CN103694757B - 一种变压器用耐电晕漆包线漆及其制备方法 - Google Patents
一种变压器用耐电晕漆包线漆及其制备方法 Download PDFInfo
- Publication number
- CN103694757B CN103694757B CN201310640299.2A CN201310640299A CN103694757B CN 103694757 B CN103694757 B CN 103694757B CN 201310640299 A CN201310640299 A CN 201310640299A CN 103694757 B CN103694757 B CN 103694757B
- Authority
- CN
- China
- Prior art keywords
- wire enamel
- hydroxyethyl
- add
- resistant wire
- corona
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种变压器用耐电晕漆包线漆,是由下列重量份(公斤)的原料制成:纳米氮化铝粉10-12、氨基树脂9-12、四(2-羟乙基)己二酰胺3-4、三(2-羟乙基)异氰尿酸酯2-3、苯乙烯2-3、硅烷偶联剂KH560?2-3、二月桂酸二丁基锡2-3、烟片胶1-2、云母粉2-3、聚乙烯醇3-4、尼龙11?12-15、助剂7-9、二甲苯100-120、间对甲酚100-120;漆液透明的变压器用耐电晕漆包线漆,可直接用于涂制耐电晕漆包线,解决了以往的纳米型变压器用耐电晕漆包线漆与漆液不相溶、沉淀、漆液粘度高以及涂制漆包线工艺繁杂的问题;本发明制备工艺简单,操作方便;提高了漆包线漆的绝缘性能和耐磨性能。
Description
技术领域
本发明涉及一种漆包线漆,尤其是一种变压器用耐电晕漆包线漆及其制备方法。
背景技术
漆包线是一种电工材料,它是在一根圆形的铜线表面加工一层薄薄的高强度绝缘层,起到与外界绝缘的作用。按规格可加工成比发丝还细的毛丝线,像拇指般粗的纱包线。漆包线具有很好的绝缘效果和防水能力。在电器方面应用很广泛,如电动机,发电机,水泵,电磁铁,电焊机,家用电器,无线通讯,扬声器,电报机,变压器等。漆包线漆是生产漆包线的必要绝缘材料,漆包线漆要求具有良好的附着性、机械强度、绝缘性能、耐热性能、耐磨性能、耐盐雾及耐恶劣环境性能等,但是普通的漆包线漆存在耐热性、耐磨性差、强度不够、耐热级低于120℃等问题,难以满足不同环境的要求。需要对漆包线漆的配方与生产工艺进行改进,进一步提高漆包漆的性能,降低其生产成本。
发明内容
本发明的目的就是提供一种变压器用耐电晕漆包线漆及其制备方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种变压器用耐电晕漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:纳米氮化铝粉10-12、氨基树脂9-12、四(2-羟乙基)己二酰胺3-4、三(2-羟乙基)异氰尿酸酯2-3、苯乙烯2-3、硅烷偶联剂KH5602-3、二月桂酸二丁基锡2-3、烟片胶1-2、云母粉2-3、聚乙烯醇3-4、尼龙1112-15、助剂7-9、二甲苯100-120、间对甲酚100-120;
所述的助剂由下列重量份原料制成:纳米云母粉0.2-0.3、三乙醇胺1.2-1.3、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2-3、六次甲基四胺1-2、聚酯丙烯酸酯3-5、三羟甲基丙烷三丙烯酸酯12-15、柠檬酸三乙酯3-6、交联剂TAC1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。
所述的变压器用耐电晕漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到35-45℃,加入尼龙11,搅拌并加热到146-188℃,至尼龙11完全溶解后,再加入四(2-羟乙基)己二酰胺、聚乙烯醇、苯乙烯、云母粉,保温5-6小时;
(2)、将步骤(1)反应物料降温至60-80℃,加入硅烷偶联剂KH560、三(2-羟乙基)异氰尿酸酯、助剂,保持温度,搅拌反应1-3小时;
(3)、再加入剩余物料,升温至125-140℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。
本发明有以下优点:1.本发明制备工艺简单,操作方便;2.纳米氮化铝粉的加入提高漆包线漆的绝缘性能和耐磨性能;3.漆液透明的变压器用耐电晕漆包线漆,可直接用于涂制耐电晕漆包线,解决了以往的纳米型变压器用耐电晕漆包线漆与漆液不相溶、沉淀、漆液粘度高以及涂制漆包线工艺繁杂的问题。
具体实施方式
所述的变压器用耐电晕漆包线漆是由下列重量份(公斤)的原料制成:纳米氮化铝粉10、氨基树脂9、四(2-羟乙基)己二酰胺4、三(2-羟乙基)异氰尿酸酯2、苯乙烯2、硅烷偶联剂KH5602、二月桂酸二丁基锡2、烟片胶1、云母粉2、聚乙烯醇4、尼龙1112、助剂7、二甲苯100、间对甲酚100;
所述的助剂由下列重量份(公斤)原料制成:纳米云母粉0.2、三乙醇胺1.2、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2、六次甲基四胺2、聚酯丙烯酸酯5、三羟甲基丙烷三丙烯酸酯12、柠檬酸三乙酯3、交联剂TAC1、没食子酸丙酯2、薏仁油1;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。。
制备方法包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到35-45℃,加入尼龙11,搅拌并加热到146-188℃,至尼龙11完全溶解后,再加入四(2-羟乙基)己二酰胺、聚乙烯醇、苯乙烯、云母粉,保温5-6小时;
(2)、将步骤(1)反应物料降温至60-80℃,加入硅烷偶联剂KH560、三(2-羟乙基)异氰尿酸酯、助剂,保持温度,搅拌反应1-3小时;
(3)、再加入剩余物料,升温至125-140℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。
与现有技术相比,本发明制备工艺简单,操作方便;由于纳米氮化铝粉的加入,提高了漆包线漆的绝缘性能和耐磨性能;漆液透明的变压器用耐电晕漆包线漆,可直接用于涂制耐电晕漆包线,解决了以往的纳米型变压器用耐电晕漆包线漆与漆液不相溶、沉淀、漆液粘度高以及涂制漆包线工艺繁杂的问题。
使用本发明漆制线材主要性能指标如下:
1、耐磨性好;
2、耐热等级≥145℃,热冲击达到180℃漆膜不开裂;
3、粘结强度14N/mm2;
4、耐变压器油1200小时/105℃,漆膜无损坏。
Claims (2)
1.一种变压器用耐电晕漆包线漆,其特征在于,由下列重量份的原料制成:纳米氮化铝粉10-12、氨基树脂9-12、四(2-羟乙基)己二酰胺3-4、三(2-羟乙基)异氰尿酸酯2-3、苯乙烯2-3、硅烷偶联剂KH5602-3、二月桂酸二丁基锡2-3、烟片胶1-2、云母粉2-3、聚乙烯醇3-4、尼龙1112-15、助剂7-9、二甲苯100-120、间对甲酚100-120;
所述助剂由下列重量份原料制成:纳米云母粉0.2-0.3、三乙醇胺1.2-1.3、异丙基三(二辛基焦磷酸酰氧基)钛酸酯2-3、六次甲基四胺1-2、聚酯丙烯酸酯3-5、三羟甲基丙烷三丙烯酸酯12-15、柠檬酸三乙酯3-6、交联剂TAC1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将聚酯丙烯酸酯、三羟甲基丙烷三丙烯酸酯、柠檬酸三乙酯混合,加热至60-70℃,加入交联剂TAC、没食子酸丙酯、薏仁油,搅拌反应30-40分钟,再加入其它剩余成分,继续搅拌反应1-2小时,即得。
2.根据权利要求1所述的变压器用耐电晕漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到35-45℃,加入尼龙11,搅拌并加热到146-188℃,至尼龙11完全溶解后,再加入四(2-羟乙基)己二酰胺、聚乙烯醇、苯乙烯、云母粉,保温5-6小时;
(2)、将步骤(1)反应物料降温至60-80℃,加入硅烷偶联剂KH560、三(2-羟乙基)异氰尿酸酯、助剂,保持温度,搅拌反应1-3小时;
(3)、再加入剩余物料,升温至125-140℃,继续搅拌反应2-3小时;
(4)、冷却物料至50-60℃,研磨至20-40μm浆料,过滤即得。