CN107262116A - 一种分级结构MoS2/Cu2S复合材料及其制备方法 - Google Patents
一种分级结构MoS2/Cu2S复合材料及其制备方法 Download PDFInfo
- Publication number
- CN107262116A CN107262116A CN201710398457.6A CN201710398457A CN107262116A CN 107262116 A CN107262116 A CN 107262116A CN 201710398457 A CN201710398457 A CN 201710398457A CN 107262116 A CN107262116 A CN 107262116A
- Authority
- CN
- China
- Prior art keywords
- mos
- composites
- preparation
- source
- hierarchy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种分级结构MoS2/Cu2S复合材料,它为由MoS2纳米片和Cu2S纳米片组装而成的呈花状结构的微纳米球,它以钼源、硫源、铜源和还原剂为原料进行水热反应而成。本发明利用水热法制备MoS2/Cu2S复合材料,涉及的原料来源广、成本低,工艺简单易行,产量大,可解决目前MoS2与其他材料复合的难点,并可改善MoS2在催化反应过程中电导率低的问题,所得复合材料表现出优异的光催化性能和电催化性能,适合推广应用。
Description
技术领域
本发明属于无机材料技术领域,具体涉及一种具有分级结构的MoS2/Cu2S复合材料及其制备方法。
背景技术
随着社会的发展,能源与环境问题也变得日益严峻。制备新型清洁能源来替代不可再生能源成为人们关注的热点,其中电催化制氢具有无毒、材料廉价易得且很少产生二次污染等优点,是一种十分有前景的技术。
MoS2作为一种纳米级层状结构的电催化材料,因其独特的电性能和优异的机械性能引起科学家关注。这类化合物是以金属原子层排布在两个硫原子片层形成三文治结构,硫原子片层间通过范德华力相互作用,一层一层迭加而形成稳定的层状结构。近来,一些研究者对其进行形貌调控及复合改性,使MoS2的电催化性能得到提升,从而使MoS2材料受到人们的广泛关注。但MoS2本身存在着与其他材料难复合,电导率低的问题,导致其在实际应用上受到限制。
发明内容
本发明的目的是提供一种具有分级结构的MoS2/Cu2S复合材料,该材料为MoS2纳米片和Cu2S纳米片组装而成的微纳球状,可表现出优异的电化学性能,且涉及的制备方法简单、原料常见易得、可重复性好,能够实现大规模生产。
为实现上述目的,本发明采用的技术方案为:
一种分级结构MoS2/Cu2S复合材料,它为由MoS2纳米片和Cu2S纳米片组装而成的呈花状结构的微纳米球。
上述方案中,所述微纳米球的直径为500~1000nm。
上述一种分级结构MoS2/Cu2S复合材料的制备方法,包括如下步骤:将钼源、硫源、铜源和还原剂加入到水和乙醇的混和溶液中搅拌混合均匀,然后将所得混合液加热进行水热反应,反应结束后进行抽滤、洗涤、干燥,即得所述分级结构MoS2/Cu2S复合材料。
上述方案中,所述钼源为钼酸钠。
上述方案中,所述硫源为硫代乙酰胺或硫脲。
上述方案中,所述铜源为硫酸铜或硝酸铜。
上述方案中,所述还原剂为乙二胺。
上述方案中,所述钼源、硫源、铜源的摩尔比为1:(2.5~7):(0.05~0.2)。
上述方案中,铜源与乙二胺的摩尔比为1:(900~2000)。
优选的,所述溶液中钼酸钠的浓度为0.025mol/L,所述溶液中硫代乙酰胺的浓度为0.075~0.15mol/L,所述溶液中硫酸铜的浓度为0.003-0.005mol/L。
优选的,所述乙二胺、水与乙醇的体积比为1:(0.5~2):(0.5~1)。
按上述方案,所述水热反应条件为:加热至180~220℃恒温反应24~48h。
优选的,所述水热反应条件为:加热至200℃恒温反应24h。
上述方案所述分级结构MoS2/Cu2S复合材料在光催化和电催化领域中的应用。
本发明的原理为:
本发明以钼源、硫源、铜源为主要原料,并以乙二胺为还原剂,采用水热法一步反应得到MoS2/Cu2S复合材料,在本发明所述反应体系中,MoS2自身属于一种层片状化合物,其二维材料的不稳定性使得在这个反应体系中为了降低自身表面能,反应所得的MoS2纳米片和Cu2S纳米片进一步进行自组装形成花状微纳米球,有效地实现了MoS2与Cu2S的复合,显著改善了MoS2在催化反应过程中,电导率低的问题;此外MoS2/Cu2S复合材料形成的异质结结构(光生电子空穴对分离机理原理图见图1)使得在光催化反应过程中可有效促进光生电子空穴对的分离,减少光生电子空穴的复合率,提高复合材料的量子效率,进而显著提高其光催化性能。
本发明的有益效果在于:
1)本发明所述分级结构MoS2/Cu2S复合材料,可实现MoS2与Cu2S的有效复合;此外其结构为纳米片组装而成的微纳米球,具有较大的比表面积和反应的活性位点,可表现出优异的光催化和电催化性能。
2)本发明涉及的原料廉价、易得,无需额外使用其他有毒有害的有机表面活性剂和添加剂,安全环保;且涉及的制备方法简单、反应条件温和、无需煅烧,符合符合绿色合成的制备理念。
附图说明
图1.MoS2/Cu2S复合样品形成异质结在光催化过程中光生电子空穴对分离机理图。
图2为本发明实施例1所制备的MoS2/Cu2S微纳球复合材料的XRD图;
图3为实施例1所制备的MoS2/Cu2S微纳球复合材料的SEM照片;
图4为实施例1所制备的MoS2/Cu2S微纳球复合材料的光催化性能图;
图5为实施例1所制备的MoS2/Cu2S微纳球复合材料的电催化性能图;
图6为实施例2所制备的MoS2/Cu2S微纳球复合材料的XRD图;
图7为实施例2所制备的MoS2/Cu2S微纳球复合材料的SEM照片;
图8为实施例3所制备的MoS2/Cu2S微纳球复合材料的XRD图;
图9为实施例3所制备的MoS2/Cu2S微纳球复合材料的SEM照片;
图10为实施例4所制备的MoS2/Cu2S微纳球复合材料的XRD图;
图11为实施例4所制备的MoS2/Cu2S微纳球复合材料的SEM照片。
具体实施方式
下面结合附图和实施例进一步对本发明进行说明,但本发明的内容不仅仅局限于下面的实施例。
实施例1
一种分级结构MoS2/Cu2S复合材料,其制备方法包括如下步骤:
将0.4g钼酸钠、0.4g硫代乙酰胺、0.04g五水硫酸铜加入到20mL乙二胺、40mL水和20mL乙醇的混和溶液中,搅拌混合均匀(搅拌温度为25℃,搅拌速率为700r/min),然后将所得混合液置于反应釜中,密闭后加热至200℃进行恒温晶化反应(水热反应),反应24h后进行抽滤、洗涤、再进行60℃干燥处理,得分级结构MoS2/Cu2S复合材料。
将本实施例所得产物经X射线衍射分析确定与六方晶型的MoS2和Cu2S相匹配,并且结晶度较好,其X射线衍射图见图2。扫描电镜结果显示(图3)所得产物为纳米片组装成的微纳米球,尺寸为1μm左右,该微纳米球由纳米片组装而成,有利于提供比表面积和增加反应的活性位点,并有利于溶液的浸润。
将本实施例所得产物进行光催化性能测试,光催化反应器为石英玻璃容器,器真空系统主要有玻璃真空管道组成,其光源为氙灯光源,型号为PLS-SXF300C,光强度为300W。测试系统为气相色谱仪,型号为美国安捷伦(GC),载气为高纯氩气,流速为40ml/min,热导检测器为7890B的TCD热导检测器。测试过程中,测试样品的质量为0.05g,溶剂为100mL蒸馏水,选用浓度均为0.1mol/L的Na2S和Na2SO3作为光催化反应的牺牲剂;具体步骤为:称量0.05g光催化剂(分级结构MoS2/Cu2S复合材料),加入100mL的水中,在磁力搅拌器上搅拌30min,使得样品均匀的分散在水溶液中得混合溶液;称量2.40g的九水硫化钠和1.26g的亚硫酸钠,作为光催化产氢反应的牺牲剂,加入上述混合液体中,再磁力搅拌器上继续搅拌30min,使其充分溶解,此时,硫化钠和亚硫酸钠的浓度均为0.1mol/L。然后再将上述混合溶液加入到光催化反应装置后,对装置进行抽真空处理;之后用氙灯光源进行照射,光源光强度为300W。利用气相色谱仪进行测试;(测试结果见图4)。结果表明,掺杂使得本实施例所得产物的光催化性能有所增强,降低了产物中光生电子和空穴的复合率,从而提高了样品的光催化性能。
将本实施例所得产物进行电催化性能测试,具体步骤为:4mg本实施例所得产物与30μL的Nafion溶液加入到0.75mL水、0.25ml乙醇的混合溶液中,超声一个小时混合均匀;然后取5μL的混合溶液样品滴到直径为3mm的玻碳电极上,然后在0.5M的H2SO4溶液中,用甘汞电极作为参比电极,铂电极为对电极,用线性伏安法,以5mV/s的速度进行测试(测试结果见图5)。结果表明:掺杂使得本实施例所得产物的导电性有所增强,有利于电荷的传输,从而提高了样品的电催化性能。
实施例2
一种分级结构MoS2/Cu2S复合材料,其制备方法包括如下步骤:
将0.4g钼酸钠、0.8g硫代乙酰胺、0.08g五水硫酸铜加入到20mL乙二胺、40mL水和20mL乙醇的混和溶液中,搅拌混合均匀(搅拌温度为25℃,搅拌速率为700r/min),然后将所得混合液置于反应釜中,密闭后加热至220℃进行恒温晶化反应(水热反应),反应48h后进行抽滤、洗涤、再进行60℃干燥处理,得分级结构MoS2/Cu2S复合材料。
本实施例所得产物经X射线衍射分析确定与六方晶型的MoS2和Cu2S相匹配,并且结晶度较好,其X射线衍射图见图6。扫描电镜结果显示(图7)所得产物为纳米片组装成的微纳米球,尺寸为0.5-1μm,该微纳米球由纳米片组装而成,有利于提供比表面积和增加反应的活性位点,并有利于溶液的浸润。
实施例3
一种分级结构MoS2/Cu2S复合材料,其制备方法包括如下步骤:
将0.4g钼酸钠、0.4g硫代乙酰胺、0.08g五水硫酸铜加入到40mL乙二胺、20mL水和20mL乙醇的混和溶液中,搅拌混合均匀(搅拌温度为25℃,搅拌速率为700r/min),得到溶液,然后将得到的溶液放入反应釜中,密闭后加热至180℃进行恒温晶化反应,反应24h后进行抽滤、洗涤、再于60℃干燥处理,得到分级结构的六方晶型的MoS2/Cu2S复合材料。
本实施例步骤中得到的产物经X射线衍射分析确定与六方晶型的MoS2和Cu2S相匹配,并且结晶度较好,其X射线衍射图见图8。扫面电子显微镜分析结果显示(图9)步骤中所得产物为纳米片组装的微纳球状,尺寸为0.5-1μm,微球由纳米片组装而成,有利于溶液的浸润。
实施例4
一种分级结构MoS2/Cu2S复合材料,其制备方法包括如下步骤:
将0.4g钼酸钠、0.4g硫脲、0.04g三水合硝酸铜加入到20mL乙二胺、40mL水和20mL乙醇的混和溶液中,搅拌混合均匀(搅拌温度为25℃,搅拌速率为700r/min),得到溶液,然后将得到的溶液放入反应釜中,密闭后加热至200℃进行恒温晶化反应,反应24h后进行抽滤、洗涤、再于60℃干燥处理,得到分级结构的六方晶型的MoS2/Cu2S复合材料。
本实施例步骤中得到的产物经X射线衍射分析确定与六方晶型的MoS2和Cu2S相匹配,并且结晶度较好,其X射线衍射图见图10。扫面电子显微镜分析结果显示(图11)步骤中所得产物为纳米片组装的微纳球状,尺寸为0.5-1μm,微球由纳米片组装而成,有利于溶液的浸润。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明的范围内。本发明要求保护范围由所附属的权利要求书及其等效物界定。
Claims (10)
1.一种分级结构MoS2/Cu2S复合材料,它为由MoS2纳米片和Cu2S纳米片组装而成的呈花状结构的微纳米球。
2.根据权利要求1所述的分级结构MoS2/Cu2S复合材料,其特征在于,所述微纳米球的直径为500~1000nm。
3.权利要求1或2所述分级结构MoS2/Cu2S复合材料的制备方法,其特征在于,包括如下步骤:将钼源、硫源、铜源和还原剂加入到水和乙醇的混和溶液中搅拌混合均匀,然后将所得混合液加热进行水热反应,反应结束后进行抽滤、洗涤、干燥,即得所述分级结构MoS2/Cu2S复合材料。
4.根据权利要求1所述的制备方法,其特征在于,所述钼源为钼酸钠。
5.根据权利要求1所述的制备方法,其特征在于,所述硫源为硫代乙酰胺或硫脲。
6.根据权利要求1所述的制备方法,其特征在于,所述铜源为硫酸铜或硝酸铜。
7.根据权利要求1所述的制备方法,其特征在于,所述还原剂为乙二胺。
8.根据权利要求1所述的制备方法,其特征在于,所述钼源、硫源、铜源的摩尔比为1:(2.5~7):(0.05~0.2)。
9.根据权利要求1所述的制备方法,其特征在于,所述铜源与乙二胺的摩尔比为1:(900~2000)。
10.根据权利要求1所述的制备方法,其特征在于,所述水热反应条件为:加热至180~220℃恒温反应24~48h。