CN105088292A - 一种金属材料的表面电镀方法 - Google Patents

一种金属材料的表面电镀方法 Download PDF

Info

Publication number
CN105088292A
CN105088292A CN201510573801.1A CN201510573801A CN105088292A CN 105088292 A CN105088292 A CN 105088292A CN 201510573801 A CN201510573801 A CN 201510573801A CN 105088292 A CN105088292 A CN 105088292A
Authority
CN
China
Prior art keywords
metallic substance
metal material
electroplating
minute
minutes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510573801.1A
Other languages
English (en)
Inventor
汪春洪
蒋建龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Ruimeike Materials Technology Co Ltd
Original Assignee
Suzhou Ruimeike Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Ruimeike Materials Technology Co Ltd filed Critical Suzhou Ruimeike Materials Technology Co Ltd
Priority to CN201510573801.1A priority Critical patent/CN105088292A/zh
Publication of CN105088292A publication Critical patent/CN105088292A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种金属材料的表面电镀方法，包括以下步骤：(1)对金属材料进行酸洗，将金属材料放入PH值为5-6的酸洗溶液中浸洗5-10分钟，以去除金属材料表面的杂质；(2)对金属材料进行碱洗，将金属材料放入PH值为8-9的碱洗溶液中浸洗5-8分钟，以去除金属材料表面的油污；(3)对金属材料进行水洗，将金属材料在清洁水中清洗3-5分钟；(4)将金属材料在硫酸铜溶液中接通电流密度为3A/dm2的电流进行电镀，电镀持续时间为3～4分钟。通过本发明的电镀方法对金属制品的表面进行电镀处理后，金属产品的表面光亮度高、耐磨、耐腐蚀。

Description

一种金属材料的表面电镀方法
技术领域
本发明涉及一种金属材料的表面电镀方法。
背景技术
金属制品的表面一般需要进行处理，以避免容易出现的生锈、表面光洁度差等问题。电镀是一种表面处理方法，但是电镀又容易产生污染，工艺难控制、成本高等问题。
发明内容
本发明主要解决的技术问题是提供一种金属材料的表面电镀方法，该电镀方法对金属制品的表面进行电镀处理后，金属产品的表面光亮度高、耐磨、耐腐蚀。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种金属材料的表面电镀方法，其包括以下步骤：
(1)对金属材料进行酸洗，将金属材料放入PH值为5-6的酸洗溶液中浸洗5-10分钟，以去除金属材料表面的杂质；
(2)对金属材料进行碱洗，将金属材料放入PH值为8-9的碱洗溶液中浸洗5-8分钟，以去除金属材料表面的油污；
(3)对金属材料进行水洗，将金属材料在清洁水中清洗3-5分钟；
(4)将金属材料在硫酸铜溶液中接通电流密度为3A/dm2的电流进行电镀，电镀持续时间为3～4分钟。
在本发明一个较佳实施例中，在电镀前，硫酸铜溶液中同时加入活性剂和稳定剂以及光亮剂，混合搅拌3-5分钟。
在本发明一个较佳实施例中，将电镀后金属材料在120°-150°温度下干燥。
在本发明一个较佳实施例中，所述活性剂为聚乙二醇。
本发明的有益效果是：本发明的电镀方法对金属制品的表面进行电镀处理后，金属产品的表面光亮度高、耐磨、耐腐蚀。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
一种金属材料的表面电镀方法，包括以下步骤：
(1)对金属材料进行酸洗，将金属材料放入PH值为5-6的酸洗溶液中浸洗5-10分钟，以去除金属材料表面的杂质；
(2)对金属材料进行碱洗，将金属材料放入PH值为8-9的碱洗溶液中浸洗5-8分钟，以去除金属材料表面的油污；
(3)对金属材料进行水洗，将金属材料在清洁水中清洗3-5分钟；
(4)将金属材料在硫酸铜溶液中接通电流密度为3A/dm2的电流进行电镀，电镀持续时间为3～4分钟。
优选地，在电镀前，硫酸铜溶液中同时加入活性剂和稳定剂以及光亮剂，混合搅拌3-5分钟。增加电镀后产品表面的稳定性。
优选地，将电镀后金属材料在120°-150°温度下干燥。
优选地，所述活性剂为聚乙二醇。
本发明金属材料的表面电镀方法的有益效果是：
本发明的电镀方法对金属制品的表面进行电镀处理后，金属产品的表面光亮度高、耐磨、耐腐蚀。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种金属材料的表面电镀方法，其特征在于，包括以下步骤：
(1)对金属材料进行酸洗，将金属材料放入PH值为5-6的酸洗溶液中浸洗5-10分钟，以去除金属材料表面的杂质；
(2)对金属材料进行碱洗，将金属材料放入PH值为8-9的碱洗溶液中浸洗5-8分钟，以去除金属材料表面的油污；
(3)对金属材料进行水洗，将金属材料在清洁水中清洗3-5分钟；
(4)将金属材料在硫酸铜溶液中接通电流密度为3A/dm2的电流进行电镀，电镀持续时间为3～4分钟。
2.根据权利要求1所述的金属材料的表面电镀方法，其特征在于，在电镀前，硫酸铜溶液中同时加入活性剂和稳定剂以及光亮剂，混合搅拌3-5分钟。
3.根据权利要求2所述的金属材料的表面电镀方法，其特征在于，将电镀后金属材料在120°-150°温度下干燥。
4.根据权利要求1所述的金属材料的表面电镀方法，其特征在于，所述活性剂为聚乙二醇。
CN201510573801.1A 2015-09-10 2015-09-10 一种金属材料的表面电镀方法 Pending CN105088292A (zh)