CN107841059A - Ps、pe共混增韧配方 - Google Patents

Ps、pe共混增韧配方 Download PDF

Info

Publication number
CN107841059A
CN107841059A CN201711168970.2A CN201711168970A CN107841059A CN 107841059 A CN107841059 A CN 107841059A CN 201711168970 A CN201711168970 A CN 201711168970A CN 107841059 A CN107841059 A CN 107841059A
Authority
CN
China
Prior art keywords
parts
formula
blending toughening
blending
sbs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711168970.2A
Other languages
English (en)
Inventor
黄风山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711168970.2A priority Critical patent/CN107841059A/zh
Publication of CN107841059A publication Critical patent/CN107841059A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种PS、PE共混增韧配方，每100份PS树脂配备：21～24份LDPE、11～14份PS‑b‑SBS。本发明显著提高韧性。

Description

PS、PE共混增韧配方
技术领域
本发明涉及一种高分子复合材料配方，特别是一种PS共混改性配方。
背景技术
PS共混改性材料广泛应用于板片、仪表，但韧性较低，易损坏。
发明内容
本发明针对现有技术的不足，提出一种能显著提高韧性的PS、PE共混增韧配方。
本发明通过下述技术方案实现技术目标。
PS、PE共混增韧配方，其改进之处在于：每100份PS树脂配备：21～24份LDPE、11～14份PS-b-SBS。
进一步改进在于：每100份PS树脂配备：22～23份LDPE、12～13份PS-b-SBS。
本发明与现有技术相比，具有以下积极效果：
1、PS、PE共混，显著提高韧性。
2、每100份PS树脂配备：22～23份LDPE、12～13份PS-b-SBS，可进一步提高韧性。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1：
PS、PE共混增韧配方，每100份PS树脂配备：21份LDPE、11份PS-b-SBS。
实施例2：
PS、PE共混增韧配方，每100份PS树脂配备：24份LDPE、14份PS-b-SBS。
实施例3：
PS、PE共混增韧配方，每100份PS树脂配备：22份LDPE、12份PS-b-SBS。
实施例4：
PS、PE共混增韧配方，每100份PS树脂配备：23份LDPE、13份PS-b-SBS。

Claims (2)

1.一种PS、PE共混增韧配方，其特征在于：每100份PS树脂配备：21～24份LDPE、11～14份PS-b-SBS。
2.根据权利要求1所述的PS、PE共混增韧配方，其特征在于：每100份PS树脂配备：22～23份LDPE、12～13份PS-b-SBS。
CN201711168970.2A 2017-11-21 2017-11-21 Ps、pe共混增韧配方 Pending CN107841059A (zh)