625
Other languages
English (en)
Other versions
CN1032912C (zh
Inventor
袁伟
金鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING COLLEGE OF CHEMICAL TECHNOLOGY
Beijing University of Chemical Technology
Original Assignee
BEIJING COLLEGE OF CHEMICAL TECHNOLOGY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING COLLEGE OF CHEMICAL TECHNOLOGY filed Critical BEIJING COLLEGE OF CHEMICAL TECHNOLOGY
Priority to CN 93108625 priority Critical patent/CN1032912C/zh
Publication of CN1080909A publication Critical patent/CN1080909A/zh
Application granted granted Critical
Publication of CN1032912C publication Critical patent/CN1032912C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明是一种片状晶形轻质碳酸钙的制备方 法。本发明采用硼化物做晶形控制剂，用液相一步碳 化法制备片状晶形良好的轻质碳酸钙。本发明采用 的晶形控制剂硼化物，具有毒性低，价格便宜的优点， 又采用一步法生产工艺，具有操作人员操作安全、简 便的优点，并适合工业化生产。

Description

本发明涉及一种片状晶形轻质碳酸钙的制备方法。
轻质碳酸钙在造纸、塑料、橡胶和涂料中被广泛用作填料。片状晶形轻质填料能使表面的平整度和光洁度提高，特别是在造纸行业中，可用来代替片状高领土，在制造高级纸时供表面涂敷用。
片状轻质碳酸钙的研制始自八十年代。由于碳酸钙的稳定晶体形状一般是链状、纺锤状和立方体状，而不是片状的，因此现有的研究路线多数采用两步碳化法。即首先在液相中将Ca（OH）2用CO2碳化到一定程度，将片状的中间产物分离出来，再在不致改变晶体形状的条件下完成后半程的碳化反应来制取片状晶形轻质碳酸钙（日本专利昭58-193495，昭63-50316，昭61-219715，昭61-219717，德国专利 DE-3245103），由于反应步骤分割成二步，致使工艺复杂且第二步碳化的工艺，能耗较多，故二步法生产工艺存在有工艺复杂、耗能增多、成本上升的缺点，以致至今未能工业化。
1990年日本专利（平2-184519）提出使用晶形控制剂有机膦的方法，来一步碳化制取片状碳酸钙。具体工艺为，在一定浓度的石灰乳溶液中（CaO+H2O），通入一定流速的CO2，反应十分钟后添加有机膦，继续通CO2至碳化完全。产品经过滤、干燥后即得直径为1-2μ、厚度为0.1-0.2μ的片状粒子的轻质碳酸钙。该工艺较二步法简单，具有可推广的基础，但由于所用晶形控制剂有机膦价格昂贵、毒性较大、且从该专利说明书所附电子显微镜照片看到所制备的片状晶形碳酸钙片状晶形不太理想，因此其工业化前景并不妙。
本发明的目的是用硼化物做晶形控制剂，用液相一步碳化法制备片状晶形良好的轻质碳酸钙。
本发明的技术方案为：按剂量配比，在水中加入CaO，配成石灰乳溶液，控制到一定温度，通入以一定流量CO2，加入晶形控制剂硼化物，再继续通入CO2，直到碳化完全。产品经过滤、干燥得到片状晶形轻质碳酸钙。
上述工艺中所使用的晶形控制剂硼化物，可以是硼酸、硼砂、Na3B3O6、K3B3O6、K2[B5O8（OH）]2H2O、B2H6、HBO2、B2O3、BX3，其加入量为CaO量的0.3%-3.5%。
硼化物在反应开始及反应过程中加入均可，以反应中加入效果为好。
本反应温度可控制在0-25℃，CO2流量控制在每克CaO0.2-1.2ml/秒，石灰乳浓度为CaO3-18g/100ml水。
本发明的效果：本发明采用价廉、低毒的硼化物做晶形控制剂，用液相一步碳化法制备片状晶形轻质碳酸钙，具有操作人员操作安全、简便的优点，并适合工业化生产。通过本发明制备的片状晶形碳酸钙的扫描电镜照片看到，该碳酸钙的片状晶形良好，比用日本专利有机膦做为晶形控制剂生产的轻质碳酸钙的扫描电镜照片效果好。
图1、日本专利（平2-184519）制备的片状晶形轻质CaCO3扫描电镜照片。
图2、用本发明（实施例1）制备的片状晶形轻质CaCO3的扫描电镜照片。
实施例1：
制备浓度为10克CaO/100ml水的石灰乳150ml，待温度降到18℃时，通CO2，速率为0.5ml/秒。起始电导率为7.2×103μS/cm，反应半小时后加0.1克H3BO3，继续通CO2直到电导率降为1×103μS/cm，反应时间2小时40分产品过滤，100℃下干燥后得25克。用扫描电子显微镜观察晶形，如图2所示。其晶粒平均直径为1-2μ，片径与片厚之比为5∶1到10∶1。
比较例1：
除不加H3BO4外，其它条件与实施例1相同。反应时间3小时，产品重25克，扫描电子显微镜照片表明，多数为粒状和立方体状晶体。
实施例2：
将CaO600g加入于6升水中，待温度降至20℃时通CO2，流量为0.17M3/h，反应半小时后加10克H3BO3，继续通CO2，使电导率由起始的5.8×103μS/cm降至小于1×103μS/cm，得碳酸钙1公斤。扫描电子显微镜照片表明，晶体为片状多边形，平均直径1μ，片径5片厚之比大于10∶1。
实施例3：
加8克CaO于100ml水中，待温度降至15℃时，通CO2流量为0.6ml/秒，起始电导率为6.2×103μS/cm，反应20分钟后加0.2克硼砂，继续通CO2直到电导率小于1×103μS/cm。反应时间2小时10分。产品过滤、干燥。扫描电子显微镜照片表明，晶体为片状多边形，平均直径2μ，片径与片厚之比为5∶1至8∶1。

Claims (3)

1、一种通过用晶形控制剂并采用液相一步碳化法制备片状晶形轻质碳酸钙的方法，按剂量配比，在水中加入CaO，配成石灰乳溶液，控制到一定温度，通入以一定流量CO2，加入晶形控制剂，再继续通入CO2，直到碳化完全，产品经过滤、干燥得到片状晶形轻质碳酸钙，其特征在于：所用的晶形控制剂是硼化物。
2、根据权利要求1所述的制备方法，其特征在于：硼化物可以是硼酸、硼砂、Na3B3O6、K3B3O6、K2[B5O8（OH）]2H2O、B2H6、HBO2、B2O3、BX3其加入量为CaO量的0.3%-3.5%。
3、根据权利要求1所述的制备方法，其特征在于：硼化物在反应开始及反应过程中加入均可，以反应中加入效果为好。
CN 93108625 1993-07-15 1993-07-15 片状晶形轻质碳酸钙的制备方法 Expired - Fee Related CN1032912C (zh)