CN103694885B - 一种经有机硅树脂改性的漆包线漆及其制备方法 - Google Patents
一种经有机硅树脂改性的漆包线漆及其制备方法 Download PDFInfo
- Publication number
- CN103694885B CN103694885B CN201310640316.2A CN201310640316A CN103694885B CN 103694885 B CN103694885 B CN 103694885B CN 201310640316 A CN201310640316 A CN 201310640316A CN 103694885 B CN103694885 B CN 103694885B
- Authority
- CN
- China
- Prior art keywords
- silicone resin
- add
- wire enamel
- hour
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种经有机硅树脂改性的漆包线漆及其制备方法,其特征在于,由下列重量份的原料制成:有机硅树脂12-14、二甲基二氯硅烷5-7、2-氨乙基十七烯基咪唑啉1-2、硅藻土4-6、丙烯酸乙酯2-3、纳米硅藻土2-4、2-硫醇基苯骈咪唑2-5、抗氧剂1010?1-2、萤石粉3-6、甲基异噻唑啉酮2-3、尼龙12?20-24、1,6-己二异氰酸酯2-3、助剂7-9、间对甲酚100-120、二甲苯80-90;经有机硅树脂改性后的漆包线漆可使漆包线漆膜耐热程度得到有效的提高,生产工艺简便可靠,在常压条件下即可生产,产品的储存稳定性好。
Description
技术领域
本发明涉及一种漆包线漆,尤其是一种经有机硅树脂改性的漆包线漆及其制备方法。
背景技术
漆包线是一种电工材料,它是在一根圆形的铜线表面加工一层薄薄的高强度绝缘层,起到与外界绝缘的作用。按规格可加工成比发丝还细的毛丝线,像拇指般粗的纱包线。漆包线具有很好的绝缘效果和防水能力。在电器方面应用很广泛,如电动机,发电机,水泵,电磁铁,电焊机,家用电器,无线通讯,扬声器,电报机,变压器等。漆包线漆是生产漆包线的必要绝缘材料,漆包线漆要求具有良好的附着性、机械强度、绝缘性能、耐热性能、耐磨性能、耐盐雾及耐恶劣环境性能等,但是普通的漆包线漆存在耐热性、耐磨性差、强度不够、耐热级低于120℃等问题,难以满足不同环境的要求。需要对漆包线漆的配方与生产工艺进行改进,进一步提高漆包漆的性能,降低其生产成本。
发明内容
本发明的目的就是提供一种经有机硅树脂改性的漆包线漆及其制备方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种经有机硅树脂改性的漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:有机硅树脂12-14、二甲基二氯硅烷5-7、2-氨乙基十七烯基咪唑啉1-2、丙烯酸乙酯2-3、纳米硅藻土2-4、2-硫醇基苯骈咪唑2-5、抗氧剂10101-2、萤石粉3-6、甲基异噻唑啉酮2-3、尼龙1220-24、1,6-己二异氰酸酯2-3、助剂7-9、间对甲酚100-120、二甲苯80-90;
所述的助剂由下列重量份原料制成:纳米云母粉0.2-0.3、三乙醇胺1.2-1.3、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2-3、六次甲基四胺1-2、聚酯丙烯酸酯3-5、三羟甲基丙烷三丙烯酸酯12-15、柠檬酸三乙酯3-6、交联剂TAC1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。
所述的经有机硅树脂改性的漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到45-50℃,加入尼龙12,搅拌并加热到155-185℃,至尼龙12完全溶解后,再加入甲基异噻唑啉酮、2-氨乙基十七烯基咪唑啉、萤石粉,保温4-5小时;
(2)、将步骤(1)反应物料降温至75-80℃,加入二甲基二氯硅烷、丙烯酸乙酯、2-硫醇基苯骈咪唑、1,6-己二异氰酸酯、助剂,保持温度,搅拌反应2-3小时;
(3)、再加入剩余物料,升温至110-130℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。
本发明的经有机硅树脂改性的漆包线漆有以下有益效果:铜包铝电磁线生产过程中油漆的性能得到改善,有机硅树脂改性后的漆包线漆可使漆包线漆膜耐热程度得到有效的提高,生产工艺简便可靠,在常压条件下即可生产,产品的储存稳定性好。
具体实施方式
所述的经有机硅树脂改性的漆包线漆是由下列重量份(公斤)的原料制成:有机硅树脂12、二甲基二氯硅烷7、2-氨乙基十七烯基咪唑啉1、丙烯酸乙酯3、纳米硅藻土2、2-硫醇基苯骈咪唑2、抗氧剂10102、萤石粉3、甲基异噻唑啉酮2、尼龙1220、1,6-己二异氰酸酯3、助剂9、间对甲酚100、二甲苯80;
所述的助剂由下列重量份(公斤)原料制成:纳米云母粉0.2、三乙醇胺1.2、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2、六次甲基四胺2、聚酯丙烯酸酯5、三羟甲基丙烷三丙烯酸酯12、柠檬酸三乙酯3、交联剂TAC1、没食子酸丙酯2、薏仁油1;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。。
制备方法包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到45-50℃,加入尼龙12,搅拌并加热到155-185℃,至尼龙12完全溶解后,再加入甲基异噻唑啉酮、2-氨乙基十七烯基咪唑啉、萤石粉,保温4-5小时;
(2)、将步骤(1)反应物料降温至75-80℃,加入二甲基二氯硅烷、丙烯酸乙酯、2-硫醇基苯骈咪唑、1,6-己二异氰酸酯、助剂,保持温度,搅拌反应2-3小时;
(3)、再加入剩余物料,升温至110-130℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。
与现有技术相比本发明的经有机硅树脂改性的漆包线漆有以下有益效果:经有机硅树脂改性后的漆包线漆可使漆包线漆膜耐热程度得到有效的提高,生产工艺简便可靠,在常压条件下即可生产,产品的储存稳定性好。
使用本发明漆制线材主要性能指标如下:
1、附着性好;
2、耐热等级≥155℃,热冲击达到180℃漆膜不开裂;
3、粘结强度15N/mm2;
4、耐变压器油1200小时/105℃,漆膜无损坏。
Claims (2)
1.一种经有机硅树脂改性的漆包线漆,其特征在于,由下列重量份的原料制成:有机硅树脂12-14、二甲基二氯硅烷5-7、2-氨乙基十七烯基咪唑啉1-2、丙烯酸乙酯2-3、纳米硅藻土2-4、2-硫醇基苯骈咪唑2-5、抗氧剂10101-2、萤石粉3-6、甲基异噻唑啉酮2-3、尼龙1220-24、1,6-己二异氰酸酯2-3、助剂7-9、间对甲酚100-120、二甲苯80-90;
所述的助剂由下列重量份原料制成:纳米云母粉0.2-0.3、三乙醇胺1.2-1.3、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2-3、六次甲基四胺1-2、聚酯丙烯酸酯3-5、三羟甲基丙烷三丙烯酸酯12-15、柠檬酸三乙酯3-6、交联剂TAC1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。
2.根据权利要求1所述的经有机硅树脂改性的漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到45-50℃,加入尼龙12,搅拌并加热到155-185℃,至尼龙12完全溶解后,再加入甲基异噻唑啉酮、2-氨乙基十七烯基咪唑啉、萤石粉,保温4-5小时;
(2)、将步骤(1)反应物料降温至75-80℃,加入二甲基二氯硅烷、丙烯酸乙酯、2-硫醇基苯骈咪唑、1,6-己二异氰酸酯、助剂,保持温度,搅拌反应2-3小时;
(3)、再加入剩余物料,升温至110-130℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。