CN107869077A - 一种涤棉色织布的制作工艺 - Google Patents

一种涤棉色织布的制作工艺 Download PDF

Info

Publication number
CN107869077A
CN107869077A CN201711208769.2A CN201711208769A CN107869077A CN 107869077 A CN107869077 A CN 107869077A CN 201711208769 A CN201711208769 A CN 201711208769A CN 107869077 A CN107869077 A CN 107869077A
Authority
CN
China
Prior art keywords
polyester
dyeing
yarn
cotton
dyed fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711208769.2A
Other languages
English (en)
Inventor
张永辉
刘海瑞
王文元
孙亚楠
朱枝群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU MINGYUAN TEXTILE CO Ltd
Original Assignee
JIANGSU MINGYUAN TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU MINGYUAN TEXTILE CO Ltd filed Critical JIANGSU MINGYUAN TEXTILE CO Ltd
Priority to CN201711208769.2A priority Critical patent/CN107869077A/zh
Publication of CN107869077A publication Critical patent/CN107869077A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种涤棉色织布的制作工艺，包括以下工艺步骤：选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.46～0.48g/cm³；染色工序所需的水在染色前加入0.2～0.4 g/L的硫酸钠，并搅拌8～10min，在水温35～40℃下，先加入碳酸钠，12～15min后再加入硫酸钠12～15min，等温度上升至62℃时，保持42～46 min。本发明提高染色的效果，染色更加的均匀，保证染色的重新性，使用防静电剂使涤纶纱线上的静电性降低了，有利于从整体降低了织造完成的涤棉色织织物的静电率，另外也降低三跳以及断纱和沉纱，提高上浆率。

Description

一种涤棉色织布的制作工艺
技术领域
本发明属于纺织技术领域，尤其涉及一种涤棉色织布的制作工艺。
背景技术
色织布是用染色的纱线织成的织物，给纱染色一般分为色纺纱和染色纱二种方式，通常说的色织布是指梭织机织的布，但针织机也同样可以做出色织针织布，色织布根据原材料的不同可以分为色织棉布、色织涤棉布、色织中长仿毛花呢、全毛花呢、毛涤花呢、毛涤粘三合一花呢、竹节纱布、疙瘩纱布等等，还有以丝麻为原材料的色织布很多；涤棉色织布中采用了涤纶作为原料，涤纶容易产生静电，因此对于织造完成的涤棉色织布来说必不可免的会产生静电，另外，在色织布的织造过程中，染色是尤其重要的，但是目前在染色过程中会出现染色的不均，染色的效果不理想，鉴于此，需要对面料的生产工艺进行改进。
发明内容
为解决现有技术的不足，本发明提供保证染色的均匀，提高染色的效果的一种涤棉色织布的制作工艺。
本发明所采用的技术方案为：一种涤棉色织布的制作工艺，其特征在于：包括以下工艺步骤：
(1)选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.46～0.48g/cm3；染色工序所需的水在染色前加入0.2～0.4g/L的硫酸钠，并搅拌8～10min，在水温35～40℃下，先加入碳酸钠，12～15min后再加入硫酸钠12～15min，等温度上升至62℃时，保持42～46min；
(2)将烘干后的涤棉混纺纱线在室温环境下，浸泡在混合液中，浸泡5～8h，然后捞出烘干，做成备用涤棉混纺纱线；
(3)将备用涤棉混纺纱线依次进行浆纱、穿综、织造、胚检、烧毛、退浆、丝光、定型、预缩、成检工序，成检合格后制成涤棉色织布，其中，在穿综工序中，采用的是飞穿法，布边每边是26根，每综2根，每筘4根，在浆纱的工序中，采用的是聚乙烯醇，在54～58℃下上浆，在烧毛工序中，烧毛温度是55～60℃，车速是110～120m/min，在定型工序中，定型的温度是185～190℃，车速是30～40m/s。
作为本发明的进一步优选，所述的涤棉混纺纱线是含有60％的涤纶和40％的棉纱混纺纱线。作为本发明的进一步优选，所述的混合液包括按照质量比20∶1的防静电剂和瑞香提取液。作为本发明的进一步优选，所述的混合液包括去离子水80～85份、醋酸盐8～10份、丙酮 5～8份、异氰酸酯3～5份、氧氯丙烷15～20份和甲苯10～15份。
作为本发明的进一步优选，步骤(1)所述的煮练工序中煮练的时间是55～65min，煮练的温度是95～100℃。
作为本发明的进一步优选，步骤(2)所述的室温环境的温度是25～28℃，室温环境的湿度是70～75％。
本发明的有益效果在于：本发明提高染色的效果，染色更加的均匀，保证染色的重新性，使用防静电剂使涤纶纱线上的静电性降低了，有利于从整体降低了织造完成的涤棉色织织物的静电率，另外也降低三跳以及断纱和沉纱，提高上浆率。
具体实施方式：
下面结合实施例对本发明做具体的介绍。
实施例1
一种涤棉色织布的制作工艺，其特征在于：包括以下工艺步骤：
(1)选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.46g/cm3；染色工序所需的水在染色前加入0.2g/L的硫酸钠，并搅拌8min，在水温35℃下，先加入碳酸钠，12min后再加入硫酸钠12min，等温度上升至62℃时，保持42min；
(2)将烘干后的涤棉混纺纱线在室温环境下，浸泡在混合液中，浸泡5h，然后捞出烘干，做成备用涤棉混纺纱线；其中混合液包括按照质量比20∶1的防静电剂和瑞香提取液；
(3)将备用涤棉混纺纱线依次进行浆纱、穿综、织造、胚检、烧毛、退浆、丝光、定型、预缩、成检工序，成检合格后制成涤棉色织布，其中，在穿综工序中，采用的是飞穿法，布边每边是26根，每综2根，每筘4根，在浆纱的工序中，采用的是聚乙烯醇，在54℃下上浆，在烧毛工序中，烧毛温度是55℃，车速是110m/min，在定型工序中，定型的温度是 185℃，车速是30m/s。
本实施例中的涤棉混纺纱线是合有60％的涤纶和40％的棉纱混纺纱线。
本实施例中混合液包括去离子水80份、醋酸盐8份、丙酮5份、异氰酸酯3份、氧氯丙烷 15份和甲苯10份。
本实施例中步骤(1)所述的煮练工序中煮练的时间是55min，煮练的温度是95℃。
本实施例中步骤(2)所述的室温环境的温度是25～28℃，室温环境的湿度是70％。实施例2
一种涤棉色织布的制作工艺，其特征在于：包括以下工艺步骤：
(1)选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.47g/cm3；染色工序所需的水在染色前加入0.3g/L的硫酸钠，并搅拌9min，在水温38℃下，先加入碳酸钠，13min后再加入硫酸钠14min，等温度上升至62℃时，保持44min；
(2)将烘干后的涤棉混纺纱线在室温环境下，浸泡在混合液中，浸泡7h，然后捞出烘干，做成备用涤棉混纺纱线；其中混合液包括按照质量比20∶1的防静电剂和瑞香提取液；
(3)将备用涤棉混纺纱线依次进行浆纱、穿综、织造、胚检、烧毛、退浆、丝光、定型、预缩、成检工序，成检合格后制成涤棉色织布，其中，在穿综工序中，采用的是飞穿法，布边每边是26根，每综2根，每筘4根，在浆纱的工序中，采用的是聚乙烯醇，在56℃下上浆，在烧毛工序中，烧毛温度是58℃，车速是115m/min，在定型工序中，定型的温度是 187℃，车速是35m/s。
本实施例中的涤棉混纺纱线是含有60％的涤纶和40％的棉纱混纺纱线。
本实施例中的混合液包括去离子水83份、醋酸盐9份、丙酮7份、异氰酸酯4份、氧氯丙烷17份和甲苯13份。
本实施例中的步骤(1)所述的煮练工序中煮练的时间是55～65min，煮练的温度是98℃。本实施例中的步骤(2)所述的室温环境的温度是25～28℃，室温环境的湿度是73％。
实施例3
一种涤棉色织布的制作工艺，其特征在于：包括以下工艺步骤：
(1)选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.48g/cm3；染色工序所需的水在染色前加入0.4g/L的硫酸钠，并搅拌10min，在水温40℃下，先加入碳酸钠，15min后再加入硫酸钠15min，等温度上升至62℃时，保持46min；
(2)将烘干后的涤棉混纺纱线在室温环境下，浸泡在混合液中，浸泡8h，然后捞出烘干，做成备用涤棉混纺纱线；其中混合液包括按照质量比20∶1的防静电剂和瑞香提取液；
(3)将备用涤棉混纺纱线依次进行浆纱、穿综、织造、胚检、烧毛、退浆、丝光、定型、预缩、成检工序，成检合格后制成涤棉色织布，其中，在穿综工序中，采用的是飞穿法，布边每边是26根，每综2根，每筘4根，在浆纱的工序中，采用的是聚乙烯醇，在58℃下上浆，在烧毛工序中，烧毛温度是60℃，车速是120m/min，在定型工序中，定型的温度是 190℃，车速是40m/s。
本实施例中的涤棉混纺纱线是含有60％的涤纶和40％的棉纱混纺纱线。
本实施例中的混合液包括去离子水85份、醋酸盐10份、丙酮8份、异氰酸酯5份、氧氯丙烷20份和甲苯15份。
本实施例中的步骤(1)所述的煮练工序中煮练的时间是65min，煮练的温度是100℃。
本实施例中的步骤(2)所述的室温环境的温度是28℃，室温环境的湿度是75％。
本发明提高染色的效果，染色更加的均匀，保证染色的重新性，使用防静电剂使涤纶纱线上的静电性降低了，有利于从整体降低了织造完成的涤棉色织织物的静电率，另外也降低三跳以及断纱和沉纱，提高上浆率。
以上所述仅是本发明专利的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明专利原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明专利的保护范围。

Claims (6)

1.一种涤棉色织布的制作工艺，其特征在于： 包括以下工艺步骤：
（1）选取涤棉混纺纱线，依次进行煮练、漂白、染色、皂煮、水洗、烘干工序，其中染色的方法采用的是经轴染色，在染色的过程，整经机的经纱的卷绕密度为0.46～0.48g/cm³；染色工序所需的水在染色前加入0.2～0.4 g/L的硫酸钠，并搅拌8～10min，在水温35～40℃下，先加入碳酸钠，12～15min后再加入硫酸钠12～15min，等温度上升至62℃时，保持42～46 min；
（2）将烘干后的涤棉混纺纱线在室温环境下，浸泡在混合液中，浸泡5～8h，然后捞出烘干，做成备用涤棉混纺纱线；
（3）将备用涤棉混纺纱线依次进行浆纱、穿综、织造、胚检、烧毛、退浆、丝光、定型、预缩、成检工序，成检合格后制成涤棉色织布，其中，在穿综工序中，采用的是飞穿法，布边每边是26根，每综2根，每筘4根，在浆纱的工序中，采用的是聚乙烯醇，在54～58℃下上浆，在烧毛工序中，烧毛温度是55～60℃，车速是110～120m/min，在定型工序中，定型的温度是185～190℃，车速是30～40m/s。
2.根据权利要求1所述的一种涤棉色织布的制作工艺，其特征在于，所述的涤棉混纺纱线是含有60%的涤纶和40%的棉纱混纺纱线。
3.根据权利要求1所述的一种涤棉色织布的制作工艺，其特征在于，所述的混合液包括按照质量比20：1的防静电剂和瑞香提取液。
4.根据权利要求1或3所述的一种涤棉色织布的制作工艺，其特征在于，所述的混合液包括去离子水80～85份、醋酸盐8～10份、丙酮5～8份、异氰酸酯3～5份、氧氯丙烷15～20份和甲苯10～15份。
5.根据权利要求1所述的一种涤棉色织布的制作工艺，其特征在于，步骤（1）所述的煮练工序中煮练的时间是55～65min，煮练的温度是95～100℃。
6.根据权利要求1所述的一种涤棉色织布的制作工艺，其特征在于，步骤（2）所述的室温环境的温度是25～28℃，室温环境的湿度是70～75%。
CN201711208769.2A 2017-11-27 2017-11-27 一种涤棉色织布的制作工艺 Pending CN107869077A (zh)